Boundary trend of α1/(α1 +α2) phase region at lower Cu side in Al-Zn-Cu system

The range of miscibility gap above 300 ℃ at low Cu side in Al-Cu-Zn ternary system was obtained by EPMA of the designed alloys and diffusion-couples treated for equilibrium. The results about the boundary trend of the α1 / (α1 α2 ) phase region was obtained. The α1 / (α1 α2 ) boundary moves towards the lower Zn side with the increase of Cu content. The results are opposite to traditional phase diagrams obtained by experiments, but consistent with recent thermodynamic calculations.     

基于HTTP用WORD向Web服务器提交数据

就各类项目管理中的普遍需求,研究了基于HTTP协议在WORD中直接提交数据(离线填写、在线申报)的技术路线及其实现,进一步分析提出自动生成WORD模板的可行性;同时基于流行通用的J2EE开源框架SSH2,研究设计了接收WORD模板所提交数据的服务器端Web应用架构.     

Mg-Zn-Al三元系富镁角335°C等温截面(英文)

采用平衡合金法,利用X射线衍射、扫描电镜及能谱分析,系统地研究了Mg-Zn-Al三元系富镁角335°C的平衡相组成及其成分。从实验上证实,α-Mg固溶体并不与Mg32(Al,Zn)49(τ)三元金属间化合物或q准晶相平衡,而仅与一个三元化合物Al5Mg11Zn4(φ)相平衡。获得了φ相在335°C的整个成分范围,即:52.5%~56.4%Mg、13.6%~24.0%Al、19.6%~33.9%Zn(摩尔分数)。Al在Mg Zn相中的固溶度远大于在Mg7Zn3相中的固溶度,其最大值可达8.6%Al(摩尔分数)。Al和Zn可以同时固溶在α-Mg固溶体中。     

消灭火炬 节约能源 增加收益

前言曙光化工厂裂解尾气,从建厂投产以来,一直作为燃料用气,并将多余的尾气送入火炬烧掉。1980年10月,对尾气组成进行分析的结果表明,在尾气中含有大量的乙烯、丙烯等有用成份。但是,过去对这一宝贵资源没有合理利用而白白烧掉,是一个极大的浪费。为此,1981年组织制订了回收这部分尾气的方案,并于1982年2月,尾气压缩机系     

管范畴中的短正合列的进一步研究

讨论管范畴中模的满同态.运用不可分解模的特殊生成元的定义,分析出满同态的一些性质,得到关于管范畴中模的满同态和短正合列的几个结论,为研究与管范畴对应的Hall代数的Hall多项式打下了一定的基础.     

Mg-Zn-Al三元系富镁角350℃等温截面

采用合金法,利用X射线衍射、扫描电镜及能谱成分分析等手段测定Mg-Zn-Al合金350℃时的相平衡关系及其成分,建立富镁角350℃等温截面。结果表明:α-Mg固溶体与L、φ、γ三相保持相平衡关系,不存在以前普遍认为的τ与α-Mg的相平衡。获得350℃时φ相成分范围,即53.5%～57.2%Mg、17.7%～30.7%Zn和15.8%～27.7%Al(摩尔分数)。Zn和Al两种元素可以同时固溶于α-Mg相中。但Al的加入提高了Zn在α-Mg中的溶解度,当α-Mg和L相平衡时,溶解度最大可达3.9%,远大于Mg-Zn二元系的2.1%。而当α-Mg与γ相平衡时,Zn的加入降低Al在α-Mg中的溶解度,即由Mg-Al二元系的7.8%降至5.2%。Al在Mg-Zn二元金属间化合物中的固溶度较大,可达7.7%,从而使其热稳定性得到提高。     

Partial phase relationships of Mg-Zn-Ce system at 350℃

The alloys were prepared in Mg-rich corner of Mg-Zn-Ce system. Partial phase equilibrium relationships of these alloys at 350 ℃ were identified by using scanning electron microscopy(SEM), electron probe microanalysis(EPMA), X-ray diffraction(XRD) analysis and selected area electron diffraction(SAED) pattern analysis of transmission electron microscopy(TEM). Partial isothermal section of Mg-Zn-Ce system in Mg-rich corner was identified. The results show that there is one ternary compound (T-phase) in Mg-Zn-Ce system. The T-phase is a linear ternary compound in which the content of Ce is about 7.7% (molar fraction); while the content of Zn is changed from 19.3% to 43.6% (molar fraction). The crystal structure of T-phase is C-centered orthorhombic. In addition, one two-phase region of Mg+T-phase and one three-phase region of Mg+T-phase+MgZn(Ce) exist in the Mg-rich corner of Mg-Zn-Ce system at 350 ℃.     

Al-Zn-Cu系合金不连续析出组织变形后的结构与性能

采用扫描电镜、透射电镜、X射线衍射及硬度测试等手段研究了添加2at％Cu的AlZn对称成分合金在冷轧后重新加热过程中的组织结构变化。结果发现：该合金不连续析出组织在冷变形后重新加热时发生了再结晶，以连续粗化与不连续粗化2种机制进行，再结晶温度约为100℃：而且相组成物由Al相、Zn相和细小的ε相转变为Al相、Zn相和粗大的T'相。AlZn-2Cu合金不连续析出组织在冷变形后重新加热时，硬度的变化是由再结晶软化、T’相粗化以及Zn原子的固溶强化共同影响的结果。     

Al-Zn对称成分合金不连续析出组织的再结晶

采用光学显微镜、扫描电镜和透射电镜研究了Al 4 0 %Zn(摩尔分数 )二元合金的不连续析出细片层组织在冷轧后重新加热时所发生的再结晶。根据加热过程中的显微组织变化 ,确定了该合金再结晶的形核及长大机制。结果发现 ,再结晶的 2种机制为非典型形核长大机制的连续粗化和典型形核长大机制的不连续粗化 ,后者又分为在团域界面、滑移带等处发生的以变形储能为主要驱动力的粗化和在变形量很小区域发生的以界面能为主要驱动力的粗化。