Theoretical estimation of dielectric loss of oxide glasses using nonequilibrium molecular dynamics simulations

To theoretically explore amorphous materials with a sufficiently low dielectric loss, which are essential for next-generation communication devices, the applicability of a nonequilibrium molecular dynamics simulation employing an external alternating electric field was examined using alkaline silicate glass models. In this method, the dielectric loss is directly evaluated as the phase shift of the dipole moment from the applied electric field. This method enabled us to evaluate the dielectric loss in a wide frequency range from 1 GHz to 10 THz. It was observed that the dielectric loss reaches its maximum at a few THz. The simulation method was found to qualitatively reproduce the effects of alkaline content and alkaline type on the dielectric loss. Furthermore, it reasonably reproduced the effect of mixed alkalines on the dielectric loss, which was observed in our experiments on sodium and/or potassium silicate glasses. Alkaline mixing was thus found to reduce the dielectric loss.     

Characterization of anisotropic gas permeability and thermomechanical properties of highly textured porous alumina

Porous alumina with a highly textured microstructure was fabricated by pulse electric current sintering (PECS) using alumina platelets. Highly oriented porous alumina with a porosity of 3%–50% was obtained by a pressure-controlled method of PECS. The properties of the highly textured porous alumina were measured in two directions. The nitrogen gas permeance and thermal conductivity at room temperature were higher in the direction along the platelet length due to the higher continuity of pores and the connectivity of alumina platelets, respectively. The anisotropy of the thermal conductivity at room temperature was investigated and explained by the effect of grain size of platelets as well as morphology and orientation of pores. The bending strength was higher with the loading direction along the platelet thickness. The thermal shock strength was clearly different in the two directions. The difference in the thermal shock strength was investigated by the measurement of properties and thermal stress analysis.     

An efficient manufacturing method for I-shaped cross-sectional CFRP beam with arbitrary arrangement of carbon fiber using electro-activated resin molding

Abstract

The I-shaped cross-sectional beam of CFRP (CFRP I-beam) is usually manufactured by the continuous protrusion method. Carbon fibers can only be arranged in the longitudinal direction. The CFRP I-beam with arbitrary arrangement of carbon fiber was manufactured with applying the electro-activated deposition molding method. The carbon fiber fabric was immersed in the deposition solution and energized, epoxy resin precipitated around carbon fiber and impregnated. The resin-impregnated fabric was installed to the mold, and the CFRP I-beam was fabricated. The CFRP I-beam was subjected to three-point bending tests, and the relationship between load-deflection was simulated by finite-element analysis.     

Vapor absorption by LiBr aqueous solution in vertical smooth tubes

Heat and mass transfer in a falling film vertical in-tube absorber was studied experimentally with LiBr aqueous solution. The presented results include the effect of solution flow rate, solution subcooling and cooling water temperature on the absorption in a smooth copper tube 16.05 mm I.D. and 400 mm long. The experimental data in the previous report for a 1200-mm-long tube was also re-examined and compared. It was demonstrated by the observation of the flow in the tube that the break down of the liquid film into rivulets leads to deterioration of heat and mass transfer at lower film Reynolds number or in longer tubes. An attempt to evaluate physically acceptable heat and mass transfer coefficients that are defined with estimated temperature and concentration at the vapor–liquid interface was also presented.     

Fracture toughness evaluation of adjacent flow weld line in polystyrene by the SENB method

Fracture toughness of adjacent flow weld lines, defined as weld lines that occur when two flow fronts meet and continue to flow together in the same direction (meld line or hot weld line), was evaluated by the single‐edge notched‐bend (SENB) method using three differently‐shaped obstructive pins. Although the fracture toughness varied depending upon the shapes of the pin, the values could be standardized as the distance from the meeting point of the two flow fronts flowing around the pin. The fracture toughness decreased drastically from the meeting point along the weld line and then slightly increased. These characteristic features could be explained by flow‐induced molecular orientation at the weld line interface. The molecules around the meeting point that were initially oriented parallel to the weld line due to fountain flow were able to relax, and then entanglement across the weld line interface developed because the flow stopped in the middle of the filling process, resulting in high fracture toughness. In contrast, the material at the downstream side of the weld line continued flowing during the filling process, being stretched along the flow direction. So, the molecular orientation at this area could not relax. In addition, the V‐notch shape, i.e., the depth and length at the surface of the weld line, which also varied depending on the shape of the obstacles, was considered to be identical when the meeting point was allowed to be a datum point. Thus, the meeting point was found to be a significant factor when the properties of weld lines are investigated. POLYM. ENG. SCI., 45:1059–1066, 2005. © 2005 Society of Plastics Engineers     

Theoretical model for flash generation

Reduction of flash generated in a gas vent is of great concern for manufacturers of electronic parts. The present study proposes a theoretical model for flash generation through consideration of flow characteristics in a gas vent. The model predicts the factors controlling flash, i.e., material parameters such as zero‐shear viscosity, crystallization temperature, thermal conductivity, and heat capacity, and process parameters such as injection and mold wall temperatures, packing pressure, and the clearance of a gas vent. On the other hand, we measure the amount of flash generated in the molding of poly(phenylene sulfide) (PPS) composites containing glass fiber and spherical fillers (CaCO₃ or Al₂O₃). Flash reduces with decreasing size of spherical fillers. These experimental data are successfully interpreted using the flash model. Polym. Eng. Sci., 45:198–206, 2005. © 2005 Society of Plastics Engineers     

A flow simulation for the epoxy casting process using a 3D finite‐element method

A three‐dimensional flow simulation for epoxy casting has been developed. A control‐volume‐based finite‐element method is employed, containing a conservative upwind formulation for the advection terms and equal order interpolations for all variables. This simulation predicts the non‐isothermal and reactive flow behavior under the gravity. The viscosity and reaction‐rate parameters were estimated by using a dynamic rheometer and a differential scanning calorimeter. The predicted flow front advancement and temperature profiles in the calculation domain similar to the mold cavity were in close agreement with the corresponding experimental results. The variation of epoxy surface configuration with flow rate also showed the same tendency between the prediction and the experiment. This simulation seems to be applicable not only to the epoxy casting, but also to other molding processes of various thermoset resins. POLYM. ENG. SCI. 45:364–374, 2005. © 2005 Society of Plastics Engineers.     

Characterization and electrochemical properties of CF4 plasma-treated boron-doped diamond surfaces

The effect of CF₄ plasma etching on diamond surfaces, with respect to treatment time, was investigated using scanning electron microscopy (SEM), Raman spectroscopy, X-ray photoelectron spectroscopy (XPS), and electrochemical measurements. SEM observations and Raman spectra indicated an increase in surface roughening on a scale of 10–20 nm, and an increase in crystal defect density was apparent with treatment time in the range of 10 s to 30 min. In contrast, alteration of the diamond surface terminations from oxygen to fluorine was found to be rather rapid, with saturation of the F/C atomic ratio estimated from XPS analysis after treatment durations of 1 min and more. The redox kinetics of Fe(CN)₆^3−/4− was also found to be significantly modified after 10 s of CF₄ plasma treatment. This behavior shows that C–F terminations predominantly affect the redox kinetics compared to the effect on the surface roughness and crystal defects. The double-layer capacitance (C_dl) of the electrolyte/CF₄ plasma-treated boron-doped diamond interface was found to show a minimum value at 1 min of treatment. These results indicate that a short-duration CF₄ plasma treatment is effective for the fabrication of fluorine-terminated diamond surfaces without undesirable surface damage.     

Resource contention in shared-memory multiprocessors: A parameterized performance degradation model

A standard metric conventionally employed to compare the performance of different multiprocessor systems is speedup. Although providing a measure of the improvement in execution speed achievable on a system, this metric does not yield any insight into the factors responsible for limiting the potential improvement in speed. This paper studies the performance degradation in shared-memory multiprocessors as a result of contention for shared-memory resources. A replicate workload framework with a flexible mechanism for workload specification is proposed for measuring performance. Two normalized performance metrics—efficiency and overhead factor—are introduced to quantify the factors limiting performance and facilitate comparison across architectures. Finally, the proposed model is employed to measure and compare the performance of three contemporary shared-memory systems, with special emphasis on the newly released BBN Butterfly-II (TC2000), currently undergoing Beta test.