新型相变材料Ti0.5Sb2Te3刻蚀工艺及其机理研究

采用CF4和Ar混合气体研究了新型相变材料Ti0.5Sb2Te3(TST)的刻蚀特性,重点优化和研究了刻蚀气体总流速、CF4/Ar的比例、压力和功率等工艺参数对刻蚀形貌的影响。结果表明,当气体总流量为50 sccm、CF4浓度为26%﹑刻蚀功率为400 W和刻蚀压力为13.3 Pa时,刻蚀速度达到126 nm/min,TST薄膜刻蚀图形侧壁平整而且垂直度好(接近90°)﹑刻蚀表面平整(RMS为0.82 nm)以及刻蚀的片内均匀性等都非常好。     

Dry etching of new phase-change material Al_(1.3)Sb_3Te in CF_4/Ar plasma

正The dry etching characteristic of Al_(1.3)Sb_3Te film was investigated by using a CF_4/Ar gas mixture.The experimental control parameters were gas flow rate into the chamber,CF_4/Ar ratio,the O_2 addition,the chamber background pressure,and the incident RF power applied to the lower electrode.The total flow rate was 50 sccm and the behavior of etch rate of Al_(1.3)Sb_3Te thin films was investigated as a function of the CF_4/Ar ratio,the O_2 addition,the chamber background pressure,and the incident RF power.Then the parameters were optimized.The fast etch rate was up to 70.8 nm/min and a smooth surface was achieved using optimized etching parameters of CF_4 concentration of 4%,power of 300 W and pressure of 80 mTorr.     

三维相变存储阵列驱动二极管的制备研究

结合新一代高集成度三维集成电路和新型相变存储技术,以三维相变存储单元阵列的实现为目标,进行了用于存储单元的驱动和开关作用的二极管阵列的制备实验。在借助低温等离子体活化键合技术获得了良好的键合界面之后,利用智能剥离法成功转移了单晶PN结二极管层到含有金属W电极阵列的基片上,并制备了垂直二极管阵列。经过聚焦离子束加工和电镜观察得知基片上小型W电极与转移来的PN结构Si层接触良好,测试得到了标准的二极管特性曲线,开关比达到4个数量级。不过实验制备的二极管漏电流较大,开关比偏低,这些问题还需要在将来实验环境的改进和工艺的优化中得到解决。     

新型相变材料Al1.3Sb3Te使用CF4/Ar等离子体干法刻蚀

对使用CF4/Ar 混合气体刻蚀Al1.3Sb3Te的特性进行了研究。实验控制的参数是：气体流入刻蚀腔的速率,CF4/Ar 比例,O2的加入量,腔内压强以及加在底电极上的入射射频功率。总的气体流量是50sccm ,研究刻蚀速率与CF4/Ar的比例,O2加入量,腔内压强和入射射频功率的关系。最后刻蚀参数被优化。 使用优化的刻蚀参数CF4的浓度4%,功率300W,压强800mTorr,刻蚀速率达到70.8nm/min,刻蚀表面平整