On the Growth of Thin-Film AlGaN/GaN Epitaxial Heterostructures on Hybrid Substrates Containing Layers of Silicon Carbide and Porous Silicon

Semiconductors - Abstract—In our work, we carry out a structural-spectroscopic study of AlGaN/GaN epitaxial layers grown by molecular-beam epitaxy with nitrogen-plasma activation on a hybrid...     

Phase formation,structure and properties of light-weight aluminosilicate proppants based on clay-diabase and clay-granite binary mixes

One of the drawbacks of fusible clays is the narrow sintering interval due to a sharp increase in the amount of iron-silicate melt at a temperature of 1000–1100 °C, which hardens in the form of a glass phase upon cooling. This leads to a relatively low mechanical strength of the calcined samples and causes the danger of melting the granular material surface from such clays during the firing process. To increase the strength of samples of fusible clays, the influence of diabase and granitoid rocks was considered. It was found that the strengthening effect of diabase and granitoid rock additives in an amount of 20–50% in a mixture with fusible clay is due to an increase of total content of the crystalline phase (mullite, cristobalite and residual quartz) from 18–20% in clays without additives to 22–28 % - in mixtures with diabase and to 28–34% - with granitoid additives) at a temperature of 1050–1100 °C. This increase is due to the activation of synthesis processes of secondary mullite and crystallization from alkali-rich feldspar melt of amorphous silica, released from the structure of clay minerals. The established influence of the igneous rocks used made it possible to develop compositions and propose process flow sheet for producing aluminosilicate proppants based on fusible clays. The use of granitoid and diabase rocks in an amount of 20–70% with fusible clays produces lightweight aluminosilicate proppants with bulk density of 1.40–1.46 g/cm³ at temperature range of 1050–1100 °C, which can endure destructive pressures up to 34.5–52 MPa.     

Structure–phase state of the surface layers in rails subjected to differential hardening

A layer-by-layer analysis of the structures, the phase compositions, and the defect substructures of differentially hardened rails has been carried by optical and transmission electron microscopy. It is found that the material volume of the rail head fillet is cooled faster than the volume located along the central axis.     

An automated system based on cryogenic probe station for integrated studies of semiconductor light-emitting structures and wafers in the range of 15 to 475 K

An automated system for integrated electrophysical and optical studies of semiconductor nanoheterostructures, which operates in a wide temperature range from 15 to 475 K, is designed. The setup is intended to measure the temperature and frequency admittance and electroluminescence spectra of light-emitting diode and laser chips formed on substrates of diameter up to 50.2 mm, and the distribution of parameters over the wafer. The setup includes the closed-cycle helium cryogenic station, LCR meter, and temperature controller. The characterization results of nanoheterostructures with InGaN/GaN multiple quantum wells, which are used for creating highly efficient white and blue light-emitting diodes, are presented.     

Irreversible deformation and the superplasticity of a TN-1 alloy during thermal cycling through the martensitic transformations ranges under loading

The influence of the thermal cycling conditions on the thermal-cycling creep of a TN-1 alloy and the related irreversible deformations is studied. The conditions under which an anomalous increase in the irreversible deformations begins are determined. The structural mechanism of the irreversible deformations of an equiatomic alloy is shown to be analogous to the structural mechanism of metal creep at high temperatures: it predominantly has a dislocation character. It is proposed to use the effect of anomalous increase in the deformation of materials with reversible martensitic transformations for forming parts made of these materials at low temperatures.     

Basic trends in development of drilling equipment for ore mining with block caving method

The authors have determined the causes of drop in performance of induced block caving using fans of blastholes 105 mm in diameter and single blastholes 250 mm in diameter, as well as the sources of increased drilling cost and expansion of start-up time of production blocks in Abakan underground mine. Alternatives of improvement in drilling efficiency under current conditions are discussed.     

Production technology for low-carbon,low-sulfur boron steel

A technology for slag formation in the ladle–furnace unit is considered; the slag is based on the CaO–SiO₂–MgO–Al₂O₃–B₂O₃ system. This technology permits both microalloying of the steel with boron (reduced from the oxide phase) and desulfurization of the steel. The resulting boron content in the steel is 0.001–0.008%; the sulfur content in low-alloy steel and pipe steel is low (0.004–0.010%); and the consumption of manganese ferroalloys is reduced to 0.5 kg/t for 08кп steel and 1.4 kg/t for 09Г2C steel. In addition, the proposed technology increases the strength of the rolled steel, without loss in its plasticity; and reduces the environmental impact thanks to the replacement of fluorspar by colemanite.