Environmental effects on the strength and impact damage resistance of alumina based oxide/oxide ceramic matrix composites

In this study the effects of high temperature and moisture on the impact damage resistance and mechanical strength of Nextel 610/alumina silicate ceramic matrix composites were experimentally evaluated. Composite laminates were exposed to either a 1050°C isothermal furnace-based environment for 30 consecutive days at 6 h a day, or 95% relative humidity environment for 13 consecutive days at 67°C. Low velocity impact, tensile and short beam strength tests were performed on both ambient and environmentally conditioned laminates and damage was characterized using a combination of non-destructive and destructive techniques. High temperature and humidity environmental exposure adversely affected the impact resistance of the composite laminates. For all the environments, planar internal damage area was greater than the back side dent area, which in turn was greater than the impactor side dent area. Evidence of environmental embrittlement through a stiffer tensile response was noted for the high temperature exposed laminates while the short beam strength tests showed greater propensity for interlaminar shear failure in the moisture exposed laminates. Destructive evaluations exposed larger, more pronounced delaminations in the environmentally conditioned laminates in comparison to the ambient ones. External damage metrics of the impactor side dent depth and area directly influenced the post-impact tensile strength of the laminates while no such trend between internal damage area and residual strength could be ascertained.     

When danger lurks in the background: Attentional capture by animal fear-relevant distractors is specific and selectively enhanced by animal fear.

Across 2 experiments, a new experimental procedure was used to investigate attentional capture by animal fear-relevant stimuli. In Experiment 1 (N = 34), unselected participants were slower to detect a neutral target animal in the presence of a spider than a cockroach distractor and in the presence of a snake than a large lizard distractor. This result confirms that phylogenetically fear-relevant animals capture attention specifically and to a larger extent than do non-fear-relevant animals. In Experiment 2 (N = 86), detection of a neutral target animal was slowed more in the presence of a feared fear-relevant distractor (e.g., a snake for snake-fearful participants) than in presence of a not-feared fear-relevant distractor (e.g., a spider for snake-fearful participants). These results indicate preferential attentional capture that is specific to phylogenetically fear-relevant stimuli and is selectively enhanced in individuals who fear these animals. (PsycINFO Database Record (c) 2010 APA, all rights reserved)     

The effect of solidification time and heat treatment on the fatigue properties of a cast 319 aluminum alloy

Solidification time and heat treatment are known to have a large effect on the microstructure of cast aluminum alloys. This study was conducted to quantify how the fatigue properties of a 319-type aluminum alloy are affected by solidification time and heat treatment. Both porosity-containing (non-hot isostatically pressed (HIP)) and porosity-free (HIP) samples in the T6 (“peak aged”) or T7 (“overaged”) heattreated conditions were tested. As the solidification time increased, the average initiating pore diameter increased and stress-controlled fatigue life decreased. Heat treatment was observed to have a large effect on fatigue properties of the HIP samples. However, in the non-HIP fatigue samples, heat treatment did not significantly change the fatigue life or fatigue strength of the cast 319-type alloy. The absence of an influence of heat treatment on fatigue response is attributed to the predominance of the microporosity in fatigue crack initiation in cast aluminum.     

Learning Organizations in Construction

The transformation of organizations from production-oriented entities to proactive learning entities that continuously leverage the knowledge of the workforce is a primary objective of management researchers. This focus has significant relevance to the construction industry where production-related research has predominantly overshadowed organizational development research. As one effort to change this emphasis, the writers present a research effort designed to study current organization learning techniques and technologies fielded by organizations both inside and outside of the construction industry. Through a series of exploratory case studies, the writers developed a maturity model together with the Construction Industry Institute that provides construction organizations with a framework for developing a learning organization culture. The maturity model focuses on learning organization characteristics of leadership, processes and infrastructure, communication/collaboration, education, and culture at the organization, community, and individual levels. This paper introduces the results of that effort including a presentation of the learning organization maturity model, framework application, and the overall characteristics of a learning organization.     

Pulsed phase-locked loop calibration over frequency

This paper presents a method of correcting for unwanted phase shifts introduced by interchanging ultrasonic transducers and other measurement system components when using the pulsed phase-locked loop (PPLL) ultrasonic system. Theory is derived mathematically separating phase errors into their constituents. The relationship to a previously derived method of determining the number of periods into the tone-burst, at which the system samples, is established, and a method of adjusting this number to be an integer is presented. Implementation of the technology on a computer is demonstrated through experimental results on transducers of differing frequencies and diameters. Sensitivity to path-length is tested. This work has resulted in a straightforward means of calibrating transducers in conjunction with PPLL measurements using a single, fixed reference block     

Early intervention for spelling problems: Teaching functional spelling units of varying size with a multiple-connections framework.

Poor spellers in 2nd grade (n?=?128) participated in 24 20-min sessions that included (a) direct instruction in the alphabet principle (most frequent phoneme-spelling connections); (b) modeling of different approaches, singly and in combination, for developing connections between spoken and written words for 48 words ordered by sound-spelling predictability; and (c) practice in composing. Results of this multilayered intervention showed that (a) more than 1 way of developing sound-spelling connections is effective in teaching spelling but that after training in the alphabet principle, combining whole word and onset-rime training is most effective in achieving transfer of the alphabet principle across word contexts; (b) functional spelling units of not only a single letter but also 2 or more letters are important in beginning spelling; and (c) training in spelling transfers to composition and word recognition. (PsycINFO Database Record (c) 2010 APA, all rights reserved)     

Spatial retardation of carrier heating in scaled 0.1-μmn-MOSFET's using Monte Carlo simulations

A comprehensive Monte Carlo simulator is employed to investigate nonlocal carrier transport in 0.1 μm n-MOSFET's under low-voltage stress. Specifically, the role of electron-electron (e-e) interactions on hot electron injection is explored for two emerging device designs biased at a drain voltage V_d considerably less than the Si/SiO₂ injection barrier height φ_b. Simulation of both devices reveal that 1) although qV_d<φ_b, carriers can obtain energies greater than φ_b, and 2) the peak for electron injection is displaced approximately 20 nm beyond the peak in the parallel channel electric field. These phenomena constitute a spatial retardation of carrier heating that is strongly influenced by e-e interactions near the drain edge. (Virtually no injection is observed in our simulations when e-e scattering is not considered.) Simulations also show that an aggressive design based on larger dopant atoms, steeper doping gradients, and a self-aligned junction counter-doping process produces a higher peak in the channel electric field, a hotter carrier energy distribution, and a greater total electron injection rate into the oxide when compared to a more conventionally-doped design. The impact of spatially retarded carrier heating on hot-electron-induced device degradation is further examined by coupling an interface state distribution obtained from Monte Carlo simulations with a drift-diffusion simulator. Because of retarded carrier heating, the interface states are mainly generated further over the drain region where interface charge produces minimal degradation. Thus, surprisingly, both 0.1 μm n-MOSFET designs exhibit comparable drain current degradation rates     

Laminated beams subjected to transverse load

A simple elastic solution has been developed for predicting the shear stress distribution in a laminated beam subjected to a variety of transverse loading conditions. Photoelastic tests on composite models involving a single bonding layer have been used to validate the theory, and also to comment upon the significance of these results in interpreting the interlaminar shear strength and bending modulus of the simplest form of laminated strip.     

Demonstration of an endurance limit in cast 319 aluminum

An investigation of the fatigue properties of cast W319-T7, an Al-Si-Cu alloy used in automotive engine components, was conducted using ultrasonic testing equipment with operating frequencies of 20 kHz. The stress-life (S-N) behavior at room temperature was determined for three solidification conditions of this alloy, where stresses for fatigue lives ranging from 10⁵ to 10⁹ cycles were determined. The results are compared to fatigue data acquired using servohydraulic equipment operating at 40 Hz. No influence of loading frequency has been observed. A discrete endurance limit is indicated for each of the three solidification conditions of W319-T7. The scientific and practical implications of this result are discussed. A material model presented previously is modified by introducing a crack growth threshold condition in order to predict the observed endurance limits. The model is shown to effectively predict the influence of solidification time on the fatigue properties of W319-T7.     

Toward the reduction of population obesity: Macrolevel environmental approaches to the problems of food, eating, and obesity.

The authors reviewed the evidential basis of three environmental approaches to reducing population obesity: What are the effects of (a) taxing or subsidizing foods, (b) manipulating the ease of food access, and (c) restricting access to certain foods? A narrative review evaluated evidence using National Heart, Lung, and Blood Institute criteria. There was strong evidence that subsidization influences food purchases, but not necessarily food consumption or body weight. Ease of food access may influence food purchases, and possibly food intake and body weight. Data on restriction were lacking. More studies are needed to justify that altering these macro-environmental variables will necessarily reduce population obesity. A proposed conceptual model posits that the steps through environmental interventions may exert intended and unintended influences on body weight and obesity prevalence. Contemplated policy changes should weigh scientific evidence with social judgments and values concerning changes to the environment. (PsycINFO Database Record (c) 2010 APA, all rights reserved)