Corrosion behaviors of carbon steel induced by life activities of Phaeodactylum tricornutum in a marine environment

Microbiologically influenced corrosion induced by bacteria has been studied for many years. Corrosion is known to be sensitive to the presence of microalgae, such as Phaeodactylum tricornutum. However, the life activity of P. tricornutum that influences the general and localized corrosion of carbon steel is not fully understood. The current study uses a combination of immersion tests and electrochemical experiments with a detailed surface characterization to reveal the naturally formed corrosion products with/without the presence of P. tricornutum. The results show that samples suffer from pitting corrosion and the averaged pit depths are approximately 15 μm under a light–dark cycle condition or a 24-h constant light condition. Meanwhile, the corrosion products are mainly comprised of γ-FeOOH and Fe₃O₄ in a constant light condition. However, γ-FeOOH, Fe₃O₄, and FeCO₃ are found in a light–dark cycle. This study proposes the fundamental mechanisms of the effect of P. tricornutum life activities on the corrosion performance of Q235 carbon steel, to fulfill the knowledge gaps of the presence of microalgae inducing the general and pitting corrosion of carbon steel.     

Organic mesh template-based laminated object manufacturing to fabricate ceramics with regular micron scaled pore structures

A new aqueous slurry-based laminated object manufacturing process for porous ceramics is proposed: firstly, an organic mesh sheet is pre-paved as a pore-forming template before slurry layer scraping; secondly, the 2D pattern is built with laser outline cutting of the dried mesh–ceramic composite layer; finally, the pore structure is formed after degreasing and sintering. Alumina parts with porosities of 51.5 %, round hole diameters of 80 ± 5 μm were fabricated using 70 wt. % solid content slurry and 100 mesh nylon net. Using an organic mesh as the framework and template not only reduces the risk of damage of the green body but also ensures the regularity, uniformity and connectivity of the micron scaled pore network. The layer-by-layer drying method avoids the delamination phenomenon and improves the paving density. The new method can realize the flexible design of the pore structure by using various organic mesh templates.     

Tunable multicolor upconversion luminescence of Yb3+ sensitized Na3La(VO4)2 crystals

Multicolor upconversion luminescence materials show significantly applications in materials science. In this paper, the novel Yb³⁺-sensitized Na₃La(VO₄)₂ upconversion luminescence crystals are synthesized by the solid-state reaction method. Three primary colors upconversion luminescence are successfully achieved in Na₃La(VO₄)₂:Yb³⁺,Tm³⁺, Na₃La(VO₄)₂:Yb³⁺,Er³⁺, and Na₃La(VO₄)₂:Yb³⁺,Ho³⁺ crystals excited by the single 980 nm LD. Multicolor upconversion luminescence can be obtained by simply adjusting the combination ratios of these three samples. Luminescence mechanisms of the Yb³⁺-sensitized system are discussed in detail. In the Na₃La(VO₄)₂ host material, the Yb³⁺/Ho³⁺ codoped system exhibits unusual red upconversion luminescence based on the short decay time of Ho³⁺ ion ⁵I₆ level, which provides the possibility of three primary color luminescence under 980 nm excitation.     

建筑工业化发展的多群体演化博弈与仿真研究

新型建筑工业化具有高质量、低消耗、可循环发展等特征，其推广已上升到国家战略层面。利用演化博弈方法，建立“政府-开发商-银行” 的三方动态演化博弈模型，进行各博弈主体策略的演化稳定性分析，并针对初始状态、奖惩力度、借贷风险和开发成本等对演化结果的影响进行动态仿真。在此基础上， 考虑开发商群体的网络拓扑特征对演化真实性的影响，引入复杂网络理论， 以无标度网络为载体描述开发商个体的连接偏好和决策机制，构建政府监管下的建筑工业化扩散模型，并通过仿真深入研究相关因素对扩散深度的影响作用，最后结合仿真结果给出相应对策建议。     

Ferulic acid and EGCG alter the structural characteristics of ovalbumin and its application in mineral loading

This study aims to fabricate mineral-loading nanocarriers using natural materials. The interaction patterns between ovalbumin (OVA) and four water-soluble polyphenols, namely ferulic acid (FA), (-)-Epigallo-catechin 3-gallate (EGCG), gallic acid (GA) and epicatechin (EC), were investigated. Results showed that the optimised conditions for preparing stable OVA–polyphenol complexes are at the OVA–polyphenol ratio of 4:1 at pH 6, under which OVA–FA and OVA–EGCG showed the highest stability and mineral-loading capacity among four OVA–polyphenol complexes. The fluorescence results indicated that the addition of EGCG and FA induced a significant fluorescence quenching to OVA. The interaction between OVA and polyphenols involved hydrogen bonding, hydrophobic interaction and electrostatic interaction. Fourier transform infrared spectroscopy (FTIR) analysis suggested that both FA and EGCG enhanced the stability and orderliness of the structure of OVA. The transmission electron microscopy images also exhibited the spherical structure of OVA after the addition of FA and EGCG. Furthermore, scanning electron microscope–energy dispersive X-ray spectrum results suggested that OVA–FA and OVA–EGCG complexes were better mineral carriers than OVA–GA and OVA–EC. This study may serve as the theoretical support for the promising application of OVA in the fabrication of mineral-loading nanocarriers in functional food and pharmaceutic.     

Optical and electrical properties of ITO film on flexible fluorphlogopite substrate

Indium Tin Oxide (ITO) films were prepared, at room temperature, on a fluorphlogopite substrate using magnetron sputtering technology. At various temperatures of 500 °C, 600 °C, 700 °C, 800 °C, and 900 °C, the samples were (had) annealed for 2 h (a 2-h duration). The results showed improvement in the crystalline performance of ITO film at selected annealing temperatures, with a significant reduction in resistivity at 800 °C. The lowest resistivity is 4.08 × 10^?4 Ω-cm, which is nearly an order of magnitude lower than the unannealed sample. All samples have an average light transmittance above 85% in the visible light range (400–800 nm), and with increasing annealing temperature, the average light transmittance tends to decrease. Besides, at the sensitive wavelength of 550 nm, the light transmittance is as high as 93.74%. The sheet resistance testing of the sample was through the number of bending times, which revealed that with the increase of the number of bending, the sheet resistance increases. However, after 1200 bending times, the change rate of the sheet resistance remains below 5%. Thus, the ITO film prepared on the flexible fluorphlogopite substrate revealed excellent optical and electrical properties, good flexibility, and improved stability after high-temperature annealing, which guarantees successful application in flexible electronic devices.     

Synthesis and luminescence properties of reddish-orange-emitting Ca2GdNbO6:Sm3+ phosphors with good thermal stability for high CRI white applications

Novel reddish-orange-emitting Ca₂GdNbO₆:Sm³⁺ phosphors based on the emission of ⁴G_5/2 → ⁶H_9/2 transition at 651 nm with the chromatic coordinate of (0.633, 0.366) were synthesized. The crystal structure and chemical purity were identified in detail. Under the 407 nm excitation, the optimum concentration of Sm³⁺ ion was found to be 5 mol% dominated by the dipole-dipole interaction in the Ca₂GdNbO₆ host material. The color purity of the sample with optimum doping was estimated to be about 78.38%. Besides, the thermal stability was also studied, and it was further found that the emission intensity remained 65.32% at 423 K. The packaged white LED device exhibited excellent CRI and CCT values of 92.43 and 4896 K. Finally, the polydimethylsiloxane film with a stable structure and flexible property was prepared. These above results reveal that novel reddish-orange-emitting Ca₂GdNbO₆:Sm³⁺ phosphors can be applied in high CRI white communication and flexible display applications.     

The influence of processing methods on the dielectric properties of BaTi1-xGdxO3-x/2 - Based materials

In this study, the intermediate rare-earth oxide Gd₂O₃ (Gd) was substituted in different amounts (x = 0.2–2 mol%) for the formulation of BaTi_1-xGd_xO_3-x/2 (BTG_x) dielectric materials. The effect of B-site substitution was confirmed by the additional Raman active A_1g octahedral peak at ~835cm^-1 strengthened at x ≥ 0.4 mol%. Additionally, properties of 0.9BTG_0.007-0.1BA dielectric ceramics were analysed based on the influence of various processing methods as a function of sintering temperature. The focal samples were labelled Method-A (direct-mix) and Method-B (indirect-mix). As the sintering temperature (1075–1200 °C) increased, the 1 kHz response of the ε–T curves of Method-A samples transformed from a single peak to broad-narrow double peaks of high dielectric loss tangent (tan δ). Nonetheless, samples of Method-B possessed a clearly defined transmission electron microscopy (TEM) core-shell structure, flattened double-peak ε-T curves, optimised dielectric properties (ε = ~1563–1851 and tan δ < 1.5% at room temperature), and a wide-ranging temperature behaviour that meets the X8R dielectric standards (ΔC/C_25°C < ±15%). The maximum dielectric breakdown strength of Method-B samples reached ~131 kVcm, while the energy storage density was ~0.726 J/cm³ at a maximum efficiency of ~80% at 1100 °C. Thus, exhibiting good potentials for balancing temperature stability with energy storage applications.