Parameter optimization for plasma-sprayed Al_2O_(3P)/Al composite coatings on AZ31 magnesium alloy

Al_2O_(3P)/Al composite coatings were prepared on the surface of AZ31 magnesium alloy by plasma spraying technology with mixed powders of Al and Al_2O_3. An orthogonal test containing six factors and five levels was carried out to acquire the optimum technical parameters. Microstructures and properties of the composite coatings were studied. The results show that the coatings consist of Al_2O_3 particulates distributed uniformly and Al matrix, and the interface between the particulate and matrix is continuous, compact and clean. With increasing the mass fraction of Al_2O_3 in the mixed powders, the volume fraction of Al_2O_3 in the coatings increases. The Al_2O_(3P)/Al composite coating with 14% Al_2O_3 volume fraction has more compact microstructure and more satisfactory properties.     

等离子喷涂Al_2O_(3p)/NiCrBSi涂层优化设计

利用二次回归正交组合设计法优化喷涂工艺参数,建立了等离子喷涂Al2O3p/NiCrBSi复合材料涂层冲蚀磨损失重率的二次回归方程.研究了等离子喷涂参数对涂层冲蚀磨损失重率的影响.结果表明,利用Matlab软件编程计算,优化等离子喷涂参数,明显提高了涂层的抗冲蚀磨损性能.为等离子喷涂制备以氧化铝(Al2O3)颗粒增强金属基(NiCrBSi)复合材料涂层(Al2O3p/NiCrBSi)的实际应用提供必要的理论依据和技术数据.     

恒电流控制软开关点焊电源的研究

根据点焊脉冲大电流输出的特点，改进了采用辅助网络的移相控制ZVS PWM DC／DC全桥变换器．最大限度地减少了二次侧占空比丢失；通过编程、设计并优化了滞后桥和辅助网络参数；采用双环控制。使输出电流能够高度精确跟踪电流编程基准，防止了偏磁。     

Microstructural features and properties of plasma sprayed YPSZ/NiCrAlY thermal barrier coating (TBC)

0　IntroductionThermalbarriercoatings(TBCs)arewidelyusedontheturbinebladesforaircraftpropulsionorpowergenerationtoreducethemetallicsubstratetemperature,whichleadstoincreasingengineefficiencyandloweringpollutantemissionsresultingfromallowableincreaseofoperationtemperature[1,2].Today,TBCsareattractingmoreattentionandhavewiderpotentialapplicationstoprotecthightemperaturecomponents.However,thermalbarriercoatingshaveatendencytocrackandspallinserviceduetothermalshockandthermalcyclingbetweenambient…     

渗铝及扩散处理对电弧喷涂层结合强度的影响

利用电弧喷涂技术、渗铝和扩散处理工艺,在铸铁表面制作了具有微冶金结合的18-8不锈钢耐热耐蚀涂层.采用光学显微镜,SEM及X射线衍射等方法,对经过不同渗铝和扩散处理工艺得到的涂层的组织形貌,相结构及成分进行了分析研究.并采用热疲劳试验对渗铝和扩散处理后涂层的结合强度进行评价.结果表明,通过渗铝和扩散处理,涂层与基体之间产生了微冶金结合,涂层的结合强度得到了显著提高.并且渗铝时间过长不利于提高涂层结合强度,应合理控制渗铝时间.     

弹簧钢点焊缺陷及工艺措施

分析了弹簧钢电阻电焊接头常见的缺陷类型、形貌、成因及危害，提出了通过采用增大电极压力，调制焊接电流脉冲和随机多脉冲回火热处理等工艺措施可获得优质点焊接头，为钢质弹性件的以焊代铆提供了依据     

高铬铸铁堆焊层组织对冲蚀磨损性能的影响

采用正交试验法研究了粘结焊剂中高碳铬铁、石墨、钼铁对埋弧堆焊层组织、硬度及耐冲蚀磨损性能的影响规律。堆焊层为亚共晶组织时,硬度低,耐冲蚀磨损性能差;共晶堆焊层硬度高,耐冲蚀性能有所提高;堆焊层为含有少量一次碳化物的过共晶组织时,硬度高,耐冲蚀磨损性能最好;一次碳化物过多时,虽然硬度高,但耐中磨损性能下降。试验得到了最佳粘结焊剂配方。     

多功能电脑焊接电源的研究与设计

本文介绍了最新研制成的ＺＸ５－４００Ｄ型多功能可控硅整流弧焊机的硬件与软件研究设计成果。这种新型焊机在硬件电路不变的情况下，通过改变控制软件就可实现直流脉冲，直流方波，外特性斜率与拐点可调等多种功能，充分发挥了微计算机程序控制的优势，为发展及改造现有普通焊接电源提供了有效的途径。     

薄件点焊熔核旋流现象的形成

本文对薄件点焊熔核旋流现象进行了较系统的研究，指出旋流的实质是严重的宏观偏析，产生的内部原因是二种材料成分，组织和性能的不同，而外部条件是点焊工艺方法本身特点，尤其是采用硬焊接规范。     

点焊熔核的孕育处理研究

通过孕育处理可扩大熔核凝固组织中的等轴晶区，并在合适的工艺条件下获得呈单一等轴晶组织的熔核，同时，对孕育处理前后的点焊接头力学作了系统的比较研究。