Microstructure and wear property of hardfacing alloy with nitrogen strengthening

The nitrogen-alloying hardfacing alloy of the martensitic stainless steel was deposited on a low carbon steel substrate using hardfacing flux-cored wire. Microstructure and surface hardness of hardfacing alloy were investigated and measured by optical microscope and microhardness tester. Carbonitrides of the hardfacing alloy were observed by electron probe. The wear behaviour of the hardfacing alloy was studied using the belt abrasion test apparatus and the worn surface was analyzed by scanning electron microscopy. The results showed that carbonitride particles in the hardfacing alloy are complex MX (M:alloy elements; X:C, N) precipitate with fine size. These carbonitride particles distributed homogeneously in the hardfacing alloy and had a good strengthening effect on the wear property. The wear property of the hardfacing alloy with nitrogen was better than the one without nitrogen.     

焊剂中加入CeO2对E36钢埋弧焊焊缝组织与性能的影响

通过向研制的高碱度焊剂中加入质量分数为0%,2%,4 %的稀土氧化铈(CeO2),实现向焊缝金属中添加不同含量的稀土,研究了不同含量的CeO2对焊缝金属显微组织和性能的影响.结果表明:加入稀土后的焊缝组织以针状铁素体为主,晶粒得到了细化,焊缝的冲击韧性明显改善;其中,焊剂中CeO2加入量为2%的焊缝金属的冲击性能要好于...     

电弧喷涂粉芯丝材的研究进展与应用

简述了电弧喷涂粉芯丝材的优点及制作工艺,介绍了电弧喷涂粉芯丝材的发展历程,以及耐磨损、耐腐蚀、耐高温电弧喷涂粉芯丝材的最新研究进展,展望了电弧喷涂粉芯丝材的应用前景,指出了金属陶瓷复合粉芯丝材、非晶态粉芯丝材、纳米粉芯丝材是未来电弧喷涂粉芯丝材的发展方向。     

电弧喷涂4Cr13涂层预处理工艺及组织与性能研究

采用喷砂粗化、喷砂+喷涂打底涂层、喷砂+电拉毛这3种工艺对QSTE420TM钢板进行表面预处理,之后采用相同工艺进行电弧喷涂4Cr13涂层,分析了涂层组织和断口形貌,测试了涂层的显微硬度和结合强度,对比了3种预处理工艺对涂层组织和性能的影响.结果表明:电弧喷涂4Cr13涂层组织呈现出典型的层状结构;不同的表面预处理工艺对涂层的结合强度影响显著,喷砂粗化+喷涂打底涂层能使4Cr13涂层获得最优的综合性能.     

电弧喷涂4Cr13涂层的组织与性能研究

研究了喷砂粗化、喷涂打底涂层、电拉毛三种表面预处理工艺下电弧喷涂4Cr13涂层的组织与性能.利用扫描电镜、能谱仪等手段对涂层组织和断口形貌进行分析,同时对涂层的显微硬度和结合强度进行了测试.结果表明:电弧喷涂4Cr13涂层组织呈现出典型的层状结构.不同的表面预处理工艺对涂层的结合强度影响显著,喷砂粗化并喷涂打底涂层能使...