硼酸铝晶须增强Al复合材料的性能及界面结构

采用挤压铸造工艺制备出复合良好的9Al_2O_3 2B_2O_3晶须增强6061Al合金及纯Al复合材料研究表明,T6处理不能提高9Al_2O_3 2B_2O_3w/6061Al复合材料的力学性能,其原因是T6处理后复合材料中的界面反应明显加重利用透射电子显微术对此复合材料界面的观察与分析认为,界面上存在着严重的化学反应,反应物为Al_2MgO_4将制造态与T6态的界面结构对比发现,正是这种界面化学反应对材料的性能产生不利影响而在9Al_2O_3 2B_2O_3w/纯Al界面上未发现任何化学反应。界面能谱EDS成分分析结果表明,上述界面化学反应是由材料制造过程中基体合金中的Mg在界面上原子偏聚造成的     

难互溶Cu－Fe系机械合金化过程中的结构变化研究

机械合金化可使室温下几乎不互溶体系Ｃｕ＿ｘＦｅ＿（１００－ｘ）形成过饱和国溶体。ｆｅｅ相区的固溶度范围扩展到Ｘ＞３５ａｔ．％。对Ｃｕ＿（４０）Ｆｅ＿（６０）进行的高分辨电镜观察表明：球磨３小时后ｂｅｅ相与ｆｅｅ相之间存在Ｎ－Ｗ关系，即〈００１〉＿α／／〈１１０〉＿γ，〈１１０〉＿α／／〈１１１〉＿γ。表明在球磨的过程中可能发生了逆马氏体相变，ｆｅｅ相区的扩展与此密切相关。球磨６０小时后形成了尺寸比较均匀的纳米晶结构。高分辨电镜同时观察到了层状结构的形成。     

气瓶钢中白点焊合的研究

42Mn2气瓶钢中存在有内部白点(即不露头白点)和露头白点,经正常冲压和拔伸制成气瓶后,进行解剖,用低倍、断口、超声波、金相以及扫描电子显微镜观条,证实内部白点可以焊合。而露头白点因表面在高温热成形过程中被氧化需要较大的变形才能焊合完全。强度考核证明,这类气瓶的静压爆破强度(在550—630kg/cm~2)符合正常要求,在10?150 kg/cm~2循环应力下,整体疲劳次数达到30,000—60,000次,声发射仪跟踪监听,未发现有疲劳裂纹产生和扩展的信号。     

难互溶Cu—Fe系机械合金化的高分辨电镜研究

机械合金化可使室温下几乎不互溶体系Ｃｕｘ－Ｆｅ（１００－ｘ）形成过饱和固溶体。ｆｃｃ相区的固溶度范围扩展到ｘ＞３５ａｔ．－％．对Ｃｕ４０Ｆｅ６０进行的高分辨电镜观察表明：球磨３ｈ后ｂｃｃ相与ｆｃｃ相之间存在Ｎ－Ｗ关系，即＜００１＞α∥＜１１０＞γ∥＜１１０＞α∥＜１１１＞γ表明在球磨的过程中发生了逆马氏体相变，ｆｃｃ相区的扩展与此密切相关，球磨６０ｈ后形成了尺寸比较均匀的钠米晶结构，高分辨电镜同时     

机械合金化诱导Fe—Cu系固溶度的扩展

X射线衍射(XRD)表明室温下几乎不固溶的Fe—Cu系经5h球磨后可形成亚稳过饱和固溶体.对于Fe_(1-x)Cu_x,当0≤x≤0.10时形成单一的bcc相,x≥0.30时形成单一的fcc相,0.10相似文献   

Microstructure of SiC Whiskers with Different Cross-sections Perpendicular to the Whiskers Axis

Microstructure of β-SiC whiskers with differ-ent cross-sections perpendicular to their growingdirection was studied in detail by transmission elec-tron microscopy (TEM).It was indicated that therewere three types of cross-sections:round,hexagonal and trigonal.The whiskers with roundand hexagonal cross-sections had a high density ofplanar faults lying on the (111) close packed planesperpendicular to the whisker axis.There existed afew stacking faults on the other {111} planes insome hexagonal whiskers.The whiskers withbicrystals were also found in hexagonal whiskers.The microstructure of trigonal SiC whiskers wasbasically perfect but there were a few intrinsic stack-ing faults on the (11) planes (mostly) and (111)planes.The characters of electron diffraction pat-terns of β-SiC whiskers with different cross-sec-tions were reasonably analyzed using a reciprocalspace model with continuous diffraction streaksalong the [111] reciprocal direction.     

THE IMMUNIZATION OF FLAKES IN A MEDIUM CARBON MANGANESE STEEL BY HOT WORKING

42Mn2气瓶钢中存在有内部白点(即不露头白点)和露头白点,经正常冲压和拔伸制成气瓶后,进行解剖,用低倍、断口、超声波、金相以及扫描电子显微镜观条,证实内部白点可以焊合。而露头白点因表面在高温热成形过程中被氧化需要较大的变形才能焊合完全。 强度考核证明,这类气瓶的静压爆破强度(在550—630kg/cm~2)符合正常要求,在10?150 kg/cm~2循环应力下,整体疲劳次数达到30,000—60,000次,声发射仪跟踪监听,未发现有疲劳裂纹产生和扩展的信号。