Preparation of a Near-Infrared Ray Absorption Film from N-Phenylthiocarbamoyl Chitosan Derivative

We recently observed that the decanoylation of N-phenylthiocarbamoyl chitosan (2) with a mixture of decanoic anhydride and pyridine at 60 °C for 24 h afforded N,N-(decanoyl)phenythiocarbamoyl-/2-isothiocynato chitosan decanoate (3b) rather than the expected product N,N-(decanoyl)phenylthiocarbamoyl chitosan decanoate (3a). This result suggested that some of the N,N-(decanoyl)phenylthiocarmbamoyl groups had been converted to isothiocyanate groups during the decanoylation process. The subsequent reaction of compound 3b with aniline gave N,N-(decanoyl)phenylthiocarbamoyl/N-phenylthiocarbamoyl chitosan decanoate (4) in high yield. A solution of compound 4 in CHCl₃ was then added to a solution of copper decanoate (5) in the same solvent, and the resulting mixture was cast onto a glass plate to give a cast film. The film was annealed at 200 °C in an oven to give a greenish film, which showed good near-infrared absorption characteristic in the range of 800–2200 nm.     

Synthesis and luminescence of Sr2CeO4 fine particles

Fine particles of a blue emission phosphor Sr₂CeO₄ have been synthesized using a chemical co-precipitation technique, and the textual and luminescent properties were compared with the one synthesized by the conventional solid-state reaction method. Particle size and distribution of the Sr₂CeO₄ fine powder prepared by the co-precipitation process were smaller and narrower than those obtained by the samples prepared from the conventional one. The emission intensity of the fine particles was equal to that of the larger particles prepared from the solid-state reaction, on the contrary to the general tendency that emission intensity decrease with particle size reduction. Although no Ce³⁺ peaks were observed in EPR measurements, X-ray photoelectron spectra of the samples clearly elucidated the existence of Ce³⁺ only on the surface of Sr₂CeO₄.     

Comparison of activities in selective catalytic reduction of NOx by C3H8 over Co/MFI, Fe/MFI, and H/MFI zeolite catalysts

The Co/MFI(SiO₂/Al₂O₃ = 30) were prepared by a precipitation method with NaOCl in alkali solutions exhibited high activities to N₂ at 250 °C for the selective catalytic reduction (SCR) of NO_x. These catalysts showed two UV–vis bands at 700 and 400 nm, indicating the presence of octahedral Co(III) as well as tetrahedral Co(II). The high SCR activity over such Co(III, II)/MFI(30) seems to come from Co(III)---O moieties. The Co(II)MFI(30) catalysts prepared from Co(II)Cl₂ exhibited low SCR activities due to the presence of tetrahedral Co(II) ions in MFI. Less CO formation occurred over Co/MFI catalysts. The Fe/MFI(30) catalyst exhibited high activity due to the presence of some Fe---O species in MFI but more amount of CO were produced during SCR. H/MFI(30) catalyst exhibited a good SCR activity. However, more amount of carbonaceous deposits were produced on it. The correlation between acid concentration and SCR activity was discussed over H/MFIs.     

Color registration error reduction method compensating the influence of belt thickness variation in electrophotographic process

This paper proposes a new belt drive control method for reducing a belt velocity-fluctuation that is caused by a belt thickness-variation in the circumferential direction. A belt driving system performs feedback control with a rotary encoder-output mounted on a driven roller. This proposed method correct the reference value of the feedback control for the purpose of the belt velocity regulation. The correction includes two steps. The first step acquires the encoder-output of the driven roller and calculates the rotational angular velocity-fluctuation with one cycle of the belt rotation. The second step converts from the velocity-fluctuation to the correction value of the feedback reference. The correction value cancels a detection error of the driven roller caused by the belt thickness-variation. After these steps, the belt driving system controls the belt velocity as compensating the belt velocity-fluctuation. Experimental result showed the significant fluctuation reduction on a typical tandem-engine printer.     

Environmental effect on room- temperature ductility of isothermally forged tial- base alloys

Isothermally forged TiAl-base alloys (Al-rich, Mn-containing, and Cr-containing TiAl) were heat-treated in various conditions, and equiaxed grain structures consisting of γ and α₂ or Β phases were obtained. The heat-treated alloys were tensile tested in vacuum and air at room temperature, and the environmental effect on tensile elongation was studied. The ductility of the alloys consisting of equiaxed γ grains and a large amount of α₂ grains was not largely affected by laboratory air, and a decrease in the amount of α₂ grains resulted in a large reduction of ductility in air. The Β phase in the Cr-containing alloy improved the ductility in vacuum, but it resulted in a large reduction of ductility in air. Formerly with Kougakuin University, Shinjyuku-ku, Tokyo, Formerly with National Research Institute for Metals, Meguro-ku, Tokyo,     

Restoration of the red colour of photo-bleached carthamine in calcium-alginate gel membranes

The restoration of the red colour of carthamine (photo-bleached in polymeric heterosaccharide gels) was investigated using sodium salts, potassium salts, and alkali. Ca-alginate gel was stained with carthamine, and the red-dish membranes were exposed to fluorescent light for 2·5, 4·0 and 20 h (at 28°C). The resulting orange-yellow gel membranes were treated with Na- or K-citrate solution and the restoration of the red colouration was followed spectrophoto-metrically. The results indicate that the red colour of carthamine can be retained within the gel membranes, while yellow-coloured compounds were removed and/or transformed by the alkaline salt solutions.     

A load dispatch method using fractional programming and semidefinite programming

This paper describes a load dispatch method which minimizes power cost—[fuel cost]/[electric output]—for a power system with thermal plants and energy storage facilities. The proposed method employs fractional programming to convert a minimization problem with fractional objective function to a series of quadratic minimization problems, and semidefinite programming to solve converted problems. The method provides the optimum time‐dependent power output/input and storage level of energy storage facilities as well as time‐dependent power output of thermal plants. The method has been applied to a power system with five thermal plants, two energy storage facilities of various performances, and five load demands. The optimum load scheme of four time mesh points is obtained for the thermal plants and energy storage facilities. The fractional programming successfully converges the optimal scheme through a few iterations. The semidefinite programming deals with a variable matrix of 164 dimensions, and 185 inequality constraints. © 2001 Scripta Technica, Electr Eng Jpn, 138(2): 49–58, 2002     

Superconductivity in W-containing diamond-like nanocomposite films

Superconductivity in a tungsten-containing carbon-oxide film was reported. The film with 500 nm thickness was deposited onto polycrystalline silicon oxides using chemical vapor deposition and the co-sputtering of a tungsten metal target. The bonding state of the carbon atoms and the macroscopic and microscopic crystal structure of the film were investigated by Raman spectroscopy, X-ray diffraction and transmission electron microscopy measurements. From the experimental results, we determined that this film essentially had an amorphous structure. The temperature dependence on resistivity was measured in the temperature range of 2–300 K. Resistive superconducting transition was observed at 3.8 K. The dc magnetizations were measured in the temperature range of 1.8–6.5 K. The diamagnetism resulting from a superconductive state was observed below 3.75 K, which is consistent with a resistive superconducting transition. It is thought that the finite sized clusters of the different superconductive transition temperatures cooperatively produce a macroscopic superconducting phenomenon.     

Effect of 8 MeV electron irradiation on electrical properties of CuInSe2 thin films

Radiation damages due to 8 MeV electron irradiation in electrical properties of CuInSe₂ thin films have been investigated. The n-type CuInSe₂ films in which the carrier concentration was about 3×10¹⁶ cm⁻³, were epitaxially grown on a GaAs(0 0 1) substrate by RF diode sputtering. No significant change in the electrical properties was observed under the electron fluence <3×10¹⁶ e cm⁻². As the electron fluence exceeded 10¹⁷ e cm⁻², both the carrier concentration and Hall mobility slightly decreased. The carrier removal rate was estimated to be about 0.8 cm⁻¹, which is slightly lower than that of III–V compound materials.