离心铸造WC/钢组织结构的研究

选用GCr15轴承钢为基体,WC颗粒为增强相,采用离心铸造工艺制备WC/钢复合材料—LGJW20。用金相分析、电镜扫描(SEM)、X射线衍射(XRD)及能谱分析(EDS)等方法研究材料铸态的相变过程及显微组织。研究结果表明:LGJW20显微组织中基体主要为细小的珠光体组织,基体中析出大量M23C6及MC型等细小碳化物颗粒;WC原始颗粒以各种复式碳化物的形式析出,分别形成枝状或鱼骨状共晶碳化物、网状二次碳化物及大块状碳化物。     

钴磷镀层表面热疲劳裂纹的萌生及扩展机理

在自约束型热疲劳试验机上对化学镀钴磷合金镀层进行了热疲劳试验,采用光学显微镜、扫描电子显微镜研究了在热应力作用下镀层表面热疲劳裂纹萌生、扩展的方式和形态。结果表明:200次冷热循环后,V型缺口处发生塑性变形,并且随冷热循环的进行,热疲劳裂纹由缺口底部萌生并沿着循环方向扩展。重点分析了钴磷合金镀层表面热疲劳裂纹的萌生及扩展机理。     

钢表面镀覆层热疲劳性能研究的进展

综述了表面镀覆层的制备工艺和在合金钢基体上通过电镀、化学镀、熔覆等表面处理技术获得的镀覆层的热疲劳性能,指出影响表面镀覆层热疲劳性能的因素和提高热疲劳抗力的方法.     

颗粒增强钢基复合材料轧辊研究的现状

分析了轧辊的发展趋势,探究了颗粒增强钢基复合材料的力学性能,揭示了颗粒增强钢基复合材料轧辊的性能优势;概述了颗粒增强钢基复合材料轧辊的发展现状和各种制备工艺,并简要分析了轧辊材料的发展.     

起始粉末粒径对Al2O3-TiC陶瓷力学性能的影响

热压烧结制备了Al2O3和Al2O3-TiC复合陶瓷。研究了起始粉末粒径对Al2O3-TiC复合陶瓷力学性能的影响。试验结果表明,添加TiC显著地提高了氧化铝陶瓷的力学性能,σf和K1c分别提高了70％和90％。其中大颗粒TiC对氧化铝陶瓷的增韧尤为有利,其裂纹偏转增长了扩张路径,提高了材料的断裂抗力。     

Microstructure and wear properties of tungsten carbide reinforced steel matrix composites

WC（27%） reinforced steel matrix composites were produced by using an electroslag melting casting technique. The microstructure of the material was characterized using scanning electron microscopy（SEM）, optical microscopy and X-ray diffraction （XRD）. Energy dispersive spectroscopy（EDS） and transmission electron microscopy were performed to investigate the interracial composition between WC particle and steel matrix. The results reveal that the WC particles are partially melted into the steel substrate. At the same time, a reaction layer was detected along with the periphery of WC particle, which significantly enhances the bonding strength of the interface. A slipping wear （high stress abrasion） test was utilized to understand the wear behavior of this material. Abrasive experiment displays a better wear resistance than unreinforced steel matrix when coarse WC particles are dispersed into it. The coarse particles provide greater wear-resistance than the fine particles and operatively takes on the most applied loads. Additionally, the large particles have not been peeled during the wear process for a long time, which indicates the effect of interfacial reaction on wear behavior at the ambient temperature. A double carbide （Fe, W）3C is detected in the interface zone between particles and matrices using transmission electron microscopy.     

电冶钢结硬质合金热处理的研究

研制一种新型的钢结硬质合金--电冶熔铸钢结硬质合金,对其进行热处理试验.结果表明,该合金具有良好的热处理性能,而且热处理可以有效地改善合金原始态中不良的组织结构,经淬火与回火处理后,合金的力学性能有较大幅度的提高.     

长颗粒(柱状晶)Si3N4陶瓷的研究及进展

Si3N4陶瓷材料由于具有很好的高温性能及高的力学性能，而被广泛地用于结构陶瓷，如切削刀具等。然而，因为其对缺陷很敏感，故易受灾难性的失效。人们发展了多种Si3N4增韧陶瓷，其中自增韧由于一些优异的性能越来越受到人们的重视。在此文中，着重介绍了影响Si3N4陶瓷长颗粒(柱状晶)晶粒生成的因素，并介绍了国内外对长颗粒Si3N4晶的控制研究。     

提高Cr12型钢材冷作模具寿命的方法

前言在冷作模具用钢中,Cr12型钢材的(Cr12和 Cr12MoV)用量最大。据估算,我国现在每年消耗 Cr12型钢材已超过1万吨。近十年来。为了减少耗量,降低成本,有利于提高Cr12型钢材模具寿命的热处理新工艺发展。本文对其中已用于生产实践,且效果显著的方法作一系统介绍,以促进其更广泛的应用和发展。一、预先热处理