改性纳米SiO_2/尼龙复合塑料性能的研究

采用熔融共混法制备改性纳米SiO2/PA6复合塑料,研究了纳米SiO2用量及其粒径对SiO2/PA6复合PA6力学性能、耐热性能和阻隔性能的影响。结果表明:纳米SiO2粒子在纳米SiO2/PA6复合材料中的分散增强了树脂之间的作用力;在一定范围内,随着纳米SiO2用量的增加,改性纳米SiO2/PA6的耐冲击性能、弯曲强度、拉伸强度和耐热性均有一定提高,而纳米SiO2粒径越小,力学性能提高就越显著;当纳米SiO2质量分数为2%~3%时,改性纳米SiO2/PA6透氧性最小,当纳米SiO2质量分数为3%~4%时,改性纳米SiO2/PA6透湿性最小。     

水基乳液型纸塑复合粘合剂的制备

以丙烯酸丁酯、醋酸乙烯酯、丙烯酸、十二烷基硫酸钠、过硫酸铵、水性松香树脂等为原料,采用预乳聚合法成功制备了性能优良的水基乳液型纸塑复合粘合剂.讨论了软硬单体配比、引发剂、功能单体、增粘剂用量及聚合反应时间等因素对粘合剂的剥离强度和粘度的影响,确定了水基乳液型纸塑复合粘合剂的最佳工艺条件,各组分质量分数为:丙烯酸丁酯65.3%、醋酸乙烯酯21.2%、丙烯酸5.5%、十二烷基硫酸钠3.8%、过硫酸铵0.4%、水性松香树脂3.0%,聚合反应时间为2.5 h.     

三价铬超声-脉冲电沉积Cr/SiC纳米复合镀层

利用超声-脉冲电沉积法,在三价铬镀液中,添加羧酸盐-尿素配合剂和SiC纳米颗粒,制备了Cr/SiC复合镀层。研究了超声-脉冲工艺参数对纳米SiC复合量、镀层厚度的影响。利用电化学法分析了超声波对三价铬电沉积Cr/SiC复合镀层的电化学行为。结果表明,超声-脉冲作用均有利于基质金属铬的电沉积,从而提高镀层厚度及SiC复合量。利用SEM、XRD、和EDS分别对Cr/SiC复合镀层的表面形貌、微观结构和组成等进行表征。结果表明,采用该技术可制备厚度为13.5μm、SiC含量为5.5%的Cr/SiC纳米复合镀层。     

扣肉高温蒸煮异型袋包装设计

采用高温蒸煮袋技术,围绕蒸煮袋的结构及蒸煮袋材料的选择、材料厚度的确定、理论保质期的计算等内容对扣肉蒸煮异型袋袋装设计.通过理论分析计算,确定所设计的扣肉异型高温蒸煮袋的透明阻隔层材料为BOPP25/EVOH16/CPP50、不透明阻隔层材料为BOPP25/Al10/CPP50;根据扣肉的最大允许透水量、所设计材料透湿系数和厚度,理论估算该高温蒸煮袋的保质期为1.6年,符合设计要求.     

咪唑类离子液体电化学窗口影响因素的研究进展

咪唑类离子液体具有较宽的、稳定的电化学窗口,引起科技工作者的研究兴趣。对咪唑类离子液体的电化学窗口进行了总结和分析。考察了咪唑类离子液体阴、阳离子结构和正离子还原极限与负离子氧化极限及电极材料分别对电化学窗口的影响,并从离子液体的结构-性质方面,分析了其相关基本规律。     

三价铬超声-脉冲电沉积Fe-Ni-Cr/SiC纳米复合镀层

利用超声-脉冲复合电沉积法,在三价铬镀液体系中,添加羧酸盐-尿素配合剂和SiC纳米颗粒,制备了Fe-Ni-Cr/SiC纳米复合镀层.研究了超声-脉冲工艺参数与SiC纳米粒子复合量、Cr含量及镀层厚度的关系;利用稳态极化曲线和循环伏安法分析了超声波对阴极电化学行为的影响.结果表明,超声-脉冲作用均有利于基质金属Fe、Ni和Cr的电沉积,提高了镀层中SiC和Cr的含量以及镀层的厚度.利用扫描电镜、X射线衍射仪和能谱仪对Fe-Ni-Cr/SiC纳米复合镀层的表面形貌、微观结构和组成等进行表征,发现采用该技术可制备厚度为23.56μm,SiC和Cr质量分数分别为4.1%和25.1%的Fe-Ni-Cr/SiC纳米复合镀层.磨损量和腐蚀曲线测试结果表明,SiC含量高的复合镀层,其耐磨性和耐蚀性更好.      

Process of pulse electrodeposition nanocrystalline chromium from trivalent chromium bath

Nanocrystalline chromium coating was prepared by pulse electrodeposition from trivalent chromium bath containing carboxylate-urea as complexing agent. The effects of electrodeposition parameters such as current density, bath temperature and solution concentration on the thickness and electrodeposition velocity of Cr deposited films were investigated. The crystallographic structures, morphology and chemical composition of Cr deposited films were analyzed by means of XRD, SEM and EDS. The results indicate that the deposited films with thickness up to 11.2 μm possess a smooth and clean appearance, and the grain size is less than 100 nm. The coating is pure chromium and the Cr deposit has face-centered cubic （fcc） structure and exhibits a （210） growth preference. Both the electrodeposition velocity and thickness exist maximum under different concentration complex agents, ureas, acetates, different temperatures and current densities. Compared with direct current electrodeposition, the thicker coating and finer grains can be obtained at lower temperature and current density by pulse electrodeposition. The electrodepostion velocity is about 0.24 μm/min, which is faster than that by direct current electrodeposition. In l mol/L H2SO4, 3.5% NaCl and 10% NaOH solution, corrosion potential of Cr pulse-deposited film is about 100 mV higher than that of direct current. Corrosion and passivation current densities are lower and the nanocrystalline exhibits better corrosion resistance.     

三价铬脉冲电沉积纳米晶Ni-Cr合金工艺

采用脉冲电沉积方法对三价铬电沉积Ni-Cr合金镀层工艺进行研究,确定并优化三价铬脉冲电沉积Ni-Cr合金的最佳镀液配方及工艺参数。研究镀液中各成分及工艺参数对三价铬脉冲电沉积Ni-Cr合金厚度及合金镀层中铬的影响,利用扫描电镜和电子能谱分析Ni-Cr合金镀层的形貌、微观结构和化学组成。结果表明,镀层厚度和Ni-Cr合金中铬含量在不同浓度的络合剂、稳定剂、乙酸钠及不同的电流密度、温度、pH值、占空比和脉冲频率下都存在极大值,且Ni-Cr合金厚度随合金中铬含量的增加而减少。当铬含量为24%时,镀层的厚度大于10μm,无裂纹,其晶粒为纳米球状晶粒。     

原料对氧化淀粉改性PVA薄膜水溶性的影响

采用氧化淀粉改性的方法制备流延改性PVA水溶性薄膜。研究了各组分不同浓度对氧化淀粉改性PVA水溶性薄膜水溶性的影响。实验结果表明:氧化淀粉和明胶用量对氧化淀粉改性PVA水溶性薄膜的水溶性影响非常显著,而甘油、十二烷基醚硫酸钠、甲基丙烯酸酯对水溶时间的影响较小。当氧化淀粉浓度为23%,明胶质量浓度为5%,甘油质量浓度为16%,氨基硅油质量浓度为0.05%,十二烷基醚硫酸钠质量浓度为0.12%,甲基丙烯酸酯质量浓度为0.2%,十二烷基硫酸钠质量浓度为4%时,制备的薄膜水溶性时间仅为133 s。     

三价铬超声-脉冲电沉积Ni-Cr/SiC纳米复合镀层

利用超声-脉冲复合电沉积法,在三价铬镀液体系中,添加羧酸盐-尿素配合剂和SiC纳米颗粒,制备了Ni-Cr/SiC纳米复合镀层。研究了超声-脉冲工艺参数对SiC纳米粒子复合量、铬含量以及镀层厚度的影响;利用电化学法分析了超声波对基质金属电沉积行为的影响。结果表明,超声-脉冲作用均有利于基质金属铬-镍的电沉积,从而提高镀层厚度及SiC与Cr的含量。利用SEM、XRD、和EDS分别对Ni-Cr/SiC纳米复合镀层的表面形貌、微观结构和相组成等进行表征。结果表明,采用该技术可制备厚度为21.2μm、SiC和Cr含量分别为3.8%和24.68%(质量分数)的Ni-Cr/SiC纳米复合镀层。磨损量和腐蚀曲线测试结果表明,SiC含量高的复合镀层,其耐磨性和耐蚀性更好。