Vimanyu Chadha Waltraud M. Kriven 《International Journal of Applied Ceramic Technology》2021,18(4):1097-1105
Geopolymer composites reinforced with refractory, chopped basalt fibers, and low melting glass were fabricated and heat treated at higher temperatures. K2O·Al2O3·4SiO2·11H2O was the stoichiometric composition of the potassium-based geopolymer which was produced from water glass (fumed silica, deionized water, potassium hydroxide), and metakaolin. Addition of low melting glass (Tm ~815°C) increased the flexure strength of the composites to ~5 MPa after heat treatment above 1000°C to 1200°C. A Weibull statistical analysis was performed exhibiting how the amorphous self-healing and self-glazing effect of the glass frit significantly improved the flexure strength of the geopolymer and ceramic composites after exposure for 1 hour to high temperatures. At 950-1000°C, the K-based geopolymer converted to primarily a crystalline leucite ceramic, but the basalt fiber remained intact, and the melted glass frit flowed out of the surface cracks and sealed them. 1150℃ was determined to be the optimum heat treatment temperature, as at ≤1200°C, the basalt fibers melt and the strength of the reinforcement in the composites is significantly reduced. The amorphous self-healing and amorphous self-glazing effects of the glass frit significantly improved the room temperature flexure strength of the heat-treated geopolymer and ceramic composites. 相似文献
3.
Patrick F. Keane John S. Foltz Vimanyu Chadha Charles P. Marsh Waltraud M. Kriven 《Journal of the American Ceramic Society》2021,104(7):3443-3451
Geopolymer composites containing refractory, chopped basalt fibers and low-melting glass were made and systematically heat-treated at higher temperatures. Potassium-based geopolymer of stoichiometric composition K2O·Al2O3·4SiO2·11H2O was produced by high shear mixing from fumed silica, deionized water, potassium hydroxide, (i.e., water glass) and metakaolin. With the addition of low-melting glass (Tm ~815°C) the flexure strengths of the composites increased to ~6 MPa after heat treatment above 900°C to 1100°C. A Weibull statistical analysis was performed showing how the amorphous self-healing effect of the glass frit significantly improved the flexure strength of the geopolymer and ceramic composites after high-temperature exposure. At temperatures up to 900°C, the geopolymer-basalt composite remained amorphous and the low-melting glass frit flowed into the dehydration cracks in the geopolymer matrix. This type of composite could be described as amorphous self-healed geopolymer (ASH-G). At ~1000°C, the geopolymer converted to primarily a crystalline leucite ceramic, but the basalt fiber remained intact, and the melted glass frit flowed and sealed the cracks developed at that temperature. This type of composite could then be described as amorphous self-healed ceramic (ASH-C). A temperature of 1150°C was determined to be optimum as at 1200°C the basalt fibers melted and the strength of the reinforcement was lost in the composites. The amorphous self-healing effect of the glass frit significantly improved the room temperature flexure strength of the heat-treated geopolymer-based composites. 相似文献
1