The structure solution of the F-type i-ZnMgHf from the X-ray diffraction

ABSTRACT

We report a successful growth of the ZnMgHf F-type icosahedral quasicrystal in the form of faceted single grains. By varying the heat treatment parameters we were able to obtain single crystals with a quality suitable for a single crystal X-ray diffraction which was conducted in a synchrotron facility. Ab initio structure solution by a charge flipping algorithm manifests the existence of two types of Bergman clusters. Clusters are differentiated by the preferential occupation of the high-symmetry positions by hafnium in a rhombic triacontahedron, being the outer shell of the atomic cluster.

This paper is part of a Thematic Issue on The Crystallographic Aspects of Metallic Alloys.     

Bottom-up synthesis of oxygen-containing carbon materials using a Lewis acid catalyst

Oxygen-containing carbon materials have been studied extensively because of their excellent dispersibility, absorptivity, separability, and supportability of catalysts. However, structural control by existing top-down methods is almost impossible. Our group has demonstrated that phloroglucinol (PG, 1,3,5-trihydroxybenzene) can be a promising raw material to synthesize structurally controlled oxygen-containing carbon materials. In this study, in addition to PG, hexahydroxybenzene (HHB), which has more oxygen and high symmetry, was used as the raw material, and a Lewis acid catalyst, tris (pentafluorophenyl) borane (TPB), was used to enhance the structural control rate and the removability of catalysts from the carbonized samples. The solubility of heat-treated HHB was lower than that of heat-treated PG, but the oxygen content of heat-treated HHB was higher than that of heat-treated PG even at 673 K. By adding TPB to PG, dibenzofuran-like structures formed, and the structural control rate increased up to 93.6%. Besides, the content of fluorine in the catalyst was reduced to 0%, indicating that TPB can be a promising recyclable catalyst to promote the structural control rate of carbonized PG.

Graphical abstract

     

Additive effects of methyl ammonium bromide or formamidinium bromide in methylammonium lead iodide perovskite solar cells using decaphenylcyclopentasilane

Journal of Materials Science: Materials in Electronics - Fabrication and characterization of methylammonium lead iodide perovskite solar cells incorporated with methylammonium bromide (MABr),...     

Changes in dietary bioaccumulation of tributyltin chloride (TBTCl) in red sea bream (Pagrus major) with the concentration in feed

The effect of the concentration of tributyltin (TBT) in feed on the dietary bioaccumulation of tributyltin chloride (TBTCl) was studied in an 8-week uptake experiment and a 4-week elimination experiment using red sea bream (Pagrus major). The biomagnification factor (BMF) and the assimilation efficiency (AE) decreased from 0.30 to 0.15 and from 13% to 5.9%, respectively, as the TBT concentration in feed increased from 1.3 to 20 microg/g. The elimination rate constant (k(2)) was independent of the TBT concentration in the fish. Laboratory measurements of the BMF and AE of TBTCl underestimate actual field values if highly contaminated feed is used. Judging from the BMF and AE, the risk of the bioaccumulation of TBTCl through the food chain might be smaller than that of polychlorinated biphenyls.     

Effect of TiO2 on morphology and mechanical properties of PVDF/PMMA blend films prepared by melt casting process

Effect of titanium dioxide (TiO₂) on morphology and mechanical properties of poly(vinylidene fluoride) (PVDF)/poly(methyl methacrylate) (PMMA) blend films prepared at different TiO₂ contents by a melt casting process was studied. The results showed that tensile moduli in both the machine direction (MD) and the transverse direction (TD) increased with increasing TiO₂ content, and calculated tensile moduli based on the Halpin–Tsai and the Kerner model were consistent with experimental ones in both the MD and TD of films containing 10 wt % TiO₂. However, experimental tensile moduli exhibited smaller values compared with calculated ones, as the TiO₂ content increased to 30 wt %_, and it was assumed that this is due to the decrease of crystallinity of PVDF. Morphological observations indicated that TiO₂ particles did not affect crystal structures of PVDF and the morphology of PVDF/PMMA amorphous phase, but hindered the crystallization of PVDF. The MD and TD elongation at break exhibited >200 and <20%, respectively. The SEM micrographs revealed that spherulites could deform along the MD when the tensile force was applied along the direction. By contrast, spherulites could not deform along the TD and fractured at very small elongation, owing to the anisotropic morphology of spherulites. © 2014 Wiley Periodicals, Inc. J. Appl. Polym. Sci. 2014 , 131, 40454.