Synthesis of nanopowders with low agglomeration by elaborating Φ values for producing Gd2O3-MgO nanocomposites with extremely fine grain sizes and high mid-infrared transparency

Refining ceramic microstructures to the nanometric range to minimize light scattering provides an interesting methodology for developing novel optical ceramic materials. In this work, we reported the fabrication and properties of a new nanocomposite optical ceramic of Gd₂O₃-MgO. The citric acid sol-gel combustion method was adopted to fabricate Gd₂O₃-MgO nanocomposites with fine-grain sizes, dense microstructures and homogeneous phase domains. Nanopowders with low agglomeration and improved sinterability can be obtained by elaborating Φ values. Further refining of the microstructure of the nanocomposites was achieved by elaborating the hot-pressing conditions. The sample sintered at 65 MPa and 1300 °C showed a quite high hardness value of 14.3 ± 0.2 GPa, a high transmittance of 80.3 %–84.7 % over the 3?6 μm wavelength range, due mainly to its extremely fine-grain size of Gd₂O₃ and MgO (93 and 78 nm, respectively) and high density.     

Achieving fabrication of highly transparent Y2O3 ceramics via air pre-sintering by deionization treatment of suspension

An easy albeit quite effective deionization suspension treatment was adopted to alleviate the detrimental effects related to the hydrolysis of Y₂O₃ in an aqueous medium. Fabrication of highly transparent Y₂O₃ ceramics with a fine grain size via air pre-sintering and post–hot isostatic pressing (HIP) treatment without using any sintering additive was achieved using the treated suspensions. The hydrolysis issue of Y₂O₃ powder in an aqueous medium was effectively alleviated by using deionization treatment, and a well-dispersed suspension with a low concentration of dissolved Y³⁺ species was obtained. The dispersed suspensions were consolidated by the centrifugal casting method, and the green bodies derived from the suspension of 35.0 vol% solid loading showed an improved homogeneity with a relative density of 52.1%. Fully dense Y₂O₃ transparent ceramic with high transparency was obtained by pre-sintering consolidated green compacts at a low temperature of 1400°C for 16 h in air followed by a post-HIP treatment at 1550°C for 2 h under 200 MPa pressure. The sample had a fine average grain size of 690 nm. The in-line transmittance of the sample reached 83.3% and 81.8% at 1100 nm and 800 nm, respectively, very close to the theoretical values of Y₂O₃.     

遥感卫星随遇接入互联网星座和在轨智能处理

低轨互联网星座是当前全球研究和发展的热点,互联网星座支持随遇接入遥感卫星和信息在轨直接处理的应用前景备受期待,但由于轨道高度不同会产生双向高动态异构星座的接入互联问题。首先,通过设定低轨卫星互联网星座在不同轨道特性、不同卫星数量情况下的随遇接入仿真场景,重点探讨了时空非连续可视性和多普勒频移问题对遥感卫星接入性能的影响;其次,基于遥感卫星随遇接入互联网星座场景的特点,分析了不同时延性在轨处理任务的流程及其星地功能分配;最后,对当前在轨智能处理算法存在的问题和未来研究重点进行阐述,为未来低轨互联网星座及遥感卫星的发展和联合组网应用提供可靠的理论支撑。     

综合设计性实验在药物分析学实验中对学生综合能力的培养

《药物分析学实验》是药学专业的一门独立必修课程,是药学科学领域中的一个重要组成部分,具有较强的实践性和综合性,旨在培养学生综合运用所学知识分析药品质量的能力.综合设计性实验作为《药物分析学实验》的重要组成部分,对学生实践操作能力,发现问题、分析问题、解决问题的能力,创新能力,应用能力,团结协作能力,劳动素养等综合能力的培养具有极其重要的意义.     

Field-Effect Chiral Anomaly Devices with Dirac Semimetal

Charge-based field-effect transistors (FETs) greatly suffer from unavoidable carrier scattering and heat dissipation. Analogous to valley degree of freedom in semiconductors, chiral anomaly current in Weyl/Dirac semimetals is theoretically predicted to be nearly nondissipative over long distances, but still lacks experimental ways to efficiently control its transport. Here, field-effect chirality devices are demonstrated with Dirac semimetal PtSe₂, in which its Fermi level is close to the Dirac point in the conduction band owing to intrinsic defects. The chiral anomaly is further corroborated by the planar Hall effect and nonlocal valley transport measurement, which can also be effectively modulated by external fields, showing robust nonlocal valley transport with micrometer diffusion length. Similar to charge-based FETs, the chiral conductivity in PtSe₂ devices can be modulated by electrostatic gating with an ON/OFF ratio of more than 10³. Basic logic functions in the devices are also demonstrated with electric and magnetic fields as input signals.     

Thermo-adjusted self-healing epoxy resins based on Diels–Alder dynamic chemical reaction

Micro-damage in materials could be repaired by endowing materials with self-healing performance. Herein, an epoxy resin with excellent self-healing performance grounded on thermo-reversible Diels–Alder dynamic chemical reaction was developed. Results showed that the bending strength and adhesive behavior of epoxy resin were influenced dramatically upon treatment with various temperatures. More importantly, damages created in epoxy resin could be repaired completely after suitable heat treatments. What is more, the healed epoxy resin exhibited much higher bending strength and adhesive performance than the pristine one did. The materials could be damaged and then repaired repeatedly. Meanwhile, the as-prepared self-healing epoxy resin exhibited excellent thermal reversibility and controllable adhesion. The thermo-adjusted self-healing performance endowed epoxy resin with recyclable and reusable performance. Therefore, the research made it possible of recycling waste epoxy resins.     

Peer-to-peer electricity trading system: smart contracts based proof-of-benefit consensus protocol

Wireless Networks - Nowadays, people trade electricity through centralized companies or organizations which is vulnerable to cyber attacks and incapable of coping with increasing demands from...     

Large electrostrictive effect and high energy storage performance of Pr3+-doped PIN-PMN-PT multifunctional ceramics in the ergodic relaxor phase

The photoluminescence, dielectric relaxation, ferroelectric hysteresis, and field-induced strain properties of Pr³⁺-doped 0.24Pb(In_1/2Nb_1/2)O₃-0.42Pb(Mg_1/3Nb_2/3)O₃-0.34PbTiO₃ (PIN-PMN-PT:Pr³⁺) multifunctional ceramics have been investigated. It was found that Pr³⁺ doping enhanced the dielectric diffuseness and relaxation behavior of PIN-PMN-PT ceramics. Slim P-E loops and S-E curves appear in PIN-PMN-PT:Pr³⁺ ceramics when the Pr³⁺ doping concentration reaches 1.4 mol%. Local domain configurations associated with phase transitions were investigated by piezoresponse force microscopy (PFM). Large electrostrictive coefficient Q₃₃ (?0.03 m⁴/C²) and high energy-storage efficiency η (92%) were obtained in 2 mol% Pr³⁺-doped PIN-PMN-PT ceramic in the ergodic relaxor (ER) phase at room temperature. The giant electrostrictive effect and excellent energy-storage performance are related to the field-induced dynamic behavior of polar nanoregions (PNRs). The results show that the PIN-PMN-PT:Pr³⁺ system is an excellent multifunctional material for making electromechanical and energy storage devices.     

A strategy for defects healing in 3D printed ceramic compact via cold isostatic pressing: Sintering kinetic window and microstructure evolution

In this study, we developed a unique defect healing method for 3D printed ceramic compact via cold isostatic pressing (CIP) after debinding, and typical features of interlayer interface defects of 3D-printed zirconia compact were characterized and found to be reduced significantly. The characteristic sintering kinetics window and microstructure evolution of the healed sintered bodies were systematically investigated, which was found to be quite different from conventional shaping methods. The three sintering stages are probed by their feature microstructure details such as the mechanically flattening surface at the early sintering stage, the heterogeneous microstructure and high porosity in the interlayer interface region at the middle stage, and the slightly ripple-like structural features combined with the healed interlayer defects at the final stage. The evolution of the pore structure of the healed 3D printed bodies were traced and the mechanical properties such as the Young's modulus, hardness, and fracture toughness were measured to understand the significance of the heal effect.     

Biodegradation of Endocrine Disrupting Chemicals with Laccase Isozymes from Recombinant Pichia pastori

Catalysis Letters - In this paper, five recombinant strains: GS115-LacA, GS115-LacB, GS115-LacC, KM71H-Lcc1 and GS115-Lcc2 were selected to produce laccase isozymes with high activities, which...