一种大量元素水溶肥料的制备及其在玉米上的喷施效果

根据玉米需肥特性设计氮磷钾比例,制备了含中微量元素的大量元素水溶肥料,产品氮、磷、钾比例为2∶1∶4,属于高钾中氮低磷型.在河北省安平县前子文村和浙江省新昌县孟家塘村玉米上开展了叶面喷施试验.结果表明:玉米生物学性能得到改善,玉米产量、出籽率、百粒重与容重得到提高;与空白对照相比,平均增产率为5.45％,平均纯增收896.40元/公顷,平均产投比为5.43∶1.     

负极添加NMP对电池性能的影响

锂离子电池负极浆料中添加N-甲基吡咯烷酮(NMP),在极片加热干燥时不能完全除去.残留的NMP吸附在石墨表面,使得SEI膜与石墨结合不牢固.研究了其对电池性能的影响,结果显示,在电池的循环过程中,SEI膜逐渐脱落,导致电池循环寿命缩短,但对电池的容量、内阻、倍率、存储等初期性能不影响.     

Preparation and electrochemical characterization of Ti-based amorphous metallic glass with high strength

Ti-based amorphous metallic glasses have excellent mechanical, physical, and chemical properties, which is an important development direction and research hotspot of metal composite reinforcement. As a stable, simple, efficient, and large-scale preparation technology of metallic powders, the gas atomization process provides an effective way of preparing amorphous metallic glasses. In this study, the controllable fabrication of a Ti-based amorphous powder, with high efficiency, has been realized by using gas atomization. The scanning electron microscope, energy-dispersive spectrometer, and X-ray diffraction are used to analyze surface morphology, element distribution, and phase structure, respectively. A microhardness tester is used to measure the mechanical property. An electrochemical workstation is used to characterize corrosion behavior. The results show that as-prepared microparticles are more uniform and exhibit good amorphous characteristics. The mechanical test shows that the hardness of amorphous powder is significantly increased as compared with that before preparation, which has the prospect of being an important part of engineering reinforced materials. Further electrochemical measurement shows that the corrosion resistance of the as-prepared sample is also significantly improved. This study has laid a solid foundation for expanding applications of Ti-based metallic glasses, especially in heavy-duty and corrosive domains.     

5G时代下VR/AR在广电新媒体行业中的应用探究

近年来,随着国民经济的快速增长,人们的生活质量得到进一步提升,基于此,新媒体行业得到快速发展.对此,基于VR、AR技术特点,探析"5G+4K/8K+AR/VR"新技术在广电新媒体制播领域的实践应用.     

基于S32K144的燃料电池堆控制系统设计

基于汽车级微控制器S32K144芯片,完成了车用质子交换膜燃料电池堆控制系统的软硬件设计,分别设计了膜电极单模电压检测电路和燃料电池堆控制电路,开发了基于C语言的膜电极电压采集程序和燃料电池堆控制程序,并且用样机验证了设计.     

Characteristics of reaction and product microstructure during light calcination of magnesite in transport bed

A gas-heating laboratory transport bed was adopted to simulate the industrial transportbed reactor for flash calcination of magnesite, and a method based on TG analysis of a reacted sample was further developed to calculate the decomposition rate or conversion of its containing MgCO₃. The study investigated how the conversion and product reactivity as well as microstructure vary with reaction conditions including temperature, particle size and times of re-calcination for powder magnesite. Magnesite powder (<150 μm) calcination is a quick reaction that reaches 98% decomposition of its containing MgCO₃ in 1—2 s,corroborating the feasibility of magnesite flash-calcination in transport bed reactors. The coloration time given by the citric acid chromogenic method was 17—55 s and 294 s for the obtained products from transport and fixed beds, respectively. This proves the obviously higher activity and thus improved microstructure of the product from transport bed. During the calcination process, the MgO grain size of the product gradually increases, and the surface structure changes from loose and porous to dense and smooth. This structural change can be completed within a few seconds.     

基于禁忌搜索的晶体位置谱分割与校准方法

为满足不同规格晶体探测器对分割校准晶体条响应事件位置数据的需求，开发了一种以禁忌搜索算法为核心，结合UDP数据帧、二维高斯模型及光导折射率的位置信息分割校准方法。实验结果表明，本方法在溢出率为5%时，峰谷比可达1218，空间分辨率达17 mm，晶体条响应位置识别准确度高达99%，滤除了引发伪峰的噪声，避免了过分割问题。在面对多种规格晶体阵列的位置谱时，本方法能依照阵列规格将晶体条区域的响应自动校准编号并输出晶体位置查找表，实现响应事件的精确校准。