Microstructures and properties of nickel-titanium carbide composites fabricated by laser cladding

In this work, Ni/TiC composites were synthesized by the laser cladding technique (LCT). A scanning electron microscope (SEM), X-ray diffractometer (XRD), microhardness meter, electrochemical workstation, and friction and wear tester examined the microstructure, surface morphology, phase structure, microhardness, wear, and corrosion resistances of the Ni/TiC composites. These results indicated the Ni/40TiC composite contained finer equiaxed crystals than the Ni and Ni/20TiC composites. In addition, numerous TiC particles in the Ni/40TiC composite impeded growth of the nickel crystals, which resulted in the fine microstructure of the Ni/40TiC composite. The Ni, Ni/20TiC, and Ni/40TiC composites exhibited face-centered cubic (f c c) lattices. The average microhardness values of the Ni/20TiC and Ni/40TiC composites were approximately 748 HV and 851 HV, respectively. The Ni/40TiC composite had the lowest friction coefficient (0.43) among all three coatings, and only some shallow scratches appeared on the surface of the Ni/40TiC composite. The corrosion potential (E) of Ni/40TiC exceeded the Ni/20TiC composite, and both were larger than the Ni composite, which indicated the Ni/40TiC composite had outstanding corrosion resistance and the Ni composite had poor corrosion resistance. The corrosion current densities (i) of Ni, Ni/20TiC, and Ni/40TiC composites were 5.912, 4.405, and 3.248 μA/cm², respectively.     

Catalytic combustion synthesis of CNTs/MgO composite powders and the influences on the thermal shock resistance of low-carbon Al2O3–C refractories

Using MgC₂O₄, Mg powders as raw materials and Ni(NO₃)₂?6H₂O as a catalyst, CNTs/MgO composite powders were prepared by a catalytic combustion synthesis method. The CNTs/MgO composite powders were characterized by XRD, Raman spectroscopy, FESEM/EDS and HRTEM. The effects of catalyst content on the degree of graphitization and aspect ratio of the CNTs in composite powders were investigated. Moreover, the thermal shock resistance of low-carbon Al₂O₃–C refractories after adding the composite powder was investigated. The results indicated that the CNTs prepared with 1 wt% Ni(NO₃)₂?6H₂O addition had a higher degree of graphitization and aspect ratio. In particular, the aspect ratio could reach approximately 200. The growth mechanism of hollow bamboo-like CNTs in the composite powders was proven to be a V-L-S mechanism. The thermal shock resistance of Al₂O₃–C samples could be improved significantly after adding CNTs/MgO composite powders. In particular, compared with CM0, the residual strength ratio of Al₂O₃–C samples with added 2.5 wt% composite powders could be increased 63.9%.     

成分配比对稀土钨电极材料组织及力学性能影响

通过固液掺杂、等静压压制、中频烧结的方法，制备了不同的氧化镧、氧化钇、氧化锆三元掺杂成分比例的钨电极材料烧结棒材，探究了不同成分配比对样品显微组织、第二相粒子分布以及宏观力学性能的影响。结果表明，氧化镧、氧化钇、氧化锆三元复合添加能够有效改善第二相粒子在钨基体中的分布形态，降低第二相在晶界的过度富集，提高钨电极材料的综合力学性能。并且当添加成分镧、钇、锆质量比为3:1:1时，材料具有最好的综合力学性能，致密度可达96.04%，显微硬度可达549.37HV0.3，抗压强度可达3785MPa，原因是此配比下第二相粒子最为细小均匀，弥散程度最高，对基体晶粒的细化作用最好，该配比下钨基体平均晶粒尺寸达到10.3μm。     

Data fusion and transfer learning empowered granular trust evaluation for Internet of Things

In the Internet of Things (IoT), a huge amount of valuable data is generated by various IoT applications. As the IoT technologies become more complex, the attack methods are more diversified and can cause serious damages. Thus, establishing a secure IoT network based on user trust evaluation to defend against security threats and ensure the reliability of data source of collected data have become urgent issues, in this paper, a Data Fusion and transfer learning empowered granular Trust Evaluation mechanism (DFTE) is proposed to address the above challenges. Specifically, to meet the granularity demands of trust evaluation, time–space empowered fine/coarse grained trust evaluation models are built utilizing deep transfer learning algorithms based on data fusion. Moreover, to prevent privacy leakage and task sabotage, a dynamic reward and punishment mechanism is developed to encourage honest users by dynamically adjusting the scale of reward or punishment and accurately evaluating users’ trusts. The extensive experiments show that: (i) the proposed DFTE achieves high accuracy of trust evaluation under different granular demands through efficient data fusion; (ii) DFTE performs excellently in participation rate and data reliability.     

Interface regulation effects on mechanical behavior of heterostructure Ti6Al4V/TiAl-based laminated composite sheets

Design of architectured composites with layered-ordered structure can solve the strength-toughness mismatch problem of structural materials. In the present study, heterostructure Ti6Al4V/TiAl laminated composite sheets with different thicknesses of interface layer and TiAl composite layer were successfully produced by hot-pressing technology. The effects of interface regulation and laminated structure on their mechanical properties, crack propagation, and fracture behavior were studied. The results indicated that compressive strength of the sheets increased with the decrease in interface thickness. Compressive strength of TiAl composite sheet with thicker composite layer reached 1481.55 MPa at the arrester orientation with sintering holding time of 40 min, which was 25.96% higher than that of the sheet obtained at 120 min. Analysis indicated that the interface area transferred stress through slip bands and through-interface cracks. Compressive strength at the divider orientation reached 1443.06 MPa, which was 45.78% higher than that of the sheet obtained at 120 min. In this case, the interface area transferred stress through slip bands and along-interface cracks. For TiAl composite sheets with thinner composite layer, compressive strength was further improved to 1631.01 MPa and 1594.66 MPa at the arrester and divider orientations with sintering holding time of 40 min, respectively. The ductile metal layer exerted a significant toughening effect. Both interface regulation and laminated structure transformation could enhance the hetero-deformation induced (HDI) strengthening and improve the comprehensive mechanical properties of the composite sheets.     

Development of a H2-permeable Pd60Cu40-based composite membrane using a reverse build-up method

A new reverse build-up method is developed to fabricate an economical H₂-permeable composite membrane. Sputtering and electroplating are used for the formation of a membrane comprised of a 3.7-μm-thick Pd₆₀Cu₄₀ (wt.%) alloy layer and a 13-μm-thick porous Ni support layer, respectively. The H₂-permeation measurements are performed under the flow of a gaseous mixture of H₂ and He at 300–320 °C and 50–100 kPa of H₂ partial pressure. The H₂/He selectivity values exceed 300. The activation energy at 300–320 °C is 10.9 kJ mol⁻¹. The H₂ permeability of the membrane is 1.25 × 10⁻⁸ mol m⁻¹ s⁻¹ Pa^−0.5 at 320 °C after 448 h. The estimated Pd cost of the proposed membrane is approximately 1/8 of the cost for a pure Pd₆₀Cu₄₀ membrane. This study demonstrates that the proposed method allows the facile production of low-cost, Pd-based membranes for H₂ separation.     

Microstructure,wear and corrosion characteristics of multiple-reinforced (SiC–B4C–Al2O3) Al matrix composites produced by liquid metal infiltration

In this study, AA7075 aluminum matrix composites reinforced with the combination of SiC, Al₂O₃, and B₄C particles were fabricated by the liquid metal infiltration method. The effects of the relative ratio of B₄C and Al₂O₃ particles on the microstructural, wear, and corrosion features of the composite samples were analyzed using XRD, light metal microscopy, SEM, EDS, Brinell hardness, ball-on-disc type tribometer, and potentiodynamic polarization devices. It was determined that infiltration occurred more successfully, and homogenously distributed particles with reduced porosity were obtained as the amount of Al₂O₃ increased. Worn surface studies revealed that the specimens were predominantly worn by abrasion and adhesion. The increase in B₄C/Al₂O₃ ratio caused a decrease in the hardness and wear strength, whereas it increased the corrosion resistance.     

Environmental effects on the strength and impact damage resistance of alumina based oxide/oxide ceramic matrix composites

In this study the effects of high temperature and moisture on the impact damage resistance and mechanical strength of Nextel 610/alumina silicate ceramic matrix composites were experimentally evaluated. Composite laminates were exposed to either a 1050°C isothermal furnace-based environment for 30 consecutive days at 6 h a day, or 95% relative humidity environment for 13 consecutive days at 67°C. Low velocity impact, tensile and short beam strength tests were performed on both ambient and environmentally conditioned laminates and damage was characterized using a combination of non-destructive and destructive techniques. High temperature and humidity environmental exposure adversely affected the impact resistance of the composite laminates. For all the environments, planar internal damage area was greater than the back side dent area, which in turn was greater than the impactor side dent area. Evidence of environmental embrittlement through a stiffer tensile response was noted for the high temperature exposed laminates while the short beam strength tests showed greater propensity for interlaminar shear failure in the moisture exposed laminates. Destructive evaluations exposed larger, more pronounced delaminations in the environmentally conditioned laminates in comparison to the ambient ones. External damage metrics of the impactor side dent depth and area directly influenced the post-impact tensile strength of the laminates while no such trend between internal damage area and residual strength could be ascertained.     

毫米波三维异质异构集成技术的进展与应用

三维异质异构集成技术是实现电子信息系统向着微型化、高效能、高整合、低功耗及低成本方向发展的最重要方法,也是决定信息化平台中微电子和微纳系统领域未来发展的一项核心高技术。文章详细介绍了毫米波频段三维异质异构集成技术的优势、近年来的发展趋势以及面临的挑战。利用硅基MEMS 光敏复合薄膜多层布线工艺可实现异质芯片的低损耗互连,同时三维集成高性能封装滤波器、高辐射效率封装天线等无源元件,还能很好地处理布线间的电磁兼容和芯片间的屏蔽问题。最后介绍了一款新型毫米波三维异质异构集成雷达及其在远距离生命体征探测方面的应用。