砂岩酸化中水化硅沉淀的影响因素分析

讨论了砂岩酸化中产生水化硅沉淀的反应机理。使高岭土与1.0%HF和多种配比的HCl HF在不同温度(20-90℃)反应不同时间(10-300分钟),用等离子吸收光谱法(ICP)测定酸液中可溶性硅的浓度(mg/L),取某时段测定值的减小量为该时段水化硅沉淀生成量,讨论了多种因素的影响,得到了如下结果和结论。反应温度越高,则高岭土与HF之间的反应越快,形成水化硅沉淀的时间越短,最终生成的沉淀量越大;在HF中加入HCl(使用土酸体系)、减小土酸中HF质量分数、加大土酸中HCl、HF质量分数比,均可使生成沉淀时间延后,使最终生成沉淀量减少。60℃时300分钟沉淀量,在1.0%HF、5.0%HCl 1.0%HF、9.0%HCl 1.0%HF中分别为482、321、201mg/L。提出了在酸化设计与施工中可以采取的6条简便易行的减少水化硅沉淀量的措施。图4表1参6。     

一种制备插层和无定形高岭土的新方法

利用甲醇钠强烈的夺氢作用 ,介绍了一种制备插层和无定形高岭土的方法。利用XRD为主要检测手段研究了甲醇钠的质量分数、反应温度等因素对反应的影响。结果表明 :在反应温度较低、质量分数较低的甲醇钠溶液中 ,高岭土容易被插层而膨胀 ,反之高岭土的层状结构被破坏而无定形化。红外光谱分析进一步证明了插层和无定形高岭土结构的变化     

Dispersion—flocculation studies on a Goethite-clay system

Dispersion–flocculation studies on a Goethite–clay system using flocculants were carried out as a function of flocculant concentrations, pH of slurry, time of agitation and dispersant dosage. Also, the effects of pH and polymer concentrations on the adsorption behaviour of the system were investigated. Results show that well flocculated goethite was preferentially obtained from 4% goethite/kaolinite clay suspensions, with 50 ppm causticised starch in the slurry at pH values of 3–11·5 and with 50 ppm polyacrylamide at pH values of 3–8. Good flocs were also obtained on flocculation of the goethite suspension with 50 ppm polyacrylamide at pH values of 5–7, while the kaolinite suspension did not respond to the same dosage of causticised starch in the same pH range. Results further reveal that for the goethite/kaolinite suspension, the best results was obtained with 50 ppm polyacrylamide at pH values of 7–10. Based on the data generated in the study, it was concluded that causticised starch is a better flocculant than polyacrylamide for goethite suspensions although polyacrylamide is an excellent flocculant for kaolinite suspensions.     

高岭土改性聚酯纤维

介绍了高岭土在改性聚酯中的作用、纤维级高岭土的性质以及改性聚酯的制造方法．指出了我国开发高岭土改性聚酯纤维的的前景．     

A novel depressor useful for flotation separation of diaspore and kaolinite

The floatation of the minerals diaspore and kaolinite was investigated using dodecylamine as the collector.Separating diaspore and kaolinite in a neutral pH pulp is difficult since they then have similar floatability.A depressor consisting of an AlCl3/Na2SiO3 mixture is demonstrated to solve this problem.Diaspore sinking may be seen when the ratio of AlCl3 to Na2SiO3 is 3.1.We refer to this mixture as ATNO.The influence of Al/Si ratio in the feedstock and the grain size of fed minerals on separation was examined.An Al/Si ratio in the concentrate greater than 11 may be obtained when the Al/Si ratio of the feed is between 2.53 and 4.96.However,the grain size of the diaspore greatly influences the concentrate grade.Finer grain size of the diaspore (＜40 μm)in pulp makes the flotation separation less than ideal,no matter what the kaolinite grain size.     

高岭石声化学插层的XRD研究

以乙二醇、二甲基甲酰胺、二甲基亚砜及双氧水/冰醋酸等为插层剂,采用声化学法对高岭石进行了插层研究,考察了插层剂种类对高岭石插层率的影响.在此基础上,重点研究了以二甲基亚砜作为插层剂的情况下超声波功率、插层时间及插层剂的质量分数等工艺因素对插层率的影响,并采用XRD分析方法测试了高岭石的插层效率.结果表明：二甲基亚砜作为插层剂时插层率最高,插层率可达100%,二甲基甲酰胺和乙二醇次之,双氧水/冰醋酸插层率最低,插层率仅为14.9%.以二甲基亚砜为插层剂时,随着超声功率的增大,插层率先升高后降低;随着插层时间的延长,插层率呈增长趋势,而二甲基亚砜的质量分数对插层率的影响不大.在二甲基亚砜质量分数为75%、超声功率为300W、插层时间为2h的条件下,插层率达到100%,高岭石层间距从0.71nm被有效增大到1.10nm.     

Fabrication of phytic acid embellished kaolinite and its effect on the flame retardancy and thermal stability of ethylene vinyl acetate composites

A modified kaolinite by grafting with phytic acid (PA-g-Kaol) is fabricated, and it was introduced into ethylene vinyl acetate (EVA) with intumescent flame retardancy (IFR) together to improve the flame retardancy of EVA composites. The results show the limiting oxygen index value of EVA/ (18.0 wt% IFR)/ (2.0 wt% PA-g-Kaol) is 30.8%. Meanwhile, there is only one dripping produced in the vertical burning test. What's more, the flame-retardant mechanism is demonstrated by TG-IR, real-time-IR and GC–MS analysis. The results indicate that some pyrolytic products of IFR and PA-g-Kaol, like ammonia and phosphoric acid, catalyze the crosslinking of EVA and flame retardant, the resultant compact char protects the substrate from further burning.     

高岭石脱水反应的非等温热重法研究

在系统分析非等温固相反应特点的基础上,建立了非等温脱水反应速率方程.采用非等温热重法、通过计算机辅助计算,对高岭石脱水反应动力学规律进行了研究.结果表明:由于高岭石晶体结构中内、外羟基脱除的顺序不同,其脱水反应机制在反应分数(α)为0.7左右时发生改变.在反应前期(0＜α＜0.7)时,脱水反应遵循二维扩散控制规律,脱水反应表观活化能为159.682 kJ/mol、表观频率因子为1.007×10 10/min.     

微波对制备高岭石插层作用的研究

为了明确微波对制备高岭石插层的作用,采用乙酰胺对高岭石的微波熔融插层和油浴熔融插层进行了对比实验.借助于XRD、FTIR等分析测试手段,通过对比不同时间段2种插层环境下的插层率,分析了微波对插层反应的影响,进而探讨了微波对插层反应的作用机理.研究发现在反应初期微波对插层反应起促进作用,但随着时间的延长这种促进作用减弱,并呈现出一定的阻碍作用,认为是微波对乙酰胺的热作用和极化作用综合作用的结果.