A thermoelectric generator comprising selenium-doped bismuth telluride on flexible carbon cloth with n-type thermoelectric properties

Carbon cloth was used as a flexible substrate for bismuth telluride (Bi₂Te₃) particles to provide flexibility and improve the overall thermoelectric performance. Bi₂Te₃ on carbon cloth (Bi₂Te₃/CC) was synthesized via a hydrothermal reaction with various reaction times. After over 12 h, the Bi₂Te₃ particles showed a clear hexagonal shape and were evenly adhered to the carbon cloth. Selenium (Se) atoms were doped into the Bi₂Te₃ structure to improve its thermoelectric performance. The electrical conductivity increased with increasing Se-dopant content until 40% Se was added. Moreover, the maximum power factor was 1300 μW/mK² at 473 K for the 30% Se-doped sample. The carbon cloth substrate maintained its electrical resistivity and flexibility after 2000 bending cycles. A flexible thermoelectric generator (TEG) fabricated using the five pairs of 30% Se-doped sample showed an open-circuit voltage of 17.4 mV and maximum power output of 850 nW at temperature difference ΔT = 30 K. This work offers a promising approach for providing flexibility and improving the thermoelectric performance of inorganic thermoelectric materials for wearable device applications using flexible carbon cloth substrate for low temperature range application.     

Synthesis and characterization of G/TiO1.80 bulk composite thermoelectric material under high temperature and high pressure

The primary purpose of this work is to introduce the second phase of graphene (G) into non-stoichiometric TiO_1.80 successfully and optimize the thermoelectric properties of this composite material through high pressure and high temperature (HPHT) technology. The purpose of doping Ti powder under high pressure is to create a closed reducing atmosphere to change the ratio of titanium to oxygen in the titanium oxide base. The addition of graphene can considerably improve the electrical properties of the material and reduce its resistivity. An X-ray diffractometer, X-ray photoelectron spectrometer, scanning electron microscope, and transmission electron microscope were used to analyze and characterize the phase structure, chemical bond, micro morphology and crystal morphology of the samples. An abundance of grain boundaries and lattice dislocation defects can inhibit the lattice thermal conductivity. We also tested and analyzed the thermoelectric performance of the high-temperature and high-pressure synthetic samples through a variable temperature system. The variation of the absorption intensity of the ultraviolet UV spectrum with wavelength shows that high pressure can reduce the band gap, which is beneficial to the carrier transition and improves the conductivity of semiconductors. HPHT optimizes both the electrical and the thermal parameters of the sample. At a final sintering pressure of 5.0 GPa, the dimensionless figure of merit (zT) of the bulk composite material G/TiO_1.80 was found to be 0.23 at 700 °C.     

Grain orientation evolution and multi-scale interfaces enhanced thermoelectric properties of textured Sr0.9La0.1TiO3 based ceramics

Sr_0.9La_0.1TiO₃ based textured ceramics (SLTT-S3T) with a texture fraction of 0.81 are successfully fabricated by the reactive template grain growth method, in which Sr_0.9La_0.1TiO₃/20 wt%Ti was used as matrix and 10 wt% plate-like Sr₃Ti₂O₇ template seeds were used as templates. The phase transition, microstructure evolution, and the anisotropic thermoelectric properties of SLTT-S3T ceramics were investigated. The results show that the ceramics are mainly composed of Sr_0.9La_0.1TiO₃ and rutile TiO₂ phases. Grains grow with a preferred orientation along (h00). A maximum ZT of 0.26 at 1073 K was achieved in the direction perpendicular to the tape casting direction. The low lattice thermal conductivity of 1.9 W/(m K) at 1073 K was obtained decreased by 34%, 40%, and 38% compared with non-textured, SrTiO₃ and Sr_0.9La_0.1TiO₃ ceramics prepared by the same process, can be attributed to the enhanced phonon scattering by the complex multi-scale boundaries and interfaces. This work provides a strategy of microstructural design for thermoelectric oxides to decrease intrinsic lattice thermal conductivity and further regulate thermoelectric properties via texture engineering.     

Transverse magnetoresistance peculiarities of thermoelectric Lu-doped Bi2Te3 compound due to strong electrical disorder

The n-type thermoelectric Bi_1.9Lu_0.1Te₃ was prepared by microwave-solvothermal method and spark plasma sintering. The magnetic field and temperature dependences of transverse magnetoresistance measured within temperature 2–200 K interval allow finding the peculiarities characteristic for strongly disordered and inhomogeneous semiconductors. The first peculiarity is due to appearance of linear-in-magnetic field contribution to the total magnetoresistance reflected in a crossover from quadratic magnetoresistance at low magnetic fields to linear magnetoresistance at high magnetic fields. The linear magnetoresistance can result from the Hall resistance picked up from macroscopically distorted current paths due to local variations in stoichiometry of the compound studied. The second peculiarity is that both linear magnetoresistance magnitude and crossover field are functions of carrier mobility which is in agreement with the Parish and Littlewood model developed for disordered and inhomogeneous semiconductors. An increase in the mobility due to a decrease in temperature is accompanied by an increase in the magnetoresistance magnitude and a decrease in the crossover field. Finally, the third peculiarity is related to the remarkable deviation of the total magnetoresistance measured at various temperatures from the Kohler's rule. Presence of strong inhomogeneity and disorder in the Bi_1.9Lu_0.1Te₃ structure concluded from the magnetoresistance peculiarities can be responsible for the remarkable reduction in the total thermal conductivity of this compound.     

Thermal and transport properties of as-grown Ni-rich TiNi shape memory alloys

Electrical resistivity, Seebeck coefficient, specific heat and thermal conductivity measurements on the Ti_50−xNi_50+x (x = 0.0–1.6 at.%) shape memory alloys are performed to investigate their thermal and transport properties. In this study, anomalous features are observed in both cooling and heating cycles in all measured physical properties of the slightly Ni-rich TiNi alloys (x ≤ 1.0), corresponds to the transformation between the B19′ martensite and B2 austenite phases. Besides, the transition temperature is found to decrease gradually with increasing Ni content, and the driving force for the transition is also found to diminish slowly with the addition of excess Ni, as revealed by specific heat measurements. While the signature of martensitic transformation vanishes for the Ni-rich TiNi alloys with x ≥ 1.3, the characteristics of strain glass transition start to appear. The Seebeck coefficients of these TiNi alloys were found to be positive, suggesting the hole-type carriers dominate the thermoelectric transport. From the high-temperature Seebeck coefficients, the estimated value of Fermi energy ranges from ∼1.5 eV (Ti_48.4Ni_51.6) to ∼2.1 eV (Ti₅₀Ni₅₀), indicating the metallic nature of these alloys. In addition, the thermal conductivity of the slightly Ni-rich TiNi alloys with x ≤ 1.0 shows a distinct anomalous feature at the B19′ → B2 transition, likely due to the variation in lattice thermal conductivity.     

Theoretical study of a thermoelectric-assisted vapor compression cycle for air-source heat pump applications

This paper proposes a thermoelectric-assisted vapor compression cycle (TVCC) for applications in air-source heat pump systems which could enhance the heating capacity of the system. Performances of TVCC are calculated and then compared with that of basic vapor compression cycle (BVCC). The simulation results show that when coefficients of performance (COPs) of the two cycles are almost equal, the TVCC under maximum COP condition of the thermoelectric modules still performs better than BVCC by 13.0% in heating capacity through selecting the appropriate intermediate temperature. In addition, the TVCC can also achieve an improvement of 16.4%–21.7% in both the heating COP and capacity when compared with the BVCC with an assistant electric heater that is provided with the equivalent power input of thermoelectric heat exchanger. Thus, the TVCC could be beneficial to the applications in small heat pumps if there is always need for auxiliary electric heat.     

Enhanced thermoelectric properties of atomic-layer-deposited Hf:Zn16O/18O superlattice films by interface-engineering

This study examines three novel approaches for enhancing the thermoelectric (TE) properties of atomic-layer-deposited (ALD) ZnO thin films: 1) Hf-doping, which preserved the crystallinity of ZnO and provided effective phonon scattering owing to Hf's similar atomic radius to and large mass difference with Zn, leading to high power factor (PF) and low thermal conductivity (κ); 2) controlling the distribution of Hf into an alternating scattered phase/clustered phase superlattice, which balanced the high PF of the scattered phases with the low κ of the clustered phases, while providing significant energy-filtering effect to raise the Seebeck coefficient; 3) introducing ¹⁸O/¹⁶O periodicity into the Hf:ZnO films—by alternately using H₂¹⁶O and H₂¹⁸O as oxidants in the ALD processes, which further suppressed κ without compromising PF. The combination of the three approaches resulted in a maximum improvement in ZT of ~1600% over that of the undoped ZnO.     

Effects of anion and cation doping on the thermoelectric properties of n-type PbS

The PbCl_xS_1-x and Pb_1-xBi_xS (x? =?0–0.05) bulks were fabricated with a facile method of hydrothermal synthesis and microwave sintering, and the effect of anionic and cationic donors on the thermoelectric performance of PbS was investigated. Although Cl^? and Bi³⁺ both effectively improved the thermoelectric properties of n-type PbS, more excellent thermoelectric performance was obtained from Cl^? doped samples because of higher electrical property and lower thermal conductivity at higher temperature (T? >?600?K). The thermoelectric figure of merit (ZT) reaches 1.04 for PbCl_0.015S_0.985 at 800?K and increases with temperature increasing without sign of saturation, which is probably the highest value ever reported for single-phase polycrystalline n-type PbS. The results also indicate that the hydrothermal synthesis and microwave sintering can realize anion doping as well as cation doping for n-type PbS at low cost, and PbS should be a robust alternative for PbTe thermoelectric materials.     

Application of SiC-Si functionally gradient material to thermoelectric energy conversion device

Because of its high–temperature chemical stability, SiC ceramic is a promising material for high-temperature device applications such as thermoelectric energy converters. However, the electrical conductivity of SiC ceramic is too low for it to be used as a thermoelectric energy converter at the cold junction. Therefore, we propose a SiC-Si functionally gradient material (FGM) in order to improve the electrical conductivity of the SiC ceramic at the cold junction. An SiC rod was fired in a temperature gradient furnace. One end of the SiC rod was maintained at 2473 K and the other end was maintained at 1973 K for 30 min. After firing, the porous SiC edge fired at 1973 K was dipped into molten Si in order to infiltrate molten Si into the porous SiC. The microstructure of the FGM is classified into three regions: the SiC-Si composite material; the porous SiC ceramic; and the densified SiC ceramic. The electrical conductivity, the Seebeck coefficient and the thermal conductivity for each region of SiC-Si FGM was measured at 300 K; a figure of merit was calculated. The figure of merit of the SiC-Si FGM at the cold junction, at room temperature, was 10⁸ times higher than that of a nongradient SiC ceramic.