成分配比对稀土钨电极材料组织及力学性能影响

通过固液掺杂、等静压压制、中频烧结的方法，制备了不同的氧化镧、氧化钇、氧化锆三元掺杂成分比例的钨电极材料烧结棒材，探究了不同成分配比对样品显微组织、第二相粒子分布以及宏观力学性能的影响。结果表明，氧化镧、氧化钇、氧化锆三元复合添加能够有效改善第二相粒子在钨基体中的分布形态，降低第二相在晶界的过度富集，提高钨电极材料的综合力学性能。并且当添加成分镧、钇、锆质量比为3:1:1时，材料具有最好的综合力学性能，致密度可达96.04%，显微硬度可达549.37HV0.3，抗压强度可达3785MPa，原因是此配比下第二相粒子最为细小均匀，弥散程度最高，对基体晶粒的细化作用最好，该配比下钨基体平均晶粒尺寸达到10.3μm。     

Achieving superior hydrogen storage properties via in-situ formed nanostructures: A high-capacity Mg–Ni alloy with La microalloying

Mg-based hydride is a promising hydrogen storage material, but its capacity is hindered by the kinetic properties. In this study, Mg–Mg₂Ni–LaH_x nanocomposite is formed from the H-induced decomposition of Mg₉₈Ni_1·67La_0.33 alloy. The hydrogen capacity of 7.19 wt % is reached at 325 °C under 3 MPa H₂, attributed to the ultrahigh hydrogenation capacity in Stage I. The hydrogen capacity of 5.59 wt % is achieved at 175 °C under 1 MPa H₂. The apparent activation energies for hydrogen absorption and desorption are calculated as 57.99 and 107.26 kJ/mol, which are owing to the modified microstructure with LaH_x and Mg₂Ni nanophases embedding in eutectic, and tubular nanostructure adjacent to eutectic. The LaH_2.49 nanophase can catalyze H₂ molecules to dissociate and H atoms to permeate due to its stronger affinity with H atoms. The interfaces of these nanophases provide preferential nucleation sites and alleviate the “blocking effect” together with tubular nanostructure by providing H atoms diffusion paths after the impingement of MgH₂ colonies. Therefore, the superior hydrogenation properties are achieved because of the rapid absorption process of Stage I. The efficient synthesis of nano-catalysts and corresponding mechanisms for improving hydrogen storage properties have important reference to related researches.     

5G核心网业务模型的智能化预测研究

摘 要：核心网业务模型的建立是5G网络容量规划和网络建设的基础，通过现有方法得到的理论业务模型是静态不可变的且与实际网络存在偏离。为了克服现有5G核心网业务模型与现网模型适配性较差以及规划设备无法满足用户实际业务需求的问题，提出了一种长短期记忆（long short-term memory，LSTM）网络与卷积LSTM （convolution LSTM，ConvLSTM）网络双通道融合的 5G 核心网业务模型预测方法。该方法基于人工智能（artificial intelligence，AI）技术以实现高质量的核心网业务模型的智能预测，形成数据反馈闭环，实现网络自优化调整，助力网络智能化建设。     

使能未来工厂的5G能力综述

5G系统将移动通信服务从移动电话、移动宽带和大规模机器通信扩展到新的应用领域，即所谓对通信服务有特殊要求的垂直领域。对使能未来工厂的5G能力进行了全面的分析总结，包括弹性网络架构、灵活频谱、超可靠低时延通信、时间敏感网络、安全和定位，而弹性网络架构又包括对网络切片、非公共网络、5G局域网和边缘计算的支持。希望从广度到深度，对相关的理论及技术应用做透彻、全面的梳理，对其挑战做清晰的总结，从而为相关研究和工程技术人员提供借鉴。     

Performance of BaZrO3/Y2O3 dual-phase refractory applied to TiAl alloy melting

Vacuum induction melting is a potential process for the preparation of TiAl alloys with good homogeneity and low cost. But the crucial problem is a selection of high stability refractory. In this study, a BaZrO₃/Y₂O₃ dual-phase refractory was prepared and its performance for melting TiAl alloys was studied and compared with that of a Y₂O₃ refractory. The results showed the dual-phase refractory consisted of BaZr_1-xY_xO_3-δ and Y₂O₃(ZrO₂), exhibited a thinner interaction layer (30 μm) than the Y₂O₃ refractory (90 μm) after melting the TiAl alloy. Although the TiAl alloys melted in the dual-phase and Y₂O₃ refractory exhibited similar oxygen contamination (<0.1 wt%), the alloy melted in the dual-phase refractory had smaller Y₂O₃ inclusion content and size than that in the Y₂O₃ refractory, indicating that the dual-phase refractory exhibited a better melting performance than the Y₂O₃ refractory. This study provides insights into the process of designing highly stable refractory for melting TiAl alloys.     

Nickel‒cobalt bimetallic catalysts prepared from hydrotalcite-like compounds for dry reforming of methane

Ni–Co/Mg(Al)O alloy catalysts with different Co/Ni molar ratios have been prepared from Ni- and Co-substituted Mg–Al hydrotalcite-like compounds (HTlcs) as precursors and tested for dry reforming of methane. The XRD characterization shows that Ni–Co–Mg–Al HTlcs are decomposed by calcination into Mg(Ni,Co,Al)O solid solution, and by reduction finely dispersed alloy particles are formed. H₂-TPR indicates a strong interaction between nickel/cobalt oxides and magnesia, and the presence of cobalt in Mg(Ni,Co,Al)O enhances the metal-support interaction. STEM-EDX analysis reveals that nickel and cobalt cations are homogeneously distributed in the HTlcs precursor and in the derived solid solution, and by reduction the resulting Ni–Co alloy particles are composition-uniform. The Ni–Co/Mg(Al)O alloy catalysts exhibit relatively high activity and stability at severe conditions, i.e., a medium temperature of 600 °C and a high space velocity of 120000 mL g^?1 h^?1. In comparison to monometallic Ni catalyst, Ni–Co alloying effectively inhibits methane decomposition and coke deposition, leading to a marked enhancement of catalytic stability. From CO₂-TPD and TPSR, it is suggested that alloying Ni with Co favors the CO₂ adsorption/activation and promotes the elimination of carbon species, thus improving the coke resistance. Furthermore, a high and stable activity with low coking is demonstrated at 750 °C. The hydrotalcite-derived Ni–Co/Mg(Al)O catalysts show better catalytic performance than many of the reported Ni–Co catalysts, which can be attributed to the formation of Ni–Co alloy with uniform composition, proper size, and strong metal-support interaction as well as the presence of basic Mg(Al)O as support.     

Development of a H2-permeable Pd60Cu40-based composite membrane using a reverse build-up method

A new reverse build-up method is developed to fabricate an economical H₂-permeable composite membrane. Sputtering and electroplating are used for the formation of a membrane comprised of a 3.7-μm-thick Pd₆₀Cu₄₀ (wt.%) alloy layer and a 13-μm-thick porous Ni support layer, respectively. The H₂-permeation measurements are performed under the flow of a gaseous mixture of H₂ and He at 300–320 °C and 50–100 kPa of H₂ partial pressure. The H₂/He selectivity values exceed 300. The activation energy at 300–320 °C is 10.9 kJ mol⁻¹. The H₂ permeability of the membrane is 1.25 × 10⁻⁸ mol m⁻¹ s⁻¹ Pa^−0.5 at 320 °C after 448 h. The estimated Pd cost of the proposed membrane is approximately 1/8 of the cost for a pure Pd₆₀Cu₄₀ membrane. This study demonstrates that the proposed method allows the facile production of low-cost, Pd-based membranes for H₂ separation.     

Role of the HSP70 Co-Chaperone SIL1 in Health and Disease

Cell surface and secreted proteins provide essential functions for multicellular life. They enter the endoplasmic reticulum (ER) lumen co-translationally, where they mature and fold into their complex three-dimensional structures. The ER is populated with a host of molecular chaperones, associated co-factors, and enzymes that assist and stabilize folded states. Together, they ensure that nascent proteins mature properly or, if this process fails, target them for degradation. BiP, the ER HSP70 chaperone, interacts with unfolded client proteins in a nucleotide-dependent manner, which is tightly regulated by eight DnaJ-type proteins and two nucleotide exchange factors (NEFs), SIL1 and GRP170. Loss of SIL1′s function is the leading cause of Marinesco-Sjögren syndrome (MSS), an autosomal recessive, multisystem disorder. The development of animal models has provided insights into SIL1′s functions and MSS-associated pathologies. This review provides an in-depth update on the current understanding of the molecular mechanisms underlying SIL1′s NEF activity and its role in maintaining ER homeostasis and normal physiology. A precise understanding of the underlying molecular mechanisms associated with the loss of SIL1 may allow for the development of new pharmacological approaches to treat MSS.     

Bifunctional nanoporous ruthenium-nickel alloy nanowire electrocatalysts towards oxygen/hydrogen evolution reaction

A class of ruthenium-nickel alloy catalysts featured with nanoporous nanowires (NPNWs) were synthesized by a strategy combining rapid solidification with two-step dealloying. RuNi NPNWs exhibit excellent electrocatalytic activity and stability for oxygen evolution reaction (OER) and hydrogen evolution reaction (HER) in which the RuNi-2500 NPNWs catalyst shows an OER overpotential of 327 mV to deliver a current density of 10 mA cm^?2 and the RuNi-0 NPNWs catalyst requires the overpotential of 69 mV at 10 mA cm^?2 showing the best HER activity in alkaline media. Moreover, the RuNi-1500 NPNWs catalyst was used as the bifunctional electrocatalyst in a two-electrode alkaline electrolyzer for water splitting, which exhibits a low cell voltage of 1.553 V and a long-term stability of 24 h at 10 mA cm^?2, demonstrating that the RuNi NPNWs catalysts can be considered as promising bifunctional alkaline electrocatalysts.     

Interfacial microstructure and mechanical properties of Ti3SiC2 ceramic and TC11 alloy joint diffusion bonded with a Cu interlayer

Reliable joints of Ti₃SiC₂ ceramic and TC11 alloy were diffusion bonded with a 50 μm thick Cu interlayer. The typical interfacial structure of the diffusion boned joint, which was dependent on the interdiffusion and chemical reactions between Al, Si and Ti atoms from the base materials and Cu interlayer, was TC11/α-Ti + β-Ti + Ti₂Cu + TiCu/Ti₅Si₄ + TiSiCu/Cu(s, s)/Ti₃SiC₂. The influence of bonding temperature and time on the interfacial structure and mechanical properties of Ti₃SiC₂/Cu/TC11 joint was analyzed. With the increase of bonding temperature and time, the joint shear strength was gradually increased due to enhanced atomic diffusion. However, the thickness of Ti₅Si₄ and TiSiCu layers with high microhardness increased for a long holding time, resulting in the reduction of bonding strength. The maximum shear strength of 251 ± 6 MPa was obtained for the joint diffusion bonded at 850 °C for 60 min, and fracture primarily occurred at the diffusion layer adjacent to the Ti₃SiC₂ substrate. This work provided an economical and convenient solution for broadening the engineering application of Ti₃SiC₂ ceramic.