两种3D打印用雾化Ti-6Al-4V粉末的对比研究

本研究分别利用水冷铜坩埚真空感应熔炼气雾化(VIGA-CC)和等离子旋转电极(PREP)两种技术制备出球形Ti-6Al-4V合金粉末,作者利用SEM、同步辐射CT扫描-三维重建和氩气含量测试等分析手段对不同粒径的Ti-6Al-4V合金粉末的孔洞缺陷和氩气含量、硬度值进行了表征。实验结果表明, VIGA-CC粉末粒度分布宽,细粉收得率较多,粉末粒度分布在40~180 μm之间, PREP粉末的粒度分布较窄,主要集中在110~180 μm之间；金属粉末内部的孔隙率、气体含量和孔尺寸随着粉末粒度的增大而增大,且同一粒径范围内VIGA-CC粉末的气孔概率多于PREP粉末；随着粉末粒径减小,粉末截面组织逐渐细化,其硬度值逐渐升高,整体上VIGA-CC粉末硬度值高于PREP粉末。     

Formation and wear mechanism of nickel titanium intermetallics during heat treatment of nickel coating on Ti-6Al-4V substrate

In the present work, inter-diffusion of nickel and titanium and formation of Ni-Ti intermetallic compounds on Ti-6Al-4V substrate have been studied. Initially, nickel was electrodeposited on the alloy using a modified Watts bath solution at a current density of 2 A dm^?2 for 1?h. The coated specimens were then heat treated for different durations at 750, 800 and 850 °C under argon atmosphere. The effects of temperature and time on the characteristics, hardness and wear resistance of intermetallic phases were investigated. The results showed that a multilayer structure was formed after heat treatment, an outer layer of residual nickel, an area of intermetallic layers with different compositions followed by a solid solution of Ni-Ti. It was also observed that an increase in time or temperature at first led to the formation of thicker intermetallic layers; however, after passing a critical point, the intermetallic layers seem to dissolve into the substrate. Furthermore, the wear rates of the diffusion treated samples were four times lower compared to Ti-6Al-4V alloy when sliding against AISI 52100 hardened steel.     

喷射轧制Fe-4.5%Si硅钢片的组织和性能

采用喷射成形和轧制工艺制备了厚度为0.5mm的Fe-4.5%Si高硅钢片，并对其密度、显微组织和电磁性能进行了测试分析，研究结果表明：在最佳的喷射成形和轧制工艺条件下，所制备硅钢片的磁感应强度B25为1.544T、B50为1.641T；铁损P1050为1.437W/kg、P1550为3.43W/kg，说明喷射成形轧制技术可以制备出高磁感应强度、低铁损的高硅钢片。     

浅析氩弧焊焊接铝镁合金的质量控制

铝镁合金具有良好的耐腐蚀性和较高的低温强度,目前广泛应用于空分装置的制氧设备中。结合铝合金管道焊接中常见的缺陷.从选材、清洗、焊接等环节简述了提高铝镁合金的焊接质量控制措施。     

非晶Sm5Fe74.3Nb1.5Si11.7B4.5C2.5Cu0.5合金经预退火后的晶化动力学的DTA研究

研究了非晶Sm5Fe74.3Nb1.5Si11.7B4.5C2.5Cu0.5合金经400℃，保温10min预退火后的晶化动力学。结果表明；该合金的晶化相为α-Fe固溶体和Sm2Fe17Cx金属间化合物，两相的晶化表观激活能分别为557KJ/mol和514KJ/mol，当晶化体积分数为60%时，α-Fe相的晶化激活能达极大值；Sm2Fe17Cx相晶化激活能则随其晶化体积分数的增加而逐渐减小。     

Ti-23Al-14Nb-3V合金氩弧焊接头的显微组织及其力学性能

研究了预热对Ｔｉ－２３Ａｌ－１４Ｎｂ－３Ｖ合金焊接性，特别是对消除氩弧焊冷裂纹的作用以及对接头显微组织和力学性能的影响。结果表明，焊前预热可有效降低该合金的冷裂倾向。经预热处理后，焊缝区的结晶层状线消失，热影响区的硬度峰得到缓和，整个焊缝的显微硬度分布趋于均匀，但焊缝区的枝晶发生粗化，热影响区有所扩大。焊件接头的拉伸试验表明，预热可使焊缝区的接头强度系数增加，但无论预热与否，接头强度均低于母材强度，且不显示宏观塑性。     

LF6铝合金的超塑性／扩散连接组合工艺试验及理论研究EI

本文研究了ＬＦ６铝合金的超塑性／扩散连接组合工艺，用变形和再结晶的方法细化晶粒，成功地进行了ＳＰＦ／ＤＢ工艺试验，利用电子探针观察了扩散连接接头的界面微观区域，并从机理上分析了金属的超塑性／扩散连接两种工艺之间的内部联系及其金属学行为。     

高能超声处理Al-1Si合金凝固组织分析

采用高能超声处理Al-1Si合金熔体,借助金相显微镜和电子探针进行组织分析,并测定合金的熔化潜热,分析了熔体中超声空化效应和声流效应影响凝固过程的机理。结果表明,试样晶粒平均尺寸由超声处理前的94μm减小到超声处理后的34μm;合金试样的熔化吸热量由263.90J/g降低为159.81J/g,在熔体中施加高能超声显著改善了合金成分的均匀性并细化了晶粒。     

Advances in titanium metal injection molding

The approaches to production of titanium powder injection molded parts are reviewed. Historically, oxygen levels have been too high for structural use (particularly with the Ti-6Al-4V alloy). However, recent advances in starting powders, binders and sintering facilities now allow oxygen levels in the Ti-6Al-4V alloy to be controlled to about 0.2 wt.% oxygen. This should result in significant expansion of the titanium PIM market place into aerospace, automobiles, surgical instruments, dentistry, communication devices (such as computers and cell phones), knives and guns. __________ Translated from Poroshkovaya Metallurgiya, Vol. 46, No. 5–6 (455), pp. 118–125, 2007.     

Measurement of the heat of fusion of titanium and a titanium alloy (90Ti-6Al-4V) by a microsecond-resolution transient technique

A microsecond-resolution pulse heating technique was used for the measurement of the heat of fusion of titanium and a titanium alloy (90Ti-6Al-4V). The method is based on rapid (50- to 100-s) resistive self-heating of the specimen by a high-current pulse from a capacitor discharge system and measuring, as functions of time, current through the specimen, voltage across the specimen, and radiance of the specimen. Melting of the specimen is manifested by a plateau in the measured radiance. The time integral of the net power absorbed by the specimen during melting yields the heat of fusion. The values obtained for heat of fusion were 272 J · g^–1 (13.0 kJ · mol^–1) for titanium and 286 J · g^–1 for the alloy 90Ti-6Al-4V, with an estimated maximum uncertainty of ±6% in each value.Paper presented at the Second Workshop on Subsecond Thermophysics, September 20–21, 1990, Torino, Italy.