| 成型活性炭的制备及脱硫的影响因素分析 |
| |
| 引用本文： | 刘瑾.成型活性炭的制备及脱硫的影响因素分析[J].化工技术与开发,2014(12):9-11. |
| |
| 作者姓名： | 刘瑾 |
| |
| 作者单位： | 陕西理工学院化学与环境科学学院,陕西 汉中,723000 |
| |
| 摘 要： | 以粘胶基活性炭纤维与酚醛树脂分别作为吸附剂和粘接剂制备成型活性炭，通过脱硫实验，考察了炭化温度、活化温度、活化时间和原料配比因素对成型活性炭脱硫能力的影响。结果表明，于700℃下炭化60min，然后以CO2为活化剂，850℃下活化60min，制备出了较高吸附性能的成型活性炭产品。
|
| 关 键 词： | 成型活性炭 脱硫 影响因素 |
Preparation of Formed Activated Carbon and Desulfurization Influence Factor Analysis |
| |
| LIU Jin.Preparation of Formed Activated Carbon and Desulfurization Influence Factor Analysis[J].Technology & Development of Chemical Industry,2014(12):9-11. |
| |
| Authors: | LIU Jin |
| |
| Affiliation: | LIU Jin;School of Chemistry and Environment Science, Shaanxi University of Technology; |
| |
| Abstract: | Monolith activated carbon was prepared with phenolic resin as binder and activated carbon fiber as absorbent. Effect of experimental parameter including carbonization temperature, activation time and temperature and material ratio were investigated. The results showed that applied the equal proportion of activated carbon fiber and the phenolics as raw material, carbonized under 700℃for 1h, then activated with carbon dioxide under 850℃for 1h, the formed activated carbon product with high adsorption per-formance could obtained. |
| |
| Keywords: | activated carbon desulphurization influence factor |