Effect of low-pressure carburizing and plasma nitriding on mechanical properties and fatigue endurance limits of low alloy sintered steels

ABSTRACT

Thermochemical treatments like plasma nitriding or surface carburizing are commonly used to enhance surface hardness of steel components. An important difference between these treatments is the temperature at which they are carried out. In the present paper, the surface carburizing was carried out following a recently reported non-isothermal low pressure carburizing (LPC) treatment. In order to gain a comparative view of the effect of different treatments on the microstructure, microhardness, fatigue and impact properties, materials with distinct hardenability and widely used in the industrial production were evaluated. Tests were also carried out using industrially processed components aimed to an application demanding high wear resistance. The microstructural evolution during case hardening was studied by optical and electron microscopy.     

Micro-irrigation development in India: an analysis of distributional pattern and potential correlates

ABSTRACT

In India, of late, micro-irrigation has received considerable policy focus. However, as of 2017, only about 10% of the potential area is under micro-irrigation. The present study analyzes the pattern and equity issues of distribution of micro-irrigation in India and identifies the potential correlates. The regression analysis reveals that the stage of groundwater development and agro-climatic differences significantly influence the spread of micro-irrigation. The relatively low spread of micro-irrigation in states with over-exploited groundwater needs attention. Overall, the study points to the need to revamp the current micro-irrigation development programmes, which focus excessively on subsidy.     

Inactivation efficacy of plasma-activated water: influence of plasma treatment time,exposure time and bacterial species

This study aimed to evaluate the influence of plasma treatment time, bacterial exposure time to PAW and bacterial species on the inactivation efficacy of plasma-activated water (PAW), with additional investigation of the inactivation mechanisms of PAW. Six bacterial species, including Listeria innocua, Staphyloccus aureus, Escherichia coli, Pseudomonas fluorescens, Shewanella putrefaciens and Aeromonas hydrophila were selected as the representative bacteria. The initial bacterial concentration was around 7 log CFU ml⁻¹ after mixing with PAW, and the inactivation efficacy was measured after different exposure times during the 4 °C storage. Scanning electron microscopy (SEM) images of the bacteria after PAW treatment were carried out to inspect the cell structure damage, and physicochemical properties of PAW, including pH, conductivity and long-living reactive species of H₂O₂, , and , were examined. The results showed that the inactivation efficacy of PAW was positively correlated with plasma treatment time and bacterial exposure time, and for the species examined in this study, the Gram-negative species were more sensitive to PAW than the Gram-positive species. Cell structure damage, including shrinkage, distortion, or holes, was observed after PAW treatment. The pH of PAW was acidified to 2.5–2.9, and conductivity was significantly increased to 518.0 μs cm⁻¹. and H₂O₂ were reduced during the 48 h storage, while an increased concentration was observed for . This study demonstrated that the processing parameters of plasma treatment time, exposure time and characteristics of bacteria can significantly affect the inactivation efficacy of PAW.     

Tunable passively Q-switched thulium doped fluoride fibre (TDFF) laser using reduced graphene oxide-silver (rGO-Ag) as saturable absorber

A tunable, passively Q-switched thulium doped fluoride fibre (TDFF) laser using a reduced-graphene oxide-silver (rGO-Ag) thin film as a saturable absorber (SA) for S band operation is proposed and its efficacy demonstrated. Over a pump power range of 91.4?mW up to 158.6?mW, passively generated Q-switched pulses are observed with repetition rates from 20 to 34.5?kHz and pulse widths from 3.1 to 7.1?µs. The highest pulse energy observed is 101.2?nJ with a signal to noise ratio of ～42?dB. The proposed laser has a tuning range ～52?nm from 1458 to 1510?nm with a tunable bandpass filter (TBPF) introduced into the cavity.     

Modification of structure and conductivity of nanohorns by toluene addition in carbon arc

Abstract

In the present work, we compare the structure and transport properties of carbon nanohorns (CNHs) synthesized by arc evaporation of graphite alone and with the addition of some portion of toluene. The materials have been investigated using transmission electron microscopy, Raman and infrared spectroscopies, thermogravimetric and BET analyses. The addition of a small amount of toluene during the evaporation of graphitic rod increases the length of CNHs, affects their hierarchical arrangement in aggregates and results in surface functionalization. All these features significantly enhance the conductivity of CNHs obtained with toluene additive in comparison with the pristine CNHs.     

An evaluation of Acacia mearnsii tannin as an aluminum corrosion inhibitor in acid,alkaline, and neutral media

The electrochemical behavior of aluminum in tannin from Acacia mearnsii bark was evaluated by potentiodynamic polarization curves and electrochemical impedance spectroscopy (EIS) in media under three different pH conditions: acid, alkaline, and neutral. A relationship among pH, polymerization grade (PG), zeta potential, surface, and electrochemical properties was observed in the inhibition performance of the tannin. At high pH, the oligomer structure of the tannin was affected, resulting in a low PG (4) and high zeta potential (−75 mV), and consequently, the inhibition efficiency decreased (68%) in comparison with that in acid (99%) and neutral media (96%). The values obtained indicate a physisorption mechanism for the aluminum corrosion inhibition in the studied conditions.     

Carbon nitride materials: impact of synthetic method on photocatalysis and immobilization for photocatalytic pollutant degradation

Different synthesis routes for carbon nitride materials (CN) and the resulting products were compared to study the photocatalytic activity (pollutant degradation) in dependence on structure and properties. The CN materials were synthesized by thermal decomposition of dicyandiamide in air and under argon as well as in sealed ampoules with or without the use of a salt melt. The as-prepared materials were characterized by IR spectroscopy, nitrogen adsorption measurement, solid-state NMR spectroscopy, diffuse reflectance UV–Vis spectroscopy, elemental analysis and powder X-ray diffraction (PXRD). The surface polarity of the CN materials was estimated by adsorption of the dicyano-bis(1,10-phenanthroline)-iron(II) complex, which allows an evaluation of the degree of condensation. The CN materials were tested with regard to the photocatalytic degradation of rhodamine B (RhB). It is shown that the photocatalytic activity increases with higher surface polarity. Promising CN materials with high RhB degradation of 85% within 25 min and high surface polarity of 0.89 were selected for an immobilization approach to obtain coatings on a silicone substrate using a high-volume low-pressure (HVLP) spray coating technique. To study the photocatalytic activity of the catalyst coatings, the degradation rates of an aqueous RhB solution and solutions of organic pollutants such as triclosan and ethinyl estradiol were examined. Pollutants are decomposed with up to 63% of the initial concentration. Xenon lamps and different LEDs were used as light sources for comparison. Particularly high degradation efficiencies were obtained using LEDs, and the degradation rates are increased by adjusting the emission spectrum of the lamp to the pollutant and absorption edge of the catalyst, which results in a 40 times higher degradation efficiencies of LEDs compared to a Xe lamp.

Graphical abstract

     

Effects of SiC particles codeposition and ultrasound agitation on the electrocrystallisation of nickel-based composite coatings

This study analysed the influence of the codeposition of SiC particles with different sizes: 50 nm, 500 nm and 5 μm, and the type of bath agitation (stirring or ultrasonic) on the electrocrystallisation of nickel coatings. The composites matrix microstructure was analysed by means of SEM, EBSD and XRD, to evaluate the grain size, crystal orientation, and internal stresses and was benchmarked against pure nickel samples electrodeposited in equivalent conditions. The codeposition of nano- and microsize particles with an approximate content of 0.8 and 4 vol.%, respectively, caused only a minor grain refinement and did not vary the dominant?<?100?>?crystal orientation observed in pure Ni. The internal stress was, however, increased by particles codeposition, up to 104 MPa by nanoparticles and 57 MPa by microparticles, compared to the values observed in pure nickel (41 MPa). The higher codeposition rate (11 vol.%) obtained by the addition of submicron-size particles caused a change in the grain growth from columnar to equiaxial, resulting in deposits with a fully random crystal orientation and pronounced grain refinement. The internal stress was also increased by 800% compared to pure nickel. The ultrasound (US) agitation during the deposition caused grain refinement and a selective particle inclusion prompting a decrease in the content of the particles with the larger particles. The deposits produced under US agitation showed an increase in the internal stresses, with double values compared to stirring. The increase in the deposits microhardness, from 280 HV in pure Ni to 560 HV in Ni/SiC submicron-US, was linked to the microstructural changes and particles content.

Graphical abstract

     

A Compact Semi-circular Slot MIMO Antenna with Enhanced Isolation for Sub-6 GHz 5G WLAN Applications

In this paper, a novel compact semi-circular slot (SCS) 2 × 2 MIMO antenna is presented for 5G NR sub-6 GHz applications with high isolation. The proposed antenna consists of a semi-circular slot in ground plane, U-shaped stub, and 50-ohm microstrip feed line. The novelty of this paper are the Semi-Circular Slot acts a radiator, the port isolation  is enhanced using a simple conductor strip as a neutralization line, very compact in size, low ECC, and good impedance matching. The overall size of the proposed SCS MIMO antenna is 16 mm x 21 mm, and FR4 substrate is used with thickness of 1.6 mm. The two SCS antenna elements are separated by edge-to-edge distance of 1mm (\(=0.019\lambda _{0}\)). The proposed compact MIMO antenna design is simulated using Ansys HFSS. To validate SCS MIMO antenna, a prototype was fabricated and tested. The measured results are attained at 5.5 GHz with isolation greater than 25dB, impedance bandwidth (S11\(<-10\) dB) covers from 5.10 GHz to 5.80 GHz with return loss of ? 39.5 dB. The MIMO antenna parameters, ECC, CCL, TARC, and MEG are studied, and the values are obtained within acceptable limits. The measured and simulated antenna results are almost similar. This compact MIMO antenna is suitable for 5G communications in sub-6 GHz wifi-5 band applications.