Investigation of crystal characteristics,Raman spectra,and microwave dielectric properties of Mg1-xZnxTa2O6 ceramics

Mg_(1-x)Zn_xTa₂O₆ (x = 0.00?0.08) dielectric ceramics were synthesized via the traditional solid-state reaction method. We used XRD and Rietveld refinement to demonstrate that a pure Mg_(1-x)Zn_xTa₂O₆ phase with trirutile structure was formed. Zn²⁺ substitution helped to decrease the Raman full width at half width of the A_1g mode at 703 cm^?1, which resulted in an increase in the order and rigidity of the TaO₆ octahedron, this in turn contributed to improving the Q×f values. Additionally, the introduction of Zn²⁺ significantly promoted grain growth and increased the dense, and the molecular polarizability, these factors lead to a higher permittivity. Moreover, enhanced Ta-O bond energy resulted in a more stable TaO₆ octahedron in the Mg_(1?x)Zn_xTa₂O₆ system, which contributed to enhanced τ_f values via substitution of Zn²⁺ doped on the A-site. Correspondingly, the microwave dielectric properties were significantly improved for 0.04-doped samples, obtaining: ε_r = 27, Q × f = 185,000 GHz (at 7.47 GHz), τ_f =32 ppm/°C.     

Fabrication and characterizations of Cr3+-doped ZnGa2O4 transparent ceramics with persistent luminescence

0.5 at.% Cr:ZnGa₂O₄ precursor was synthesized by the co-precipitation method with nitrates as raw materials, using ammonium carbonate as the precipitant. Low-agglomerated Cr:ZnGa₂O₄ powders with an average particle size of 43 nm were obtained by calcining the precursor at 900℃ for 4 h. Using the powders as starting materials, 0.5 at.% Cr:ZnGa₂O₄ ceramics with an average grain size of about 515 nm were prepared by presintering at 1150℃ for 5 h in air and HIP post-treatment at 1100℃ for 3 h under 200 MPa Ar. The in-line transmittance of 0.5 at.% Cr:ZnGa₂O₄ ceramics with a thickness of 1.3 mm reaches 59.5% at the wavelength of 700 nm. The Cr:ZnGa₂O₄ ceramics can be effectively excited by visible light and produce persistent luminescence at 700 nm. For Cr:ZnGa₂O₄ transparent ceramics, the brightness of afterglow was larger than 0.32 mcd/m² after 30 min, which is far superior to that of Cr:ZnGa₂O₄ persistent luminescence powders.     

某矿快速掘进最优炮孔间距的选择

山西某矿5308底抽巷在掘进过程中速度慢、效率低，直接影响工作面的瓦斯抽采，为了改善上述情形，对炮孔间距进行研究。通过使用ANSYS软件对不同炮孔间距下快速掘进效果的模拟分析，并经现场验证，得出了适应该矿的最佳炮孔间距。结果表明：炮孔间距为500 mm时，爆破产生裂隙发育范围和岩石损伤区域都最大，快速掘进的效果最好。     

Toughness enhancement and equivalent initial fracture toughness of cementitious composite reinforced with aligned steel fibres

Based on theoretical analysis and numerical simulation, the impact of steel fibres on the stress intensity factor (SIF) at the crack tip for cementitious composite was studied. The enhanced toughness of steel fibre reinforced cementitious composite (SFRC) in resisting cracks was explained by the decrement of SIF caused by steel fibre inclusions at the crack tip of the composite. The equivalent initial fracture toughness was used to characterize the crack initiation of SFRC. A simplified method for determining the of SFRC was proposed based on a linear regression method. Fracture tests were conducted on three‐point bending notched beams with different steel fibre volume fractions and specimen sizes to study the crack initiation behaviour of aligned steel fibre reinforced cementitious composite (ASFRC). of ASFRC was calculated, and the size effect of was analysed. The results showed that slightly increased with the steel fibre volume fraction and gradually became stable. For the tested specimens, whose heights varied between 40 and 100 mm, the specimen size had little impact on the .     

PIXE study on recovery of making-technology of Chinese Longquan celadon made in the Southern Song Dynasty (1127–1279 CE)

Proton induced X-ray emission (PIXE) technique and factor analysis were used to study the recovery of making-technology of Chinese Longquan celadon made in the late Southern Song Dynasty (1127–1279 CE). Based on factor analysis, for the raw material for body and the recipe for glaze, there is a close but slightly different relationship between these Longquan celadons unearthed from the core area of Dayao and the non-core area, despite all the Longquan celadons belong to the high-calcium-glaze system. The chemical compositions of most of the tentative body and glaze samples are very close to those of Longquan celadons unearthed from the core area of Dayao and the non-core area. This study can provide a guidance for recovery of making-technology of Longquan celandon.