Novel TiC-based composites with enhanced mechanical properties

Novel TiC-based composites were synthesized by reactive hot-pressing at 1800 °C for 1 h with ZrB₂ addition as a sintering aid for the first time. The effects of ZrB₂ contents on the phase composition, microstructure evolution, and mechanical properties were reported. Based on the reaction and solid solution coupling effects between ZrB₂ and TiC, the product ZrC may be partially or completely dissolved into the TiC matrix, and then phase separation within the miscibility gap is observed to form lamellar nanostructured ZrC-rich (Zr, Ti)C. The TiC-10 mol.% ZrB₂ (starting batch composition) exhibits good comprehensive mechanical properties of hardness 27.7 ± 1.3 GPa, flexural strength 659 ± 48 MPa, and fracture toughness of 6.5 ± 0.6 MPa m^1/2, respectively, which reach or exceed most TiC-based composites using ceramics as sintering aids in the previous reports.     

中药桂枝总黄酮的提取工艺研究

优化桂枝总黄酮的提取工艺，建立桂枝的提取和含量测定方法。通过单因素试验，考察提取方法、提取溶剂浓度、提取体积、提取时间对药材总黄酮含量的影响，采用正交试验，优化提取工艺条件，筛选出桂枝总黄酮的最佳提取工艺。总黄酮最佳提取工艺为75%乙醇、料液比1:40、回流提取时间60 min。该方法能有效测定桂枝药材总黄酮的含量，为该药材的质量标准研究提供一定的科学依据。本方法重复性较好、方法稳定、可行。     

用于厚屏蔽小探测器的蒙特卡罗模拟减方差方法研究

反应堆屏蔽计算中经常出现厚屏蔽、小探测器问题，常规蒙特卡罗方法难以有效解决。基于自动重要抽样（AIS）方法，本文提出了小探测器自动重要抽样(SDAIS)方法，并针对小探测器问题，优化了AIS方法的虚粒子赌分裂算法。该方法在自主开发的蒙特卡罗屏蔽程序MCShield上进行了实现。使用NUREG/CR-6115 PWR基准题验证该方法的正确性和计算效率。结果表明，SDAIS方法可有效地解决厚屏蔽小探测器问题，相比AIS方法及传统的重要性方法，计算效率提升1~2个量级。     

中速柴油机机体铸造裂纹的原因分析及防止措施

根据柴油机机体裂纹产生的原因,对机体裂纹缺陷进行分析,找到了机体裂纹产生的主要原因。其主要原因可概括为铸件结构、化学成分、铸件补缩条件及开箱温度等,针对裂纹的主要原因采取相应的措施后,裂纹缺陷得到了根本的控制。     

Multiply Charged Conjugated Polyelectrolytes as a Multifunctional Interlayer for Efficient and Scalable Perovskite Solar Cells

A series of anionic conjugated polyelectrolytes (CPEs) is synthesized based on poly(fluorene-co-phenylene) by varying the side-chain ionic density from two to six per repeat units (MPS2-TMA, MPS4-TMA, and MPS6-TMA). The effect of MPS2, 4, 6-TMA as interlayers on top of a hole-extraction layer of poly(bis(4-phenyl)-2,4,6-trimethylphenylamine (PTAA) is investigated in inverted perovskite solar cells (PeSCs). Owing to the improved wettability of perovskites on hydrophobic PTAA with the CPEs, the PeSCs with CPE interlayers demonstrate a significantly enhanced device performance, with negligible device-to-device dependence relative to the reference PeSC without CPEs. By increasing the ionic density in the MPS-TMA interlayers, the wetting, interfacial defect passivation, and crystal growth of the perovskites are significantly improved without increasing the series resistance of the PeSCs. In particular, the open-circuit voltage increases from 1.06 V for the PeSC with MPS2-TMA to 1.11 V for the PeSC with MPS6-TMA. The trap densities of the PeSCs with MPS2,4,6-TMA are further analyzed using frequency-dependent capacitance measurements. Finally, a large-area (1 cm²) PeSC is successfully fabricated with MPS6-TMA, showing a power conversion efficiency of 18.38% with negligible hysteresis and a stable power output under light soaking for 60 s.