沸石催化剂在甲苯甲基化中的择形催化形用

综述了影响甲苯甲基化择形催化的因素,讨论了沸石的内外表面酸中心及酸强度、沸石的孔道、反应物和产物的吸附等因素对提高对二甲苯选择性的影响。     

前馈和反馈相结合的控制策略在宝钢线材厂控冷轧线上的应用实践

在详细分析料坯在水箱内冷却热过程特点的基础上，提出了前馈和反馈相结合的水流量优化控制策略，并将该策略应用于宝钢线材厂控冷轧线上。实际运行结果表明：该策略能够合理地控制水箱水流量，从而保证了线材水箱出口处的温度满足工艺要求，大大提高了线材成品的质量。所做工作对国内同类企业有重要的意义。     

镁合金表面喷铝防腐蚀层的微观组织分析

在AZ91D镁合金表面热喷铝，用以提高其表面的耐腐蚀性能。采用SEM，EPMA等方法对AZ91D表面喷铝扩散层的组织进行了仔细的观察与分析，发现在防腐蚀层上有大量的Mg17Al12相存在，且呈决状及非连续片状分布。经显微硬度测定，喷铝层硬度较镁合金基体高；腐蚀后这种相凸出于基体，比镁合金基体有较好的耐腐蚀性能。     

Temperature dependence of hydrogenated amorphous silicon thin-film transistors

The temperature dependence characteristics of hydrogenated amorphous silicon thin-film transistors were investigated. The results indicate that as the temperature was increased, the threshold voltage and the field-effect mobility were first increased, and then decreased, which may be controlled by different mechanisms at low and high temperatures. In addition, if the temperature was higher than 420 K, the Fermi level was promoted to the degenerate-like states, the current channel always existed due to the temperature effect, and the threshold voltage became negative.     

黄河小浪底郑州集中控制系统的实现

黄河小浪底郑州集中控制系统将多个相互联系的不同专业领域子系统有机地连接成一个整体。文中介绍了该系统的硬件配置和主要功能,并简单介绍了该系统所采用的网络安全措施。     

论住宅中的厨房设计

从多方面论述厨房设计中应遵循的原则及注意事项，以期对我国目前城市住宅建设中的厨房设计有所启示。     

大庆油田杏1-3区三次加密试验区剩余油分布研究

通过对试验区近年完钻的检查井各单砂层水淹状况及其影响因素的分析。利用神经网络模式识别方法建立起单层剩余油识别模型，在此基础上对三次加密试验区各小层剩余油分布进行研究，总结出各类油层剩余油分布特征及成因类型，并分析了试验区剩余油潜力分布，从而为三次加密布井及射孔方案编制提供了可靠的依据。     

三峡工程明渠提前截流方案及水力学试验研究

论述了三期明渠提前截流方案的综合比较分析及截流水力学试验研究成果。认为拟定的提前截流诸方案各有利弊 ,其截流难度较初设方案显著增加。对于截流“基本方案”及“比较方案”的成功实施 ,必须辅之以一定的工程技术措施降低截流难度     

石英砂脱水性能的研究

通过大量试验结果 ,研究了各种粒度范围的石英砂的脱水性能 ,包括沉降特性、过滤性能、极限压缩浓度等 ,为进行此类产品的固液分离提供了重要的参考数据     

Thermal—Mechanical Fatigue Behavior and Life Analysis of Cast Ni—base Superalloy K417

In-phase(IP) and out-of-phase(OP)thermal-mechanical fatigue(TMF) behavior of cast Ni-base superalloy K417 was studied.All experiments were carried out under total strain control with temperature cycling between 400-850℃.Both in-phase and out-of-phase TMF specimens exhibited cyclic hardening followed by cyclic softening at the minimum temperature.Besides,they cyclically hardened in the early stage of life followed by cyclic softening at the minimum temperature.Besides,they cyclically hardened in the early stage of life followed by cyclic softening at the maximum temperature.OP TMF life was longer than of IP TMF.Various damage mechanisms operating in different controlled strain ranges and phasing were discussed.A few life prediction methods for isothermal fatigue were used to handle TMF fatigue and their applicability to superalloy K417 was evaluated.The SEM analysis of the fracture surface showed that transgranular fracture was the principal cracking mode for both IP and OP TMF.Oxidation was the main damage mechanism in causing shorter fatigue life for IP TMF compared with OP TMF.