Fabrication of NiO Nanoparticle-Coated Lead Zirconate Titanate Powders by the Heterogeneous Precipitation Method

NiO nanoparticle-coated lead zirconate titanate (PZT) powders are successfully fabricated by the heterogeneous precipitation method using PZT, Ni(NO₃)₂·6H₂O, and NH₄HCO₃ as the starting materials. The amorphous NiCO₃·2Ni(OH)₂·2H₂O are uniformly coated on the surface of PZT particles. XRD analysis and the selected-area diffraction (SAD) pattern indicate that the amorphous coating layer is crystallized to NiO after being calcined at 400°C for 2 h. TEM images show that the NiO particles of ∼8 nm are spherical and weakly agglomerated. The thickness of the nanocrystalline NiO coating layer on the surface of PZT particle is ∼30 nm.     

过量TiO2助烧剂对Ba0.998La0.002TiO3陶瓷晶粒生长的影响

采用电性能测定和微观结构分析等方法研究了过量TiO2助烧剂对Ba0.998La0.002TiO3陶瓷晶粒生长的影响.结果表明:对于Ba0.998La0.002TiO3陶瓷在有液相参与烧结的晶粒溶解-淀析过程中,晶粒生长的必要条件是不仅要有液相的形成,而且BaTiO3晶粒必须在液相中有一定的溶解度.由于BaTiO3晶粒在Ba6Ti17O40和Ba2TiSi2O8液相中有足够的溶解度,促进了晶粒的生长,同时旌主掺杂离子进入晶格而释放氧,形成半导性的陶瓷,而BaTiO3晶粒不能溶解于Ba2Ti2SiP2O13液相中,抑制了晶粒的生长.     

双层推板式PTC隧道窑及其控制过程

针对目前工业化大生产Ｔｃ＝１２０，２４０℃等ＰＴＣ陶瓷，以其烧结机理和典型的烧成曲线为依据，设计建造出双层推板式电脑控制隧道窑，通过半年多生产实践表明：只要选择适当的配方，能够满足大规模连续生产的要求，其窑温控制精度在±２℃内，产品合格率大于９０％；日产量达１．８片左右（片子尺寸为２５×１５×２．８ｍｍ）；其正常消耗功率为３０ｋＷ左右吡同类窑节约１／４－１／３能源。     

Development of three-electrode type micro-electrochemical reactor on anodized aluminum with photon rupture and electrochemistry

Photon rupture with a focused single pulse of pulsed YAG-laser irradiation was used to fabricate an aluminum electrochemical micro-reactor. Porous type anodic oxide film formed on aluminum specimens was irradiated in solutions with a pulsed Nd-YAG laser beam through a convex lens to fabricate micro-channels, micro-electrode, and through holes (for reference electrode, solution inlet, and outlet). During irradiation, specimens were moved by a computer controlled XYZ stage. After irradiation, the surface of the micro-channel and through hole were again treated to form anodic oxide film and the surface of the micro-electrode was treated electrochemically to provide an Au layer. The calculated volume of the micro-reactor including micro-channel and through holes is about 1.5 μl. The cyclic voltammogram of the micro-electrochemical cell was measured in K₃Fe(CN)₆/K₄Fe(CN)₆ with both static and flowing solution at different scanning rates. The anodic and cathodic peak currents were measured and the values depended on scanning rate and ion concentration when the solution was static. With the flowing solution, limiting currents were observed and the anodic limiting current was increased with the cubic root of the solution flow rate.     

降温速率对Ba0.92Ca0.08TiO3 PTCR陶瓷室温电阻率"反常"现象的影响

通过系统研究烧结工艺对BaO92Ca0.08TiO3电阻正温度系数(possitive temperature coefficient resistance，PTCR)陶瓷的影响，在晶粒生长过程中分析液相在晶界中的分布。着重研究降温速率对PTCR室温电阻率的影响。发现在1300～1150℃温区内，当降温速率大于15℃／min时，出现随降温速率增加，室温电阻率增大的“反常”现象。根据液相在晶界区分布随降温速率的变化规律，对这种“反常”进行解释。     

负载钛酸酯催化剂催化合成己二酸二异辛酯

聚乙烯醇与四氯化钛在二甲基亚砜和无水乙醇的混合溶剂中反应，制得负载钛酸酯催化剂PVAC-1，用红外光谱对其进行了表征。结果表明：合成中投入3g聚乙烯醇，3mL四氯化钛时，过程容易控制，且催化剂的活性已达很高。确定了在PVAC-1催化作用下，合成己二酸二异辛酯的最佳反应条件及结果：即200℃～210℃下，加入0.3g催化剂，0．1mol己二酸与0．3mol异辛醇反应60min后，己二酸的转化率可达99．7％，PVAC-1重复使用16次后，己二酸的转化率仍保持在96％以匕。     

SHS of mineral-like ceramics for immobilization of radioactive nuclear wastes

Synthetic analogs of titanate ceramics (perovskite and zirconolite) designed for use as a matrix for immobilization of high-level nuclear fuel reprocessing wastes (HLW). Such ceramics have been prepared by SHS method from a mixture of titanate ceramics and non-radioactive model oxides. Synthesis conditions have been optimized. The synthesized low-porosity cylindrical compacts exhibited a high strength and low rate for leaching Cs, Sr, Y, Ce, and La in bidistilled water. The phase composition and microstructure of synthesized products have been characterized. The immobilization of Cs was found to be accompanied by a marked loss of this element. The text was submitted by the authors in English.     

一种螯合型钛酸酯偶联剂的制备

介绍了一种以钛酸四异丙酯、丙烯酸和焦磷酸烷基酯为原料,乳酸为螯合剂合成的钛酸酯偶联剂,它适用于无机粉末有机包覆改性中的粉末预处理。     

掺锰BaTiO3 PTCR陶瓷的电子顺磁共振研究

利用电子顺磁共振（EPR）方法对Mn掺杂的BaTiO3 PTCR陶瓷在120－450K的温度范围内进行了研究，研究结果表明：高自旋Mn^2 离子的6重谱线非常明显，表征谱线位置的g因子为2．009 9,Mn^2 离子信号弱弱与BaTiO3晶体结构密切相关，Mn^2 离子信号的温度分布呈U型，即在三方相和立方相时，信号强度较强，而在四方相和斜方相时信号很弱，这是因为在四方相和斜方相中，由于BaTiO3晶体结构的扭曲和畸变，导致Mn^2 和Vo空位缔合生成Mn^2 -Vo复合缺陷，未成对电子的消失以及复合缺陷n^2 -Vo的生成最Mn^2 在四方相和斜方相（200－380K）消失的主因，实验中没有发现Mn^3 和Mn^4 的信号，而与实验的环境条件一致，掺Mn后样品Curie点的漂移可能是Mn进入晶格的一个判据，此外，由于试样的n(Ba)/n(Ti)=1，因而没有发现钡空位VBa及其它的复合缺陷（如：VBa-Mn^2 ,Mn^3 -Vo,La^3 -Mn^3 等），Mn^2 离子等电子陷阱的生长是Curie温度处电阻骤然增加的主要原因。     

Barium Carbonate Phase on the Surfaces of Barium Titanate Particles and in Situ Transmission Electron Microscopy Observation of Its Decomposition

A BaCO₃ phase is found on the surfaces of hydrothermally synthesized BaTiO₃ particles; it occurs as aggregates or small protuberances. A small proportion of the phase decomposes to BaO crystallites when heated by a convergent electron beam in a transmission electron microscope. The BaO and BaCO₃ crystallites disappear when they are irradiated successively by the convergent electron beam. The BaO crystallites and the BaCO₃ phase sublimate and/or react with BaTiO₃ crystals whose surface layers are deficient in Ba²⁺ ions.