The chloride stress-corrosion cracking behavior of stainless steels under different test methods

Chloride-induced stress-corrosion cracking (SCC) is one of the failure modes of stainless steels. Highly alloyed austenitic stainless steels S32654, S31254, and N08028, and duplex grades S32750 and S31803 possess much improved resistance to SCC compared with S30400 and S31600 steels. With the development of a database, SSData, experimental data collected from calcium chloride tests, autoclave tests, and drop evaporation tests were evaluated. Stress-corrosion cracking data generated by autoclave tests agreed well with the practical service conditions and can be used to discriminate alloys for SCC resistance in sodium chloride solution. Drop evaporation test data can be used in situations where evaporation may occur and cyclic loading may be involved. The SCC resistance of alloys under each method increased with increasing molybdenum equivalent Mo + 0.25Cr + 0.1Ni. For a given alloy, the testing result depends on the stress state and environment; different test methods can give different ranking orders concerning SCC resistance. The performance of duplex stainless steels in a chloride-containing environment at higher temperatures was not as good as expected when dynamic loading was involved.     

前馈和反馈相结合的控制策略在宝钢线材厂控冷轧线上的应用实践

在详细分析料坯在水箱内冷却热过程特点的基础上，提出了前馈和反馈相结合的水流量优化控制策略，并将该策略应用于宝钢线材厂控冷轧线上。实际运行结果表明：该策略能够合理地控制水箱水流量，从而保证了线材水箱出口处的温度满足工艺要求，大大提高了线材成品的质量。所做工作对国内同类企业有重要的意义。     

镁合金表面喷铝防腐蚀层的微观组织分析

在AZ91D镁合金表面热喷铝，用以提高其表面的耐腐蚀性能。采用SEM，EPMA等方法对AZ91D表面喷铝扩散层的组织进行了仔细的观察与分析，发现在防腐蚀层上有大量的Mg17Al12相存在，且呈决状及非连续片状分布。经显微硬度测定，喷铝层硬度较镁合金基体高；腐蚀后这种相凸出于基体，比镁合金基体有较好的耐腐蚀性能。     

微电机与微加工

简述了和微电机相关的微加工生产中的方法，介绍了微型机电部件成型的实现途径。     

金线断口的分析

运用扫描电子显微镜技术，对金线断口观察分析，讨论金线在拉伸过程中断裂时断口形貌及断裂的原因，发现，断裂是由于金锭中的气体和杂质引起的，并提出改进生产工艺的意见。     

含微量元素铜焊锡丝的研制

在６０／４０的锡铅焊料中加入０．２％左右的铜，凝固后具有均匀细小的共晶组织，其熔点为１８３℃，焊点强度和扩展率均高于未加铜的６０／４０锡铅焊料，并且含铜的锡铅焊料在焊接时，对铜烙铁头和微细铜线了小的熔蚀性。     

提高气门弹簧钢丝质量的途径

指出了影响气门弹簧钢丝疲劳性能的主要因素是冶金因素，介绍了国外先进的气门弹簧钢丝生产的冶炼、轧制和拉拔新工艺，提出了提高国产气门弹簧钢丝质量应采取的措施。     

回火处理对高碳冷拔钢丝强度和塑性的影响

研究了６５钢冷拔钢丝在５００℃不同时间回火时的抗拉强度和延伸率的变化。试验结果发现，在回火初期，抗拉强度首先增长，然后随口火时间的延长连续降低，而延伸率始终在增长，增长速度是先快后慢。这种行为可归因于第一内应力的消除和ε－碳化物在形变铁素体中的析出以及后来再结晶的发生。     

Direct electroless Ni-P deposition on AM50 magnesium alloy from sulfate bath

A bright electroless Ni-P deposition on AM50 magnesium alloy in a sulfate plating bath was proposed by using direct plating process with non-chromate pretreatment. The electroless Ni-P plating on AM50 magnesium alloy has an admirable appearance and good adhesion. The results indicate that the electroless Ni-P deposition with non-chromate pretreatment has better adhesion than that of zinc immersion coating. Anodic polarization curves indicate that the electroless Ni-P deposition obtained from the sulfate bath has similar corrosion-resistance to that obtained from basic nickel carbonate bath. The deposition process generates less pollutant by a non-chromate plating bath and is suitable for the magnesium alloys manufacture because of its low cost. The hardness of the electroless Ni-P plated AM50 is about HV 720.6 and HV 969.7 after heat treatments at 180℃ for 2 h. The wear resistance of Ni-P plated magnesium alloy specimens is about 5 to 9 times as high as that of bare magnesium alloys.