Enhanced photoelectric properties of PbSnSe thin films via quick oxygen ion-implantation sensitization

Journal of Materials Science - Although chalcogenide materials continue to generate considerable interest due to great potentials for various optoelectronic devices, annealing for a long time in...     

One step from nanofiber to functional hybrid structure: Pd doped ZnO/SnO2 heterojunction nanofibers with hexagonal ZnO columns for enhanced low-temperature hydrogen gas sensing

In this paper, a novel hybrid structure of Pd doped ZnO/SnO₂ heterojunction nanofibers with hexagonal ZnO columns was one step synthesized from electrospun precursor nanofibers. Due to the synergistic effect of hexagonal ZnO, SnO₂ and Pd, the structure exhibited excellent hydrogen (H₂) gas sensing properties. At low-temperature of 120 °C, the response (R_a/R_g) to 100 ppm H₂ gas exceeded 160, the response/recovery time was only 20 s and 6 s respectively and the limit of detection was only 0.5 ppm. Meanwhile, it also had good selectivity for H₂ gas and excellent linearity. In addition, the materials were characterized by XRD, FESEM, HRTEM, XPS, and the synthesis mechanism and gas sensing mechanism were proposed.     

Improving gelling properties of myofibrillar proteins incorporating with cellulose micro/nanofibres

The effects of cellulose microfibres (CMFs, Average size: 100 ± 5 μm) and cellulose nanofibres (CNFs, Average size: 60 ± 3 nm) on the properties of myofibrillar protein (MP) gels from duck breast meat were studied. The results demonstrated that CMFs and CNFs were mostly connected to MP by non-covalent bonds, the diffusion and cross-linking of MP molecules was promoted, and a denser and more complete gel network was formed. With the increases of CMFs and CNFs concentration (0–10%), the hardness was increased by 13.15% and 19.78% for CMFs10% and CNFs10% gels, respectively, and the elasticity was increased by 40% and 80%, respectively. At the same concentration (0–10%), the increase in gel hardness, viscoelasticity and immobilised water content was greater in the CNFs-MP group than in the CMFs-MP group. The CNFs-MP group had a tighter gel network, and CNFs had a better potential to improve the gelation performance of MP.     

Inhibitory effects of curcumin and piperine on fluorescent advanced glycation end products formation in a bovine serum albumin–fructose model

This study investigated the inhibitory effects of curcumin and piperine on fluorescent advanced glycation end products (fAGEs) formation in a bovine serum albumin (BSA)–fructose model. Model systems of BSA and fructose were prepared, and curcumin or piperine was added. fAGEs and BSA oxidation product (dityrosine, kynurenine and N'-formylkynurenine) contents were determined. The results showed that fAGEs content decreased with increasing concentration of curcumin and piperine (P < 0.05). Addition of curcumin and piperine at 160 µg mL⁻¹ could inhibit fluorescent AGEs by 100% and 93% respectively. Dityrosine and N'-formylkynurenine contents decreased as curcumin and piperine concentration increased (P < 0.05). Furthermore, the result of principal component analysis indicated that curcumin and piperine markedly impeded BSA oxidation, resulting in a lower level of fAGEs in model systems. Therefore, adding curcumin and piperine may facilitate reduced fAGEs levels in BSA–fructose model.     

Transgenerational Effects of Di(2-Ethylhexyl) Phthalate on Anogenital Distance,Sperm Functions and DNA Methylation in Rat Offspring

Di(2-ethylhexyl) phthalate (DEHP) is widely used as a plasticizer in the manufacture of polyvinylchloride plastics and has been associated with concerns regarding male reproductive toxicity. In this study, we hypothesized that maternal exposure to DEHP induces transgenerational inheritance of adult-onset adverse reproductive outcomes through the male germline in the F1, F2, and F3 generations of male offspring. Pregnant rats were treated with 5 or 500 mg of DEHP/kg/day through gavage from gestation day 0 to birth. The offspring body weight, anogenital distance (AGD), anogenital index (AGI), sperm count, motility, and DNA fragmentation index (DFI) were measured for all generations. Methyl-CpG binding domain sequencing was performed to analyze sperm DNA methylation status in the F3. DEHP exposure at 500 mg/kg affected AGD, AGI, sperm count, mean DFI, and %DFI in the F1; AGD, sperm count, and mean DFI in the F2; and AGD, AGI, mean DFI, and %DFI in the F3. DEHP exposure at 5 mg/kg affected AGD, AGI, sperm count, and %DFI in the F1; sperm count in the F2; and AGD and AGI in F3. Compared with the control group, 15 and 45 differentially hypermethylated genes were identified in the groups administered 5 mg/kg and 500 mg/kg DEHP, respectively. Moreover, 130 and 6 differentially hypomethylated genes were observed in the groups administered 5 mg/kg and 500 mg/kg DEHP. Overall, these results demonstrated that prenatal exposure to DEHP caused transgenerational epigenetic effects, which may explain the observed phenotypic changes in the male reproductive system.     

传统牦牛酸奶源高产胞外多糖乳酸菌特性及发酵性能

为了研究四川藏区传统牦牛酸奶中高产胞外多糖乳酸菌特性及发酵性能，以本实验室分离出的六株高产胞外多糖乳酸菌为研究对象，以菌株生长量、耐酸性、胆盐耐受力、渗透压耐受力和细胞表面疏水性为指标进行特性研究；以发酵酸奶的凝乳时间、持水力、酸化及后酸化能力、挥发性物质及质构等为指标进行发酵性能研究。菌株的生长曲线表明，6株菌株分别在14 h（218、276、266）、16 h（271、285、231）进入对数生长稳定期，其中编号218的菌株生长量最高，OD值为2.188。耐受性实验结果表明，菌株276具有良好的耐酸能力（P<0.05）；菌株266、218、231耐胆盐的能力较强；6株菌株均具有较好的耐渗透压的能力，其中菌株285对高渗透压的耐受性较强；菌株285和218在两种有机试剂中的疏水性均显著（P<0.05）高于其他菌株，且与十六烷的结合效果较好。发酵试验结果表明，6株菌株所发酵酸奶均在6~8 h内凝固，酸乳在冷藏期间，活菌数均保持在107 CFU/mL以上，均符合发酵剂的标准，其中菌株276的最高为3.22×106 CFU/mL；菌株218发酵制得的酸奶质构特性较好，持水力和酸化能力较其余菌株均最强，分别为60.98%和83 °T；菌株276、266抗后酸化能力较好；菌株231产香性能最优，乙醛含量为24~26 μg/mL，双乙酰含量为1.58~3.73 μg/mL，能够明显改善酸奶的风味。通过综合比较6株高产胞外多糖乳酸菌特性及发酵性能，菌株218为一株性能良好、具有良好稳定性的菌株，可作为乳酸菌发酵剂且具有一定的应用潜力。研究为利用四川藏区传统牦牛酸奶中分离出的高产胞外多糖乳酸菌在发酵乳制品的应用提供理论依据。     

基于禁忌搜索的晶体位置谱分割与校准方法

为满足不同规格晶体探测器对分割校准晶体条响应事件位置数据的需求，开发了一种以禁忌搜索算法为核心，结合UDP数据帧、二维高斯模型及光导折射率的位置信息分割校准方法。实验结果表明，本方法在溢出率为5%时，峰谷比可达1218，空间分辨率达17 mm，晶体条响应位置识别准确度高达99%，滤除了引发伪峰的噪声，避免了过分割问题。在面对多种规格晶体阵列的位置谱时，本方法能依照阵列规格将晶体条区域的响应自动校准编号并输出晶体位置查找表，实现响应事件的精确校准。     

Dense and core-rim structured B4C-TiB2 ceramics with Mo-Co-WC additive

B₄C-TiB₂ ceramics (TiB₂ ranging 5~70 vol%) with Mo-Co-WC as the sintering additive were prepared by spark plasma sintering. In comparison with B₄C-TiB₂ without additive, the enhanced densification was evident in the sintered specimen with Mo-Co-WC additive. Core-rim structured grain was observed around TiB₂ grains. The interface of the rim between TiB₂ and B₄C phases demonstrated different feature: the inner borderline of the rim exhibited a smooth feature, whereas a sharp curved grain boundary was observed between the rim and the B₄C grain. The formation mechanism is discussed: the epitaxial growth of (Ti,Mo,W)B₂ rim around the TiB₂ core may occur as a result of the solid solution and dissolution-precipitation between TiB₂ phase and the sintering additive. It was revealed that the fracture toughness increased as the content of TiB₂ content increased, alongside the decreased hardness. B₄C-30 vol% TiB₂ specimen demonstrated the optimal combination of mechanical properties, reaching Vickers hardness of 24.3 GPa and fracture toughness of 3.33 MPa·m^1/2.     

Optical and electrical properties of ITO film on flexible fluorphlogopite substrate

Indium Tin Oxide (ITO) films were prepared, at room temperature, on a fluorphlogopite substrate using magnetron sputtering technology. At various temperatures of 500 °C, 600 °C, 700 °C, 800 °C, and 900 °C, the samples were (had) annealed for 2 h (a 2-h duration). The results showed improvement in the crystalline performance of ITO film at selected annealing temperatures, with a significant reduction in resistivity at 800 °C. The lowest resistivity is 4.08 × 10^?4 Ω-cm, which is nearly an order of magnitude lower than the unannealed sample. All samples have an average light transmittance above 85% in the visible light range (400–800 nm), and with increasing annealing temperature, the average light transmittance tends to decrease. Besides, at the sensitive wavelength of 550 nm, the light transmittance is as high as 93.74%. The sheet resistance testing of the sample was through the number of bending times, which revealed that with the increase of the number of bending, the sheet resistance increases. However, after 1200 bending times, the change rate of the sheet resistance remains below 5%. Thus, the ITO film prepared on the flexible fluorphlogopite substrate revealed excellent optical and electrical properties, good flexibility, and improved stability after high-temperature annealing, which guarantees successful application in flexible electronic devices.