Improving gelling properties of myofibrillar proteins incorporating with cellulose micro/nanofibres

The effects of cellulose microfibres (CMFs, Average size: 100 ± 5 μm) and cellulose nanofibres (CNFs, Average size: 60 ± 3 nm) on the properties of myofibrillar protein (MP) gels from duck breast meat were studied. The results demonstrated that CMFs and CNFs were mostly connected to MP by non-covalent bonds, the diffusion and cross-linking of MP molecules was promoted, and a denser and more complete gel network was formed. With the increases of CMFs and CNFs concentration (0–10%), the hardness was increased by 13.15% and 19.78% for CMFs10% and CNFs10% gels, respectively, and the elasticity was increased by 40% and 80%, respectively. At the same concentration (0–10%), the increase in gel hardness, viscoelasticity and immobilised water content was greater in the CNFs-MP group than in the CMFs-MP group. The CNFs-MP group had a tighter gel network, and CNFs had a better potential to improve the gelation performance of MP.     

Statistical Piezotronic Effect in Nanocrystal Bulk by Anisotropic Geometry Control

Utilizing inner-crystal piezoelectric polarization charges to control carrier transport across a metal-semiconductor or semiconductor–semiconductor interface, piezotronic effect has great potential applications in smart micro/nano-electromechanical system (MEMS/NEMS), human-machine interfacing, and nanorobotics. However, current research on piezotronics has mainly focused on systems with only one or rather limited interfaces. Here, the statistical piezotronic effect is reported in ZnO bulk composited of nanoplatelets, of which the strain/stress-induced piezo-potential at the crystals’ interfaces can effectively gate the electrical transport of ZnO bulk. It is a statistical phenomenon of piezotronic modification of large numbers of interfaces, and the crystal orientation of inner ZnO nanoplatelets strongly influence the transport property of ZnO bulk. With optimum preferred orientation of ZnO nanoplatelets, the bulk exhibits an increased conductivity with decreasing stress at a high pressure range of 200–400 MPa, which has not been observed previously in bulk. A maximum sensitivity of 1.149 µS m⁻¹ MPa⁻¹ and a corresponding gauge factor of 467–589 have been achieved. As a statistical phenomenon of many piezotronic interfaces modulation, the proposed statistical piezotronic effect extends the connotation of piezotronics and promotes its practical applications in intelligent sensing.     

Pseudocapacitive contributions to electrochemical kinetics in NiOx electrochromic anodes

Because of its ability to change optical absorption dynamically by applied electric field, nickel oxide (NiO) is a promising anodic material in smart windows, which can improve energy conversion efficiency in construction buildings. Although many works have achieved high electrochromic performance with different method. The underlying mechanism is still not fully investigated. In this article, we prepared the NiO films with large specific surface area and high stability by electron beam evaporation. X-ray diffraction (XRD), scanning electron microscopy (SEM) and X-ray photoelectron spectroscopy (XPS) were employed to figure out the surface morphology and composition of as-deposited films. Afterwards, the electrochemical properties and optical performance of the prepared NiO films were investigated. On this basis, the origin of surface charge was fully analyzed by cyclic voltammetry and diffusion coefficient test. These experimental and theoretical results firmly confirm that both the surface reaction and capacitive effect bring about the excellent EC performance in NiO films. These results not only provide clear evidence about electrochemical kinetics in NiO films, but also offer some useful guidelines for the design of EC materials with higher performance and longer stability.     

Dual effect synergistically triggered Ce:(Y,Tb)3(Al,Mn)5O12 transparent ceramics enabling a high color-rendering index and excellent thermal stability for white LEDs

Ce:Y₃Al₅O₁₂ transparent ceramics (TCs) with appropriate emission light proportion and high thermal stability are significant to construct white light emitting diode devices with excellent chromaticity parameters. In this work, strategies of controlling crystal-field splitting around Ce³⁺ ion and doping orange-red emitting ion, were adopted to fabricate Ce:(Y,Tb)₃(Al,Mn)₅O₁₂ TCs via vacuum sintering technique. Notably, 85.4 % of the room-temperature luminescence intensity of the TC was retained at 150 °C, and the color rendering index was as high as 79.8. Furthermore, a 12 nm red shift and a 16.2 % increase of full width at half maximum were achieved owing to the synergistic effects of Tb³⁺ and Mn²⁺ ions. By combining TCs with a 460 nm blue chip, a warm white light with a low correlated color temperature of 4155 K was acquired. Meanwhile, the action mechanism of Tb³⁺ ion and the energy transfer between Ce³⁺ and Mn²⁺ ions were verified in prepared TCs.     

复杂难选铁矿石悬浮磁化焙烧-高效分选技术

针对传统铁矿石磁化焙烧技术与装备存在焙烧产品质量差、产能低、能耗高和环境污染严重等问题，创造性提出了一种“预热-蓄热还原-再氧化”悬浮磁化焙烧新工艺。该工艺具有原料适应性广、焙烧产品质量均匀、回收率高、生产能耗低、无污染等特点，适合处理赤铁矿、褐铁矿、菱铁矿及其混合型难选铁矿石。通过多年的潜心基础研究与技术攻关，形成了非均质矿石颗粒悬浮态流动控制、蓄热式高效低温还原、铁物相精准调控与余热同步回收等一系列关键技术，建成了500kg/h复杂难选铁矿石悬浮磁化焙烧-高效分选半工业试验平台。