再生混凝土骨料含水状态与新拌混凝土的性能

研究了再生混凝土骨料在不同的含水 (自然干燥、饱和面干、完全干燥 )状态下 ,制得的新混凝土的流动性、抗压强度、劈裂张拉强度和干缩性能。试验结果表明 ,新拌混凝土的初始坍落度随着再生骨料含水量的增大而减小 ,坍落度损失也随着再生骨料含水量的增大而减小。用 10 0 %再生骨料制备的混凝土的早期强度较低 ,但经过2 8d之后 ,各种混凝土的抗压强度趋于接近。但是 ,由饱和面干状态和干燥状态的再生骨料制备的混凝土的劈裂张拉强度和干缩值明显高于其它混凝土。     

非连续级配再生粗骨料自密实混凝土的工作性能试验研究

为了研究非连续级配再生粗骨料自密实混凝土的工作性能,采用控制变量法,研究了再生粗骨料取代率、砂率和经时损失对其工作性能的影响。试验结果表明:非连续级配的再生粗骨料可以配制出满足工作性能要求的自密实混凝土。当再生粗骨料取代率为50%时工作性能最好;当砂率为45%时,新拌混凝土的工作性能最好;随着时间的延长,新拌混凝土工作性能下降,添加适量的聚羧酸高性能减水剂可以恢复其坍落扩展度;给出的坍落扩展度经时损失公式计算简单,计算结果准确,可以作为新拌混凝土经时损失评价的参考。     

再生粗骨料最大堆积密度及其对混凝土性能影响

为研究再生粗骨料级配对混凝土性能的影响,通过测定连续级配再生粗骨料最大堆积密度、吸水率、筛分析及新拌混凝土坍落度和硬化混凝土7,28,60d抗压强度,最终确定达到最紧密堆积状态时16.0~31.5mm与5.0~20.0mm两种单粒级再生粗骨料的最佳混合质量比.结果表明:随着16.0~31.5mm与5.0~20.0mm两种单粒级再生粗骨料混合质量比的逐渐降低,连续级配再生粗骨料的最大堆积密度及吸水率均呈现出先增大后减小的趋势,但波动不大.随着5.0~20.0mm单粒级再生粗骨料所占比例的增加,不同连续级配再生粗骨料对新拌混凝土的工作性影响十分明显,同时,对硬化混凝土的抗压强度也有较大影响,两者均呈现出先增大后减小的趋势;16.0~31.5mm与5.0~20.0mm两个单粒级再生粗骨料存在一个最佳的混合质量比7.0∶3.0.     

高强再生骨料混凝土的耐久性能及影响因素研究

目前,国内外所制备的再生骨料混凝土的强度值都较低,只能用于非承重构件,另外对再生骨料混凝土耐久性方面的研究仍不多。本文利用废弃混凝土,按照所提出的一种新生产工艺制备再生骨料,然后按照要求配制成高强度再生骨料混凝土。研究发现:采用取代率为50%的再生粗骨料和取代率为30%的再生细骨料所配制的再生骨料混凝土强度能够达到高强混凝土强度要求。此外,本文研究了高强再生骨料混凝土的耐久性能,探讨了粉煤灰、二次搅拌、再生粗骨料最大粒径和初始含水状态对高强再生骨料混凝土的收缩性能、抗碳化性能、抗氯离子渗透性能和抗硫酸盐侵蚀性能的影响。     

再生粗集料初始含水率对混凝土性能的影响

通过设计试验研究了再生粗集料初始含水率对新拌再生集料混凝土塌落度及其物理力学性能的影响。研究结果表明:再生粗集料初始含水率将显著影响新拌混凝土塌落度及其经时损失。当再生粗集料为干燥或气干状态时,其较大的吸水率导致混凝土初始塌落度随再生粗集料替代率的增大而明显增大且经时损失减小。另外,由不同初始含水率再生粗集料配制的混凝土抗压强度和劈裂抗拉强度均出现下降,饱和面干再生粗集料内部大量自由水导致混凝土抗压强度及劈裂抗拉强度下降最大;当再生粗集料为干燥状态时,混凝土抗压强度和劈裂抗拉强度下降最小,但劈裂抗拉强度值较为离散,与其抗压强度值相关性较差。因此,在再生混凝土的实际工程应用中,应尽量避免使再生粗集料处于干燥或潮湿状态。     

再生粗骨料取代率对混凝土各项性能的影响

利用不同品质的3种再生粗骨料,研究了再生粗骨料取代率对混凝土的工作性能、力学性能及干缩性能的影响.结果表明,利用再生粗骨料取代碎石,高品质再生粗骨料可以使碎石混凝土的性能得到改善,而低品质再生粗骨料则降低碎石混凝土的性能,且再生粗骨料取代率不宜超过50%.     

再生粗骨料特性及对混凝土性能的影响研究

研究了再生粗骨料的物理力学特性,以再生粗骨料部分或全部取代天然粗骨料、以活性掺合料部分取代水泥,制成再生混凝土,对再生混凝土的物理力学性能和耐久性能进行了研究.结果表明,随着再生粗骨料掺量的增加,混凝土的抗气渗性能、抗氯离子渗透性能、收缩性能均有下降趋势.掺加活性掺合料,可以改善再生混凝土的抗气渗性能.     

再生骨料粗细级配对水泥混凝土性能影响研究

通过将废弃水泥混凝土试块破碎、筛分制备成再生粗细骨料,重新拌制水泥混凝土,研究再生粗骨料粒径大小、级配情况以及再生细骨料颗粒级配、粗细程度对水泥混凝土的影响规律。结果表明,再生骨料可用于制备水泥混凝土,通过界面胶结以及微粉填充密实,使得级配连续的大粒径再生粗骨料或Ⅱ区中砂的再生细骨料更有利于新拌混凝土的和易性以及硬化后混凝土的强度和抗渗性能,但同时应注意控制再生骨料中石粉及针片状含量。     

高强再生混凝土干缩特性

研究了再生粗细骨料对混凝土干缩性能的影响,试验结果表明,再生骨料对混凝土的干缩影响显著,尤其是再生细骨料。重点研究了高强再生粗骨料混凝土的干缩特性,通过高强再生混凝土配合比优化设计,再生粗骨料混凝土的干缩率仅稍大于天然粗骨料混凝土,与其基本相当。在再生混凝土中掺膨胀剂具有很好的补偿收缩效果,达到高强再生混凝土微干缩的目的。研究表明,干燥环境养护对再生混凝土强度的影响明显大于普通混凝土,因此,再生混凝土更需注意保湿养护。还从界面结构和骨料特性分析了再生混凝土的干缩机理。     

施工条件对再生混凝土性能的影响

研究了不同施工条件下再生混凝土性质,并与原生混凝土对比.本研究设置了三种不同的施工条件,即再生粗骨料是否预吸水、振捣密实程度及养护方式,同时考虑四种不同的再生粗骨料取代率的影响;通过测试施工期新拌再生和原生混凝土的坍落度、含气量,以及结硬后再生和原生混凝土的28 d抗压强度、渗气性、密实性、均匀性等,探究不同施工条件、不同再生粗骨料取代率对于再生混凝土施工期性能及力学性能等的影响规律,并与原生混凝土进行对比.试验结果表明:再生粗骨料取代率以及施工条件对再生和原生混凝土的性质都有较大的影响.     

再生粗骨料混凝土性能的研究

将几种取自不同地点的废弃混凝土破碎制成粗骨料,然后通过不同搭配,配制成几种不同水灰比、坍落度的再生混凝土,并对其新拌混凝土早期的性能进行测试比较,研究结果表明,在相同条件下,再生混凝土的流动性比普通混凝土的差;再生混凝土的凝结时间比普通混凝土要短;再生混凝土的抗压强度一般随再生骨料掺量的增加而降低;吸水率高的再生骨料对应的再生混凝土强度低;通过各种方法的复合运用,可配得较高抗压强度的再生混凝土;混合再生骨料配制的再生混凝土,其中原始混凝土强度低的再生骨料,对低水灰比和高水灰比的再生混凝土有不同的影响效果。     

The role of industrial by-products in self-compacting concrete

The development of self-compacting concrete is considered as a milestone achievement in concrete technology due to several advantages. In order to be self-compactable the fresh concrete must show high fluidity besides good cohesiveness. For the purpose of evaluating these properties, several concrete mixtures were prepared with a water to cement ratio of 0.45 in the presence of an acrylic-based superplasticizer at a dosage ranging from 1% to 2% by weight of very fine material fraction (maximum 150 μm). Either limestone powder or fly ash or recycled aggregate powder (that is a powder obtained from the rubble recycling process) were used as mineral addition, in order to assure adequate rheological properties, in terms of cohesiveness, in the self-compacting concretes. Preliminary rheological tests were carried out on cement pastes containing these mineral additions. In some cases, recycled instead of natural aggregate was used by substituting either the coarse or the fine aggregate fraction. The fresh concrete properties were evaluated through slump flow, L-box test and segregation resistance. Compressive strength of concrete was determined at 1, 3, 7 and 28 days of wet curing. Results obtained showed that an optimization of self-compacting concrete mixture seems to be achievable by the simultaneous use of rubble powder and coarse recycled aggregate with improved fresh concrete performance and unchanged concrete mechanical strength.     

再生骨料高强高性能混凝土配制研究

通过对不同强度等级旧混凝土破碎而成的再生粗骨料与天然粗骨料性能的对比研究 ,表明再生粗骨料与天然粗骨料性能具有相似性 ,能够满足行业标准对碎石的性能要求 ,并尝试将再生粗骨料用于配制高强混凝土和自流平高性能混凝土 ,结果表明 ,采用原强度在 15～ 2 0MPa以上的旧混凝土破碎而成的再生骨料均可用于配制高强混凝土 ,但在配合比相近情况下 ,原混凝土强度等级越高 ,再生混凝土各龄期强度越高 ,其再生利用价值也越高。再生粗骨料亦可用于配制自流平高性能混凝土 ,水胶比为 0 4 0 ,净用水量为 2 0 5kg m3左右时 ,配制得到的新拌混凝土坍落度和坍落扩展度分别在 2 4 5、5 6 0mm以上 ,其 2 8、6 0d强度分别在 5 8 0、6 7 3MPa以上     

无粘结预应力再生粗骨料混凝土梁力学性能

设计制作了5根不同粗骨料替换率的无粘结预应力再生粗骨料混凝土试验梁,并采用两点加载对其进行正截面受弯性能试验,研究了无粘结预应力再生粗骨料混凝土的梁破坏形态、承载力、裂缝宽度及跨中挠度等力学性能。基于试验数据建立了与《混凝土结构设计规范》（GB 50010—2010）相协调的无粘结预应力再生粗骨料混凝土梁预应力钢筋应力增量计算公式,提出了无粘结预应力再生粗骨料混凝土梁的最大裂缝宽度及刚度的设计建议。结果表明:再生粗骨料替换率对无粘结预应力再生粗骨料混凝土梁的破坏形态、裂缝宽度、跨中挠度影响不大;达到承载力极限状态时无粘结预应力再生粗骨料混凝土梁的无粘结预应力钢筋应力增量比无粘结预应力混凝土梁的无粘结预应力钢筋应力增量大,但再生粗骨料替换率对应力增量的影响不显著。     

再生骨料特性对再生混凝土强度和碳化性能的影响

为了评价再生骨料表面砂浆的强度及附着率对再生混凝土性能的影响,以再生骨料表面不同的砂浆强度及附着率为变量,配制了不同强度等级的再生骨料混凝土,通过对比性强度试验和碳化试验评价了再生混凝土内部存在的2个界面过渡区与混凝土性能的关系.结果表明:以高强度原生混凝土为再生骨料配制相对较低强度等级的再生骨料混凝土时,其强度与普通混凝土几乎相同,再生骨料表面砂浆的强度及附着率对再生骨料混凝土强度影响不大,但碳化深度有所增大;以相对较低强度原生混凝土为再生骨料配制同强度等级以上的再生骨料混凝土时,其强度与普通混凝土相差较大,再生骨料表面砂浆的强度及附着率对再生混凝土强度影响较大,碳化深度也相应增大.     

新拌次轻混凝土流变特性的研究

通过对新拌次轻混凝土的流变特性研究,分析了集料组成对新拌次轻混凝土屈服剪切应力和粘性系数的影响、新拌次轻混凝土的结构形成特点及其粒子的运动特点.结果表明:利用普通集料部分替代轻集料可显著改善混凝土的流变性能,提高水泥浆体的粘度、减小轻集料粒径可提高混凝土的匀质性,从而改善次轻混凝土的力学性能和耐久性.     

再生粗骨料混凝土梁抗弯性能试验研究

通过对4组再生粗骨料混凝土粱和1组普通混凝土粱的对比试验分析,主要研究在相同混凝土强度下,不同取代率的再生粗骨料混凝土梁和普通混凝土梁在抗弯性能上的差异和共同点.试验结果分析表明:再生混凝土梁的受弯过程仍有弹性、开裂、屈服、破坏四个明显的特征;再生混凝土粱的极限承载力小于普通混凝土梁,并随着取代率的增加有减小的趋势;再生混凝土粱的抗弯刚度小于普通混凝土梁;再生混凝土抗裂度比普通混凝土差.     

不同取代率再生粗骨料混凝土的力学性能

系统研究了坍落度相同的情况下再生粗骨料取代率对混凝土基本性能的影响.试验中再生粗骨料的掺入量分别为0,30%,50%,70%和100%,通过调节用水量使各组混凝土达到相同的坍落度.主要研究了达到相同坍落度时混凝土的用水量以及再生粗骨料取代率对混凝土坍落度、立方体抗压强度、棱柱体抗压强度、峰值应变和泊松比、弹性模量、劈裂抗拉强度以及抗折强度的影响.试验结果表明,再生粗骨料取代率对上述各性能指标均有一定影响,但程度不同.同时发现,除劈裂抗拉强度和抗折强度外,普通混凝土各基本力学性能指标间的关系不适用各种再生骨料取代率的混凝土.     

考虑粗骨料品质和取代率的再生混凝土抗压强度计算

再生混凝土的粗骨料表面存在硬化砂浆和大量的界面结构，致使其抗压强度较普通混凝土的有所降低，且受压破坏情况更为复杂。为建立一个普遍适用的再生粗骨料混凝土抗压强度计算公式，试验中采用不同再生粗骨料品质、不同取代率的再生混凝土，研究了胶水比、再生粗骨料的品质和取代率对再生混凝土抗压强度的影响，并分析了再生粗骨料吸水率、表观密度和压碎指标等品质特征参数和其影响因子的相关性。在普通混凝土Bolomey抗压强度公式的基础上，建立了考虑骨料品质和取代率的再生粗骨料混凝土抗压强度计算公式，并与常用的抗压强度计算公式的计算结果进行了误差比较。研究结果表明：再生粗骨料混凝土抗压强度与胶水比、取代率之间均呈线性关系，并且再生粗骨料的品质对再生混凝土抗压强度影响显著；误差分析表明，与试验结果相比，普通混凝土Bolomey抗压强度公式的最大误差约为16.51%，考虑有效胶水比的再生粗骨料混凝土抗压强度的最大误差约为36.33%，而考虑再生粗骨料品质差异和取代率的再生混凝土抗压强度的最大误差仅为4.90%，具有较高的精度和较好的适用性。