氢氧化钠活化法制备木炭基活性炭

以木质炭化料为原料,NaOH为活化剂,制备活性炭。讨论了活化温度、碱炭比、保温时间对活性炭得率和吸附性能的影响。结果表明,随着活化温度、碱炭比和保温时间的增加活性炭的活化程度增加,活性炭的得率不断下降;随着活化温度、碱炭比和保温时间的延长,活性炭的吸附性能先上升后下降。在较佳工艺条件下,活化温度850℃,碱炭比为1. 0∶1. 0,保温时间1. 0 h下活性炭的碘吸附值和亚甲基蓝吸附值分别为814. 7 mg/g和127. 5 mg/g。     

煤基活性炭制备工艺对吸附铜离子性能的影响

高硫高灰煤脱灰脱硫预处理后采用KOH活化法制备活性炭.考察了碱炭比、活化温度、活化时间以及灰分、硫分含量和表面活性剂等对制备的活性炭吸附铜离子的影响.结果表明,在活化温度为820℃,活化时间为1.5h,碱炭比为2.5的条件下制得活性炭比表面积为1 004.5m2/g,铜离子去除率为67.8%;煤中灰分的脱除和添加表面活性剂有利于提高活性炭的吸附性能,但脱硫煤基活性炭吸附性能降低.     

NaOH活化法制备煤基活性炭的研究

以焦作无烟煤为原料,NaOH为活化剂,采用化学活化法制备煤基活性炭,分别考察了碱炭比、活化温度和活化时间等工艺参数对活性炭吸附性能和收率的影响;利用低温N2吸附法对活性炭的比表面积、总孔容及孔径分布进行了表征.结果表明,在碱炭比为4,活化温度为750℃和活化时间为1 h的条件下,可以制得比表面积为2 483 m2/g,总孔容为1.41 cm3/g,碘吸附值为2 530 mg/g,亚甲蓝吸附值为418 mg/g的煤基活性炭.     

利用废弃机制炭颗粒制备活性炭研究

以机制炭废弃炭颗粒为原料,水蒸汽法物理活化制备吸附性能较佳且得率较高的活性炭。通过正交试验设计,研究活化温度、活化时间和水蒸气用量对活性炭吸附性能、活化得率和固定碳含量的影响。得到最佳活化工艺条件为:活化时间1.5h、活化温度950℃、水蒸汽用量700-750g/h。制得活性炭的碘吸附值1162mg/g,亚甲基蓝吸附值9.5ml/0.1g,活化得率36.67%。     

改质煤沥青制备活性炭的研究

以改质煤沥青为原料,采用KOH活化法制备活性炭。探讨了碱炭比、炭化时间、活化温度、活化时间等对活性炭吸附性能的影响。结果表明,制备改质煤沥青基活性炭的最佳条件为:碱炭比为4,炭化时间为45 min,活化温度840℃,活化时间140 min,在此条件下,制得改质煤沥青基活性炭的碘吸附值为1 152.8 mg/g。     

兰炭制活性炭的实验研究

以多种陕北机制兰炭为原料,采用KOH活化法,在氮气氛的管式炉中进行高温活化,制备出了BET比表面为810.017 2m2/g,BJH平均孔径为6.579 3 nm的活性炭.考察了活化温度、时间、碱炭比、碱炭混合方式和兰炭种类等对活性炭吸附性能的影响,确定活性炭的最佳制备工艺为:以兴茂兰炭为原料,KOH干粉法活化,活化条件为800℃下1h,碱炭比为5∶1.     

高比表面积煤基活性炭的制备及其吸附性能的研究

以太西无烟煤为原料,KOH为活化剂,采用化学活化法制备高比表面积煤基活性炭,着重考察了碱炭比、活化温度、活化时间对活性炭吸附性能的影响。研究结果表明：当碱炭比为4、活化温度为800℃、活化时间为1h时,可以制得比表面积达3215m^2／g,碘吸附值达2884mg／g,亚甲蓝吸附值达548mg／g的高比表面积煤基活性炭。     

微波辐射氢氧化钾法制备黄麻杆活性炭工艺

研究了以黄麻杆为原料,微波辐射黄麻杆氢氧化钾法制备活性炭的工艺,讨论了碱炭比,活化时间,微波功率对活性炭吸附性能和得率的影响。研究表明,碱炭比为1,活化时间为14min,微波功率为700W时制得的活性炭碘吸附值为1264.02mg/g、亚甲基蓝吸附值为210mL/g,活化得率11.29%。     

磷酸活化褐煤制备活性炭影响因素研究

研究了用磷酸水溶液预浸渍处理云南先锋褐煤 ,在氮气保护下 40 0℃～ 60 0℃一步炭活化制备活性炭的影响因素 .研究结果表明 ,加温浸渍优于常温浸渍 ,并可提高制备的磷酸活性炭的碘吸附值 2 5 % ;磷酸活化褐煤反应中活化剂磷酸、添加剂硫酸主要影响活性炭的孔结构和吸附能力 ,而且磷酸浓度高活化效果好 ;炭活化温度、炭活化时间主要影响活性炭产品的收率 ,高温和长时间会导致更多的碳损失     

干熄兰炭基活性炭的制备及其吸附性能

采用物理化学活化法处理干熄兰炭进一步制备活性炭,探究了活化剂选择、碱炭比、活化温度、活化时间对活性炭吸附维生素B12溶液的影响,并且对最优条件下制备的活性炭进行SEM、BET、FIIR分析.研究表明,对比不同活化剂(ZnCl2、H3PO4、KOH)饱和溶液浸渍后得到的活性炭吸附维生素B12吸附量,KOH活化制备活性炭的...     

油茶壳微孔活性炭的制备及表征

以油茶壳为原料,经炭化、KOH活化,制备微孔活性炭。考查了活化温度、活化时间和碱炭比对微孔活性炭碘吸附值和产率的影响,并采用正交试验优化了制备条件。研究结果表明：活化温度800℃、活化时间180 min、碱炭质量比3.5：1时,活性炭的碘吸附值达3 221 mg/g,产率51.2%。采用比表面积孔隙分析仪测定了氮气吸附/脱附等温线,计算得BET比表面积为1 755.72 m²/g,平均孔径为2.15 nm,总孔容为0.328 cm³/g,微孔孔容占总孔容的55.8%;SEM分析可见活性炭表面具有大量孔隙结构;FT-IR分析表明活化促进了—CH₃、—OH热解,活性炭中仍保存含氧官能团。     

兰炭基活性炭的制备工艺优化及吸附性能研究

以榆林某公司的兰炭为原料,KOH粉末为活化剂制备活性炭。通过改变活化过程中时间、温度、炭碱比等因素,从而探究活性炭的碘吸附能力。通过响应曲面优化处理活性炭制备过程中活化因素,从而确定最佳工艺。采用比表面积测定,红外光谱分析,扫描SEM电镜等对活性炭结构及性能表征进行分析结果表明,上述活化条件都会影响活性炭吸附能力和孔隙结构。当活化过程中的温度达到750℃,时间为0.5 h,炭碱比为1:3的时候,KOH的活化效果最佳,所制样品的碘吸附值最大且为1 162.91 mg/g,其BET比表面积可达655.15m2/g,Langmuir比表面积为908.22 m2/g。通过红外分析可知活性炭与预处理兰炭原料红外光谱图走势极其相似,只是活性炭出现了较强的芳基烷基醚C-O伸缩振动峰。通过扫描显微电镜分析可知与原料兰炭相比,活性炭样品组织表面非常粗糙并且有大量的孔隙出现,样品结构非常疏松。     

KOH活化法制备棉秆基活性炭及其对含苯酚废水的吸附

以农业废弃物棉秆为原料,采用氢氧化钾活化法制备活性炭,并用于吸附含苯酚废水中的苯酚。棉秆基活性炭的最佳制备条件为棉秆先炭化,以KOH溶液为活化剂,KOH与棉秆炭的质量比(物料比)1.5:1,活化温度800 ℃、活化时间70 min,此条件下制备的棉秆活性炭亚甲基蓝的吸附值为342.33 mg/g,碘吸附值为1 368.65 mg/g,其BET比表面积达到了1 735.94 m²/g,总孔容积0.36 cm³/g,平均孔径2.33 nm。将此活性炭用于吸附苯酚,苯酚质量浓度60 mg/L的50 mL废水中,当pH值为7,吸附时间2 h,活性炭投放量为50 mg时,苯酚去除率最高可达98%。对此吸附过程进行动力学分析,结果表明准二级动力学模型能很好的描述此活性炭吸附苯酚的过程。     

Preparation of Activated Carbons from Tobacco Stems by Potassium Hydroxide Activation and Phosphine Adsorption

Activated carbon preparation from tobacco stems by KOH activation at different activation temperatures and KOH/char mass ratios were investigated in this study. The effects of preparation parameters on activated carbon pore structure, morphometrics, microcrystallinities, and surface functional groups were characterized by N₂ adsorption, SEM, XRD, and FTIR technologies, respectively. The optimum preparation condition of activated carbon was activation temperature of 850°C, and KOH/char mass ratio of 2. Under this condition, the BET surface area of 2215 m²/g, and the pore volume of 1.343 cm³/g can be obtained. Prepared activated carbon showed clearly honeycomb holes, and a predominated amorphous structure. With increase of activation temperature and KOH/char mass ratio, decrease of surface oxygen functional group, and aromatization of the carbon structure was found. The activated carbon was subject to PH₃ purification, and the maximum PH₃ adsorption capacity of 253 mg/g can be realized based on well prepared KOH-AC with modification of 2.5% Cu. It seems that the activated carbon produced from chemical activation of tobacco stem would be an effective and alternative adsorbent for PH₃ adsorption because of its high surface area, adsorption capacity, and low cost.     

油茶壳残渣制备活性炭的工艺

以油茶壳醇浸取后残渣为原料,以磷酸活化法制备活性炭,考察了浸渍比、磷酸质量分数和活化温度等对活性炭吸附性能及其得率的影响;活性炭的吸附性能由碘吸附值、亚甲基蓝吸附值表征。结果表明,在酸/炭浸渍比为3:1、磷酸质量分数70%、活化温度500℃时,活性炭的吸附性能最佳,其碘、亚甲基蓝吸附值和得率分别为1043.29mg/g、148.5mg/g和38.77%。采用物理吸附仪在77K下测定其N₂吸附脱附等温线,利用BET法和BJH法计算比表面积和孔径分布,其比表面积为1626.45m²/g,平均孔径为4.7nm,总孔容为1.94cm³/g。同时采用FTIR和XRD分析了活性炭的表面官能团和微观结构。     

椰壳基超级电容活性炭的制备及其电化学性能研究

以椰壳炭化料为原料,KOH为活化剂,在不同工艺条件下制备了超级电容器用活性炭电极材料。考察了碱炭比、活化温度和活化时间对活性炭孔隙结构及其用作电极材料的比电容的影响。结果表明,在KOH与椰壳炭化料质量比为4:1,活化温度800℃,活化时间60 min的条件下,可制得比表面积2891 m²/g,总孔容积1.488 cm³/g,中孔率73.6%,比电容达235 F/g的优质活性炭电极材料。     

磷酸活化法制备糠醛渣活性炭的研究

以碘吸附值、亚甲基蓝吸附值及活性炭得率为考察指标,选取对糠醛渣活性炭性质影响较大的浸渍比、磷酸质量分数、活化温度、保温时间4个因素进行L₁₆(4⁵)正交试验对磷酸活化法制备糠醛渣活性炭的工艺条件进行优化。由正交试验结果得到磷酸活化的最佳工艺条件为:磷酸质量分数60%,浸渍比2.5:1,活化温度550 ℃,保温1.5 h,此条件下制得的活性炭样品的碘吸附值为839.6 mg/g,亚甲基蓝吸附值为260.3 mg/g,得率为46.8%,比表面积为830.20 m²/g,孔容积为0.502 cm³/g,孔径集中在0.8~2.5 nm,具有丰富的中孔和微孔。     

原料复配制备木质素基成型活性炭研究

以碱木质素和杉木屑为原料,磷酸为活化剂,制备碱木质素基成型活性炭,考察了碱木质素质量分数、浸渍比、活化温度、活化时间等对活性炭性能的影响。研究结果表明：碱木质素复配杉木屑（碱木质素质量分数50%）后,复配料的表面润湿性显著提高,瞬时水接触角由133.2°（碱木质素）降低至86.6°（复配料）;热膨胀系数显著降低,膨胀温度区间的热膨胀系数由2 365 μm/（m·℃）（碱木质素）降低至45 μm/（m·℃）（复配料）。在最佳工艺条件即碱木质素质量分数50%、浸渍比1.5：1（纯磷酸与复配料质量比）、活化温度500℃、活化时间90 min下,制备的成型活性炭得率41.76%,碘吸附值1 070 mg/g,亚甲基蓝吸附值255 mg/g,强度90%,比表面积1 646 m²/g,总孔容积为0.795 cm³/g,其中孔径小于5 nm的孔容积占总孔容积的97.2%。     

磷酸法玉米秸秆基活性炭的制备及其表征

以成型、烘焙处理后的玉米秸秆为原料,磷酸作为活化剂制备了玉米秸秆基活性炭,并对活性炭样品进行表征。同时以碘吸附值、亚甲基蓝吸附值和焦糖脱色率为指标测定其吸附性能,并对制备条件进行优化。实验结果表明：玉米秸秆制备活性炭的最佳工艺条件为浸渍比即m(55%H₃PO₄)∶m(玉米秸秆)为4∶1、活化温度400 ℃、活化时间100 min,此条件下活性炭的得率为47.78%,制得的活性炭具有良好的吸附性能,碘吸附值、亚甲基蓝吸附值及焦糖脱色率分别达到864 mg/g、210 mg/g和100%。活性炭比表面积可达1 105 m²/g,总孔容积为0.745 cm³/g,微孔孔容为0.287 cm³/g,中孔孔容为0.354 cm³/g,孔径分布集中于5 nm以内,约占73.56%,平均孔径为2.697 nm。FT-IR分析显示：在活化过程中磷酸与玉米秸秆发生交联作用,生成的活性炭损失了玉米秸秆的部分官能团。