Phase Transition and Large Electrostrain in Lead‐Free Li‐Doped (Ba,Ca)(Ti,Zr)O3 Ceramics

Large piezoelectric effect is achieved in Li‐doped Ba_0.85Ca_0.15Ti_0.90Zr_0.10O₃(BCTZ) ceramics by use of tuning the phase boundaries. Rhombohedral–orthorhombic (R–O) and orthorhombic–tetragonal (O–T) multiphase coexistence is constructed in the ceramics by changing Li contents. The high piezoelectric constant d₃₃ (493 pC/N) and large electrostrain (dS_max/dE_max = 931 pm/V) have been observed in the Li‐doped (Ba, Ca)(Ti, Zr)O₃ ceramics at low sintering temperature (1350°C/2 h). The significant enhancement in materials properties is ascribed to the multiphase region around room temperature induced by Li‐doped effect.     

High‐Performance Small‐Amount Fe2O3‐Doped (K,Na)NbO3‐Based Lead‐Free Piezoceramics with Irregular Phase Evolution

[(K_0.43Na_0.57)_0.94Li_0.06][(Nb_0.94Sb_0.06)_0.95Ta_0.05]O₃ + x mol% Fe₂O₃ (KNLNST + x Fe, x = 0~0.60) lead‐free piezoelectric ceramics were prepared by conventional solid‐state reaction processing. The effects of small‐amount Fe₂O₃ doping on the microstructure and electrical properties of the KNLNST ceramics were systematically investigated. With increasing Fe³⁺ content, the orthorhombic‐tetragonal polymorphic phase transition temperature (T_O‐T) of KNLNST + x Fe ceramics presented an obvious “V” type variation trend, and T_O‐T was successfully shifted to near room temperature without changing T_C (T_C = 315°C) via doping Fe₂O₃ around 0.25 mol%. Electrical properties were significantly enhanced due to the coexistence of both orthorhombic and tetragonal ferroelectric phases at room temperature. The ceramics doped with 0.20 mol% Fe₂O₃ possessed optimal piezoelectric and dielectric properties of d₃₃ = 306 pC/N, k_p = 47.0%, = 1483 and tan δ = 0.023. It was revealed that the strong internal stress in the KNLNST + x Fe ceramics with higher Fe³⁺ contents (x = 0.40, 0.60) stabilized the orthorhombic phase, leading to the irregular “V” type rather than the usually observed monotonic phase transition with composition change in the ceramics.     

Mn doping effects on electric properties of 0.93(Bi0.5Na0.5)TiO3‐0.07Ba(Ti0.945Zr0.055)O3 ceramics

The validity of Mn element on 0.93(Bi_0.5Na_0.5)TiO₃‐0.07Ba(Ti_0.945Zr_0.055)O₃ ceramics (BNT‐BZT‐xMn) is certified by doping. On account of multiple effects introduced by Mn, the appropriate Mn content facilitates property improvement effectively. Compared with pure BNT‐BZT, d₃₃ of the component x = 0.25 increases about 8% up to 187 pC/N and Q_m of the component x = 1 increases about 84% up to 197. Thermally stimulated depolarization currents (TSDC) measurement reveals Mn additive is helpful to pyroelectric properties as well. The Mn‐doped component x = 0.125 exhibits better pyroelectric performance at room temperature. Corresponding pyroelectric coefficient and the figures of merit reach up to 0.061 μC/(cm² °C), F_i=217 pm/V, F_ν = 0.023 m²/C, and F_d = 12.6 μPa^?1/2, respectively, even superior to lead‐based ceramics. Similar pyroelectric advantage is also observed in the component x = 0.5 near depolarization temperature T_d. Mn doping has slight harmful influence on the ferroelectric‐to‐relaxor transition temperature T_F?R, as well as T_d, but hardly shows restriction on application. These results confirm Mn doping is an available strategy to improve BNT‐based ceramics. Therefore, Mn‐doped BNT‐BZT ceramics will be excellent candidates in area of high‐power piezoelectric application and pyroelectric detectors.     

High and Frequency‐Insensitive Converse Piezoelectric Coefficient Obtained in AgSbO3‐Modified (Li,K, Na)(Nb,Ta)O3 Lead‐Free Piezoceramics

AgSbO₃ was doped into KNN‐based lead‐free piezoceramics with an optimized composition of Li_0.02(Na_0.53K_0.48)_0.98Nb_0.8Ta_0.2O₃ (abbreviated as LKNNT) to further enhance its piezoelectric property. The doping of AgSbO₃ was found to be effective in reducing the grain sizes, resulting in more uniform microstructure in AgSbO₃‐doped LKNNT ceramics. AgSbO₃ lowers tetragonal‐orthorhombic phase transition point (T_T‐O), but with a more gentle rate as compared with other dopants. A large converse piezoelectric coefficient d₃₃* up to 598 pm/V under a relatively low electric field of 1 kV/mm was obtained in the LKNNT‐5 mol% AgSbO₃ composition, whose tetragonal‐orthorhombic phase transition point (T_T‐O) was controlled near room temperature, but its Curie temperature was kept at 235°C. The d₃₃* obtained in the present material is a very high value for nontextured KNN‐based ceramics, which is attributed to the polymorphism phase transition effect and “soft” behavior caused by the addition of AgSbO₃.     

Investigation of the Structure and Electrical Properties of (KxNa0.96−xLi0.04)(Nb0.96−yTaySb0.04)O3 Piezoelectric Ceramics Modified with Manganese

The effect of high doping levels of manganese (Mn) on the structure and electrical properties of (K_xNa_1?x)NbO₃ (KNN) ceramics containing Li, Ta, and Sb has been investigated. The samples were measured using synchrotron X‐ray diffraction whereas Rietveld refinement with Fullprof was used to determine the structural information as a function of temperature. Temperature‐dependent dielectric measurement was used to compare the phase transition temperatures. The results show that Mn decreases the temperature range of phase coexistence between the orthorhombic and tetragonal phase from ~180°C to ~120°C. The Curie temperature remained unchanged with Mn addition while the dielectric constant and dielectric loss increased with Mn addition. High amounts of Mn led to a reduction in both piezoelectric and ferroelectric properties. The remnant polarization, remnant strain, and piezoelectric coefficient values decreased from 24 μC/cm², 0.000824, 338 ± 37 pm/V to 13 μC/cm², 0,00014 and 208 ± 27 pm/V, respectively for the undoped and 5 mol% Mn‐doped sample.     

Orthorhombic‐pseudocubic phase transition and piezoelectric properties of (Na0.5K0.5)(Nb1−xSbx)‐SrZrO3 ceramics

0.96(Na_0.5K_0.5)(Nb_1?xSb_x)‐0.04SrZrO₃ ceramics with 0.0≤x≤0.06 were well sintered at 1060°C for 6 hours without a secondary phase. Orthorhombic‐tetragonal transition temperature (T_O‐T) and Curie temperature (T_C) decreased with the addition of Sb₂O₅. The decrease in T_C was considerable compared to that in T_O‐T, and thus the tetragonal phase zone disappeared when x exceeded 0.03. Therefore, a broad peak for orthorhombic‐pseudocubic transition as opposed to that for orthorhombic‐tetragonal transition appeared at 115°C‐78.2°C for specimens with 0.04≤x≤0.06. An orthorhombic structure was observed for specimens with x≤0.03. However, the polymorphic phase boundary structure containing orthorhombic and pseudocubic structures was formed for the specimens 0.04≤x≤0.06. Furthermore, a specimen with x=0.055 exhibited a large piezoelectric strain constant of 325 pC/N, indicating that the coexistence of orthorhombic and pseudocubic structures could improve the piezoelectric properties of (Na_0.5K_0.5)NbO₃‐based lead‐free piezoelectric ceramics.     

Photoluminescence and Temperature Dependent Electrical Properties of Er‐Doped 0.94Bi0.5Na0.5TiO3‐0.06BaTiO3 Ceramics

Er‐doped 0.94Bi_0.5Na_0.5TiO₃‐0.06BaTiO₃ (BNT‐6BT: xEr, x is the molar ratio of Er³⁺ doping) lead‐free piezoceramics with x = 0–0.02 were prepared and their multifunctional properties have been comprehensively investigated. Our results show that Er‐doping has significant effects on morphology of grain, photoluminescence, dielectric, and ferroelectric properties of the ceramics. At room temperature, the green (550 nm) and red (670 nm) emissions are enhanced by Er‐doping, reaching the strongest emission intensity when x = 0.0075. The complex and composition‐dependent effects of electric poling on photoluminescence also have been measured. As for electrical properties, on the one hand, Er‐doping tends to flatten the dielectric constant‐temperature (ε_r‐T) curves, leading to temperature‐insensitive dielectric constant in a wide temperature range (50°C–300°C). On the other hand, Er‐doping significantly decreases the ferroelectric‐relaxor transition temperature (T_F–R) and depolarization temperature (T_d), with the T_F–R decreasing from 76°C to 42°C for x = 0–0.02. As a result, significant composition‐dependent electrical features were found in ferroelectric and piezoelectric properties at room temperature. In general, piezoelectric and ferroelectric properties tend to become weaker, as confirmed by the composition‐dependent piezoelectric coefficient (d₃₃), planar coupling factor (k_p), and the shape of polarization‐electric field (P–E), current‐electric field (J–E), bipolar/unipolar strain‐electric field (S–E) curves. Furthermore, to understand the relationship between the T_F–R/T_d and the electrical properties, the composition of x = 0.0075 has been intensively studied. Our results indicate that the BNT‐6BT: xEr with appropriate Er‐doping may be a promising multifunctional material with integrated photoluminescence and electrical properties for practical applications.     

Large electric‐field‐induced strain and enhanced piezoelectric constant in CuO‐modified BiFeO3‐BaTiO3 ceramics

In this work, we fabricated the (1‐x)BiFeO₃‐xBaTiO₃+y‰ mol CuO ceramics by the modified thermal quenching technique. The pure perovskite phase was formed and a morphotropic phase boundary (MPB) was observed in the ceramics with x = 0.30‐0.33. The addition of CuO can significantly enhance the density of the BiFeO₃‐BaTiO₃ material. Importantly, an enhanced piezoelectric constant (d₃₃=165 pC/N), a large electric‐field‐induced strain (?S = 0.54%: peak to peak strain) and a large piezoelectric actuator constant (d₃₃*=449 pm/V) together with a high Curie temperature (T_C) of 503°C were observed in the ceramics with x = 0.30 and y = 5. As a result, the enhanced piezoelectricity and large electric‐field‐induced strain could significantly stimulate further researches in BFO‐based ceramics.     

Investigation on Resonant Vibration Performances of Fe‐Doped BiScO3–PbTiO3 Ceramics in High‐Temperature Environment

The high‐temperature performance of a series of Fe‐doped BiScO₃‐PbTiO₃ (BSPT) piezoelectric ceramics at the morphotropic phase boundary was investigated. The effects of different Fe contents on the piezoceramics were assessed with regard to variations in structure, morphology, dielectric properties, piezoelectric properties, and high‐temperature resonant vibration. X‐ray diffraction (XRD) results indicated that the Fe‐doped BSPT ceramics show a single perovskite structure and that the c/a ratio undergoes a slight increase with increasing Fe concentrations. It was also found that, as the proportion of Fe in the ceramics was increased, the grain size was enlarged somewhat, the dielectric loss (tan δ) decreased, the mechanical quality factor (Q_m) was gradually improved, and the Curie temperature (T_C) was increased from 426°C to approximately 460°C. Despite these complex effects, it was evident that Fe doping can improve the high‐temperature resonant vibration performance of BSPT ceramics, and that these materials exhibit stable resonant vibration velocities at temperatures as high as 225°C. Our results indicate that Fe‐doped BSPT ceramics have the potential to be used as piezoelectric power devices intended for high‐temperature environments.     

Properties and structures of nonstoichiometric (K,Na)NbO3‐based lead‐free ceramics

The 0.968[(K_0.48Na_0.52)]Nb_0.95+xSb_0.05O₃–0.032(Bi_0.5Na_0.5)ZrO₃ [KNN_xS–BNZ] lead‐free ceramics with nonstoichiometric niobium ion were fabricated via conventional solid‐state sintering technique and their piezoelectric, dielectric and ferroelectric properties were investigated. When x = 0.010, enhanced piezoelectric properties (d₃₃ ≈ 421 pC/N and k_p ≈ 0.47) were obtained due to the construction of rhombohendral—tetragonal phase boundary near room temperature. The KNN_xS–BNZ ceramics possesses enhanced Curie temperature (T_c) with improved piezoelectric constant. A large d₃₃ of ~421 pC/N and a high T_c ~256°C can be simultaneously induced in the ceramics with x = 0.010. Especially, good thermal stability was observed in a broad temperature range. The results indicated that our work could benefit development of KNN‐based ceramics and widen their application range.     

Sintering Behavior,Properties, and Applications of Co‐Fired Piezoelectric/Low Temperature Co‐Fired Ceramic (PZT‐SKN/LTCC) Multilayer Ceramics

Materials and processing conditions have been developed allowing co‐firing of fluxed PZT‐SKN materials with commercial low temperature co‐fired ceramic (LTCC) tapes. Previously, Pb(Zr_0.53, Ti_0.47)O₃–Sr(K_0.25, Nb_0.75)O₃ (PZT‐SKN) ceramics fluxed with 1 wt% LiBiO₂ and 1 wt% CuO addition were shown to sinter to high density at 900°C for 1 h, with a large d₃₃ piezoelectric coefficient of ~415 pm/V. Currently, the master sintering curve (MSC) approach has been used to study the densification behaviors of fluxed PZT‐SKN and LTCC tapes. Different sintering mechanisms for fluxed PZT‐SKN ceramics and LTCC materials are confirmed by analyzing the apparent activation energy (Q_a). Using knowledge gained from MSC results, an optimized sintering profile was developed. Multilayer PZT‐SKN/HL2000 (HeraLock^? Tape, Heraeus) stacks co‐fired at 900°C for 0.5 h maintain large piezoelectric coefficient (high field d₃₃ > 340 pm/V). EDS analysis reveal limited interdiffusion of Pb from PZT‐SKN layers in LTCC and the appearance of Al, Ca, and Si in the PZT‐SKN near the PZT‐SKN/LTCC interface. Further, elemental interdiffusion was not detected at the center of piezoelectric layer in PZT‐SKN/LTCC multilayer ceramics and no subsequent reduction in piezoelectric coefficient d₃₃ was observed. Finally, a piezoelectric microbalance with mass sensitivity of 150 kHz/mg was fabricated using the materials and methods developed.     

High Electric‐Induced Strain and Temperature‐Dependent Piezoelectric Properties of 0.75BF–0.25BZT Lead‐Free Ceramics

0.75BiFeO₃–0.25Ba(Zr_xTi_1?x) + 0.6 wt% MnO₂ (0.75BF–0.25BZT) ceramics with Mn addition were prepared by the solid‐state reaction method. The high‐field strain and high‐temperature piezoelectric properties of 0.75BF–0.25BZT ceramics were studied. Introduction of Zr in the solid solutions decreased the Curie temperature slightly, and improved the dielectric and piezoelectric properties obviously. The piezoelectric properties of 0.75BZT–0.25BT ceramics reached the maximum at Zr content of 10 mol%. The Curie temperature T_c, dielectric constant ε and loss tanδ (1 kHz), piezoelectric constant d₃₃, and planner electromechanical coupling factor k_p of 0.75BF–0.25BZT ceramics with 10 mol% Zr were 456°C, 650, 5%, 138 pC/N, and 0.30, respectively. The high‐field bipolar and unipolar strain under an electric field of 100 kV/cm reached up to 0.55% and 0.265%, respectively, which were comparable to those of BiScO₃–PbTiO₃ and “soft” PZT‐based ceramics. The typical “butterfly”‐shaped bipolar strain and frequency‐dependent peak‐to‐peak strain indicated that the large high‐field‐induced strain may be due to non‐180° domain switching. Rayleigh analysis reflected that the improved piezoelectric properties resulted from the enhanced extrinsic contribution by Zr doping. The unipolar strain of 0.75BF‐0.25BZT ceramics with 10 mol% Zr was almost linear from RT to 200°C. These results indicated that 0.75BF–0.25BZT ceramics were promising candidates for high‐temperature and lead‐free piezoelectric actuators.     

Structure Evolution and Electrical Properties of Y3+‐Doped Ba1−xCaxZr0.07Ti0.93O3 Ceramics

Lead free piezoelectric ceramics of Y³⁺‐doped Ba_1?xCa_xZr_0.07Ti_0.93O₃ with x = 0.05, 0.10, and 0.15 were prepared. Composition and temperature‐dependent structural phase evolution and electrical properties of as‐prepared ceramics were studied systematically by X‐ray diffraction, Raman spectroscopy, impedance analyzer, ferroelectric test system, and unipolar strain measurement. Composition with x = 0.10 performs a good piezoelectric constant d₃₃ of 363 pC/N, coercive field E_c of 257 V/mm, remanent polarization P_r of 14.5 μC/cm², and a Curie temperature T_m of 109°C. High‐resolution X‐ray diffraction was introduced to indicate presence of orthorhombic phase. Converse piezoelectric constant d₃₃* of x = 0.10 composition performed better temperature stability in the range from 50°C to 110°C. That means decreasing orthorhombic–tetragonal phase transition temperature could be an effective way to enlarge its operating temperature range.     

Preparation and characterization of Pb(Lu1/2Nb1/2)O3–Pb(In1/2Nb1/2)O3–PbTiO3 ternary ferroelectric ceramics with high phase transition temperatures

To explore new relaxor‐PbTiO₃ systems for high‐power and high‐temperature electromechanical applications, a ternary ferroelectric ceramic system of Pb(Lu_1/2Nb_1/2)O₃–Pb(In_1/2Nb_1/2)O₃–PbTiO₃ (PLN–PIN–PT) have been investigated. The phase structure, dielectric, piezoelectric, and ferroelectric properties of the as‐prepared PLN–PIN–PT ceramics near the morphotropic phase boundary (MPB) were characterized. A high rhombohedral‐tetragonal phase transition temperature T_R‐T of 165°C and a high Curie temperature T_C of 345°C, together with a good piezoelectric coefficient d₃₃ of 420 pC/N, were obtained in 0.38PLN–0.20PIN–0.42PT ceramics. Furthermore, for (0.8?x)PLN–0.2PIN–xPT ceramics, the temperature‐dependent piezoelectric coefficients, coercive fields and electric‐field‐induced strains were further studied. At 175°C, their coercive fields were found to be above 9.5 kV/cm, which is higher than that of PMN–PT and soft P5H ceramics at room temperature, indicating PLN–PIN–PT ceramics to be one of the promising candidates in piezoelectric applications under high‐driven fields. The results presented here could benefit the development of relaxor‐PbTiO₃ with enhanced phase transition temperatures and coercive fields.     

Electrocaloric behavior and piezoelectric effect in relaxor NaNbO3-based ceramics

We firstly reported the electrocaloric properties in relaxor (1−x−y)NaNbO₃–yBaTiO₃–xCaZrO₃ ceramics, and high electrocaloric effect (∆T ~0.451 K and∣∆T/∆E∣~0.282 Km/MV) can be realized in the ceramics (x = 0.04 and y = 0.10) under low temperature and low electric field. Relaxor behavior of NaNbO₃ ceramics can be found by doping both BaTiO₃ and CaZrO₃. In addition, optimized piezoelectric effects (d₃₃ ~235 pC/N and d₃₃* ~230 pm/V) can be observed in the ceramics (x = 0.04 and y = 0.10) due to the involved morphotropic phase boundary (MPB). Excellent piezoelectric effect (ie, d₃₃~330 pm/V at 41°C, and d₃₃*~332 pm/V at 60°C) can be found because of the characteristics of MPB. Good temperature reliability of piezoelectric effect can be shown because of both MPB and relaxor behavior. We believe that the ceramics with high electrocaloric effect and good piezoelectric effect can be considered as one of the most promising lead-free materials for piezoelectric devices.     

Structural evolution of the R‐T phase boundary in KNN‐based ceramics

Although a rhombohedral‐tetragonal (R‐T) phase boundary is known to substantially enhance the piezoelectric properties of potassium‐sodium niobate ceramics, the structural evolution of the R‐T phase boundary itself is still unclear. In this work, the structural evolution of R‐T phase boundary from ?150°C to 200°C is investigated in (0.99?x)K_0.5Na_0.5Nb_1?ySb_yO₃–0.01CaSnO₃–xBi_0.5K_0.5HfO₃ (where x = 0‐0.05 with y = 0.035, and y = 0‐0.07 with x = 0.03) ceramics. Through temperature‐dependent powder X‐ray diffraction (XRD) patterns and Raman spectra, the structural evolution was determined to be Rhombohedral (R, <?125°C)→Rhombohedral + Orthorhombic (R + O, ?125°C to 0°C)→Rhombohedral + Tetragonal (R + T, 0 °C to 150°C)→dominating Tetragonal (T, 200°C to Curie temperature (T_C)) → Cubic (C, >T_C). In addition, the enhanced electrical properties (e.g., a direct piezoelectric coefficient (d₃₃) of ~450 ± 5 pC/N, a conversion piezoelectric coefficient () of ~580 ± 5 pm/V, an electromechanical coupling factor (k_p) of ~0.50 ± 0.02, and T_C~250°C), fatigue‐free behavior, and good thermal stability were exhibited by the ceramics possessing the R‐T phase boundary. This work improves understanding of the physical mechanism behind the R‐T phase boundary in KNN‐based ceramics and is an important step toward their adoption in practical applications.     

Crystal Structure and Electrical Properties of Lead‐Free (1 − x)BaTiO3–x(Bi1/2A1/2)TiO3 (A = Ag,Li, Na,K, Rb,Cs) Ceramics

Ceramics of solid solutions (1  ?  x)BaTiO₃–x(Bi_1/2A_1/2)TiO₃ (A = Ag, Li, Na, K, Rb, Cs, x ≤ 0.20) were prepared and their crystal structures, dielectric, ferroelectric, and piezoelectric properties were investigated. It was found that (Bi_1/2A_1/2)TiO₃‐type doping compounds broadened the temperature range of the tetragonal phase in BaTiO₃ and all the compositions examined displayed a tetragonal structure at room temperature. The Curie temperature (T_C) was observed to increase with respect to pure BaTiO₃ to the range 140°C–210°C through solid solution. Remanent polarization (P_r) tended to decrease with increased content of doping compound, whereas the coercive field (E_C) rose and piezoelectric coefficient (d₃₃) fell. The highest d₃₃ value in the solid solutions was observed in 0.97BaTiO₃–0.03(Bi_1/2Ag_1/2)TiO₃ at 90 pC/N.     

Enhanced Piezoelectric Properties of (Ba1−xCax)(Ti0.92Sn0.08)O3 Lead‐Free Ceramics

(Ba_1?xCa_x)(Ti_0.92Sn_0.08)O₃ (x = 0.00–0.06 mol) ceramics with a high relative density over 96% were prepared by a conventional sintering method at 1480°C. At room temperature, a polymorphic phase transition from orthorhombic phase to tetragonal phase was confirmed by the XRD patterns in the composition range of 0.04 ≤ x ≤ 0.06. A high piezoelectric coefficient d₃₃ up to 568 pC/N was obtained at x = 0.05 mol, which is higher than the other component of (Ba,Ca)(Ti,Sn)O₃ system. At the same time, the corresponding planar electromechanical coupling factor k_p, converse piezoelectric coefficient dS/dE, and dielectric constant ε_r reach 47.7%, 1013 pm/V, and 23000, respectively. These results indicate that the (Ba,Ca)(Ti,Sn)O₃ ceramics are a promising candidate to replace for the lead‐based piezoelectric materials.     

Giant electromechanical strain response in lead‐free SrTiO3‐doped (Bi0.5Na0.5TiO3–BaTiO3)–LiNbO3 piezoelectric ceramics

Lead‐free 0.985[(0.94?x)Bi_0.5Na_0.5TiO₃–0.06BaTiO₃–xSrTiO₃]–0.015LiNbO₃ [(BNT–BT–xST)–LN, x=0‐0.05] piezoelectric ceramics were prepared using a conventional solid‐state reaction method. It was found that the long‐range ferroelectric order in the unmodified (BNT–BT)–LN ceramic was disrupted and transformed into the ergodic relaxor phase with the ST substitution, which was well demonstrated by the dramatic decrease in remnant polarization (P_r), coercive field (E_c), negative strain (S_neg) and piezoelectric coefficient (d₃₃). However, the degradation of the ferroelectric and piezoelectric properties was accompanied by a significant increase in the usable strain response. The critical composition (BNT–BT–0.03ST)–LN exhibited a maximum unipolar strain of ~0.44% and corresponding normalized strain, S_max/E_max of ~880 pm/V under a moderate field of 50 kV/cm at room temperature. This giant strain was associated with the coexistence of the ferroelectric and ergodic relaxor phases, which should be mainly attributed to the reversible electric‐field‐induced transition between the ergodic relaxor and ferroelectric phases. Furthermore, the large field‐induced strain showed relatively good temperature stability; the S_max/E_max was as high as ~490 pm/V even at 120°C. These findings indicated that the (BNT–BT–xST)–LN system would be a suitable environmental‐friendly candidate for actuator applications.