聚丙烯纤维接枝苯乙烯的研究

采用化学接枝法以苯乙烯(St)为接枝单体、过氧化苯甲酰(BPO)为引发剂,1,2-二乙烯苯(DVB)为交联剂、甲醇和正辛醇为溶剂,对聚丙烯(PP)纤维进行接枝改性。研究了原料配比和反应条件对其接枝的影响。结果表明,PP纤维上接枝St,适宜的原料配比和操作条件为:St质量与PP体积比(St/PP)为4,BPO质量与St体积比(BPO/St)为0.025,DVB与St体积比(DVB/St)为0.025,溶剂与St体积比为5,浸渍24～30h,在85℃恒温水浴中反应6～8h。在较佳条件下可得到导入率为110%-160%的接枝纤维。     

氯化聚丙烯/马来酸酐接枝物的合成和性能研究

以甲基环己烷为溶剂、过氧化二苯甲酰(BPO)为引发剂,加入马来酸酐(MAH)以及苯乙烯(St)对氯化聚丙烯(CPP)进行接枝改性。系统研究了单体MAH、St、过氧化二苯甲酰(BPO)对MAH接枝率的影响,并对其影响因素进行了分析。用红外光谱(FTIR)表征了产物结构,用滴定的方法测定了接枝率,实验结果表面:最佳反应条件为BPO/CPP投料比为10%,St/MAH投料比为1∶1,MAH/CPP投料比为20%,反应温度为100℃,反应时间为2 h。通过聚丙烯(PP)板涂装底漆附着力测试表明,当氯化聚丙烯接枝马来酸酐(CPP-g-MAH)接枝率达到3.14%时涂层附着力等级可达到0级。     

聚酰胺纤维

20046033 4-乙烯吡啶在尼龙6纤维上的自由基接枝Anbarasan R.…;Journal of Applied Polymer Science, 2002,86(12),P.3108(英) 氮气下、水溶液中的尼龙6纤维,以4-乙烯吡啶(4VP)作模型研究过氧化单硫酸(PMS)-氢硫基醋酸(TGA)氧化还原系统引发自由基接枝共聚物的化学特性。研究了4VP,PMS,TGA,尼龙6的浓度、时间、Rh温度以及接枝参数。报导了尼龙6-接枝-4VP的远红外图谱。测试了接枝纤维的水保持率(WRC)。(薛敏敏)     

聚丙烯水相悬浮接枝双单体苯乙烯和马来酸酐

以过氧化苯甲酰(BPO)为引发剂,采用水相悬浮法制备苯乙烯(St)、马来酸酐(MAH)双单体接枝聚丙烯共聚物(PP-g-St/MAH),结果表明,较优的接枝反应条件为BPO/St/MAH/水/PP投料质量比0.04/1.00/1.00/25.00/10.00,60℃溶胀2 h后90℃反应5 h.在此条件下,产物接枝率为8.97%,接枝效率为44.85%.     

离子液体中淀粉-g-聚己内酯共聚物的制备及表面活性研究

以1-丁基-3-甲基咪唑溴化物([bmim]Br)离子液体作为淀粉(St)和己内酯(CL)的共溶剂,合成了生物可降解的淀粉/聚己内酯接枝共聚物(St-g-PCL)。研究了St/CL/[bmim]Br投料比对单体转化率、接枝率以及产物溶解性的影响,利用1HNMR和IR考察了产物的结构和St-g-PCL中CL与淀粉单元的摩尔比。表面张力法测定了St-g-PCL水溶液的表面张力和临界胶束浓度,并通过稳态芘荧光分析了胶束内核的疏水环境。结果表明:当投料比St/CL/[bmim]Br=10/14/20(w/w/w),接枝率为65%,St-g-PCL中CL与St结构单元摩尔比为0.91/1,产物具有较好的水溶性,St-g-PCL水溶液的表面张力(γcmc)和临界胶束浓度(CMC)分别为32.7mN/m,0.64mg/ml。所形成的胶束内核具有较好的疏水环境。     

苯乙烯、丙烯腈与降解天然胶乳的共聚研究

以BPO-FeSO4为氧化还原引发体系，采用种子乳液聚合技术，在降解天然胶乳DNR粒子上接枝共聚苯乙烯(St)和丙烯腈(AN)，用正交实验法研究了较佳反应条件，考察反应温度、反应时间及投料比对单体转化率、接枝率和接枝效率的影响，并用红外光谱对共聚物进行表征。     

双单体AA/St熔融接枝OBC的研究

利用HAAKE转矩流变仪,采用熔融接枝法制备了双单体丙烯酸/苯乙烯接枝乙烯-辛烯嵌段共聚物(OBC-g-(AA-co-St)),探讨了丙烯酸(AA)、苯乙烯(St)和过氧化二异丙苯(DCP)的用量对接枝反应的影响,并通过红外光谱分析表征了该接枝产物的结构。结果表明:采用熔融接枝技术,成功地将AA接枝到OBC上,得到了OBC-g-AA接枝共聚物;当AA为4%、DCP为0.2%、反应温度为170℃、反应时间为12 min时,OBC-g-AA的相对接枝率达到峰值;另外,第二单体St的引入使接枝率有所提高,当St与AA质量比为1:2时,其相对接枝率达到1.68。     

有机分散剂协助三单体固相接枝改性聚丙烯研究

以丙烯酸丁酯(BA)、马来酸酐(MAH)和苯乙烯(St)为接枝单体,偶氮二异丁腈(AIBN)为引发剂,一种有机溶剂作分散剂,对聚丙烯(PP)进行固相接枝改性制备接枝共聚物。考察了反应时间、反应温度、引发剂用量等因素对接枝反应的影响,用红外光谱对接枝产物进行了表征。结果表明,当引发剂用量(以PP为100份基准)为0.3份,单体(BA,St,MAH的物质的量比为2:1:1)总投料量为4份(相对PP为100份)时,得到了接枝率为3.26%的接枝产品。单体利用率达到58.75%。     

水悬浮自搅拌体系中聚丙烯接枝双单体丙烯酸和苯乙烯

以水为分散介质,二甲苯、甲苯为界面剂,过氧化苯甲酰(BPO)为引发剂,在水悬浮自搅拌体系中制备双单体丙烯酸(AA)和苯乙烯(St)接枝聚丙烯共聚物(PP-g-AA/St).重点研究了加料方式、界面剂、分散介质、引发剂、溶胀时间、反应时间、水相阻聚剂、单体组成对接枝反应的影响.得出较佳的工艺条件:反应物料一次加入,投料质量比为二甲苯/水/聚丙烯/单体/过氧化苯甲酰/二氯化锡=2.6/15/10/2/0.015/0.005%,室温溶胀4 h,102℃反应6 h,此条件下双单体接枝率达11.95%,接枝效率高达59.75%.AA与St在物质的量之比为0.846处进行接枝反应时无序共聚副反应严重,傅立叶红外光谱分析结果表明,AA和St接枝到PP大分子链上.     

SAN共聚物中AN含量对PVC/ABS/DOP共混物结构与性能的影响

采用半连续乳液聚合技术将聚苯乙烯(St)和丙烯腈(AN)接枝到聚丁二烯(PB)乳胶粒子上,通过改变共聚单体的投料比(St/AN)合成了一系列不同AN含量的丙烯腈-丁二烯-苯乙烯共聚物(ABS)接枝共聚物,将其与聚氯乙烯(PVC)和增塑剂邻苯二甲酸二辛酯(DOP)熔融共混制得PVC/ABS/DOP(40/40/20)共混物。研究了共混物的热挺型性、微观形态结构和动态力学性能。结果发现,该共混物为双相连续结构,随着接枝SAN共聚物中AN含量的增加,由于DOP小分子与SAN共聚物的相互作用逐渐减弱,导致了SAN相的Tg和共混物的储能模量不断提高,改善了共混物的热挺型性,阐明了PVC/ABS/DOP共混物热挺型性的科学本质。     

Studies on the fabrication of strong‐acid/weak‐base amphoteric ion exchange fibers and their adsorption property for amino acids

The strong acid/weak base amphoteric ion exchange fibers with different ratios of acidic and basic groups and different grafting percentages were prepared by grafting styrene and 4‐vinylpyridine onto polypropylene fiber and then sulfonating with chlorosulphonic acid, under various reaction conditions, such as the feed ratio of styrene and 4‐vinylpyridine, monomers concentration, sulfonation temperature, and sulfonation time, swelling time, etc. The produced strong acidic and basic groups are the sulfonic group and the pyridyl group, respectively. Only one sulfonic group is induced into an aromatic ring in most of PP‐g‐St‐4VP and it is located in the para‐position of styrene. The contents of the strong‐acid group and the weak‐base group of the PP‐g‐SO₃H‐Py fibers produced in this work are in the range of 1.98 to 4.22 and 2.33 to 4.24 mmol/g, respectively. The strong acid/weak based amphoteric fibers obtained possess good static adsorption property for basic and acidic amino acids, and they also have a good dynamic adsorption and elution property for amino acids like related strong acid ion exchange fibers. © 2004 Wiley Periodicals, Inc. J Appl Polym Sci 92: 418–425, 2004     

合成条件对聚苯胺成纤性能的影响

以苯胺为单体、过硫酸铵为氧化剂、在盐酸水溶液中化学法合成聚苯胺 ,研究的重点是确立一个能够适合纺丝要求的合成参数体系。合成的聚苯胺重均相对分子质量达 2 9× 10 4。以不同条件下合成的聚苯胺为原料湿法纺制了聚苯胺导电纤维。     

pH and organic solvent‐sensitive properties of crosslinked polymeric spheres formed by a soap‐free emulsion polymerization

Narrowly distributed poly (styrene‐co‐(4‐vinylpyridine)) microspheres are facilely prepared by a soap‐free emulsion polymerization, and their structures and properties are investigated by TEM, FTIR spectra, DSC, and DLS, respectively. The sizes and glass transition temperatures of the polymeric spheres increase with an increase of 4‐vinylpyridine in the reactive system. In addition, these polymeric spheres show good stability in water and a series of organic solvents due to their crosslinked structures. When poly(styrene‐co‐(4‐vinylpyridine)) microspheres are obtained in the reactive system where the weight ratio of 4‐vinyl pyridine to styrene is less than 4/6, they can be well dispersed in water as well as in organic solvents such as ethanol, toluene and DMF, and show obvious pH sensitive and organic solvent‐sensitive characteristics. © 2012 Wiley Periodicals, Inc. J. Appl. Polym. Sci., 2013     

阳离子染料可染丙纶的干热定型与上染率的关系

通过广角 X射线衍射 (WAXD)和上染率测定 ,探讨阳离子染料可染丙纶的热定型温度和时间对染料上染率的影响。结果表明 :纤维在 10 0～ 12 0℃热定型 5～ 10 min,可用阳离子染料沸染 ,上染率在90 %以上     

X光显影纤维的研究

以聚丙烯为基体 ,硫酸钡为显影剂 ,共混后经双螺杆挤出造粒、纺丝 ,制得 X光显影纤维。讨论了硫酸钡的粒径大小对纺丝性能的影响 ,硫酸钡含量对纤维力学性能的影响 ,钛酸酯偶联剂和硅烷偶联剂对硫酸钡的表面作用和影响。结果表明 ,硫酸钡粒径越小 ,纺丝性能越好 ,硫酸钡含量越大 ,纤维的拉伸性能变差 ,强度下降。硅烷偶联剂较钛酸酯偶联剂与硫酸钡的粘结力强 ,分散效果好     

聚丙烯腈原丝及其干喷湿纺

介绍了用于 PAN基碳纤维的聚丙烯腈原丝的发展历史 ,阐述了聚丙烯腈纺丝工艺中的主要工序和技术关键 ,指出了可以在聚合、纺丝过程中通过控制杂质及使用高相对分子质量的 PAN树脂纺制 PAN纤维等方法来提高原丝的性能。着重介绍了目前纺丝工艺中 PAN共聚体的制备、纺丝流体的流变行为及其凝固过程等重要工序的研究成果     

极性苯乙烯-丁二烯类热塑性弹性体增韧聚丙烯性能研究

采用乙烯基吡啶改性生产的极性苯乙烯-丁二烯类热塑性弹性体(极性TPE)改性聚丙烯,研究了不同分子量、不同接枝率及不同嵌段比的极性TPE对聚丙烯(PP)力学性能的影响,对不同改性聚丙烯选择合适的极性TPE弹性体提出了建议。     

用三维卷曲中空涤纶短纤维混纺涤毛弹力织物

介绍用 3 .3 3 dtex三维卷曲中空涤纶短纤维与毛、氨纶混纺生产涤毛弹力织物的情况。着重介绍了织物织造工艺过程及产品质量 ,说明三维卷曲中空涤纶短纤维可与毛混纺生产出符合质量要求的涤毛弹力织物     

涤纶三异丝生产工艺探讨

研究了涤纶三异丝的结构、性能及生产，从异收缩原理、超喂、空气压力、纺丝速度等方面对三异丝的生产进行了探讨。ＦＤＹ 与ＤＴＹ 混纤是三异丝生产的关键工艺，采用最简化的丝路，灵活的上丝方式和不同于常规产品的合网方式可生产出品质优良的涤纶三异丝。     

远红外聚酯的研制

分析了远红外聚酯的国内外研制现状 ,指出当今国内远红外聚酯生产过程中普遍存在陶瓷粉对聚酯的相容性差、分散性差、远红外聚酯的过滤性能和流变性能差等问题。通过对陶瓷粉进行表面处理和降低聚酯熔点等途径 ,可明显改善远红外聚酯的可纺性。