硝酸铵细度对铵胺炸药性能的影响

为研究硝酸铵细度对铵胺炸药性能的影响,以六亚甲基四胺作为可燃剂制备了一种胶状炸药—铵胺炸药;对多孔粒状硝酸铵进行破碎,分别过20、40、60、80目筛区分不同的细度,对混合各细度硝酸铵颗粒铵胺炸药基质的黏度、炸药的爆速和猛度进行了测试,对炸药进行了储存稳定性实验。结果表明,当硝酸铵细度由0～20目增至80目以上时,铵胺炸药基质的混合均匀性增加,基质的初始黏度由92828mPa·s增至148637mPa·s,基质黏度随着剪切时间增加而逐渐降低,铵胺炸药基质属于触变性流体;炸药的爆速由3569m/s增至4316m/s,猛度由26.00mm增至30.50mm,能量释放更集中,对周围介质的的冲击力提升;分别储存2d和120d的铵胺炸药,爆速降幅均小于5%;说明硝酸铵细度的增加可以提高铵胺炸药的爆轰性能和储存稳定性。     

改性硝酸铵粉尘的动态静电检测

为了研究硝酸铵粉尘的静电特性,通过模拟改性硝铵炸药连续化生产线实际生产中的气流输送装置,对气流输送过程中的改性硝酸铵粉尘进行了静电测试.从14组有效试验结果可以看出,尽管气固浓度较高,放电电压较大,但是改性硝酸铵在试验过程中并未发生反应,没有因为电极放电而出现冒烟等反应现象.结果表明,改性硝酸铵的静电火花感度E50＞2 073.6 mJ,最小静电着火能E0.01＞103.7 mJ,在模拟气流输送过程中对静电是安全的.     

膨化硝酸铵的感度特征研究

膨化硝酸铵是近年来得到广泛使用的工业炸药氧化剂，本文对其撞击感度，摩擦感度，爆发点，火焰感度，静电火花感度等危险感度进行了测定，并对膨化硝酸铵进行了PSC实验，以及对雷管感度及冲击波感等实用感度进行了测定，研究表明，同普通硝酸铵相比，膨化硝酸铵具有较低的危险感度及良好的实用感度。     

改性硝酸铵研究进展及其发展方向

从粒状硝酸铵的问世和发展、抗硬化结晶粉末硝酸铵和不破乳松散性结晶硝酸铵的研究、用于膨化炸药的膨化硝酸铵研制、用于无梯炸药的敏化改性硝酸铵的研究、钝化或防爆硝酸铵的开发、液体硝酸铵在炸药中的应用、改性多孔粒状硝酸铵的研究等方面概述了我国改性硝酸铵的研究成果。开发高性能多孔硝酸铵和防爆的农用硝酸铵及其下游产品,是我国改性硝酸铵今后主要的发展方向。     

改性铵油炸药研究

通过对普通硝酸铵进行改性制得一种多微孔改性硝酸铵,并对其物理性能和爆炸性能进行了深入研究。研究结果表明,改性铵油炸药具有较低的吸湿性和结块性,吸油性好,不渗油,是一种爆轰感度高、爆炸性能优良的新型工业炸药。     

LLM-105炸药粒度及形貌对机械感度的影响

采用感度试验(摩擦感度和撞击感度)测定了高能钝感炸药1-氧-2,6-二氨基-3,5-二硝基吡嗪(LLM-105)粒度对于单质炸药机械感度的影响。试验以机械球磨法得到的LLM-105颗粒为研究对象,粒度范围为4-70μm。机械感度结果表明随着LLM-105平均粒径的增大,其摩擦感度和撞击感度均有不同程度的降低。机械球磨得到的颗粒由于表面相对于溶液结晶得到的颗粒表面更为平滑,其摩擦感度和撞击感度也相对较低。     

添加剂对硝酸铵爆轰安全性和热稳定性的影响

将磷酸二铵(DAP)、硫酸铵(DAS)、钝感剂RFM-l、RFM-2和RFM-3与硝酸铵混合后，按照工业炸药配方配制成铵木油炸药。对硝酸铵的爆轰安全性进行了评价。采用恒温热分解方法。研究了含上述添加剂的硝酸铵及铵木油炸药的热分解行为，得出如下结论：硝酸铵中含25％以上的磷酸二铵或硫酸铵，铵木油炸药不能被8号雷管起爆，在本实验务件下硝酸铵的爆炸特性得以消除；而钝感剂RFM-l、RFM-2和RFM-3阻爆效果非常理想，仅需5％的添加量就能消除硝酸铵的爆炸特性。在390℃恒温加热lmin的热分解实验结果表明，添加5％的RFM-l、RFM-2或RFM-3可以使硝酸铵的热分解率从96．8％下降至41．2％、28．5％和22．O％，40％的DAS和40％的DAP使硝酸铵的热分解率下降至28．4％和45．9％，可见硝酸铵热稳定性的提高是爆炸特性得以消除的原因。硝酸铵经过改良后是否具有爆炸性可以通过测定热分解率来判断。     

含防爆剂农用硝酸铵的感度研究

实验在169℃左右加热硝酸铵到熔融状态,加入防爆剂,冷却到室温,得到含防爆剂的硝酸铵。测试其摩擦感度、5 s延滞期爆发点、静电火花感度以及配成铵油炸药后的撞击感度、雷管感度。结果表明,含防爆剂硝酸铵较普通硝酸铵撞击感度从88%降到24%,摩擦感度降为0%,5 s爆发延滞期从462℃增加到474℃,静电火花感度和雷管感度无明显变化。     

RDX粒度对机械感度的影响

系统研究了RDX粒度对撞击感度和摩擦感度的影响．实验测试的RDX平均粒径为1．5～124μm,并在此粒度范围内分为5个粒度等级。其中撞击感度用特性落高法表示,摩擦感度用特性正压力表示。结果表明：炸药的撞击感度、摩擦感度均随粒度的减小而降低。从理论上分析了炸药粒度变化对机械感度影响的机理。     

自敏化硝酸铵的制造工艺

引　言硝酸铵是一种易溶于水的无机盐 ,由于分子中含有较高比例的氮元素 ,广泛用于农用肥料 .此外 ,由于硝酸铵燃烧时无烟或少烟以及在一定的条件下具有爆炸性能 ,在火箭推进剂和工业炸药等领域广泛用做氧化剂 .但是 ,硝酸铵最显著的特点是具有强烈的吸湿性和结块性以及低爆轰感度 ,强烈的吸湿和结块性给硝酸铵及其含硝酸铵产品的贮存和使用带来了严重困难 ,低爆轰感度使得应用硝酸铵作氧化剂的军用和民爆产品必须加入一定量的敏化剂才能保证其性能和使用效果 .而敏化剂的加入不仅增加了生产成本和生产工艺 ,而且这类敏化剂绝大多数都具有一…     

阻垢剂性能评定方法-鼓泡法的改进

本文对测定阻垢剂的阻垢性能的标准方法--鼓泡法进行了改进。令空气在预孢和器中预先被CO2和水蒸气所饱和，再通入试验水样，如此可部分或全部抵消试验水样的蒸发损失，消除了空气流量、冷凝管的长度和形状、鼓泡头等诸因素对测定结果的影响，使测定的结果更稳定、更可靠，操作更简便。将该改进应用于阻垢性能测试仪，测定结果的精密度和准确度都有了明显提高。     

AN EXPERIMENTAL STUDY OF AN INCLINED BUOYANT PLANE TURBULENT AIR JET

An experimental study of the effects of buoyancy forces resulting from temperature differences on the mean flow and turbulence characteristics of a plane turbulent jet discharged at an angle to the horizontal has been undertaken. The jets were generated by discharging air through a rounded nozzle which was 10 mm wide by 580 mm long. The discharged air could be heated and tests were undertaken with discharge temperatures of 20° and 40°C above the ambient air temperature at a single nozzle discharge velocity which gave a discharge Reynolds number of approximately 1700. Tests were undertaken with angles of jet discharge to the horizontal of 0°, 30°, 60° and 90°. Velocity and temperature measurements were undertaken using hot wire anemometers. Measurements of the mean velocity and temperature, the turbulence normal and shear stresses, the temperature fluctuation intensity and the two components of the turbulence heat flux were obtained. Profiles of these quantities were measured at six equally spaced positions to a distance of approximately 60 nozzle widths from the discharge plane. Measurements at much more closely spaced intervals were also taken along the jet “centre-line”, this being defined as the locus of the point of maximum velocity in the jet.     

非流态化气固流通过斜管与孔口的动力学

应用散料力学与多相流理论研究非流态化气体-颗粒两相流通过垂直与倾斜管道及孔口的动力学,建立了动力学方程,用以预测各种条件下的颗粒物料通过孔口的流率.方程的计算结果与各种条件下取得的大量实验数据相吻合,从而使颗粒物料通过孔口流率的计算由经验关联逐步上升为理论预测.     

卡尔曼滤波器的自适应算法

通过对一维时不变线性系统的卡尔曼滤波器的理论分析，提出了一种估计并不断修正系统噪声方差Ｒ及观察噪声方差Ｑ的自适应算法。     

AN IMPROVED VOLUMENOMETER*

A volumcnometer of improved design has been developed for measuring the solid volumes of specimens varying in size up to that of standard refractory bricks. The chief feature of the new design is the use of a closed-cistern, altitude-type mercurial barometer to replace the simple manometer previously used. The barometer is de signed for use in a constant temperature room (21.1°C.) where the acceleration of gravity is 980.1 cm. per sec.². Under these conditions, pressure readings are auto matically corrected to standard conditions. A vernier permits rapid readings to 0.1 mm. of mercury.     

INFLUENCE OF AN INDUCED MAGNETIC FIELD ON PERISTALTIC TRANSPORT IN AN ASYMMETRIC CHANNEL

In this study, we investigate the effects of an induced magnetic field on the peristaltic transport of a Phan-Thien-Tanner (PTT) fluid in an asymmetric channel. Asymmetry in the flow is induced because of wave trains with different amplitudes and phases. Development of mathematical analysis is made under long wavelength and low Reynolds number approximations. Explicit expressions of stream function, pressure gradient, magnetic force function, axial induced magnetic field, and current density are derived. Computation of pressure rise is based upon numerical integration. The obtained expressions are carefully analyzed through physical interpretation.