采用光学显微镜和X射线衍射仪对低温板坯加热Hi-B钢的组织、织构的特征演变进行了研究。结果表明：从热轧板和常化板的表面到中心，组织和织构分布不均匀。热轧板组织分为表层再结晶区域、再结晶和变形晶粒混合区域和中心变形晶粒区域，并且热轧板各层的织构类型不同。常化板表层晶粒长大，过渡层和中心层的形变晶粒基本消失，常化板继承了热轧板的织构特点。冷轧板为纤维状变形组织，冷轧后形成了以{001}<110>～{111}<110>为主的α织构。脱碳渗氮板的横断面和纵断面的晶粒平均尺寸分别为25.9μm和25.3μm，织构主要为{111}<112>、{114}<481>和{001}<120>织构。成品板晶粒平均尺寸为19.1μm，成品板为单一的高斯织构。     

低温板坯加热取向硅钢形变和初次再结晶织构的演变规律

 采用取向分布函数和取向线分析方法对低温板坯加热取向硅钢从热轧到初次再结晶工艺阶段的织构进行了研究。研究表明：一次冷轧后各层的织构组分与热轧板各层面的织构组分存在着继承关系,次表层存在很强的{001}<110>织构,中心层的织构和热轧板的中心层相似,存在强的{001}<110>和{112}<110>织构;中间退火后发生再结晶,各织构组分的强度有所减弱,Goss织构组分再次出现;二次冷轧后沿厚度方向上的织构不均匀性不明显,{111}<112>织构强度最高,几乎是其他织构组分的1倍,{001}<110>织构大幅降低;初次再结晶后织构沿厚度方向没有明显的不均匀性,{111}<110>为最强的织构组分,并且具有一定强度的Goss位向。     

“ASP+罩式退火工艺”生产Ti-IF钢的织构演变

对济钢"ASP+罩式退火工艺"下生产的Ti-IF钢的热轧、冷轧及退火试样的织构演变进行分析。借助XRD测定并计算了热轧、退火及冷轧试样的取向分布函数和相关织构组分的体积分数。结果发现,济钢Ti-IF钢热轧板形成了较强的{111}面织构;在冷轧和退火后γ纤维织构显著增强;冷轧织构在罩式退火后,{111}<110>织构强度减弱,{111}<112>织构增强,{111}/{100}比值增加。     

CSP流程试制50W270高牌号无取向硅钢织构的演变

研究了CSP流程试制50W270高牌号无取向硅钢热轧→常化→冷轧→退火过程中织构的演变.利用电子背散射衍射技术对全流程织构进行测量和分析.发现热轧板织构在厚度方向上存在较大差异,表层主要为铜型、黄铜和高斯织构,1/4层存在微弱的高斯织构和旋转立方织构,中心层以γ纤维织构和旋转立方织构为主,还含有较弱的α纤维织构.与热轧板相比,常化板表层和1/4层织构变化不大,中心层旋转立方织构和α纤维织构增强.冷轧板各层均具有α纤维织构和γ纤维织构.与冷轧板相比,成品板各层中α纤维织构基本消失,还出现了立方织构和高斯织构.      

取向硅钢板坯加热温度对热轧及冷轧板织构的影响

 采用取向分布函数及取向线分析方法对取向硅钢高温和低温板坯加热工艺的热轧及冷轧钢板织构进行了研究。结果表明：低温与高温板坯加热工艺的热轧板及冷轧板织构组分有明显不同。低温板坯加热热轧板中{100}<001>及{110}<110>织构较强,但经冷轧后{001}<110>织构最强。     

不同冷轧压下量对亚稳态奥氏体不锈钢00Cr17Ni7织构的影响

 采用X射线衍射技术(XRD)研究了不同冷轧压下量对亚稳态奥氏体不锈钢00Cr17Ni7织构的影响,分析了亚稳态奥氏体不锈钢00Cr17Ni7中马氏体相和奥氏体相的织构变化情况。研究结果表明,不同冷轧压下量下,00Cr17Ni7中的奥氏体相织构主要由Brass{110}<112>、Goss{110}<001>和少量的Copper{112}<111>、S{123}<634>组成,并且随着压下量的增加Brass和Goss织构强度显著提高;同时马氏体相织构主要以{115}<110>、{112}<110> 、{111}<112>、{332}<113>组成,织构的形成主要归因于“Kurdjumov-Sachs取向关系”和“体心立方金属轧制织构类型演变的特点”共同作用的结果。     

TSCR试制低碳低硅无取向电工钢织构的演变

 研究了模拟TSCR流程生产的低碳低硅无取向电工钢在热轧-冷轧-退火过程中织构的演变。对热轧板采用EBSD技术进行织构的测定,而对冷轧板和退火板采用X射线衍射技术进行了织构的测定。结果表明：热轧板沿板厚方向织构变化比较明显,在1/10处主要织构为α纤维织构和γ纤维织构;在1/4厚度处出现了较强的γ纤维织构;在1/2厚度处主要为较强的{001}〈110〉织构,其他织构分布漫散。冷轧板表面和中心处主要织构均为α纤维织构和γ纤维织构,但是在中心处两织构强度都显著减弱。退火板表面和中心处α纤维织构基本消失,γ纤维织构织构进一步加强,出现了{110}〈001〉高斯织构和{001}〈010〉立方织构。     

微合金冷轧高强钢组织性能的研究

运用光学显微镜(OM)、扫描电子显微镜(SEM)、X射线衍射(XRD)、电子背散射衍射(EBSD)、透射电子显微镜(TEM)等分析方法对微合金钢280VK组织、织构及析出粒子的演变规律进行分析,研究冷轧高强钢组织性能变化规律。结果表明:280VK热轧板组织主要为多边形铁素体,晶粒不均匀,冷轧板组织为形变铁素体,退火后晶粒均匀长大且晶界上析出物增多;热轧板中只有高斯织构{011}100,冷轧板中含有旋转立方织构{100}011以及铜型织构{112}110的α纤维织构,也含有面织构{111}110的γ纤维织构,退火板中含有{111}110的α纤维织构和{111}110γ纤维织构。热轧板中的位错缠结,析出粒子多沿位错线析出,冷轧板内部析出粒子无显著增加。退火板析出粒子沿晶内位错大量析出且尺寸增大。     

冷轧Ti-IF超深冲钢罩式退火机理及织构变化规律的研究

在480~750℃条件下,模拟罩式退火,利用光学显微镜、X射线衍射和金相显微硬度计研究了冷轧Ti-IF超深冲钢晶粒结构的变化,通过取向密度函数分析了再结晶过程织构演变规律。研究表明:冷轧Ti-IF超深冲钢的再结晶温度约为630℃,再结晶过程能够在660℃条件下2 h之内完成;冷轧后该钢主要有4种织构,分别是{001}〈110〉、{111}〈110〉、{111}〈112〉和{112}〈110〉;在退火再结晶过程中,{111}逐渐转变为γ-{111},当退火温度升至720℃时,{001}〈110〉和{112}〈110〉转变为纤维织构γ-{111},最终{111}〈110〉和{111}〈112〉成为主要织构类型。     

基于CSP工艺稀土冷轧板罩式退火中组织织构演变

 采用金相显微镜和X射线衍射仪对CSP(Compact Strip Production)稀土板热轧、冷轧及退火3个阶段的组织和织构进行了检测和分析,并结合文献讨论了稀土板组织织构的演变规律。结果表明：稀土冷轧板以{223}<110>、{001}<110>、{112}<110>为主要织构,退火后形成了以{223}<110>和{111}<110>为主的再结晶织构,织构密度均达8. 5以上,{223}<110>和{111}<110>取向差为10°。稀土板开始再结晶需要的温度较高,并且再结晶完成需要的时间较长。再结晶初期织构变化比后期小。试验稀土板退火后{111}/{001}值极大,{111}<011>织构与{111}<211>织构密度差约为6。     

Evolution of Through-Thickness Texture in Ultra Purified 17%Cr Ferritic Stainless Steels

 Texture inhomogeneity usually takes place in ferritic stainless steels due to the lack of phase transformation and recrystallization during hot strip rolling, which can deteriorate the formability of final sheets. In order to work out the way of weakening texture inhomogeneity, conventional hot rolling and warm rolling processes have been carried out with an ultra purified ferritic stainless steel. The results showed that the evolution of through-thickness texture is closely dependent on rolling process, especially for the texture in the center layer. For both conventional and warm rolling processes, shear texture components were formed in the surface layers after hot rolling and annealing; sharp α-fiber and weak γ-fiber with the major component at {111}<110> were developed in both cold rolled sheet surfaces, leading to the formation of inhomogeneous γ-fiber dominated by {111}<112> after recrystallization annealing. In the center layer of conventional rolled and annealed bands, strong α-fiber and weak γ-fiber textures were formed; the cold rolled textures were comprised of sharp α-fiber and weak γ-fiber with the major component at {111}<110>, and inhomogeneous γ-fiber dominated by {111}<112> was formed after recrystallization annealing. By contrast, in the centre layer of warm rolled bands, the texture was comprised of weak α-fiber and sharp γ-fiber, and γ-fiber became the only component after annealing. The cold rolled texture displayed a sharp γ-fiber with the major component at {111}<112> and the intensity of γ-fiber close to that of α-fiber, resulting in the formation of a nearly homogeneous γ-fiber recrystallization texture in the center layer of the final sheet.     

铜含量对TSCR工艺生产取向硅钢热轧织构的影响

 取向硅钢热轧板中织构梯度对发展完善的二次再结晶十分关键,通过添加Cu可以显著降低取向硅钢板坯加热温度,从而影响热轧板织构分布。本文利用X射线衍射仪,分析了实验室模拟薄板坯连铸连轧（TSCR）工艺的3种不同Cu含量的取向硅钢热轧板织构。结果表明：不同Cu含量热轧板表面到厚度1/4处均为弱的热轧织构,热轧板心部主要为{100}面织构;Cu含量约在0.4%时,热轧板次表层的{110}<001>织构比例最高,而热轧板心部的{100}<110>织构比例最低;Cu含量对热轧织构中{114}<110>和{001}<100>织构发展有显著影响。     

基于CSP工艺热轧及冷轧过程3%Si钢组织和织构的演变

3%Si钢(/%:0.067C、3.09Si、0.34Mn、0.007P、0.003S、0.70Cu、≤0.005Al、0.0080～0.0120N)由50kg真空感应炉冶炼,并在实验室轧机经6道次热轧成3.5mm板,终轧温度850℃,卷取温度650℃,热轧板经常化处理后由4辊可逆轧机6道次冷轧成0.50mm薄板。分析结果表明,热轧板表面主要为随机分布较大的等轴晶,中心处由细小等轴晶和长条状晶粒组成,并出现了很强的旋转立方织构{001}〈110〉。经过冷轧,薄板表面出现了很强的α织构和γ织构组分,并且冷轧板保留了热轧的{001}〈110〉旋转立方织构。     

再结晶阶段加热速度对低碳冷轧板罩式退火过程组织和织构的影响

在实验室条件下模拟CSP热轧板为基板生产的低碳冷轧板罩式退火过程,研究再结晶阶段加热速度对冷轧板罩式退火过程组织和织构的影响。结果表明,压下率83.3%的冷轧板,随着再结晶阶段加热速度的增加,会使试样再结晶温度降低,再结晶过程提前完成,{001}110织构变强,{111}110织构先减少后增加,{111}112织构先减少后增加出现峰值,当加热速度超过50℃/h时又减小。在加热速度30~40℃/h间变形织构{112}110有较低的密度值。再结晶阶段加热速度40℃/h的退火工艺成品组织为饼形晶粒,{001}110织构密度较低,{111}110和{111}112密度较强,密度值接近。     

Textures and Properties of Hot Rolled High Strength Ti-IF Steels

The texture evolution in a high strength Ti-IF steel during the processing of hot rolling, cold rolling, and annealing is studied. For comparison, both ferrite rolling and austenite rolling are employed. It is found that the texture type is the. same after ferrite rolling and austenite rolling, but the texture intensity is much higher in the ferrite rolled sample. Furthermore, texture characteristics at the surface are absolutely different from those at the mid sec tion in both ferrite rolled and austenite rolled samples, as well as under the cold rolled and annealed conditions. The shear texture { 110 } 〈001 〉 disappears and orientation rotates along { 110 } 〈001 〉→ { 554 } 〈 225 〉→ { 111 } 〈 112 〉→{111}〈110〉→{223}〈110〉 during cold rolling. Compared to the austenite rolled sample, the properties of the cold rolled and annealed sheet which is subjected to ferrite rolling are higher.     

普通取向硅钢轧制过程中组织和织构的演变

借助电子背散射衍射(EBSD)及ZEISS-200MAT金相显微镜对某钢厂普通取向硅钢(CGO)进行研究,研究结果表明:热轧板组织、织构沿板厚方向存在明显的不均匀性,在热轧板表层及次表层发生再结晶,同时存在强度较高的Goss织构,中心层存在较强的{001}110变形织构。冷轧组织均呈纤维状条带组织,一次冷轧后,热轧板中的Goss织构消失,织构主要为α、γ织构,经中间脱碳退火后,α、γ织构强度减弱,并出现一定强度的Goss织构和利于Goss织构发展的{554}225、{332}113等织构,经二次冷轧后,二次冷轧织构类型与一次冷轧织构一致,但织构强度不同。     

薄板坯连铸连轧流程Fe-3%Si钢热轧板和常化板织构

在实验室按照薄板坯连铸连轧工艺流程试制了Fe-3%Si硅钢热轧板,采用EBSD和X射线衍射方法观察了A钢和B钢热轧板和常化板的织构组织,分析了α、ε和γ取向线上织构取向密度变化规律。A和B钢热轧板具有相似的{110}〈112〉和、{001}〈110〉和{001}〈010〉和高斯织构组织,A试样表层的晶粒均匀性较差,B试样具有较强的γ织构取向。采用EBSD观察比较了A钢和B钢热轧板和常化板的垂直TD面的EBSD微观织构组织,A钢和B钢常化退火后基本保留了热轧时形成的中心部位的组织,而次表层和表层晶粒发生了再结晶长大,晶粒组织和织构梯度减小,织构主要集中在{001}〈^-1^-10〉和{001}〈0^10〉和之间以及高斯织构上。常化后织构的总体强度下降,高斯强度减弱。试验研究结果为开发薄板坯连铸连轧短流程生产电工钢技术提供理论依据和参考数据。     

摩擦对IF钢铁素体区热轧和退火织构的影响

采用X射线衍射仪分析IF钢铁素体区热轧织构以及退火织构的演化,在实验室热轧机上进行了IF钢的铁素体区热轧,研究了摩擦对IF钢铁素体区热轧、退火织构的影响。结果表明：无润滑轧制时,钢板表层形成强高斯织构组分{110}〈001〉,弱γ纤维织构,导致再结晶织构中高斯组分强度高,γ纤维织构强度低;润滑轧制时,钢板表层高斯织构组分强度降低,{100}〈011〉、γ纤维织构强度提高,退火后γ纤维织构强度提高。钢板中心受摩擦作用影响较小,轧制过程中发展为较强的α和γ纤维织构,退火后γ纤维织构成为主要织构组分。