Crystallization and Electrical Properties of （Ba0.4Pb0.3）Sr0.3TiO3 Thin Film by Pulsed Laser Deposition

（Ba0.4Pb0.3）Sr0.3TiO3 thin films were fabricated via pulsed laser deposition （PLD） technique on Pt/TiO2/SiO2/Si substrate. The crystallization of the films was characterized by XRD and FSEM, and the experimental results suggested deposition parameters, especially the deposition temperature was the key factor in forming the perovskite structure. The dielectric properties of the film deposited with optimized parameters were studied by an Agilent 4294A impedance analyzer at 1 MHz. The dielectric constant was 772, and the loss tangent was 0.006. In addition, the well-shaped hysteresis loop also showed that the film had a well performance in ferroelectric. The saturated polarization P, remnant polarization Pr and coercive field E were about 4.6 μC/cm2, 2.5 μC/cm2 and 23 kV/cm （the coercive voltage is 0.7 V）, respectively. It is suggested the film should be a promising candidate for microwave applications and nonvolatile ferroelectric random access memories （NvFeRAMs）.     

纳米TiO2碳热氮化制备纳米晶Ti(C0.7,N0.3)固溶体

在封闭系统中,对纳米TiO2碳热还原氮化反应合成纳米晶Ti(C,N)固溶体粉末进行研究。结果表明,当以C/Ti值为2.7配料,氮气压力为0.005 MPa时,一定量纳米TiO2/纳米碳黑混合料在1600℃下保温4 h,可以合成晶粒尺寸为32 nm的球形Ti(C0.7,N0.3)固溶体粉末。     

球磨时间对Ti(C0.7,N0.3)晶粒及Ti(C0.7,N0.3)基金属陶瓷组织和性能的影响

球磨是金属陶瓷制备中的关键工艺,滚动球磨是目前成本较低、在实际工业生产中应用最广泛的球磨方式。为了量化分析球磨时间对Ti（C_0.7,N_0.3）基金属陶瓷的影响,采用湿混的方法在固定的球料比、球磨机转速和球磨介质添加量的条件下,研究球磨时间因素对Ti（C_0.7,N_0.3）的晶粒尺寸、应变和晶格常数的影响,以及对烧结后的Ti（C_0.7,N_0.3）基金属陶瓷微观组织和物理力学性能如收缩率、密度、硬度和横向断裂强度的影响。结果表明,随球磨时间增加,Ti（C_0.7,N_0.3）晶粒尺寸下降,而微观应变增加。同时,Ti（C_0.7,N_0.3）的晶格常数也增加,这与晶粒微观应变增加以及少量原料的氧化加剧有关。对烧结后的微观组织而言,球磨时间的增加导致金属陶瓷硬质相平均晶粒尺寸下降,但是当球磨时间达到72和96 h的时候,金属陶瓷中出现了0.1 μm左右的孔隙,这与球磨过程中氧含量的增加导致烧结时脱气反应以及Ti（C,N）硬质相和Ni粘接剂之间的润湿性变差有关。Ti（C_0.7,N_0.3）基金属陶瓷微观组织中白芯结构数量随球磨时间的增加明显减少了,芯中Mo含量的下降而Ti含量的增加是白芯数量下降的原因。环形相随球磨时间的增加变薄了,这一现象与不同尺寸的颗粒溶解度以及颗粒的均匀性有关。另外,随着球磨时间的增加,Ti（C_0.7,N_0.3）基金属陶瓷的硬度增加,而横向断裂强度随球磨时间的增加先增加后下降,其中孔隙对横向断裂强度的损害作用要大于晶粒细化对强度提高的作用。     

La0.7Ca0.3MnO3多晶材料制备及其电磁特性

以化学溶液分解法制备La0.7Ca0.3MnO3粉体,常压烧结制备多晶块体样品。对La0.7Ca0.3MnO3样品的磁矩、磁致电阻效应（CMR）和电脉冲诱导电阻转变效应（EPIR）进行了研究。磁矩零场冷和场冷试验结果发现,居里温度以下,零场冷和场冷条件下磁矩具有较大差别。这说明材料中缺少真正的长程磁有序。La0.7Ca0.3MnO3多晶具有磁致电阻效应,在9 T磁场作用下,磁致电阻变化大约为70%。在80 V,20 ns电脉冲作用下,材料具有电脉冲诱导电阻转变效应。从理论上对磁致电阻效应与电脉冲诱导电阻转变效应的机理进行了分析。     

微乳液法制备Pb0.7Ca0.3ZrO3纳米晶粉体的研究

以Span-80和Tween-80混合物作为表面活性剂，正丁醇作为助表面活性剂，环己烷作为油相，Pb（NO3）2、Ca（NO3）2、Zr（NO3）4的混合溶液或氨水作为水相，采用微乳液工艺在800℃左右成功制备出了Pb0.7Ca0.3ZrO3纳米晶，并以TG-DTA、XRD和TEM对所制备的Pb0.7Ca0.3ZrO3纳米晶进行了表征。研究结果表明，所制得的Pb0.7Ca0.3ZrO3纳米晶属三方晶系，无杂相，粉末颗粒细小，颗粒尺寸在15—40 nm之间，呈球形。     

Ferroelectric properties of Bi_4Zr_(0.5)Ti_(2.5)O_(12) thin films prepared on LaNiO_3 bottom electrode by sol-gel method

The Bi4Zr0.5Ti2.5O12 (BZT) thin films were fabricated on the LaNiO3 bottom electrode using sol-gel method. The structure and morphology of the films were character-ized using X-ray diffraction, AFM and SEM. The results show that the films have a perovskite phase and dense microstructure. The 2Pr and 2Vc of the Pt/BZT/LaNiO3 capacitor are 28.2 μC/cm2 and 14.7 V respectively at an applied voltage of 25 V. After the switching of 1×1010 cycles, the Pr value decreases to 87% of its pre-fatigue val-ues. The dielectric constant (ε) and the dissipation factor (tanδ) of the BZT thin films are about 204 and 0.029 at 1 kHz, respectively. The films show good insulating behavior according to the test of leakage current. The clockwise C-V hysteresis curve observed shows that the Pt/BZT/LaNiO3 structure has a memory effect be-cause of the BZT film’s ferroelectric polarization.     

Zn_(1/3)Nb_(2/3)含量对xPMnS-(1-x)PZN性能的影响

以xPMnS-(1-x)PZN四元系压电陶瓷为研究对象,通过研究Zn1/3Nb2/3含量的变化对0.5PMnS-0.5aPZN材料结构与性能的影响,获得具有高压电活性的0.5PMnS-0.5aPZN陶瓷材料。结果表明,四方相结构的0.5PMnS-0.5aPZN材料压电活性优于三方相结构,性能最好的组成位于MPB(四方相边界)附近靠近四方相含量较高的区域,组成Zn1/3Nb2/3含量的变化影响了MPB的位置。     

稀土氧化物对金属陶瓷刀具材料性能的影响

通过添加2种不同的稀土氧化物,利用热压液相烧结法烧结,研究了2种工艺条件下稀土氧化物对Ti(C0.7N0.3)基金属陶瓷刀具材料显微结构和力学性能的影响.结果表明,稀土氧化物的添加使材料的力学性能受工艺影响很大,在烧结温度1400℃压力25 MPa,保温时间为30 min的工艺条件下,稀土氧化物的添加会大幅度的降低材料的力学性能;在温度1450℃压力25 MPa,保温时间为30 min的工艺条件下,稀土氧化物会提高材料的断裂韧性.     

Tb0.3Dy0.7Fe1.95单晶的应用研究

用提拉法磁悬浮冷坩埚技术生长的 RFe2 (Tb0 .3Dy0 .7Fe1 .95)单晶材料 ,其室温下的饱和磁致伸缩系数 λs 可达2× 10 - 3以上 ,优于同成份的定向结晶材料。采用高性能 Tb0 .3Dy0 .7Fe1 .95单晶材料 ,通过优化微位移致动器的机械、磁路参数 ,研制出具有非水冷结构的新型微位移致动器。     

Poly（styrene-co-divinylbenzene）-PAMAM-IDA chelating resin： Synthesis,characterization and application for Ni（II） removal in aqueous

PS-PAMAM-IDA chelating resins were prepared by low-generations of polyamidoamine（PAMAM） and then chloroacetic acid functionalizing commercially available ammoniated polystyrene matrix, to preconcentrate Ni2＋ from synthetic aqueous samples. Different generations of PAMAM were used to obtain different chelating resins, PS-IDA, PS-1.0G PAMAM-IDA and PS-2.0G PAMAM-IDA. The synthesized resins were characterized by FTIR and elemental analysis. The effect of solution pH, kinetic studies, resin loading capacity, matrix effects etc., on metal ion adsorption to adsorbent phase, were studied by batch method. The PS-1.0G PAMAM-IDA resin was the most excellent adsorbents, with a maximum adsorption capacity of（24.09±1.79） mg/g for Ni2＋ ion at pH=7. The interpretation of the equilibrium data was given by Langmuir isotherms model, and the correlation coefficient values for PS-IDA, PS-1.0G PAMAM-IDA and PS-2.0G PAMAM-IDA resins were 0.992, 0.994 and 0.987, respectively.     

Mg-8Zn-4Al-0.3Mn-xRE合金的时效析出过程及其动力学

采用金相显微分析和DSC分析了Mg-8Zn-4A1-0．3Mn-x RE含金时效析出过程及其动力学，结果表明，未添加RE元素的Mg-8Zn-4A1-0．3Mn合金的时效析出过程为：过饱和固溶体→细小弥散析出相→再结晶软化和析出相的聚集长大；添加RE元素的Mg-8Zn-4A1-0．3Mn合金的时效析出过程为：过饱和固溶体→细小弥散析出相→析出相的聚集长大．人工时效后，与未加RE的合金相比，合金2，3，4显微硬度峰值提高分别达5．6％，9％，13．4％；随着RE元素含量的增加，合金的析出相形成激活能呈逐渐增大的变化规律．     

用P(x)逼近π(x)

我们已有连续函数逼近法寻求π（x）的表达式。即素数定理。但由于函数类型的差异．这种逼近效果有其内在的缺陷。文中介绍了与π（x）类型相同的P（x），用P（x）逼近π（x）的方法寻找π（x）的准确表达式。     

金属间化合物Tb(Fe1-xNix)11.3Nb0.7的结构和磁性能研究

利用X射线衍射、扫描电镜和差示扫描量热等方法对化合物Tb（Fe1-xNix）11.3Nb0.7的结构和磁性能进行了研究.结果表明,金属间化合物Tb（Fe1-xNix）11.3Nb0.7（x=0,0.05,0.10,0.15,0.20,0.25）的结构均为ThMn12型结构,并且随Ni含量x的增大,Tb（Fe1-xNix）11.3Nb0.7金属间化合物的晶格常数a,c和单胞体积V均呈减少趋势,居里温度TC呈单调上升趋势.当x〉0.15时,Tb（Fe1-xNix）11.3Nb0.7金属间化合物中的杂质相明显呈现出来.     

Gd对AZ91D-0.4%Ca-0.3%Sr镁合金低周疲劳性能的影响

通过运用控制总应变幅的方法,在应力比R=-1条件下施加拉-压载荷,测试了合金元素Gd复合添加对金属型铸造镁合金AZ91D-0.4%Ca-0.3%Sr的低周疲劳性能的影响,并利用光学电子显微镜、扫描电镜分别观察了材料在不同状态下的显微组织及低周疲劳断口特征.结果表明：Gd的添加能细化铸态AZ91D镁合金的晶粒,加入3.0%Gd可以提高镁合金的低周疲劳性能.     

Li元素对Bi0.5Na0.5TiO3基无铅压电陶瓷压电性能的影响

针对目前无铅压电陶瓷的压电常数d33偏小的情况,采用传统的固相反应烧结方法制备得到了高压电性能的Bi0.5Na0.5TiO3基无铅压电陶瓷Bi0.5(Na0.7K0.3-xLix)0.5TiO3(x=0.04,0.08,0.12,0.16,0.20),研究了Li元素的添加量对陶瓷的烧结温度以及压电性能的影响.研究结果表明,Li元素对K的替代可以降低陶瓷的烧结温度,提高样品致密度,适量的Li可以大幅度提高陶瓷的压电性能.陶瓷样品的压电常数d33和平面机电耦合系数kp随着Li含量的增加先增大后减小,在1 090 ℃的烧结温度下,Li含量x=0.08时的陶瓷样品表现出最佳的压电性能,压电常数d33=212 pC/N,平面机电耦合系数kp=33%.     

n型(AgSbTe2)x(PbTe)1-x热电材料的制备和性能

采用熔融缓冷法制备了组成为(AgSbTe2)x(PbTe)1-x(x=0.04—0.20)的热电材料,研究了AgSbTe2固溶量对材料微观结构和热电传输性能的影响。结果表明,当AgSbTe2固溶量增大时,样品易发生相结构偏析,样品由富Pb和富AgSb的两相组成。样品热导率随AgSbTe2固溶量增加而降低,电性能也有一定程度的降低。样品的无量纲热电优值(ZT)随AgSbTe2固溶量的减小而增加。     

Existence of supremum and infimum in E～ and relations of (M) integral and (G) integral

Proves the existence of supremum and infimum in the noncompact fuzzy number space E～, redefines E～-valued (M) integral, and then discusses the relations between (M) integral and (G) integral of E～-valued functions.     

Ru（bipy）2（dppx）^2＋的合成,表征和性质

报道了Ｒｕ（ｂｉｐｙ）２（ｄｐｐｘ）＾２＋的合成、表征,并对其性质作了初步探讨,光谱实验表明,它在水溶液中无荧光发射,加入双链（ＤＮＡ）后能发射很强的荧光,可作为核酸分子“光开关”。     

多晶La_(0.49)Sr_(0.51)(Mn_(1-x)Nb_x)O_3的电输运特性研究

测量了B位掺杂的钙钛矿结构锰氧化物La0 49Sr0 51(Mn1-xNbx)O3(x=0,0 05,0 15和0 25)的电阻率和磁化强度的温度特性.实验结果表明,当Nb5 部分替代B位的Mn4 离子时,电阻率-温度特性由原来单一的半导体型转变成了高温时的半导体(绝缘体)型和低温时的类金属型.随Nb掺杂量增大,电阻率迅速升高3～5个数量级,半导体(绝缘体)-类金属转变温度降低.在掺杂Nb的样品中,只观察到顺磁-铁磁转变,而未观察到铁磁-反铁磁转变.上述实验结果的一种可能解释是掺杂改变了磁有序时电子自旋的排列和空间取向,从而改变载流子被自旋热涨落的散射作用和载流子转移的随机性.     

Ru(bipy)2(dppx)2+的合成、表征和性质

报道了Ru(bipy)2(dppx)2+的合成、表征,并对其性质作了初步探讨,光谱实验表明,它在水溶液中无荧光发射,加入双链DNA后能发射很强的荧光,可作为核酸分子"光开关".