水基无卤素无松香抗菌型免清洗助焊剂

以去离子水为溶剂、高沸点有机醇醚为助溶剂、有机酸为活化剂并使用复合表面活性剂研制成了一种无铅焊料用免清洗助焊剂,该助焊剂并含有一种天然的抗菌剂E以延长其保存期限。对该助焊剂的成分及配比进行了选择和优化,并对其性能进行了测试。结果表明,制备的免清洗助焊剂均匀透明,无刺激性气味,不含卤素,无腐蚀性,表面绝缘电阻大于1×108;将其用于SnAgCu系无铅焊料,焊接效果好,平均扩展率达到76.6%。     

一种醇基低固含量免清洗助焊剂的研制

通过无铅焊料的焊点铺展及润湿力实验考察了活性剂对助焊剂润湿性能的影响,并据此研制出了一种以乙醇为溶剂、以有机酸和有机胺为活性剂并使用复合表面活性剂的免清洗助焊剂.结果表明:使用复合表面活性剂的助焊剂的润湿效果要好于使用单一表面活性剂的助焊剂.其中,以使用Op-4与壬基酚聚氧乙烯醚质量比为8:1的复合表面活性剂的助焊剂的...     

零卤免清洗助焊剂的研制

复配不同分解温度的零卤有机酸活化剂,同时添加一定量的其它成分,制备出的零卤免清洗助焊剂对Sn99.3Cu0.7无铅焊料的扩展率达到80.2%,铜板无腐蚀,焊后表面绝缘电阻最小值为3.8×10^11Ω.     

无铅松香芯焊锡丝中新型助焊剂的研制

通过扩展率实验对松香芯焊锡丝用助焊剂的成分及配比进行选择及优化,然后通过添加一种天然植物油(C油)对该优化过的助焊剂进行进一步改进,依据行业标准对制备的助焊剂进行了测试。结果表明,这款助焊剂不含卤素、无腐蚀性、表面绝缘电阻高(1.68×10~(11)Ω);无铅SnCu焊锡丝在使用这款助焊剂时,焊接效果好,松香飞溅值为0.3%,扩展率为75.9%。     

Sn42Bi57Ag1无铅焊膏用活性剂的优化设计

针对Sn42Bi57Ag1无铅焊料开发出一种低温无铅焊锡膏,着重研究助焊剂中活性剂对焊锡膏润湿性能的影响。以铺展性能作为主要评价指标,通过回流焊接实验,对用于助焊剂的7种有机酸进行了筛选。最终选取了性能较好的甲基丁二酸、己二酸、水杨酸与丁二酸四种有机酸进行正交试验,通过量化分析选取正交试验水平,根据方差分析确定助焊剂中活性剂的最佳组合。结果表明:有机酸的复配能显著改善焊点铺展情况,当甲基丁二酸、己二酸、水杨酸与丁二酸质量比为2∶3∶5∶2时,Sn42Bi57Ag1无铅焊膏的润湿性能优异,焊点铺展率达86.52%。     

卤素含量与助焊剂性能的关系

本文通过实验提出了:随着助焊剂卤素含量的增加,助焊剂扩展率提高,对金属的腐蚀性也相应提高,残渣表面绝缘电阻和水溶液电阻下降。     

无铅焊料用水基无卤无VOC助焊剂

采用无卤素有机酸和有机胺作为活化剂,以去离子水为溶剂,并添加非离子表面活性剂,通过铺展率实验对各主要成分及配比进行选择和优化设计,研究了一种无铅焊料用水基无卤无VOC助焊剂。依据电子行业标准对研制的助焊剂进行了性能测试。结果表明,制备的助焊剂不含卤素、VOC物质,对无铅焊料的润湿性强,焊点光亮饱满,焊后残留少,铺展率可达78.2%,适用于SnAgCu和SnCu无铅焊料的波峰焊。     

无铅SAC0307焊料润湿性与漫流性集成测试

为节省测试时间并降低测试成本,通过测量SAC0307焊料对铜管的润湿力、爬升高度及焊料对铜片的润湿力和铺展率,建立润湿性和漫流性的对应关系,集成测试获得焊料对铜片的润湿性能和铺展能力。结果表明,松香助焊剂作用下焊料对铜片的润湿力为铜管的1.1倍,丁二酸助焊剂作用下焊料对铜片的润湿力是铜管的1.3倍,松香和丁二酸两种助焊剂作用下焊料在铜管内爬升高度与铜片上铺展率的关系都为指数关系。     

树脂芯助焊剂性能研究

树脂芯助焊剂性能对焊接质量有重要影响,为了解影响其性能的因素,研究了溶剂、活化剂及表面活性剂等的种类和配比对助焊剂性能的影响。结果表明,使用复合溶剂,按w(胺盐)为16.1%,w(有机酸)为2.0%,w(表面活性剂)为0.5%可配制成综合性能优良的助焊剂,其扩展率为80%,w(卤素)为0.07。     

Sn-9Zn合金无铅钎料用助焊剂研究

通过测量润湿面积和润湿角,研究不同助焊剂对Sn-9Zn焊料润湿性的影响。结果表明:助焊剂对Sn-9Zn焊料润湿性影响很大,由乳酸、聚乙二醇和SnCl2所构成的助焊剂与Sn-9Zn焊料有很好适应性;同时扫描电镜和能谱分析也表明焊料与Cu基体界面的IMC为Cu5Zn8相,比Sn-37Pb焊料具有更高的剪切强度。     

SnAgCu无铅焊膏用溶剂的优化研究

以SnAgCu无铅焊膏铺展性能和焊点形貌作为评价的主要指标,通过回流焊接实验,对常用于焊膏的10种溶剂进行了单一溶剂优选,并对两种性能较好的溶剂进行复配优化研究.结果表明:A醇、二缩三乙二醇和B醚作为单一溶剂时焊膏的润湿性较好、焊点外形较饱满,铺展率都大于83%;A醇和B醚按质量比3:2复配时得到的焊膏铺展率达到93%...     

Experimental Wettability Study of Lead-Free Solder on Cu Substrates Using Varying Flux and Temperature

The selection of soldering flux plays a critical role in promoting wetting and product reliability of printed circuit board assemblies. In this study, the effects of fluxes on the wetting characteristics of the Sn-3.0Ag-0.5Cu solder alloy on Cu substrates was researched by using various flux systems at different soldering temperatures. Because of the distinct characteristic of the lead-free solder—poor wettability—three kinds of fluxes [no-clean flux with high solid content (NCF), rosin mildly activated flux (RMA) and water-soluble flux (WSF)] were chosen for the wetting experiments. The wetting time and force were the evaluating indicators. The experimental observations indicated that the wettability clearly depended on the soldering temperature and flux system when using the same solder. Furthermore, the corrosion potential of flux residues was measured by surface insulation resistance (SIR) testing. Scanning electron microscope (SEM) and energy-dispersive X-ray spectroscopy (EDS) were used to determine the contents of the flux residues and corrosion products.     

无铅焊膏用无卤素松香型助焊剂的研制

通过筛选试验,调整溶剂、松香和活化剂的含量,确定助焊剂中主要成分的最佳配比。根据国标GB/T9491—2002,测试助焊剂的扩展率、腐蚀性及其他性能,并根据日本工业标准JISZ3198—4—2003进行润湿力测试。结果表明:当助焊剂中有机酸活化剂质量分数为9%、m(水白松香):m(聚合松香)为2:3时,助焊剂具有良好的物理稳定性和润湿性,平均扩展率最高能达到76.00%。焊后铜片无腐蚀,残留物少且成透明膜状。     

无VOC免清洗助焊剂焊后残留物的可靠性评价

为了研究焊后残留物的腐蚀性以及可能对PCB的电气绝缘性能造成的影响,通过表面绝缘电阻(Rs)试验和电化学迁移试验评价了三种不同固体含量的无VOC(挥发性有机物)免清洗助焊剂焊后残留物的可靠性。结果表明,使用w(固体含量)为3.6%的助焊剂,湿热试验后试件的Rs大幅下降,并且PCB表面腐蚀严重;而w(固体含量)为2.3%的助焊剂,则试件具有较高的Rs(6.4×109Ω),并且对PCB腐蚀性小。使用放大30倍的显微镜观察电化学迁移测试后的试件,均没有发现枝晶。     

非离子表面活性剂对助焊剂润湿性能的影响

在软钎焊免清洗助焊剂中分别添加了3种不同含量的非离子表面活性剂:TritonX—100、Tween—20和PEG2000,得到了3组助焊剂。使用这3组助焊剂和Sn0.7Cu无铅钎料在纯铜板上进行了铺展测试。结果表明,添加TritonX—100和添加Tween—20的质量分数均为0.6%时,钎料的润湿角最小值分别为30.07°和29.70°,铺展面积最大值分别为56.67mm2和58.53mm2;添加PEG2000质量分数为0.3%时,钎料的润湿角最小值为26.70°,铺展面积最大值为66.88mm2,比未添加时增加26.9%。适量加入非离子表面活性剂能够改善助焊剂的润湿性,并提高无铅钎料的铺展能力。     

醇胺对免清洗焊芯用助焊剂性能的影响

通过添加醇胺制备免清洗焊芯用助焊剂,研究了两种醇胺及其复配对助焊剂性能的影响。结果表明:添加适当的醇胺有利于降低助焊剂体系酸值,提高焊接性能,减少对线路板的腐蚀,提高焊接可靠性。使用任意一种醇胺,质量分数在1.0%~1.5%时,助焊剂的焊接性能较好,但酸值不能满足免清洗助焊剂的要求。两种醇胺进行复配,质量分数均为1.0%~1.5%时,助焊剂的综合性能优良,用无铅焊锡丝SnAg3.0Cu0.5测定其焊接性能,扩展率为79%,酸值148 mgKOH/g,铜板腐蚀、绝缘电阻、电迁移等可靠性指标较好。