预腐蚀7050-T7651铝合金微裂纹的萌生与扩展北大核心

开展不同预腐蚀时间下7050-T7651铝合金的扫描电子显微镜原位拉伸实验,利用扫描电子显微镜观原位、在线测试件表面微观裂纹的萌生、扩展,分析腐蚀对铝合金微裂纹行为的影响。结果表明:随着腐蚀程度加剧,试件表面腐蚀坑密度增大,形成腐蚀坑群,试件的承载能力也随之下降。微裂纹主要萌生于试件缺口粗糙表面和试件表面蚀坑处,微裂纹数量随着腐蚀时间的延长而增多;缺口产生的微裂纹与相邻的蚀坑微裂纹相互联结形成主裂纹,主导试件的损伤失效过程。腐蚀损伤较轻时,主裂纹尖端附近的蚀坑会引起裂纹分支;腐蚀损伤较重时,腐蚀坑诱导的多条微裂纹与主裂纹发生多次联合,影响了主裂纹的扩展方向与路径;切应力在裂纹扩展过程中也起到了重要作用,开裂模式为Ⅰ/Ⅱ混合断裂模式。     

基于变形场时空演化的煤冲击劈裂试验研究

采用霍普金森杆冲击加载装置,通过高速摄影机搭建实验的数据采集系统,以数字散斑相关方法作为实验的观测手段,对巴西圆盘煤试件在冲击载荷作用下的冲击劈裂变形场演化规律及裂隙扩展特征进行实验研究。试验结果表明:1从变形场演化特征分析,加载初期变形场相对均匀,随荷载增加变形局部化特征明显。变形场时空演化总体表现为两个阶段特征:峰前水平方向变形量值变化较快,垂直方向变形量值变化较慢;峰后由于裂隙演化,水平方向变形量值变化缓慢,垂直方向变形量值变化较快;2霍普金森杆加载过程中,在试件两端加载处出现了局部压碎区,加载过程中主裂纹从压碎区域萌生并沿径向加载方向扩展至另一端贯通破坏;3实验测得煤样在冲击载荷作用下峰前应力随应变呈线性增长,弹性模量与静荷载相比有较大提高,由于压碎区域存在,冲击加载实验得到的煤试件拉伸强度与实际相比偏小。     

钛铝合金原位拉伸损伤与断裂过程研究

通过原位拉伸及卸载试验,和试样断口与表面的SEM分析,对钛铝合金原位拉伸断裂过程、断裂起始点及断裂扩展情况进行了研究。结果发现该材料断口上呈现沿层断裂和穿层断裂的混合形态,并在裂纹前端取向不利的层团附近出现大量微裂纹损伤。发现其断裂过程为：随着外加载荷的增加,试样首先在晶粒沿层薄弱区开裂,继续加载会在主裂纹前端附近产生一些微裂纹损伤,接着裂纹将穿层断裂,同时积蓄的能量得到部分的释放,直至试样的整体断裂。     

微波照射后花岗岩裂纹扩展规律试验研究

硬岩裂隙的形成和扩展规律是研究岩石损伤机理的重要内容。为了探究微波照射下,岩石裂隙的扩展规律,为微波辅助破岩技术提供理论依据,利用扫描电镜(SEM)设备对花岗岩试件在微波照射及单轴抗压强度测试后进行扫描观测,分析岩石断口的形貌、裂纹的类型及断裂模型。结果表明：高功率微波照射后,试件表面出现颜色变化,并伴随有张拉裂纹出现,在压缩试验后,试件上部结构呈粉末状破碎|SEM设备观测下花岗岩断口形貌特征主要为平坦面状和条纹状断裂|花岗岩的裂纹类型主要为张拉裂纹和压剪裂纹|花岗岩的断裂模型主要为沿晶断裂、穿晶断裂以及两者叠加。     

微波照射后花岗岩裂纹扩展规律试验研究

硬岩裂隙的形成和扩展规律是研究岩石损伤机理的重要内容。为了探究微波照射下，岩石裂隙的扩展规律，为微波辅助破岩技术提供理论依据，利用扫描电镜(SEM)设备对花岗岩试件在微波照射及单轴抗压强度测试后进行扫描观测，分析岩石断口的形貌、裂纹的类型及断裂模型。结果表明：高功率微波照射后，试件表面出现颜色变化，并伴随有张拉裂纹出现，在压缩试验后，试件上部结构呈粉末状破碎|SEM设备观测下花岗岩断口形貌特征主要为平坦面状和条纹状断裂|花岗岩的裂纹类型主要为张拉裂纹和压剪裂纹|花岗岩的断裂模型主要为沿晶断裂、穿晶断裂以及两者叠加。     

304不锈钢波纹补偿器失效分析

利用金相显微镜、扫描电镜和显微硬度计等,对某304不锈钢波纹补偿器的断口进行了观察和测试分析.结果表明:304不锈钢的奥氏体晶粒内有许多变形的滑移线,且在奥氏体晶界上有碳化物沉淀析出;补偿器的断口呈冰糖状花样特征,断口面处存在较深的沿晶界的二次裂纹,断裂性质为沿晶脆性断裂;此晶界弱化的不锈钢在工作时,受工作应力作用萌生微裂纹,微裂纹扩展导致波纹管断裂.     

航空2024铝合金VIC-3D静载分析和疲劳试验VIC-3D Static Analysis and Fatigue Test of 2024 Aluminum Alloy 陈亚军 黄彦 薛程丹 洪建国

为系统研究航空2024铝合金的力学性能,首先通过VIC-3D技术测量静态拉伸全场二维应变及应力,其次基于航空载荷谱进行动态载荷疲劳试验。VIC-3D结果表明,利用Y方向应变随时间变化云图,可以探究裂缝出现及发展规律;采用运输类飞机下翼面标准载荷谱TWIST,疲劳试样在第34周循环,总第169973次循环后发生疲劳断裂。利用扫描电子显微镜对试件断口进行观察,疲劳断口可观察到疲劳源区、疲劳裂纹扩展区及瞬时断裂区,并呈扇形向外扩展。疲劳裂纹萌生于试件表面;裂纹扩展区二次长裂纹方向和裂纹扩展方向垂直,并存在疲劳辉纹;瞬时断裂区呈现出塑性断裂韧窝状形貌,局部存在冲击面形貌。     

等幅循环加载岩石非均匀变形演化试验研究

为了研究循环加载条件下岩石的变形演化规律,开展了红砂岩试件的等幅循环加载与分级等幅循环加载试验。采用CCD相机对试验过程中试件的变形图像进行采集,基于数字散斑相关方法分析了等幅循环加载过程中试件的非均匀变形演化规律。分析研究发现:循环加载过程中,随着循环次数的增加,试件的非均匀变形场逐步演化,变形局部化现象愈加明显;非均匀变形在循环加载过程中存在时间滞后和变形累积特征,且分级等幅循环加载过程中其峰值应力的增加会使非均匀变形的滞后特性与累积特征更加明显;在试件发生破坏前,加载顶点和卸载底点的非均匀变形指标数值逐渐接近。研究循环加载作用下岩石的非均匀变形演化规律,可为岩石破坏提供新的前兆信息。     

冲击荷载下层状砂岩变形破坏及其动态抗拉强度试验研究

针对层状砂岩的各向异性,探究了冲击荷载作用下层理角度对层状砂岩变形破坏的影响规律。加工制作了含软弱层理的砂岩标准试件,利用霍普金森杆试验系统进行了不同层理倾角下的砂岩动态巴西圆盘试验,并结合数字图像相关方法获得了圆盘试件变形场的演化云图。从破坏结果看,层理面与加载轴线之间的夹角对层状砂岩的变形破坏有显著影响。当软弱层理平行于加载轴线时,圆盘试件在加载端处首先产生应变集中,并随着冲击加载的作用迅速沿层理扩展,最终表现为从圆盘试件加载端向非加载端呈弧线形断裂的特征;当软弱层理垂直于加载方向时,圆盘试件中间首先形成多个应变集中区,表现为在加载轴线与软弱层理相交处萌生多个微裂纹,并在冲击加载的作用下微裂纹沿加载轴线不断相互贯通,最终形成径向扩展的宏观裂纹;当软弱层理面与加载方向成45°时,圆盘试件在加载端处首先沿层理方向形成显著的拉剪应变集中区,由于层理介质的抗拉强度和抗剪强度均低于砂岩基质体,因而表现为试件在拉、剪复合应力的共同作用下从加载端处产生多条沿层理面扩展的裂纹。从试验结果中还可以看出,在相同加载速率下,垂直层理试件的强度最高,水平层理试件的强度最低,倾斜层理试件的强度介于水平层理试件和垂直层理试件之间。随着加载速率的提高,不同层理方向的砂岩动态抗拉强度均呈线性增长的特征,但与无层理砂岩相比,含软弱层理砂岩的动态抗拉强度对加载速率的敏感程度较低。此外,层理角度对砂岩的开裂应变有较大影响,受剪应力的影响,倾斜层理砂岩的开裂应变高于垂直层理砂岩。     

含倾斜边裂纹岩石冲击断裂模拟试验

为模拟岩石在冲击荷载下,裂纹与加载方向不同角度情况下的断裂行为,利用透射式焦散线测试系统,采用单边切口三点弯曲梁试件,进行三点弯曲梁冲击断裂试验。研究结果表明：含倾斜边裂纹试件受到正应力和剪切力作用,裂纹为复合型裂纹,裂尖产生的焦散斑为复合型焦散斑;预制裂纹与加载方向的夹角变化时,动态应力强度因子、裂纹扩展时间以及裂纹扩展速度都随之变化;预制裂纹与加载方向的夹角增大时,裂纹扩展速度的最大值增大,裂纹扩展速度的振荡性增强;当荷载的加载方向与预制裂纹的方向一致时,裂纹起裂最快,裂纹为I型裂纹。冲击载荷方向与预制裂纹夹角增大时,扩展裂纹表现为复合型特征,动态应力强度因子KdⅡ表现越明显,其最大值随夹角的增大而增大。     

Current situation and future trend of China rare earth luminescent material industry

<正>Rare earth luminescent material is one of the most important application sectors of rare earths.China enjoys the exceptional advantage to develop rare earth luminescent material for its abundant rare earth resources.After several decades'endeavor,China's rare earth luminescent material industry,headed by rare earth phosphor for lamp and LED and high efficient rare earth energy-saving light source,has been gradually developed into a scale industry.China has become a major production base of rare earth phosphor for lamps and rare earth     

China rare earth market review

正June 1~10,2014Rare earth market remained weak.Quoted price of rare earth products was similar to that in May.There was no sign of recovery in downstream market.The market of NdFeB magnetic materials and phosphor was depressed.Catalyst,polishing powder and ceramic industries remained inactive.Demand from downstream industry was soft.Consumers purchased on their needs.Suppliers had strong intention to sell.Prices of rare earth products     

China rare earth market review

正November 21~30,2014Due to weak demand from downstream industries,transactions of rare earth in Chinese domestic market were inactive.It was difficult to sell any rare earth products except for dysprosium oxide and terbium oxide.Suppliers lost confidence in recent market.Demand for rare earth products was soft.Consumers continued to take a wait-and-see attitude.Rare earth export market remained slow.     

Galaxy Magnets achieved the net profit of 34.02 million yuan in the first six months of 2014

正Galaxy Magnet announced its financial results for the first half of 2014 on August 14.For the first six months ended on 30 June 2014,Galaxy Magnet achieved operation income of RMB 182.3 million,up8.40% over the same period of 2013,and the net profit attributable to the shareholders of the listed company of 34.02 million yuan,increasing 35.49% over the same period of last year.Stable performance increase was led by development of new customers and application market of magnets.     

Rare Earth Application in Steel in China

<正>China has rich rare earth resources.Output of rare earth and steel in China ranks the top first in the world.However,there is still certain distance between the steel produced in China and developed countries from the point of varieties and quality.China still has to import some types of steel.Improving the quality should be emphasiZed in future development of steel industry in China.Rare earth can be used to upgrade traditional steel     

Current situation and future trend of China rare earth luminescent materialindustry(continued)

<正>Developing ecological lighting source The world is facing the big problem of energy shortage today and the contradiction between economy development and environmental protection is worsened.Therefore,people are more likely to choose an ecological light source that is more energy efficient and environmental friendly.The choice provides great opportunity for the development of rare earth optical material industry in China.The concept of green lighting positions rare earth luminescent material as a leading player in illumination market.The light source of both rare earth luminescent lamp and LED lamp is ecological and energy saving.This is why     

稀散金属产业的观察与思考

分析了近年来国内外稀散金属产业的生产、应用、资源与市场状况.铟锡氧化物靶材、砷化镓晶片、锗红外材料、铼高温合金和硒在电解锰及玻璃的应用等已成为稀散金属的主要应用领域.稀散金属的产量快速增长达到历史高位而导致了市场的失衡.以GaInP_2/GaAs/Ge,CIGS和CdTe为代表的非硅系太阳能电池是稀散金属的新兴应用领域,将给稀散金属带来日益增长的需求.     

Brief news

正Corun invested another 50 million yuan in power battery for HEV Hunan Corun announced on 27 June that they had signed the cooperation agreement to jointly built Corun(Shaoxing)Autos Power Battery System Co.,Ltd.in Shaoxing Binhai New City.According to the announcement,total registered     

铜熔炼中锍品位对杂质元素分配行为的影响

借助于多相、多成分系统中平衡计算的手段，开发出微量元素砷、锑、铋及伴生元素铅、锌等在铜熔炼中分配行为的计算机模型。利用该模型对铜熔炼过程进行计算机模拟，分析了冰铜品位对砷、锑、铋、铅和锌等杂质元素的分压、活度系数及它们在冰铜、炉渣和气相中分配率的影响，并讨论其热力学分析结果对生产实践的指导意义。     

New energy vehicle:an opportunity for rare earth magnets

<正>Extracted from Securities Guide 1.Popularity of new energy vehicles—an irresistible market trend1.1 Progress of new energy vehicles Chinese Premier Li Keqiang said recently on a visit to Xi'an BYD Autos that new energy vehicles,especially new energy bus,can lessen environment and noise pollution.He encouraged the use of new