拜耳法赤泥沉降分离因素的探讨

通过正交试验重点探讨了在添加絮凝剂的情况下,固含、沉降温度、絮凝剂添加量对赤泥沉降分离过程的影响。稀释矿浆温度越高、稀释矿浆固含越低,赤泥沉降速度越快;而赤泥沉降速度先随絮凝剂浓度增加而增加,达到一定浓度后沉降速度又会降低。     

细粒级氧化铜矿浸出矿浆絮凝沉降试验

采用复合絮凝剂对某细粒级氧化铜浸出矿浆进行沉降试验,考察了絮凝剂种类和用量、矿浆浓度等对沉降性能的影响。结果表明,当矿浆质量浓度为8%,每吨干渣PHP-5与PHP-8用量分别为48g和12g时,矿浆沉降速度达到5.1m/h,完全满足工业要求。     

细粒全尾矿絮凝沉降特性研究

细粒全尾矿沉降速度慢、脱水困难,影响到膏体制备;该类尾矿必须借助絮凝剂改善沉降特性。根据某矿山尾矿物理特性,从7种阴离子聚丙烯酰胺絮凝剂中选出1种沉降速度最快的絮凝剂N123,并使用N123进行了室内沉降试验。采用均匀设计法建立了3因素5水平试验方案,回归不同水平沉降速度和极限沉降浓度方程,得到最佳因素组合。最后,探索了矿浆停留时间对絮凝效果的影响。     

拜尔法赤泥的沉降分离过程初探

重点探讨了在添加絮凝剂的情况下,稀释矿浆温度、浓度及固含,预脱硅时间和絮凝剂添加量对赤泥沉降分离过程的影响。稀释矿浆温度越高,稀释矿浆固含越低,矿浆浓度越低,赤泥沉降速度越快。     

超细粒级锰矿浸出矿浆絮凝沉降试验

采用不同絮凝剂对电解锰锰矿浸出矿浆进行絮凝沉降试验,考察了絮凝剂电性、离子度、分子量以及添加量对矿浆絮凝沉降效果的影响。结果表明,矿浆含固率为6%时,添加60g/t分子量1 400万~1 700万、离子度30%的阳离子絮凝剂,矿浆沉降速度由自然沉降时的0.04m/h提高到0.69m/h,能够满足电解锰行业制液工序生产要求。     

刚果(金)某氧化铜钴矿絮凝沉降试验研究

对刚果(金)某氧化铜钴矿进行絮凝沉降试验研究。结果表明,原矿在磨矿粒度-0.150mm占80%、矿浆浓度10%～12%、絮凝剂用量5～10g/t,絮凝剂浓度0.05%～0.1%的条件下,沉降速度最高可达25m/h,底流浓度可达54%以上。对于磨矿粒度-0.150mm占80%、酸矿比132kg/t、初始矿浆浓度25%、常温浸出时间4h的浸出矿浆,在矿浆浓度6%、絮凝剂用量20g/t,絮凝剂浓度0.1%的条件下,沉降速度最高可达22m/h,底流浓度可达47%以上。     

超细全尾砂最优絮凝剂配比优化试验研究

针对某铜矿超细全尾砂在絮凝沉降过程中存在底流浓度偏低和沉降速度较缓等问题，选择了适当的絮凝剂并进行参数优化，以提高絮凝沉降效果。首先，对涉及矿浆尾砂等关键试验材料进行详尽的物化分析；然后，对多个候选絮凝剂进行了比较与筛选，通过参数优化，最终确定了最为合适的絮凝剂型号。这一研究成果为突破矿浆絮凝沉降过程中的性能瓶颈提供了有力的理论和实践支持，并显著提高了絮凝沉降效能。此外，深入探究了全尾砂矿浆浓度、絮凝剂投加量以及絮凝剂溶液浓度等因素对超细尾砂絮凝沉降过程的影响。研究结果显示，超细尾砂絮凝沉降受到多个因素的交互作用影响，通过执行回归分析，得出了最佳参数配比，即全尾砂矿浆浓度为10%，絮凝剂单耗为20 g/t，絮凝剂溶液浓度为0.05%。本研究为矿山生产实践提供了有价值的指导，并为下一步的参数优化工作提供了参考。通过优化絮凝剂的选择和参数调整，可以进一步改善超细全尾砂絮凝沉降过程，提高底流浓度和沉降速度，从而提升矿生产效率。     

应用改性剂改善红土镍矿超细矿浆的沉降及过滤性能的研究

介绍了在红土镍矿超细矿浆中加入适量的改性剂后的沉降及过滤效果,研究表明不管来自哪个矿山的红土镍矿,其超细矿浆在絮凝剂种类及用量相同的情况下加改性剂后矿浆沉降速度都比不加改性剂的矿浆沉降速度快,单位面积处理量明显增大,而且在矿浆浓度一样的情况下加改性剂后的过滤速度都要比不加改性剂的快,这说明该改性剂不仅有加快矿浆沉降速度、提高单位面积处理量、减少絮凝剂用量的功能,也有提高矿浆过滤速度的功能。     

尾矿干排工艺中高泥质尾矿浆絮凝浓缩处理试验研究

尾矿干排工艺高泥质尾矿中细粒级物料的脱水较为困难。为确定某金矿高泥质尾矿合理的沉降参数,选取高泥质尾矿浆浓度、絮凝剂单耗和絮凝剂种类作为影响因素,依据单一变量试验原则,进行全泥氰化尾矿浆絮凝沉降试验及正交试验。结果表明:各因素对矿浆沉降效果的影响程度为絮凝剂种类高泥质尾矿浆浓度絮凝剂单耗;当FS3802型絮凝剂(质量分数0.1%)用量为50 g/t,高泥质尾矿浆浓度为4%时,矿浆的沉降效果最好,且此条件下,动态沉降试验装置的最高底流浓度为46.7%,已初步具备膏体性能。研究结果对选矿厂全泥氰化尾矿干排工艺中絮凝沉降各因素的控制具有很好的指导作用。     

龙岩市某矿业有限公司选铁尾矿浆絮凝沉降试验研究

选铁尾矿资源综合利用是重要发展趋势,具有广阔的市场前景。本试验选取聚铝、聚丙烯酰胺、烧碱-Na OH三种絮凝剂对龙岩市某矿业有限公司选铁尾进行矿浆絮凝沉降试验研究。结果表明,该尾矿中细粒级含量较高,自然沉降困难,必须加絮凝剂,使微细颗粒絮凝成团,加速沉降;3#絮凝剂对该尾矿絮凝沉降效果较好;矿浆浓度10%时,3#絮凝剂用量25g/t絮凝沉降效果较好。     

湿法炼锌矿浆絮凝沉降效果研究

针对中性浸出—弱酸浸出—还原浸出—沉铜—赤铁矿法除铁的湿法炼锌过程中的各种矿浆进行絮凝沉降试验,全面分析了影响矿浆絮凝沉降效果的主要因素,包括絮凝剂分子结构、分子量、配制浓度、加入量、加入方式,矿浆温度、pH、固含量、胶体含量等;根据矿浆的性质选择不同种类的絮凝剂,并通过采取一些调控措施,优化矿浆絮凝沉降效果,以取得良好的液固分离效果和经济效益。     

全尾砂物理特性对絮凝沉降性能影响规律的研究

随着浅部矿产资源的日益枯竭,矿山开采深度逐渐增加,而深部开采环境非常复杂且开采难度更大,加之我国对环境保护工作的高度重视,充填采矿法逐渐成为我国矿山首选的采矿方法.为研究尾砂物理特性对絮凝沉降性能的影响规律,开展了粒级组成、比重对尾砂沉降效果影响的静态絮凝沉降试验.研究结果表明:尾砂的中值粒径与沉降速度、底流浓度成正相...     

基于静态沉降试验的全尾砂浓密技术参数预测

为了研究全尾砂浆浓密技术参数与尾砂物理性质之间的定量关系,对9个金属矿山的全尾砂进行了静态沉降试验。首先测定了这9个金属矿山全尾砂的粒径组成和密度大小,然后对这9个金属矿山的全尾砂分别进行了絮凝沉降试验。试验结果表明：料浆的底流浓度和沉降试验所需絮凝剂用量仅与尾砂的粒径有关,而与尾砂的密度无关,尾砂粒径越粗,底流浓度越高,试验所需絮凝剂用量就越少;单位面积尾砂通过量与尾砂粒径和密度均有关系,尾砂粒径和密度越大,固体通量越大;进一步回归分析得到了全尾砂粒径组成和密度大小与底流浓度、固体通量的关系方程。将计算结果与试验结果进行对比分析,发现预测值与试验值相差很小,证明本研究推导的关系方程方便可行,具有很好的推广应用价值。     

STUDY OF THE SETTLING OF TINCAL MINERAL PARTICLES IN DIFFERENT FLUID MEDIA

The aim of this study is to investigate the behavior and velocity ratio of tincal particles in different fluid media containing clay minerals, so that the diversion of tincal particles into slime product or not can be estimated. Tests were carried out using a settling unit and parameters such as clay content of the pulp and dissolved tincal concentration were investigated. Test results were evaluated by measuring the particle-size distribution in the settled product at the end of predefined durations. Average particle size of the settling product at the end of 8 min was observed to be 35 µm at 5% solids ratio by weight in the pulp; however, it was 55 µm at 20% solids ratio by weight. On the other hand, the presence of clay in the fluid medium was observed to directly affect the settling rate of the particles. In the suspension containing 100 g/l of clay and 5% of tincal, particle size of the settling fraction was 55 µm at the end of 8 min, which well compared to 35 µm in the clay-free suspension. The classification medium that contained considerable amounts of clay acted as a heavy and viscous medium and it was determined that fine tincal particles were lost into the tailings during the classification processes in K?rka Tincal Concentrator.     

Heavy Metal and PAH Concentrations in Highway Runoff Deposits Fractionated on Settling Velocities

The correlation between settling velocity and associated pollutant concentrations is of major importance for best management practice in designing, redesigning, or evaluation of the efficiency of existing pond facilities for retaining unwanted pollutants. The prospect of this note is to state the relationship between the settling velocity of the runoff particles and the corresponding metal and polyaromatic hydrocarbon (PAH) concentration directly instead of dealing with two unknowns—the density and the shape of a single particle fraction in a settling velocity calculations. The measurements show that the highest cadmium, chromium, zinc, and nickel concentrations is associated with the most slowly falling particles and the lowest concentration associated within the faster falling fraction. This tendency is not clear for some of the sediments due to high content of organic matter and clearly not for lead and copper and there is no significant correlation between PAH concentration and settling velocity. The largest mass of metals and PAH within each pond can be found on the particle fraction with a settling velocity of 5.5–2.5 mm/s.     

全尾砂无耙深锥稳态浓密性能分析

结合沉降和压滤实验, 对脱水性能数据进行曲线拟合获得连续网状结构形成浓度、压缩屈服应力和干涉沉降系数, 引入Usher提出的稳态浓密性能预测算法, 建立了无耙深锥浓密模型, 分析了絮凝剂单耗、底流中固相的体积分数、泥层高度等对固体通量和固体处理能力的影响规律.研究结果表明: 絮凝剂添加量对沉降区域影响大于压密区域, 20 g·t-1时浓密性能较好, 底流中固相的体积分数越大固体通量越小; 在沉降区域, 固体通量仅与浓度有关, 不受泥层高度影响; 在压密区域, 固体通量为浓度与泥层高度的方程; 模型参数范围内, 当泥层高度 < 3.5 m时, 固体处理能力为浓度与泥层高度的方程, 当泥层高度>3.5 m时, 固体处理能力与固体通量随底流中固相的体积分数变化规律一致.      

基于上澄清液浊度的超细尾砂絮凝沉降试验

为解决现有超细尾砂浓密沉降试验不考虑上层清液浊度的问题,提出了一种超细尾砂浓密沉降的絮凝剂优选方法。以某萤石矿超细尾砂为研究对象,以预制尾砂浆浓度、絮凝剂类型和絮凝剂掺量作为因变量,测试不同沉降时间下上澄清液浊度,并综合考虑沉降速度和絮凝剂成本,获得不同预制尾砂浆浓度下的最佳絮凝剂类型和掺量。试验结果表明：当预制尾砂浆浓度分别为5%、8%、11%和14%时,最佳絮凝剂类型分别为1 800万、1 600万、1 600万和1 200万阴离子聚丙烯酰胺,最佳絮凝剂掺量分别为15,25,30,30 g/t。试验结果为该矿山的超细尾砂浓密沉降工程参数提供了依据。