改性生物质作为型煤黏结剂的研究

探讨了用NaOH改性生物质秸秆作为型煤黏结剂的可行性,考察了NaOH溶液浓度对生物质改性的影响以及生物质添加量、无机物(MgO和MgCl2)添加量对型煤机械强度、防水性能和着火温度的影响。研究结果表明,NaOH改性液的质量分数为1.0%~2.0%时,制得的生物质型煤有较高的机械强度;生物质添加量在2%~20%时,随生物质添加量的增加,机械强度增加,着火温度降低,但防水性较差;而在生物质型煤中加入适量无机黏结剂后,型煤有很高的浸水强度,表现出优越的防水性能。     

NaOH改性生物质做为型煤粘结剂的成型研究

探讨了NaOH溶液改性生物质秸秆作为型煤粘结剂的可行性。实验研究了NaOH溶液浓度以及生物质种类对型煤机械强度的影响,并采用显微镜、SEN和能谱分析了生物质型煤的成型机理。微观结构分析表明改性生物质具有粘结作用;碱液浓度与纤维的降解程度成正比;生物质纤维的降解程度直接影响其制得型煤的机械强度。结果表明,1％NaOH溶液改性的稻草秸秆具有较好的粘结性,所制备的型煤机械强度较好。     

改性钢渣微粉/麦秸秆纤维/PVC复合材料性能

将钢渣微粉(SSM)、麦秸秆纤维(WSF)作为填料,通过挤出成型工艺制得聚氯乙烯(PVC)基复合材料,分别研究了不同配比(0∶10、1∶9、2∶8、3∶7、4∶6)的改性钢渣微粉和麦秸秆纤维对复合材料的力学性能、吸水特性、尺寸热稳定性能的协同作用以及微观形貌的影响。结果表明,钢渣微粉经偶联剂改性后,分散性及与PVC基体的相容性得到改善,制得的复合材料力学性能较好,拉伸强度、弯曲强度、弯曲模量、冲击强度分别提升9.8%、5.45%、13.10%、2.95%。随改性钢渣微粉/麦秸秆纤维配比的增加,复合材料的力学性能先上升后下降,其综合力学性能在配比为3∶7时,达到最优。材料的拉伸强度、弯曲强度、弯曲模量、冲击强度分别为16.67%、20.76%、4.64%、34.41%;吸水率及吸水厚度膨胀率均明显下降,分别为7.19%和4.74%,综合吸水特性在配比为3∶7时,达到最佳;尺寸热稳定性逐渐下降,当改性钢渣微粉/麦秸秆纤维配比从0∶10增加到4∶6时,复合材料的热膨胀系数LTEC值增加了26.31%。     

两种褐煤无粘结剂成型特性的对比研究

实验研究了呼伦贝尔褐煤和印尼褐煤的成型特性,分析了成型压强、粒径配比、水分、氧化、褐煤煤种等因素对型煤强度的影响,型煤强度随成型压强的增大而增大,不同煤种最佳粒径配比不同,最佳水分范围为12%¹5%,氧化煤制型煤的强度高于原煤。     

生物质型煤优化配比研究

原煤选用无烟煤,生物质选用玉米秸秆,黏结剂选用黄土,制备生物质型煤.以挥发分和发热量为指标,参考以往对生物质型煤优化配比方面的研究,结合"实验优化设计与分析"方法自身的特点,采用二元二次回归正交组合设计方法研究生物质型煤的配比,得到了实验指标与各组分之间的回归方程,并求出了优化配比.研究所得的优化配比对生物质型煤的生产具有实际意义.     

氢氧化钠水解小麦秸秆制备型煤黏结剂的研究

为改善型煤燃烧性能,提高农作物小麦秸秆利用率,用NaOH降解的小麦秸秆制备了生物质型煤黏结剂。通过正交实验,制备不同实验条件下的型煤黏结剂,并测定所制型煤的抗压强度,得到型煤黏结剂的最佳制备条件:固水比1∶30,Na OH质量分数为4%,反应温度为90℃,恒温水浴中加热4 h,固硫剂添加量为1.0 g。在此条件下制备的黏结剂中添加质量分数2%聚乙烯醇,经过型煤抗压强度测试,结果显示:添加聚乙烯醇后,黏结剂抗压强度提高;所制型煤的灰分7.1%～8.4%,挥发分27.1%～28.4%,黏结指数10.835～11.796,弹筒发热量28.453 MJ/kg～30.589 MJ/kg。     

城郊选煤厂无烟煤制作生物质型煤的试验研究

采用城郊选煤厂生产的无烟煤,外加玉米秸秆以及一定量的粘结剂制备生物质型煤,通过测量该型煤的抗压强度、跌落强度、防水性能和热稳定性,找出了适于用作锅炉型煤的最佳配方。     

煤与牛粪生物质混合成型的研究

为了解决牛粪的利用问题,利用牛粪自有的木质素、纤维素、半纤维素等的黏结作用,将牛粪与煤经过中低压型煤成型机压制成型。研究了黏结剂与原料性质对生物质型煤强度的影响。结果表明:随着黏结剂添加量的增加,型煤强度逐渐增加,当黏结剂添加量超过10%时,型煤强度增加幅度逐渐变缓,黏结剂添加量不宜超过15%;随着无机黏结剂配比的增加,型煤强度先快速增大后缓慢降低,当黏结剂配比为5%有机黏结剂+6%无机黏结剂时,型煤强度最高;随着煤样粒度的减小,牛粪湿度的增加,型煤强度逐渐增加。最后分析了牛粪添加量对型煤燃烧性能的影响,说明生物质添加量越多,型煤初期燃烧速度越快,生物质添加量由20%增加到80%时,型煤燃烧速度变化不大。     

活化污泥基黏结剂制备型煤型焦试验研究

为实现粉煤的综合利用,以城市污泥为黏结剂的基础组分,采用化学方法活化,利用粉煤成型技术制备型煤,对工艺条件进行研究,考查了成型压力、污泥含量、干燥时间对型煤冷压强度和湿压强度的影响,确定了最佳工艺条件。结果表明,污泥含量为12%、成型压力12 MPa、干燥时间8 h时,制得型煤的冷压强度为1 522.5 N,落下强度为97.7%,型煤600℃干馏2 h制得型焦的强度、灰分、挥发分、发热量等主要指标均达到《陕西省地方洁净型煤技术标准》。利用活化污泥可制备出适用于工业生产的洁净型煤。     

改性花生壳型煤的性能研究

以不同粒度的神木粉煤为原料,1.5%和2.5%NaOH改性花生壳为粘结剂,通过干法冷压成型制备型煤,测定型煤的抗压强度及落下强度,并采用红外光谱和扫描电镜对2.5%NaOH改性花生壳型煤进行表征。结果表明:2.5%NaOH改性花生壳型煤的性能较1.5%NaOH改性花生壳型煤更优越;神木粉煤粒度为3～1.5 mm时,2.5%NaOH改性花生壳型煤的性能最佳,其抗压强度和落下强度分别为2 958.05 N/个和70.29%;粉煤粒度为3～1.5 mm时与粘结剂粒径搭配最佳,表面分形维数相当,粘结剂与粉煤较充分混匀,结合最为紧密。     

Many Drugs of Abuse May Be Acutely Transformed to Dopamine,Norepinephrine and Epinephrine In Vivo

It is well established that a wide range of drugs of abuse acutely boost the signaling of the sympathetic nervous system and the hypothalamic–pituitary–adrenal (HPA) axis, where norepinephrine and epinephrine are major output molecules. This stimulatory effect is accompanied by such symptoms as elevated heart rate and blood pressure, more rapid breathing, increased body temperature and sweating, and pupillary dilation, as well as the intoxicating or euphoric subjective properties of the drug. While many drugs of abuse are thought to achieve their intoxicating effects by modulating the monoaminergic neurotransmitter systems (i.e., serotonin, norepinephrine, dopamine) by binding to these receptors or otherwise affecting their synaptic signaling, this paper puts forth the hypothesis that many of these drugs are actually acutely converted to catecholamines (dopamine, norepinephrine, epinephrine) in vivo, in addition to transformation to their known metabolites. In this manner, a range of stimulants, opioids, and psychedelics (as well as alcohol) may partially achieve their intoxicating properties, as well as side effects, due to this putative transformation to catecholamines. If this hypothesis is correct, it would alter our understanding of the basic biosynthetic pathways for generating these important signaling molecules, while also modifying our view of the neural substrates underlying substance abuse and dependence, including psychological stress-induced relapse. Importantly, there is a direct way to test the overarching hypothesis: administer (either centrally or peripherally) stable isotope versions of these drugs to model organisms such as rodents (or even to humans) and then use liquid chromatography-mass spectrometry to determine if the labeled drug is converted to labeled catecholamines in brain, blood plasma, or urine samples.     

ICP-MS法测定地球化学样品中As、Cr、Ge、V等18种微量痕量元素的研究

建立了测定地球化学样品中包括As、Cr、Ge、V等18种微量、痕量元素的ICP-MS方法。地化试样用HF-HNO3混酸分解后,以1 1 HNO3溶解干渣。由于制样不使用盐酸,避免了Cl对As、Cr、Ge、V的质谱干扰。用国家一级地球化学标准物质GBW 07309制备溶液优化仪器工作参数,并用于校准。方法测定限(6s)为:0.007~6.4μg/g,精密度(RSD%,n=12)为:29%~9.4%,经过国家一级地球化学标准物质的分析验证,结果与标准值吻合。方法已应用于国土资源调查的试样分析。     

基于ATRP法制备的触角状亲水性羟胺树脂的吸硼性能的研究

以大分子引发剂氯乙酰化聚苯乙烯微球(PS-acyl-Cl)经原子转移自由基聚合(ATRP)法引发丙烯酰胺(AM)和甲基丙烯酸缩水甘油酯(GMA)单体的共聚接枝,制得一种触角状亲水性环氧载体(PS-acyl-g-P(AM-co-GMA)),再经二乙醇胺(DEA)的环氧基开环胺化反应,得到一种含多个-NCH2CH2OH螯合配基的多齿-五元螯合环的触角状亲水性羟胺树脂(PS-acyl-g-P(AM-co-GMA)-DEA)。将此树脂用于硼吸附研究,结果表明,PS-acyl-g-P(AM-co-GMA)-DEA树脂对硼的吸附满足Langmuir方程,为单分子层吸附;饱和吸附量约为37.7 mg·g-1,且树脂5 min即可达到吸附平衡,与其它已报道的吸硼树脂相比,该树脂具有更高的吸附量和吸硼速率。吸附动力学研究表明,树脂吸附硼的过程主要由颗粒扩散过程控制。重复使用5次后该树脂的吸附量基本不变,解吸率均在90%以上,重复使用性能良好。     

工业评述2001～2002年国外塑料工业进展

收集了2001年7月到2002年6月有关国外塑料工业的相关期刊资料,介绍了2001年到2002年国外塑料工业的发展情况,提供了世界各地域塑料原材料的产量及构成比,日本、美国、加拿大、德国、法国、比利时、墨西哥、芬兰、西班牙等国家的树脂产量、消费量及增长率,以及日本、西欧、北美等地区的不同品种塑料原料消费量和增长率统计.按通用热塑性树脂(聚乙烯、聚丙烯、聚苯乙烯、聚氯乙烯、ABS树脂)、工程塑料(尼龙、聚碳酸酯、聚甲醛、热塑性聚酯、聚苯醚)、通用热固性树脂(酚醛、聚氨酯、不饱和树脂、环氧树脂)、特种工程塑料(聚苯硫醚、液晶聚合物、聚醚醚酮)不同品种的顺序,对树脂的产量、消费量及合成工艺、产品应用开发、树脂品种的延伸及应用的进一步扩展等有关技术作了详细的介绍.     

工业生产中物位测量的探讨与研究

在工业生产中常常会遇到常温,常压和一般介质的液位,料位和界面的测量,也会遇到高温,高压,易燃易爆,腐蚀性较强的液位,料位和界面的测量。在工业生产中物位测量有接触式和非接触式测量。但应根据生产工况及技术要求来合理选用。     

Confocal microscope—A valuable tool for examining wood-coating interface

The suitability of confocal laser scanning microscopy (CLSM) in examining a wood-coating interface was evaluated using a clear coating system. A comparison of the images of the wood-clear coating interface obtained using CLSM and light microscopy (LM) showed a marked superiority of CLSM in revealing the details of the physical nature of the interaction between the clear coating and the wood cell walls in the surface layer. The most distinct advantage of CLSM was in its ability to clearly resolve penetration of the coating into very fine cracks in cell walls, details not obtainable with LM. The information presented here demonstrates that CLSM has the potential to greatly enhance our understanding of the physical aspects of an interaction between the wood and coating at the interface.     

不同结构充油溶聚丁苯橡胶/炭黑/白炭黑复合材料的结构与性能

研究了炭黑/白炭黑填充的苯乙烯/乙烯基含量不同的充油溶聚丁苯橡胶(HPR 757 D和Buna VSL 5025-2 HM)的物理机械性能及动态力学性能,观察了填料在硫化胶中的微观分布情况。结果表明,炭黑与白炭黑相互镶嵌地分布在橡胶基质中,形成交织的填料网络。高苯乙烯基含量的HPR 757 D的拉伸强度、撕裂强度及耐磨性能优异,滚动阻力较小,填料与橡胶间的结合力强,填料的分散性较好。用白炭黑等量取代炭黑可以提高胶料的拉伸强度,降低其动态压缩温升。但炭黑/白炭黑的最佳配比与橡胶基质的分子结构有关,主链双键含量越高,白炭黑的用量也随之增多。