改性环氧丙烯酸酯胶粘剂的合成与性能 总被引:3,自引:0,他引:3
本文研究了环氧丙烯酸酯的改性,采用双马来酰亚胺、环氧树脂、丙烯酸酯、改性剂为主要原料合成了改性环氧丙烯酸酯胶粘剂.运用IR、DSC等分析测试手段研究了该胶粘剂的固化行为。运用TGA、DTA等分析手段研究了该胶粘剂固化后的热稳定性.同时,用改性环氧丙烯酸酯胶粘剂制得了聚酰亚胺薄膜挠性印刷电路基板并测试了有关性能. 相似文献
3.
4.
5.
6.
7.
提高环氧胶粘剂耐热性的研究进展 总被引:2,自引:0,他引:2
介绍了耐热环氧胶粘剂的主要性能特点,论述了近年来在提高环氧胶粘剂耐热性方面所采用的方法,同时指出了耐热环氧胶粘剂的研究发展方向。 相似文献
8.
利用2,2-双[4-(4-氨基苯氧基)苯1丙烷及偏苯三酸酐合成聚酰亚胺齐聚物,并用此齐聚物改性环氧树脂胶粘剂。使用红外光谱、凝胶化时间、接触角和拉伸剪切强度对改性胶粘剂性能进行表征。结果表明,齐聚物的加入对环氧树脂固化反应具有促进作用;当100质量份环氧中加入16份齐聚物时,胶粘剂力学性能最佳;当齐聚物用量为20份时;胶粘剂表面能最高。 相似文献
9.
介绍了一种研制的室温固化、耐高温、耐低温环氧有机硅胶粘剂。通过对胶粘剂的剪切强度分析,探讨了原料配比,偶联剂等因素对环氧有机硅胶粘剂力学性能的影响。研究表明,增韧剂在胶粘剂中含量适当时(质量比25%,能与固化剂充分反应,有机硅与环氧树脂也能获得较好的相溶性,制备的环氧有机硅胶粘剂的综合性能较优;硅烷偶联剂能改善胶膜界面层的胶接强度,提高环氧有机硅胶粘剂的剪切强度。 相似文献
10.
11.
The durability of aluminum and titanium adherends, plasma-sprayed with polymeric coatings, and bonded with an epoxy and a polyimide adhesive has been investigated. Organic-polymeric coatings were plasma-sprayed using epoxy, polyester, polyimide, and cyanate ester components. Durability was investigated using a wedge-type specimen by exposing the specimens to an environmental cycle that included low temperature, high relative humidity at elevated temperature, high temperature at atmospheric pressure in air, high temperature in a vacuum, and room temperature. The systems exhibiting durability comparable with that for adherends treated using standard solution methods, included aluminum or titanium coated with a bis-maleimide/cyanate ester (B-CE) or a bis-maleimide-LaRC TPI-1500® (B-TPI) mixture and bonded with an epoxy or a polyimide adhesive. For these B-CE- and B-TPI-coated specimens, failure during exposure to the environmental cycle occurred in the adhesive, indicating a favorable adherend/plasma-sprayed coating interaction. 相似文献
12.
Seong Hun Kim Dong Woo Lee Kyung‐Ho Chung Jae Ki Park Jae‐Yun Jaung Sung Hoon Jeong 《应用聚合物科学杂志》2002,86(4):812-820
An improvement in the adhesion strength of polyimide/epoxy joints was obtained by (1) introducing a functional group on the polyimide surface, (2) improving the mechanical properties of the epoxy adhesive, (3) increasing the curing temperature, and (4) using polyamic acid as an adhesion‐promoting layer. The functional group on polyimide was introduced via treatment with aqueous KOH. An adhesion‐promoting layer was formed by spin coating polyamic acid onto a modified polyimide surface. The maximum adhesion strength of the polyimide/epoxy joint was obtained using polyamic acid as both the adhesion‐promoting layer and as the curing agent. The surface energy of the modified polyimide was examined using contact angle measurements and Fourier transform infrared spectroscopy, and the peel strength was determined by the T‐peel method. The peeled surfaces were analyzed using scanning electron microscopy and X‐ray photoelectron spectroscopy.© 2002 Wiley Periodicals, Inc. J Appl Polym Sci 86: 812–820, 2002 相似文献
13.
14.
15.
16.
A two-component coupling agent layer on copper, produced by immersion of copper in poly(4-vinylimidazole) solution and then in cystamine solution, showed better anticorrosive performance and higher adhesive strength for epoxy resin and polyimide than each single component even at high temperature. 相似文献
17.
The surface preparation of stainless steel of identified martensitic structure has been studied in relation to the strength of adhesive bond with an epoxy-phenoiic, an epoxy and a polyimide adhesive. Attention has been given to replacing the inefficient mechanical removal of deposited carbon (“smut”) by chemical means. Seven different chemical treatments by acids or acid combinations were tried. Hydrofluoric or sulphuric acids modified by nitric or oxalic acids respectively were most satisfactory followed by chromic acid desmutting. 相似文献