防老剂KY310和防老剂SPT的应用对比

吉林石化公司丁苯橡胶装置一直使用防老剂SPT生产丁苯橡胶SBR1502,在后处理生产过程中防老剂SPT是影响废水COD的主要因素之一。在当前环保压力日益增加的情况下,使用新型防老剂势在必行。本文对比考察了2种防老剂的热空气老化防护性能、对丁苯橡胶SBR1502性能的影响及对后处理废水的影响。实验结果表明,防老剂KY310热空气防老化性能优于防老剂SPT,对丁苯橡胶性能没有明显影响,且大大降低了污水的COD。     

两种胺类防老剂对丁苯橡胶性能影响的对比研究

对比研究了两种常用的胺类防老剂N-(1,3-二甲基丁基)-N′-苯基对苯二胺(防老剂4020)和N,N′-二甲苯基对苯二胺(防老剂DTPD)对丁苯橡胶(SBR)性能的影响。结果表明,两种防老剂对胶料的焦烧时间和硫化时间影响不大;加入一定量的防老剂,硫化胶的拉伸强度和定伸应力略微下降,扯断伸长率和撕裂强度增加;在100℃×72h热空气老化条件下,含防老剂4020的硫化胶的耐热空气老化性能更加优异;添加一定用量的防老剂对SBR硫化胶动态力学性能影响不大;防老剂4020和防老剂DTPD可以明显提高SBR硫化胶的热稳定性;防老剂DTPD与防老剂4020相比,其硫化胶试片喷霜不明显;综合来看,当防老剂4020用量为1.5份时,SBR硫化胶综合性能最优。     

热空气老化对二烯类橡胶磨耗性能的影响规律研究

以丁苯橡胶（SBR）、顺丁橡胶（BR）和天然橡胶（NR）为研究对象,并以它们的基础配方为依据,研究了热空气老化对不同种类橡胶阿克隆磨耗和DIN磨耗性能的影响规律。研究结果表明,热空气老化对这3种橡胶的阿克隆和DIN磨耗性能的影响规律不同。对阿克隆磨耗性能来说,随老化时间的延长,丁苯橡胶和顺丁橡胶的耐磨性能提高,而天然橡胶的耐磨性随老化时间的延长而明显下降。对DIN磨耗性能来说,无论是丁苯橡胶、顺丁橡胶还是天然橡胶,它们的耐DIN磨耗性能都随着老化时间的延长而逐渐降低。防老剂的加入可以提高橡胶的耐阿克隆磨耗性能,但对DIN磨耗性能的影响却很小。     

环保型丁苯橡胶与传统丁苯橡胶性能对比

对比考察了环保型丁苯橡胶与传统丁苯橡胶的相对分子质量及其分布、微观结构、混炼胶的硫化特性、硫化胶的物理机械性能及加工性能,结果表明,环保型丁苯橡胶SBR 1500 E与SBR 1500、环保型丁苯橡胶SBR 1502 E与SBR 1502及环保型丁苯橡胶SBR 1712 E与SBR 1712的相对分子质量及其分布、分子...     

炭黑对丁苯橡胶耐热氧和紫外老化性能的影响

研究了填充不同量炭黑对丁苯橡胶耐热氧和紫外老化性能的影响,测试了各试样的交联密度及物理机械性能,并用扫描电镜观察了其表面形貌.结果表明,丁苯橡胶在热氧老化开始时内部发生了以交联为主的反应,表面氧化缓慢;而在紫外老化开始时表面的变化较大,在老化过程中交联密度出现峰值;热氧和紫外老化120 h后,橡胶的硬度增加,表面变得致密,使热氧和紫外线侵入至橡胶内部变得困难,邵尔A硬度等物理机械性能的变化趋势减缓;炭黑填充量大于20份(质量)时SBR的耐紫外老化性能得到改善,老化360 h后物理机械性能保持率仍然较高,这是因为炭黑对紫外线有很好的屏蔽作用,而炭黑对SBR耐热氧老化性能的影响却相反.     

植物基环保橡胶油在非极性丁苯橡胶中的应用

考察了自制的植物基环保橡胶油(PBRO)对丁苯橡胶(SBR)混炼胶硫化特性及硫化胶物理机械性能、耐热空气老化性能、耐寒性的影响,对比研究了PBRO与石蜡油、环烷油、芳烃油和邻苯二甲酸二辛酯(DOP)对SBR硫化胶性能的影响。结果表明,橡胶油的加入促进了SBR混炼胶的交联,硫化速率加快,且有增塑效果;当橡胶油PBRO的用量为20份时,SBR硫化胶的综合性能较优;当分别添加等量橡胶油时,PBRO和DOP对SBR硫化胶的增塑效果较差,而芳烃油的增塑效果最好,添加PBRO的SBR硫化胶的耐热空气老化性能和热稳定性最好,但物理机械性能和耐寒性能较差,而添加芳烃油的SBR硫化胶的物理机械性能最优,添加石蜡油的SBR硫化胶的耐寒性能最优。     

防老剂DH在轮胎胶料中的应用

研究防老剂DH对NR ,SBR ,BR和NR/SBR并用胶的热空气老化和天候老化的防护作用 ,并与防老剂40 2 0 ,BLE和RD进行对比试验。结果表明 ,在NR ,SBR和BR胶料中 ,对于耐热空气老化性能 ,防老剂DH的防护效果优于防老剂RD和BLE ,劣于防老剂 40 2 0。对于耐天候老化性能 ,防老剂 40 2 0的防护效果最佳 ;在NR和BR胶料中 ,防老剂DH优于防老剂BLE和RD ;在SBR胶料中 ,防老剂DH ,BLE和RD的防护效果相近。防老剂DH对胶料基本无污染。在实际应用配方胶料中 ,用 1 0～ 1 5份防老剂DH替代 2份防老剂BLE或RD可以改善胶料的耐热空气老化和耐天候老化性能 ;如果用 1份防老剂DH替代 2份防老剂RD或BLE ,则分别可降低胶料成本约 17 5或10 7 5元·t- 1 ,具有一定的经济效益     

新型胺类防老剂MC在NBR中的应用

介绍了新型胺类防老剂MC的化学结构及性能,研究了MC和其他胺类防老剂对NBR硫化特性及物理机械性能、耐热空气老化及耐臭氧老化性能的影响。结果表明,加入MC可较好地提高NBR的老化性能,可完全替代4010NA等胺类防老剂。     

热空气老化对丁苯橡胶磨耗性能的影响

以乳聚丁苯橡胶1502、溶聚丁苯橡胶T2000R和2557A为研究对象,以丁苯橡胶基础配方为依据,研究了热氧老化对不同结构丁苯橡胶阿克隆磨耗和DIN磨耗性能的影响。结果表明,热空气老化对不同结构丁苯橡胶阿克隆和DIN磨耗性能的影响不同。对于阿克隆磨耗性能,随老化时间的延长,1502硫化胶的耐磨性能提高,T2000R硫化胶的耐磨性能先升高后下降,而2557A硫化胶的耐磨性能随老化时间的延长而下降。对于DIN磨耗性能,1502,T2000R和2557A硫化胶的耐DIN磨耗性能都随老化时间的延长而逐渐降低,1502和T2000R硫化胶的耐磨耗性能随老化时间的延长明显下降,2557A硫化胶的耐磨耗性能下降却很小。加入防老剂可提高丁苯橡胶的阿克隆磨耗性能,但对DIN磨耗性能的影响却很小。     

防老剂D-50在橡胶中的应用试验

利用热空气老化和日光老化的方法,研究了复合型防老剂Ｄ５０对ＮＲ,ＳＢＲ和ＣＲ的耐热空气老化和光老化性及屈挠性能的影响,并与防老剂Ｄ进行对比。实验表明,应用防老剂Ｄ５０对硫化胶性能无不利影响,且防老化性能优于防老剂Ｄ。     

受阻酚抗氧剂在SBR/HAF混炼胶中的应用

研究了抗氧剂GM、抗氧剂264和抗氧剂2246对SBR/HAF混炼胶的硫化特性、力学性能和耐热老化性能的影响,并通过TG分析表征混炼胶的耐热稳定性.结果表明,与抗氧剂264和抗氧剂2246相比,添加抗氧剂GM的混炼胶具有更好的防焦烧性能,更高的力学性能以及更优异的耐热老化性能.TG分析表明,在三种抗氧剂中,加入抗氧剂G...     

Accelerated ageing of styrene–butadiene rubber nanocomposites stabilized by phenolic antioxidant

Organoclay‐reinforced styrene butadiene rubber (SBR) was subjected to accelerated thermo‐oxidative ageing and its physical properties were compared to the virgin material. The oxidative degradation was studied in absence and in presence of a phenolic antioxidant. Ageing test was conducted at 70°C for 7, 14, and 28 days. Then, mechanical and dynamomechanical properties were measured and related to chemical and morphological changes. The elongation at break of samples without antioxidant was found to decrease whereas the modulus and hardness of SBR and its nanocomposite increased with ageing time. Also, the storage modulus and the glass transition temperature increased monotonously with time. These results were attributed to main chain scission and crosslinks formation. The ageing mechanism, determined by infrared spectroscopy, was independent on the nanoclay presence. When the antioxidant was added, thermo‐oxidative stability markedly increased. The retention in the physical properties upon ageing 28 days suggests that the addition of 0.5–1 phr antioxidant was sufficient to provide stability of SBR nanocomposite with minimum loss in physical properties. Also, SEM images showed no signs of degradation; this demonstrates that the antioxidant protects the surface from oxidative degradation. Moreover, infrared spectroscopy suggests that nanoclay could protect the elastomer surface from deterioration. POLYM. COMPOS., 35:334–343, 2014. © 2013 Society of Plastics Engineers     

TPI/HVBR共混物用于胎面胶的研究

在传统的胎面胶配方NR／SBR1500（并用此为60／40）和SBR1712／SBR1500（并用比为60／40）的基础上，采用高反式－1，4－聚异成二烯（TPI）和／或高乙烯基聚丁二烯橡胶（HVBR）取代或部分取代SBR1500，研究共混物的物理性能和动态粘弹性。结果表明，添加了TPI和HVBR的胎面胶，其力学性性能可满足使用要求，定伸应力和抗屈挠疲劳性较大提高，滚动阻力和动态生势明显降低，而抗湿滑性仍有较高的保持率，达到了滚动阻力和抗湿润性能的良好兼备。相对而言，NR／TPI／HVBR并用胎面胶具有量的滚动阻力和生热，而SBR／TPI／HVBR并用胎面胶具有更好的抗湿滑性、抗屈挠疲劳性和耐磨性。     

Effect of Some Polymeric Phenolic Antioxidants on the Properties of SBR Vulcanizates

Polymeric antioxidants can be useful in the protection of styrene-butadiene rubber (SBR) against thermal oxidative aging as an alternative to the low molecular weight ones, which migrate out of the rubber articles. Three polymeric compounds were prepared and incorporated into SBR mixes to be evaluated as antioxidants in comparison with the commercial antioxidant, N-isopropyl-N′-phenyl-p-phenylenediamine (IPPD). The rheometric characteristics of the produced SBR mixes were measured and the cure time was determined. The mechanical, swelling, extraction, and compression properties were studied. The results obtained revealed that poly(4-mercaptophenyl)acrylamide has superior effect in the protection of SBR articles against thermal oxidative ageing.     

抗氧剂GM对SBR/HAF共混胶耐热老化性能的影响

研究了抗氧剂GM对SBR/HAF共混胶的硫化特性、力学性能和耐热老化性能的影响,并通过TG分析表征共混胶的耐热稳定性.结果表明,抗氧剂GM具有防止焦烧和软化胶料的作用,随着GM用量的增大,共混胶的伸长率和撕裂强度升高,硬度下降.共混胶的耐热老化性能随抗氧剂GM用量增大而提高,GM用量以3份为宜.TG分析表明,加入抗氧剂...     

木质素/蒙脱土复合物在丁苯橡胶中的应用研究

通过絮凝沉降法制备了木质素/蒙脱土复合物(CLM),将其跟丁苯橡胶(SBR)机械共混制备了SBR/CLM复合材料,并对其微观结构、硫化特性、交联密度、力学性能、热氧老化性能以及热稳定性进行研究。结果表明:木质素与蒙脱土的相互作用提高了CLM与SBR相容性;随着CLM用量的增加,焦烧时间与正硫化时间逐渐增加,复合材料的力学性能逐渐增大,老化性能及热稳定性也得到改善。     

黑液-硅藻土共沉物在丁腈橡胶与丁苯橡胶中的应用研究

通过絮凝-酸沉降法制备了一种复合补强剂——黑液-硅藻土共沉物(CLD),将其分别与丁腈橡胶(NBR)和丁苯橡胶(SBR)机械共混制得NBR/CLD与SBR/CLD复合材料。考察了CLD的含量对橡胶复合材料硫化特性、交联密度、力学性能、热氧老化性能以及热性能的影响。结果表明:随着CLD的加入,焦烧时间与正硫化时间逐渐降低,硫化速度逐渐提高;交联密度逐渐增加;力学性能逐渐增强;但老化性能及热性能没有得到改善。     

黑液/高岭土复合物在丁腈橡胶和丁苯橡胶中的应用研究

通过絮凝沉降法制备了一种复合补强剂——黑液/高岭土复合物(CLK),将其分别与丁腈橡胶(NBR)和丁苯橡胶(SBR)共混制备了NBR/CLK与SBR/CLK复合材料。考察了CLK的添加量对橡胶复合材料硫化特性、交联密度、力学性能、热氧老化性能以及热降解性能的影响。结果表明:随着CLK含量的增加,在NBR/CLK复合材料体系中,焦烧时间、正硫化时间和硫化速度指数先增加而后逐渐降低;交联密度和力学性能则逐渐增大;老化性能及热性能没有显著改善。在SBR/CLK复合材料中,焦烧时间、硫化速度指数先增加而后逐渐降低,正硫化时间先减少而后逐渐增加;交联密度和力学性能则逐渐增大;老化性能没有显著改善,但热性能得到了提高。