添加剂在不锈钢着色中的应用

讨论了钼酸盐,锰盐、氧化物、硫酸盐、锌盐、稀土盐等6种添加剂对不锈钢着色膜的影响.采用均匀设计法确定了最佳添加剂含量:6g/L锌盐、8 g/L钼酸盐、5g/L稀土盐、3g/L锰盐.不锈钢表面着色温度降低到55℃,膜层更加均匀,光亮,着色时间也大为缩短,同时降低了能耗.     

热浸镀锌层表面钛盐转化膜研究

利用钛盐成膜工艺在热镀锌层表面获得了色泽光亮、耐蚀性能优良的银白色转化膜层。采用扫描电镜、能谱仪、电化学极化和盐水浸泡方法研究了钛盐转化膜层的表面形貌、元素组成和耐蚀性能。分析了钛盐溶液成分及工艺参数对热镀锌层表面转化膜的耐蚀性能影响。确定的最佳工艺条件为:Ti(SO4)21g/L,H2O260mL/L,pH0.5～1.0,处理温度25～30°C,处理时间10min。热镀锌层经此工艺处理后,耐蚀性能明显提高。     

铝合金锰(Ⅶ)-钛(Ⅳ)系无铬化学转化成膜工艺

以KMnO4和TiOSO4为钝化剂主要成分,研究6063铝合金锰(VII)-钛(IV)系钝化成膜新工艺,考察钝化液成分、温度、pH值、反应时间对成膜过程及膜耐腐蚀性能的影响,并通过正交实验优化工艺方案,分析转化膜的形貌和化学组成,采用化学方法考察化学转化膜的耐蚀性能. 结果表明,最佳钝化液配方为：KMnO4 5 g/L, TiOSO4 2 g/L, NaF 0.05 g/L, ZnSO4 0.3 g/L. 在钝化温度50℃、钝化时间15 min及pH值2.7的最佳工艺条件下,锰(VII)-钛(IV)系钝化工艺制备的化学转化膜为金黄色,膜质量为589 mg/m2,膜主要由O, Mn, Al, Zn, Ti组成. 锰(VII)-钛(IV)系钝化新工艺环境友好,所制化学转化膜耐CuSO4点滴腐蚀性能优于Cr(VI)转化膜,耐人造海水腐蚀能力与Cr(VI)转化膜相近.     

铝材表面制备钼锰钛系化学转化膜的影响因素分析

分析了钼酸铵、高锰酸钾、氟钛酸、氯化钠和氟化铵等因素对铝材表面制备钼锰钛系化学转化膜的影响。最佳的成膜工艺条件为:钼酸铵10g/L,高锰酸钾1.0g/L,氟钛酸(45%)3.0g/L,氯化钠0.6g/L,氟化铵1.0g/L,室温,15min。形成的转化膜致密、均匀,耐蚀性良好。     

锆钛转化膜在镁合金车轮上耐腐蚀的研究

为了提高镁合金车轮表面的耐腐蚀性能,研究了锆钛转化膜在镁合金汽车轮毂上腐蚀性能。采用正交试验方法,研究锆钛转化膜工艺影响因素。转化膜处理后进行环氧粉末涂料喷涂,通过附着力、CASS和FILIFORM试验检查涂层性能。通过正交试验得出最佳转化膜处理工艺方案为:碱洗50 g/L,酸洗5.5 g/L,无铬钝化液40 g/L,封闭0.1 g/L,锆钛转化膜提高了镁合金轮毂表面涂层的附着力和耐腐蚀性。     

LY12铝合金表面钒–钛复合转化膜的制备与耐蚀性研究

为解决单一钒酸盐转化膜表面因存在裂纹而耐蚀性不佳的问题,采用由硫酸氧钛(Ti OSO4)、偏钒酸钠(Na VO3)组成的转化液,在LY12铝合金表面制备出钒–钛复合转化膜。通过中性盐雾(NSS)测试讨论了Ti OSO4和Na VO3质量浓度、时间、温度、p H等工艺条件对转化膜耐蚀性的影响,并通过单因素试验得到了最佳转化条件:Ti OSO4 0.5 g/L,Na VO3 0.4 g/L,p H 4.0,温度25°C,转化时间10 min。用扫描电镜和能谱分析了转化膜的表面形貌及元素组成。结果表明,由O、Ti、V、Al、Mg等元素组成的钒–钛复合转化膜无裂纹。LY12铝合金经转化处理后,在3.5%Na Cl溶液中的腐蚀电位较转化前正移56 m V,腐蚀电流密度减小约1/5,耐盐雾时间达到91 h,耐蚀性得到显著提高。     

EDTA对两种镁合金化学转化膜性能的影响

研究了EDTA对镁合金锡酸盐、磷酸盐化学转化膜性能的影响。采用扫描电镜观察了两种化学转化膜的表面形貌,采用X射线衍射仪分析了两种化学转化膜的成分,并采用电化学工作站测试了两种化学转化膜的耐蚀性。结果表明:加入0.3g/L EDTA的锡酸盐化学转化膜晶粒细小、均匀,堆积十分紧密,无缝隙;加入2.0g/L EDTA的磷酸盐化学转化膜结晶细小、均匀,结构致密。锡酸盐化学转化膜的相组成为Mg、Al12Mg17和MgSn(OH)6;磷酸盐化学转化膜的相组成为Mg、Al12Mg17和Mn2Mg(PO4)2。通过对比可知,加入EDTA对锡酸盐化学转化膜耐蚀性的影响更为显著。     

不同稀土元素对镁合金钼酸盐转化膜耐蚀性的影响

研究了硝酸铈、氧化钕和硝酸镧对镁合金钼酸盐转化膜耐蚀性的影响。通过单因素试验,得出添加氧化钕的镁合金钼酸盐化学转化的最佳配方为:钼酸铵25g/L,硝酸钠1.5g/L,硝酸锰1.0g/L,柠檬酸1.5g/L,氧化钕0.4g/L,pH值5,温度60℃,时间30min。最佳配方下得到的膜层均匀平滑,结晶颗粒细小、分布均匀、大小均等。添加氧化钕的钼酸盐转化膜的自腐蚀电流密度最低,耐蚀性最好。     

不同添加剂对镁合金锡酸盐转化膜耐蚀性的影响

研究了不同添加剂对镁合金锡酸盐转化膜耐蚀性的影响。通过单因素试验,得出了镁合金锡酸盐化学转化的最优配方:锡酸钠25 g/L,焦磷酸钠35 g/L,乙酸钠7 g/L,氢氧化钠7 g/L,EDTA 0.3 g/L,温度70℃,时间80 min。5种添加剂中,EDTA对镁合金锡酸盐转化膜耐蚀性的提高效果最显著。最优配方下得到的锡酸盐转化膜晶粒细小、均匀,堆积十分紧密,无缝隙,其相组成为Mg、Al_(12)Mg_(17)和MgSn(OH)_6。     

铝材表面制备钼锰钛系化学转化膜的研究

通过正交试验优选出一种在铝材表面形成金黄色化学转化膜的钼锰钛系表面处理工艺:钼酸铵12 g/L,高锰酸钾0.8 g/L,45%(质量分数)氟钛酸3.2 g/L,氯化钠0.6 g/L,氟化铵1.2 g/L,温度25°C,成膜时间10 min。以该处理工艺得到的转化膜在抗蚀性、与涂层的附着力和冲击强度方面达到或优于传统含铬钝化膜,可与各种涂装工艺配合使用。     

Many Drugs of Abuse May Be Acutely Transformed to Dopamine,Norepinephrine and Epinephrine In Vivo

It is well established that a wide range of drugs of abuse acutely boost the signaling of the sympathetic nervous system and the hypothalamic–pituitary–adrenal (HPA) axis, where norepinephrine and epinephrine are major output molecules. This stimulatory effect is accompanied by such symptoms as elevated heart rate and blood pressure, more rapid breathing, increased body temperature and sweating, and pupillary dilation, as well as the intoxicating or euphoric subjective properties of the drug. While many drugs of abuse are thought to achieve their intoxicating effects by modulating the monoaminergic neurotransmitter systems (i.e., serotonin, norepinephrine, dopamine) by binding to these receptors or otherwise affecting their synaptic signaling, this paper puts forth the hypothesis that many of these drugs are actually acutely converted to catecholamines (dopamine, norepinephrine, epinephrine) in vivo, in addition to transformation to their known metabolites. In this manner, a range of stimulants, opioids, and psychedelics (as well as alcohol) may partially achieve their intoxicating properties, as well as side effects, due to this putative transformation to catecholamines. If this hypothesis is correct, it would alter our understanding of the basic biosynthetic pathways for generating these important signaling molecules, while also modifying our view of the neural substrates underlying substance abuse and dependence, including psychological stress-induced relapse. Importantly, there is a direct way to test the overarching hypothesis: administer (either centrally or peripherally) stable isotope versions of these drugs to model organisms such as rodents (or even to humans) and then use liquid chromatography-mass spectrometry to determine if the labeled drug is converted to labeled catecholamines in brain, blood plasma, or urine samples.     

ICP-MS法测定地球化学样品中As、Cr、Ge、V等18种微量痕量元素的研究

建立了测定地球化学样品中包括As、Cr、Ge、V等18种微量、痕量元素的ICP-MS方法。地化试样用HF-HNO3混酸分解后,以1 1 HNO3溶解干渣。由于制样不使用盐酸,避免了Cl对As、Cr、Ge、V的质谱干扰。用国家一级地球化学标准物质GBW 07309制备溶液优化仪器工作参数,并用于校准。方法测定限(6s)为:0.007~6.4μg/g,精密度(RSD%,n=12)为:29%~9.4%,经过国家一级地球化学标准物质的分析验证,结果与标准值吻合。方法已应用于国土资源调查的试样分析。     

基于ATRP法制备的触角状亲水性羟胺树脂的吸硼性能的研究

以大分子引发剂氯乙酰化聚苯乙烯微球(PS-acyl-Cl)经原子转移自由基聚合(ATRP)法引发丙烯酰胺(AM)和甲基丙烯酸缩水甘油酯(GMA)单体的共聚接枝,制得一种触角状亲水性环氧载体(PS-acyl-g-P(AM-co-GMA)),再经二乙醇胺(DEA)的环氧基开环胺化反应,得到一种含多个-NCH2CH2OH螯合配基的多齿-五元螯合环的触角状亲水性羟胺树脂(PS-acyl-g-P(AM-co-GMA)-DEA)。将此树脂用于硼吸附研究,结果表明,PS-acyl-g-P(AM-co-GMA)-DEA树脂对硼的吸附满足Langmuir方程,为单分子层吸附;饱和吸附量约为37.7 mg·g-1,且树脂5 min即可达到吸附平衡,与其它已报道的吸硼树脂相比,该树脂具有更高的吸附量和吸硼速率。吸附动力学研究表明,树脂吸附硼的过程主要由颗粒扩散过程控制。重复使用5次后该树脂的吸附量基本不变,解吸率均在90%以上,重复使用性能良好。     

工业评述2001～2002年国外塑料工业进展

收集了2001年7月到2002年6月有关国外塑料工业的相关期刊资料,介绍了2001年到2002年国外塑料工业的发展情况,提供了世界各地域塑料原材料的产量及构成比,日本、美国、加拿大、德国、法国、比利时、墨西哥、芬兰、西班牙等国家的树脂产量、消费量及增长率,以及日本、西欧、北美等地区的不同品种塑料原料消费量和增长率统计.按通用热塑性树脂(聚乙烯、聚丙烯、聚苯乙烯、聚氯乙烯、ABS树脂)、工程塑料(尼龙、聚碳酸酯、聚甲醛、热塑性聚酯、聚苯醚)、通用热固性树脂(酚醛、聚氨酯、不饱和树脂、环氧树脂)、特种工程塑料(聚苯硫醚、液晶聚合物、聚醚醚酮)不同品种的顺序,对树脂的产量、消费量及合成工艺、产品应用开发、树脂品种的延伸及应用的进一步扩展等有关技术作了详细的介绍.     

工业生产中物位测量的探讨与研究

在工业生产中常常会遇到常温,常压和一般介质的液位,料位和界面的测量,也会遇到高温,高压,易燃易爆,腐蚀性较强的液位,料位和界面的测量。在工业生产中物位测量有接触式和非接触式测量。但应根据生产工况及技术要求来合理选用。     

Confocal microscope—A valuable tool for examining wood-coating interface

The suitability of confocal laser scanning microscopy (CLSM) in examining a wood-coating interface was evaluated using a clear coating system. A comparison of the images of the wood-clear coating interface obtained using CLSM and light microscopy (LM) showed a marked superiority of CLSM in revealing the details of the physical nature of the interaction between the clear coating and the wood cell walls in the surface layer. The most distinct advantage of CLSM was in its ability to clearly resolve penetration of the coating into very fine cracks in cell walls, details not obtainable with LM. The information presented here demonstrates that CLSM has the potential to greatly enhance our understanding of the physical aspects of an interaction between the wood and coating at the interface.     

不同结构充油溶聚丁苯橡胶/炭黑/白炭黑复合材料的结构与性能

研究了炭黑/白炭黑填充的苯乙烯/乙烯基含量不同的充油溶聚丁苯橡胶(HPR 757 D和Buna VSL 5025-2 HM)的物理机械性能及动态力学性能,观察了填料在硫化胶中的微观分布情况。结果表明,炭黑与白炭黑相互镶嵌地分布在橡胶基质中,形成交织的填料网络。高苯乙烯基含量的HPR 757 D的拉伸强度、撕裂强度及耐磨性能优异,滚动阻力较小,填料与橡胶间的结合力强,填料的分散性较好。用白炭黑等量取代炭黑可以提高胶料的拉伸强度,降低其动态压缩温升。但炭黑/白炭黑的最佳配比与橡胶基质的分子结构有关,主链双键含量越高,白炭黑的用量也随之增多。