全钢子午线轮胎胎体帘布稀线的原因分析及解决措施

对全钢子午线轮胎胎体帘布稀线产生原因进行分析并提出改进措施。造成胎体帘布稀线的主要原因包括压延相关张力/压力设置不合理或波动造成局部脱层和裁断接头异常、成型导开胎体时拉伸造成胎体帘线疏密不均、成型胶部件接头过大或接头拉开、成型胎体接头异常、半部件胶料中或成型贴合半部件层间有杂质、胎坯转运或存放过程中受伤变形等。通过合理设置压延辊筒间压力,严格控制裁断、成型胎体接头器压力,规范成型胶部件接头质量,避免杂质带入及帘布拉伸,避免胎坯转运存放过程中发生变形等措施可有效减少胎体帘布稀线的发生。     

全钢载重子午线轮胎成型充气后胎体钢丝帘线起筋的原因分析及解决措施

分析全钢载重子午线轮胎成型充气后胎体钢丝帘线起筋的原因并提出解决措施。造成胎体钢丝帘线起筋的主要原因是钢丝帘线与胶料之间的粘合性能降低,成型充气后钢丝帘线与胶料轻微分离,帘布轴向表面钢丝帘线突出。通过调整胶料配方可提高钢丝帘线与胶料之间的粘合性能,通过调整压延和成型工艺可提升帘布压延质量,解决胎体钢丝帘线起筋问题,提高成品轮胎的耐久性能。     

全钢载重子午线轮胎胎体钢丝帘线间距不均匀的原因分析及解决措施

分析胎体帘布接头附近、不固定位置及固定位置钢丝帘线间距不均匀的原因,并提出相应的解决措施。采取控制胶料门尼粘度、改进压延工艺、提高过程控制等相应解决措施后,胎体帘布钢丝帘线分布不均匀占不合格品的比例由之前的10.5%下降到6.2%,从而使成品轮胎合格率及产品质量得到大大提高。     

1670dtex/2F105 DSP帘线在轿车子午线轮胎中的应用

介绍1670dtex/2F105 DSP帘线性能,并对其代替1400dtex/2F112锦纶帘线在轿车子线轮胎胎体中的应用进行研究。1670dtex/2F105 DSP帘线与1400dtex/2F112锦纶帘线相比具有模量高、收缩率低、尺寸稳定性好等特点,采用与1670dtex/2F105 DSP相匹配的胎体胶料可以有效改善轮胎的高速和耐久性能,同时可降低成本。     

炭黑硬度对胶料与聚酯帘线粘合力的影响

研究炭黑N330粒子硬度对轮胎胎体胶料物理性能以及胶料与聚酯帘线粘合力的影响.结果表明,随着炭黑N330粒子硬度的增大,胎体胶料门尼粘度、ML/MH,绍尔A型硬度、定伸应力和拉伸强度增大,拉断伸长率减小,焦烧时间和正硫化时间缩短;炭黑N330粒子硬度对硫化胶料与聚酯帘线粘合力影响较大,两者呈正比关系.     

全钢载重子午线轮胎胎体质量缺陷原因分析及解决措施

胎体接头开裂、钢丝帘线稀线、弯曲变形和交叉质量缺陷的产生原因主要是钢丝帘线残余应力过大、直径粗细不均匀和压延时钢丝帘线跳线,平面宽度设置不合理,胎坯过度变形,以及90°裁断、成型、硫化、存放和转运等工艺波动,通过从原材料控制、施工设计和工艺控制等方面采取相应解决措施,可有效提高胎体质量,使胎体质量缺陷率降低5个百分点以上,轮胎X光检测合格率达到99.9%以上。     

子午线轮胎用钢丝帘线的发展方向

分析了子午线轮胎用钢丝帘线的发展方向。指出胶料在带束层应良好渗透以防止钢丝帘线锈蚀、粘合性能下降和带束层边缘分离，从而增加胎面的可翻新性；应开发无外缠线的紧密型钢丝帘线，防止胎体帘线的损坏。举例说明了有关用作轮胎增强材料的钢丝帘线在材料和结构方面的改进及开发的情况。     

不同骨架材料对轮胎接地印痕的影响

试验研究采用锦纶帘线、芳纶帘线以及芳纶与锦纶复合帘线作胎体帘布层或带束层骨架材料对轮胎接地印痕的影响。结果表明：采用相同帘线作胎体帘布层骨架材料、不同帘线作带束层骨架材料时,带束层帘线刚性越大,轮胎接地印痕长轴冠中长度越小,短轴长度越大,矩形率越大;采用锦纶帘线作胎体帘布层和带束层骨架材料的轮胎接地印痕形状与采用复合帘线作胎体帘布层和带束层骨架材料的轮胎相似;使用相同原材料（除骨架材料外）、采用相同工艺和模具硫化的轮胎,在相同充气压力、负荷和下沉量下,接地印痕面积比较接近。     

我国全钢载重子午线轮胎用钢丝帘线的发展趋势

介绍我国全钢载重子午线轮胎用钢丝帘线的发展趋势。胎体钢丝帘线发展趋势为高强度、小直径、无外缠丝、同向捻制和低成本;带束工作层钢丝帘线应具有全胶料渗透性能和高刚度;带束保护层钢丝帘线应具有全胶料渗透性能、高覆胶后破断伸长率和低成本。     

全钢载重汽车子午线轮胎胎体帘线常见质量问题及解决措施

针对全钢载重汽车子午线轮胎胎体帘线在生产过程中出现的胎体帘线裂缝或排列密度不均、反包高度差异、帘线弯曲和帘线接头开裂等常见质量问题进行了原因分析,并提出了相关的解决措施。     

Orthophosphates and Diphosphates Containing Zinc and Copper and Zinc and Cobalt

Solid solutions of diphosphates of zinc and copper and of zinc and cobalt were synthesized from mixtures of pure diphosphates at temperatures up to 1000°C. Their X-ray diffractometry patterns varied continuously from one end member to the other. Solid solutions of orthophosphates of composition Zn_3−xCox(PO₄)2, with x = 0.4–1.6, were formed at temperatures up to 950°C; all exhibited the structure of γ-Zn₃(PO₄)2. Solid solutions of orthophosphates of composition Zn_3−xCu_x(PO₄)2 exhibited more-complex behavior. At 1000°C and copper contents of 20–80 mol%, a phase that is related to Cu₃(PO₄)2, termed here the "ε-phase," predominated. At 850°–950°C and in the region from 20 mol% to ∼33 mol% of copper, the solid solutions (the "η-phase") adopted the structure of graftonite. At 800°–900°C and 10–15 mol% of copper, the solid solutions exhibited a new structure (the "δ-phase"), which we found to be related to the mineral sarcopside. At temperatures 950°C, the solutions that contained 5–15 mol% of copper (the "β-phase") had the structure of β-Zn₃(PO₄)2, whereas at 800°–850°C, solutions with 5 mol% of copper (the "-phase") exhibited the structure of γ-Zn₃(PO₄)2. Attempts to synthesize Cu⁺ZnPO₄ and Cu⁺Cu²⁺Zn₃(PO₄)3 were unsuccessful.     

油气储运系统中油气的回收及腐蚀与防护问题

油气储运系统已经与保障国家经济的发展息息相关,介绍了油气储运系统中油气回收问题及腐蚀与防护问题,并提出了相应的解决措施。     

油气集输处理工艺及工艺流程

为了提高油田的生产效率,设计最佳的油气集输处理的工艺流程,更好地完成油气水分离处理的任务。对油气集输工艺技术进行优化,发挥高效油气水分离处理设备的优势,提高油气水处理的质量,保证油气集输工艺顺利实施,获得最佳的油田产量外输。     

Gemini型表面活性剂结构性能与应用

Gemini型表面活性剂的结构和性质与传统的表面活性剂有很大的不同,例如Gemini型表面活性剂可以视为两个普通表面活性剂在亲水基或者靠近亲水基处由连接基团通过化学键连接而成;Gemini表面活性剂的C20值和cmc值都比传统表面活性剂的值要低很多。着重介绍了Gemini型表面活性剂的特性,结构与表面活性的关系以及应用。     

科技创新与钢铁科技进步

建设创新型国家是我们中华民族的历史责任。“自主创新、重点突破、支撑发展、引领未来”的16字方针应当成为我们未来创新活动的指南。建设创新型国家把自主创新放在首位,并提出了引领未来的高标准要求。钢铁科技创新必须突出重点,抓住创新成果产业化这个关键,支撑起行业和国民经济的发展。     

石油与天然气地质与勘探开发措施

石油天然气的地质勘探开发目的是为了获得最佳的油气产能而进行的地质研究工作。石油天然气地质勘探工作具有非常重要的意义,通过地质勘探获得有价值的地层信息资料,对储层油气的显示进行评价和分析,确定具有工业开采价值,才能投入开发生产,为油田创造最佳的经济效益。     

油气管道及储运设施安全保障技术发展现状及展望

相比已经完善丰富的开采和勘探技术,油气的运输以及储存却仍然存在不足之处。我国对能源安全提出更加严格要求的同时,对区域经济的发展规划也有足够重视。因此,保障油气管道的安全则成为了我国能源安全战略的重中之重。在阐释油气管道现阶段在储运安全保障技术发展状况的基础上,分析了现存的问题及解决问题的手段,并指出未来可能使用的目标策略,为今后研究者提供一定程度上的借鉴经验。     

膜的污染和劣化及其防治对策

较为系统地介绍了膜污染和劣化的定义和特点,因膜污染和劣化而造成的膜性能变化,以及如何预防、减少或清除膜污染和劣化的一些通用方法。     

国内外天然橡胶产销分析及趋势预测

2009年,对中国橡胶行业来说,机遇和挑战并存。国际金融危机、全球经济增长放缓、国际市场需求持续走弱,产品出口大幅度下降,国内市场压力增大等各种不利因素的挑战日益尖锐。然而国家大规模投资,实施积极的财政政策和适度宽松的货币政策,并出台十大产业调整振兴规划,都给橡胶工业带来发展机遇。 目前,2009年时间已过半,在经历过最冷的“寒冬”后,国内外橡胶业现况如何、天然胶和合成胶的市场走势如何,成为上下游企业关注的热点。 从本期开始,本刊推出《金融危机下的世界橡胶市场》专题,从天然橡胶产销、贸易概况和主要合成橡胶产品（丁苯、乙丙、氯丁、丁腈、丁基、异戊等）的市场分析及前景两个角度,对国内外橡胶业的现况和发展进行分析及预测,供业内人士参考。