采用真空感应炉抗渣法,研究了半再结合镁铬耐火材料在碱度分别为0.6、1.1、1.5和1.8的CaO-SiO2渣与Al2O3含量为37.98%的CaO-Al2O3渣中的抗侵蚀性,试验条件是真空度5kPa、1650℃保温25min。对侵蚀后的试样进行观察与测量,并用SEM与EDAX分析了试样的断面形貌和化学组成变化。结果发现:在CaO-SiO2渣中,随着炉渣碱度的升高,镁铬试样中的尖晶石更易于受到熔渣的侵蚀,并且尖晶石中的Cr2O3、Fe2O3被CO与钢水中的C还原为金属态的铬铁合金,试样的直接结合被破坏,侵蚀量变大。在CaO-Al2O3渣中,镁铬试样在边界层生成致密的MA尖晶石,抑制了熔渣的进一步侵蚀和Cr2O3、Fe2O3的还原,显示出较好的抗侵蚀性。     

MgO-C材料低压动态条件下抗侵蚀性的研究

采用真空感应炉浸棒法,在真空度为5 kPa,于1 650 ℃保温25 min的试验条件下研究了w(C)约为10%的MgO-C材料的抗熔渣侵蚀性;对试验后的试样进行观察与测量,并用SEM分析了侵蚀后试样显微结构.结果表明:在本试验条件下,熔渣的侵蚀速率大于MgO与C反应的脱碳速率,随着CaO-SiO<,2>渣系碱度的提高,MgO-C材料侵蚀量减少;MgO-C材料对CaO-Al<,2>O<,3>熔渣有较强的抗侵蚀性.     

SiC结合刚玉材料的抗高炉渣侵蚀性

采用电熔刚玉、Si粉和SiC粉为原料,用酚醛树脂做结合剂,混练成型后于1 450℃埋炭烧成,采用静态坩埚抗渣试验研究了烧后试样对碱度为1.1的高炉渣在1 500℃的抗渣侵蚀性。结果表明:Si与C、CO在高温下原位反应生成纤维状SiC,形成原位SiC结合刚玉材料,该材料具有良好的抗侵蚀性能,渣蚀厚度都在2.6mm以下,其中,加入8%(w)Si粉和5%(w)SiC粉的试样抗渣侵蚀性最好。通过对抗侵蚀后试样的侵蚀层、渗透层和未变层的相组成和显微结构的分析认为:(1)这种复合材料抗渣侵蚀性能良好的主要原因是熔渣难润湿的SiC自身抗渣侵蚀性较好,且原位生成的纤维状SiC穿插在刚玉骨架结构的空隙中,阻挡了熔渣的侵蚀和渗透;(2)熔渣侵蚀材料的过程是SiC先被氧化,然后其氧化产物SiO2与熔渣中的CaO和SiO2以及材料基质中的A l2O3反应生成钙长石低熔相。     

MgO部分稳定氧化锆陶瓷的抗渣侵蚀性研究

分别以3.5%(质量分数,下同)MgO部分稳定或4?O部分稳定的ZrO2陶瓷材料为试样,以CaO-Fe2O3-SiO2系的3种不同碱度与Fe2O3含量的渣为侵蚀剂,对试样分别进行静态和动态旋转(试样与渣的相对速率分别为0.06和0.5 m.m in-1)侵蚀试验,研究渣的碱度、流速及Fe2O3含量对材料抗侵蚀性的影响。结果发现,MgO部分稳定ZrO2材料抗渣侵蚀性较好,试样在渣线部位较严重的侵蚀归因于Marangoni效应。试样侵蚀情况与渣的碱度、成分有密切关系,高碱度渣侵蚀的方式主要是形成新的化合物而降低试样强度,中碱度或低碱度高Fe2O3渣则先将稳定剂MgO溶出,使材料遭受侵蚀的同时还发生相变化。     

铝镁浇注料的抗渣侵蚀机理

采用静态坩埚法进行了铝镁浇注料的抗渣侵蚀试验 ,从动力学和热力学角度分析了铝镁浇注料的抗渣侵蚀机理。结果表明 :浇注料的熔渣侵蚀过程受化学反应和扩散的混合控制 ;熔渣侵蚀的表观活化能约为 4 2 4 .8kJ·mol- 1;渣中CaO与Al2 O3反应生成高熔点的CA6 ,抑制了熔渣的进一步侵蚀 ;渣中CaO含量的不断降低 ,使熔渣的粘度增大 ,渗透能力降低。     

不同熔渣对钢包铝镁铬材料渣蚀行为的影响

选取冶炼取向硅钢和铝镇静钢的精炼终渣及钢包用铝镁铬砖,采用静态坩埚法于1600 ℃×3 h下进行熔渣侵蚀试验,对渣蚀后试样作显微结构分析,并测定熔渣的化学成分和熔化温度.结果显示,随着熔渣中Al2O3含量的升高和碱度的增加,熔渣的熔点升高,粘度增加.粘度较大的熔渣与耐火材料接触后扩散较慢,对耐火材料的侵蚀和渗透减弱.并且当熔渣与耐火材料的反应产物为高熔点的CA2、CA6和MA尖晶石相且连续交错分布时,能堵塞液相扩散通道,抑制熔渣向耐火材料内部的进一步渗透.     

不同碱度渣对刚玉-尖晶石浇注料的侵蚀行为研究

浇注料的抗渣侵蚀性能与钢渣的碱度密切相关。以烧结刚玉、缺陷尖晶石微粉、活性α-Al₂O₃微粉、电熔镁砂细粉和铝酸钙水泥(Secar71)为主要原料,制备了刚玉-尖晶石浇注料,采用静态坩埚法于1 600℃保温3 h进行抗渣试验,并用热力学模拟计算了液相量和液相组成,研究了刚玉-尖晶石浇注料对3种不同碱度渣(1.6、2.3和7.6)的抗渣侵蚀性能。结果表明：刚玉-尖晶石浇注料在高碱度渣中溶解能力有限,在熔渣-耐火材料界面极易形成尖晶石固溶体和六铝酸钙等高熔点物相,形成致密层阻挡熔渣渗透和侵蚀。而其在低碱度渣中溶解度较高,在浇注料-熔渣达到较高反应程度时,才开始形成尖晶石固溶体和六铝酸钙等高温相,无法形成有效的致密层阻止熔渣对浇注料的侵蚀和渗透。因此,刚玉-尖晶石浇注料对高碱度渣抗渣侵蚀能力较强,对低碱度渣抗渣侵蚀能力较弱。     

不同碱度渣对铝镁浇注料的侵蚀行为

以板状刚玉颗粒(≤5 mm)、电熔镁砂粉(≤0.088 mm)、电熔尖晶石粉(≤0.044 mm)、α-Al2O3微粉(d50≤0.7μm)为主要原料,经配料、混料、成型、烘干后制备了铝镁质坩埚试样,采用2种不同碱度的钢包渣(碱度分别为3.40和1.03),通过静态坩埚法对铝镁浇注料进行抗渣试验(1 600℃3 h),分析了抗渣试验后试样的渣蚀指数和显微结构,以研究不同碱度渣对铝镁浇注料试样的侵蚀行为。结果表明,低碱度渣对铝镁浇注料的侵蚀和渗透比高碱度渣严重,这主要是因为不同碱度渣与浇注料反应生成的产物不同。低碱度渣对铝镁浇注料侵蚀时,材料内部CA6和钙铝硅系化合物多相共存的组织以及CA6生成时的体积膨胀效应加剧了渣对材料的侵蚀和渗透;在高碱度渣条件下,渣与材料界面生成了CA2致密层和大量的原位MA,有效地降低了渣对材料的蚀损。     

侵蚀温度和煤渣脱碳对高铬材料抗侵蚀性的影响

为了研究侵蚀温度和煤渣脱碳对水煤浆气化炉用高铬材料抗侵蚀性的影响,取含碳和脱碳两种煤渣,采用静态坩埚法,在埋炭气氛中分别于1 450和1 600℃保温5 h对高铬材料进行侵蚀试验,检测试验后高铬材料的侵蚀渗透深度、脱锆层厚度,以及原砖层的气孔率和孔径分布情况,并分析了试验条件下熔渣系统的氧势。结果表明:1)随着侵蚀温度的升高,侵蚀后坩埚渣-埚界面坩埚侧表面的尖晶石层变薄,坩埚原砖层中气孔增多,孔径增大,抗煤渣侵蚀性下降。2)含碳煤渣对高铬材料的侵蚀较强,侵蚀后残渣中有金属相;脱碳煤渣对高铬材料的侵蚀较弱,侵蚀后残渣中没有出现金属相。3)经热力学分析,当采用脱碳煤渣时,试验过程中熔渣内部的氧势在10~(-9.25)MPa以上;当采用含碳煤渣时,熔渣内部的氧势为10~(-13)~10~(-15)MPa。     

Al2O3-ZrO2质风口衬套渣侵蚀SEM分析

以白刚玉、锆英石为原料制备了Al2O3-ZrO2质风口衬套样,采用静态熔渣法在1500℃保温2h进行高炉渣侵蚀试验。对侵蚀后的试样进行SEM分析,并研究其侵蚀机理。结果表明:侵蚀试样从热面到冷面侵蚀区域主要分为两层,且CaO含量逐渐减少,SiO2含量增多。在试验条件下,锆英石在碱金属Na存在的条件下容易分解生成ZrO2和SiO2;同时,SiO2、Al2O3与渣中CaO反应生成低熔点玻璃相物质,使材料的耐火度降低。     

Many Drugs of Abuse May Be Acutely Transformed to Dopamine,Norepinephrine and Epinephrine In Vivo

It is well established that a wide range of drugs of abuse acutely boost the signaling of the sympathetic nervous system and the hypothalamic–pituitary–adrenal (HPA) axis, where norepinephrine and epinephrine are major output molecules. This stimulatory effect is accompanied by such symptoms as elevated heart rate and blood pressure, more rapid breathing, increased body temperature and sweating, and pupillary dilation, as well as the intoxicating or euphoric subjective properties of the drug. While many drugs of abuse are thought to achieve their intoxicating effects by modulating the monoaminergic neurotransmitter systems (i.e., serotonin, norepinephrine, dopamine) by binding to these receptors or otherwise affecting their synaptic signaling, this paper puts forth the hypothesis that many of these drugs are actually acutely converted to catecholamines (dopamine, norepinephrine, epinephrine) in vivo, in addition to transformation to their known metabolites. In this manner, a range of stimulants, opioids, and psychedelics (as well as alcohol) may partially achieve their intoxicating properties, as well as side effects, due to this putative transformation to catecholamines. If this hypothesis is correct, it would alter our understanding of the basic biosynthetic pathways for generating these important signaling molecules, while also modifying our view of the neural substrates underlying substance abuse and dependence, including psychological stress-induced relapse. Importantly, there is a direct way to test the overarching hypothesis: administer (either centrally or peripherally) stable isotope versions of these drugs to model organisms such as rodents (or even to humans) and then use liquid chromatography-mass spectrometry to determine if the labeled drug is converted to labeled catecholamines in brain, blood plasma, or urine samples.     

Sapindaceae,cyanolipids, and bugs

Scentless plant bugs (Heteroptera: Rhopalidae) are so named because adults of the Serinethinae have vestigial metathoracic scent glands. Serinethines are seed predators of Sapindales, especially Sapindaceae that produce toxic cyanolipids. In two serinethine species whose ranges extend into the southern United States,Jadera haematoloma andJ. sanguinolenta, sequestration of host cyanolipids as glucosides renders these gregarious, aposematic insects unpalatable to a variety of predators. The blood glucoside profile and cyanogenesis ofJadera varies depending on the cyanolipid chemistry of hosts, and adults and larvae fed golden rain tree seeds (Koelreuteria paniculata) excrete the volatile lactone, 4-methyl-2(5H)-furanone, to which they are attracted.Jadera fed balloon vine seeds (Cardiospermum spp.) do not excrete the attractive lactone. Loss of the usual heteropteran defensive glands in serinethines may have coevolved with host specificity on toxic plants, and the orientation ofJadera to a volatile excretory product could be an adaptive response to save time.Mention of a commercial product does not consititute an endorsement by the USDA.     

Insect antifeedant properties of anthranoids from the genusVismia

Vismiones and ferruginins, representatives of a new class of lypophilic anthranoids from the genusVismia were found to inhibit feeding in larvae of species ofSpodoptera, Heliothis, and inLocusta migratoria.     

2008～2009年世界塑料工业进展

收集了2008年7月～2009年6月世界塑料工业的相关资料,介绍了2008～2009年国外塑料工业的发展情况,提供了世界塑料产量、消费量及全球各类树脂的需求量及产能情况。按通用热塑性树脂(聚乙烯、聚丙烯、聚苯乙烯、聚氯乙烯、ABS树脂)、工程塑料(尼龙、聚碳酸酯、聚甲醛、热塑性聚酯、聚苯醚)、特种工程塑料(聚苯硫醚、液晶聚合物、聚醚醚酮)、通用热固性树脂(酚醛、聚氨酯、环氧树脂、不饱和聚酯树脂)不同品种的顺序,对树脂的产量、消费量、供需状况及合成工艺、产品应用开发、树脂品种的延伸及应用的进一步扩展等技术作了详细介绍。     

ICP-MS法测定地球化学样品中As、Cr、Ge、V等18种微量痕量元素的研究

建立了测定地球化学样品中包括As、Cr、Ge、V等18种微量、痕量元素的ICP-MS方法。地化试样用HF-HNO3混酸分解后,以1 1 HNO3溶解干渣。由于制样不使用盐酸,避免了Cl对As、Cr、Ge、V的质谱干扰。用国家一级地球化学标准物质GBW 07309制备溶液优化仪器工作参数,并用于校准。方法测定限(6s)为:0.007~6.4μg/g,精密度(RSD%,n=12)为:29%~9.4%,经过国家一级地球化学标准物质的分析验证,结果与标准值吻合。方法已应用于国土资源调查的试样分析。