Al2O3对钢渣提铁后二次渣制取的微晶玻璃性能的影响

为了利用大量的钢渣、改质剂A和改质剂B等固体废弃物制备具有高附加值的微晶玻璃,将钢渣与改质剂A和B混合熔融提铁并采用DTA、XRD、SEM等手段研究了Al2O3对钢渣提铁后二次渣制取的微晶玻璃性能的影响.结果表明,当Al2O3质量分数为3％ ～6％时,试样的主晶相为硅灰石,微晶玻璃晶体呈粒状,晶体结构疏松且有少许气孔存在;随着Al2O3含量的增加,微晶玻璃的主相由硅灰石转变为镁黄长石和钙铝黄长石.当Al2O3质量分数为15％时,析晶动力学参数k(Tp)最大,析晶能力强,此时微晶玻璃的晶粒尺寸为1～2 μm左右,且晶相结构致密,其抗弯强度为49.85 MPa,显微硬度为3.60 GPa,抗压强度为181.47 MPa,符合建筑装饰用微晶玻璃的国家标准要求.     

热处理温度对磷渣-煤矸石微晶玻璃结构和性能的影响

以磷渣和煤矸石为原料,采用一步烧结法制备了性能优良的CaO?Al2O3?SiO2(CAS)系微晶玻璃,用差示扫描量热法(DSC),X射线衍射(XRD)和扫描电子显微镜(SEM)等对其进行分析和表征,研究了热处理温度对微晶玻璃晶相组成、微观结构和宏观性能的影响规律。结果表明,固废利用率达100%,微晶玻璃性能良好;以磷渣和煤矸石为原料在1250℃下熔融2 h、于850℃热处理保温2 h可制备主晶相为假硅灰石Ca3(Si3O9)的微晶玻璃,其抗折强度、显微硬度和体积密度分别为74.4 MPa,566.9 HV和2.75 g/cm3。随热处理温度升高,微晶玻璃主晶相由Ca3(Si3O9)相转变为硅灰石CaSiO3相,晶体形态由球状向针状、短柱状改变,对提高微晶玻璃抗折性能有利,而显微硬度和体积密度均先增加后降低。     

添加ZnO对SiO_2–CaO–Al_2O_3–MgO系微晶玻璃析晶的影响

应用扫描电子显微镜和X射线衍射等技术,研究了添加不同质量分数(下同)的ZnO对SiO2–CaO–Al2O3–MgO系玻璃析晶和显微形貌的影响。结果表明:在所研究的玻璃体系中,ZnO加入后优先与玻璃体中的钙、硅元素发生反应,生成锌黄长石Ca2ZnSi2O7。另一部分ZnO和少量Fe2O3固溶到硅灰石(CaSiO3)晶体中形成(铁,锌)辉石晶体[Ca(Fe,Zn)Si2O6]。随着玻璃中ZnO添加量的提高,越来越多的钙、硅与之反应生成Ca2ZnSi2O7,主晶相由CaSiO3逐渐转变为CaZnSi2O7。玻璃样品在随炉升温至1050℃的情况下,以表面析晶为主,析出晶体呈枝状。玻璃先在750℃低温退火处理有利于晶体的整体析出,晶体形态由ZnO为5%时的鱼骨状变为15%时的条带状组织。     

污泥焚烧灰烧制微晶玻璃

用污泥焚烧灰和废玻璃作为原料一阶段成核结晶法制备微晶玻璃,结果发现,当晶化温度从800℃升高到950℃时,微晶玻璃中玻璃相降低、球状晶体尺寸增加,微晶玻璃主晶相为硅灰石Ca Si O3和透辉石Ca(Mg,Al)(Si,Al)2O6,在晶化温度为900℃时,物理和机械性能最好,其密度达2.65 g/cm3、抗弯强度达61.8 MPa、热膨胀系数为7.3×10-6 mm/K。     

MgO对黄磷炉渣微晶玻璃析晶影响

以黄磷炉渣为基础原料,通过加入辅料和MgO,以熔融法制备CaO-Al2 O3-SiO2(CAS)系微晶玻璃;通过差热分析(DTA)、X射线衍射(XRD)和扫描电子显微镜(SEM)等分析方法分析MgO对黄磷炉渣微晶玻璃晶化行为的影响.结果显示:随着加入MgO的量的增加,基础玻璃的核化温度和晶化温度下降,析晶活化能E减小;黄磷炉渣微晶玻璃的晶相类型并未因MgO添加量的增多而改变,其主晶相为硅灰石(CaSiO3),次晶相为铝透辉石(Ca(MgAl)(SiAl)2O6);但随着MgO添加量的增多,抑制了硅灰石(CaSiO3)晶相的生成,促进铝透辉石(Ca(MgAl)(SiAl)2O6)生成.     

添加ZnO对SiO2-CaO-Al2O3-MgO系微晶玻璃析晶的影响

应用扫描电子显微镜和X射线衍射等技术,研究了添加不同质量分数(下同)的ZnO对SiO2-CaO-Al2O3-MgO系玻璃析晶和显微形貌的影响.结果表明:在所研究的玻璃体系中,ZnO加入后优先与玻璃体中的钙、硅元素发生反应,生成锌黄长石Ca2ZnSi2O7.另一部分ZnO和少量Fe2O3固溶到硅灰石(CaSiO3)晶体中形成(铁,锌)辉石晶体[Ca(Fe,Zn)Si2O6].随着玻璃中ZnO添加量的提高,越来越多的钙、硅与之反应生成Ca2ZnSi2O7,主晶相由CaSiO3逐渐转变为CaZnSi2O7.玻璃样品在随炉升温至1 050℃的情况下,以表面析晶为主,析出晶体呈枝状.玻璃先在750℃低温退火处理有利于晶体的整体析出,晶体形态由ZnO为5%时的鱼骨状变为15%时的条带状组织.     

粉煤灰微晶玻璃的晶化机理研究

以粉煤灰为主要原料制得微晶玻璃,通过XRD、SEM和EDAX等测试方法,研究了粉煤灰微晶玻璃的晶化机理.研究结果表明:粉煤灰玻璃在热处理的过程中,首先发生分相,形成富硅相和富钙相,进而形成以透辉石(CaO·MgO·2SiO2)和钙黄长石(2CaO·Al2O3·SiO2)为主晶相的微晶玻璃.     

采用一步烧结法的钢渣基微晶玻璃制备机理

以转炉钢渣作为主要原料,对钢渣熔融还原提铁后的二次渣采用一步法热处理工艺,制备出了碱度(Ca O与Si O2的质量比)分别为0.5、0.6、0.7的钢渣微晶玻璃。通过X射线衍射分析(XRD)、扫描电镜(SEM)和力学性能测试等手段,研究了不同热处理温度和时间对微晶玻璃结构和性能的影响规律。研究表明,随着基础玻璃碱度的提高,微晶玻璃的主晶相由辉石转变为钙铝黄长石;随着烧结温度逐渐升高,微晶玻璃抗折强度也逐渐升高,但不宜超过1100℃;在1100℃下,保温时间的变化对微晶玻璃的性能和微观组织的影响较小;碱度为0.7的微晶玻璃力学性能优异,在1100℃晶化20 min其内部的晶体呈方柱状交织排列,构成晶体骨架并分布在残余的玻璃基体中,从而使其具有优异的力学性能;采用一步法工艺,可减少改质剂使用量及热处理时间,具有较好的应用前景。     

ZnO对黄磷炉渣微晶玻璃析晶影响

以黄磷炉渣为主要原料,通过添加不同比例ZnO,采用熔融法制备了CaO-Al2O3-SiO2系微晶玻璃.借助Kissinger方程分析黄磷炉渣基础玻璃的析晶能力,借助化学热力学软件FactSage 6.4模拟计算黄磷炉渣微晶玻璃晶相类型,借助X射线衍射仪(XRD)和扫描电子显微镜(SEM)进行验证.结果表明:随着ZnO添加量的增加,黄磷炉渣基础玻璃的析晶峰温度Tp和析晶活化能E逐渐减小;当ZnO添加量为7wt％时,黄磷炉渣基础玻璃的析晶活化能E最小,析晶能力最强;随着ZnO的加入量的增大,黄磷炉渣微晶玻璃晶相类型并不发生改变,主晶相为硅灰石(CaSiO3),次晶相为铝透辉石(Ca(Mg,Al)(Si,Al)2O6),这与FactSage 6.4模拟计算结果一致.     

热处理制度对SiO_2-CaO-Al_2O_3-MgO-ZnO-Fe_2O_3系玻璃陶瓷析晶的影响

为了探讨热处理制度对SiO2-CaO-Al2O3-MgO-ZnO-Fe2O3系玻璃陶瓷析晶的影响,利用高温熔融法制备基础玻璃,并用扫描电子显微镜(SEM)和X射线衍射(XRD)等技术考察玻璃陶瓷的析晶特征。结果表明:在所研究的玻璃体系中析出主晶相为锌橄榄石(Ca2ZnSi2O7),部分氧化锌和氧化铁固溶到硅灰石(CaSiO3)中,形成辉石类晶体(Ca(Fe,Zn)Si2O6)。热处理制度对析出晶体的种类影响不大,但是对析出晶体的形态有较大程度的影响。在随炉升温的情况下,试样表面形成枝状Ca(Fe,Zn)Si2O6晶体,而在内部形成Ca2ZnSi2O7和Ca(Fe,Zn)Si2O6。两种晶体相互交替析出,形成条带状组织。在750℃的保温有利于晶体的整体析出。     

Many Drugs of Abuse May Be Acutely Transformed to Dopamine,Norepinephrine and Epinephrine In Vivo

It is well established that a wide range of drugs of abuse acutely boost the signaling of the sympathetic nervous system and the hypothalamic–pituitary–adrenal (HPA) axis, where norepinephrine and epinephrine are major output molecules. This stimulatory effect is accompanied by such symptoms as elevated heart rate and blood pressure, more rapid breathing, increased body temperature and sweating, and pupillary dilation, as well as the intoxicating or euphoric subjective properties of the drug. While many drugs of abuse are thought to achieve their intoxicating effects by modulating the monoaminergic neurotransmitter systems (i.e., serotonin, norepinephrine, dopamine) by binding to these receptors or otherwise affecting their synaptic signaling, this paper puts forth the hypothesis that many of these drugs are actually acutely converted to catecholamines (dopamine, norepinephrine, epinephrine) in vivo, in addition to transformation to their known metabolites. In this manner, a range of stimulants, opioids, and psychedelics (as well as alcohol) may partially achieve their intoxicating properties, as well as side effects, due to this putative transformation to catecholamines. If this hypothesis is correct, it would alter our understanding of the basic biosynthetic pathways for generating these important signaling molecules, while also modifying our view of the neural substrates underlying substance abuse and dependence, including psychological stress-induced relapse. Importantly, there is a direct way to test the overarching hypothesis: administer (either centrally or peripherally) stable isotope versions of these drugs to model organisms such as rodents (or even to humans) and then use liquid chromatography-mass spectrometry to determine if the labeled drug is converted to labeled catecholamines in brain, blood plasma, or urine samples.     

ICP-MS法测定地球化学样品中As、Cr、Ge、V等18种微量痕量元素的研究

建立了测定地球化学样品中包括As、Cr、Ge、V等18种微量、痕量元素的ICP-MS方法。地化试样用HF-HNO3混酸分解后,以1 1 HNO3溶解干渣。由于制样不使用盐酸,避免了Cl对As、Cr、Ge、V的质谱干扰。用国家一级地球化学标准物质GBW 07309制备溶液优化仪器工作参数,并用于校准。方法测定限(6s)为:0.007~6.4μg/g,精密度(RSD%,n=12)为:29%~9.4%,经过国家一级地球化学标准物质的分析验证,结果与标准值吻合。方法已应用于国土资源调查的试样分析。     

基于ATRP法制备的触角状亲水性羟胺树脂的吸硼性能的研究

以大分子引发剂氯乙酰化聚苯乙烯微球(PS-acyl-Cl)经原子转移自由基聚合(ATRP)法引发丙烯酰胺(AM)和甲基丙烯酸缩水甘油酯(GMA)单体的共聚接枝,制得一种触角状亲水性环氧载体(PS-acyl-g-P(AM-co-GMA)),再经二乙醇胺(DEA)的环氧基开环胺化反应,得到一种含多个-NCH2CH2OH螯合配基的多齿-五元螯合环的触角状亲水性羟胺树脂(PS-acyl-g-P(AM-co-GMA)-DEA)。将此树脂用于硼吸附研究,结果表明,PS-acyl-g-P(AM-co-GMA)-DEA树脂对硼的吸附满足Langmuir方程,为单分子层吸附;饱和吸附量约为37.7 mg·g-1,且树脂5 min即可达到吸附平衡,与其它已报道的吸硼树脂相比,该树脂具有更高的吸附量和吸硼速率。吸附动力学研究表明,树脂吸附硼的过程主要由颗粒扩散过程控制。重复使用5次后该树脂的吸附量基本不变,解吸率均在90%以上,重复使用性能良好。     

工业评述2001～2002年国外塑料工业进展

收集了2001年7月到2002年6月有关国外塑料工业的相关期刊资料,介绍了2001年到2002年国外塑料工业的发展情况,提供了世界各地域塑料原材料的产量及构成比,日本、美国、加拿大、德国、法国、比利时、墨西哥、芬兰、西班牙等国家的树脂产量、消费量及增长率,以及日本、西欧、北美等地区的不同品种塑料原料消费量和增长率统计.按通用热塑性树脂(聚乙烯、聚丙烯、聚苯乙烯、聚氯乙烯、ABS树脂)、工程塑料(尼龙、聚碳酸酯、聚甲醛、热塑性聚酯、聚苯醚)、通用热固性树脂(酚醛、聚氨酯、不饱和树脂、环氧树脂)、特种工程塑料(聚苯硫醚、液晶聚合物、聚醚醚酮)不同品种的顺序,对树脂的产量、消费量及合成工艺、产品应用开发、树脂品种的延伸及应用的进一步扩展等有关技术作了详细的介绍.     

工业生产中物位测量的探讨与研究

在工业生产中常常会遇到常温,常压和一般介质的液位,料位和界面的测量,也会遇到高温,高压,易燃易爆,腐蚀性较强的液位,料位和界面的测量。在工业生产中物位测量有接触式和非接触式测量。但应根据生产工况及技术要求来合理选用。     

Confocal microscope—A valuable tool for examining wood-coating interface

The suitability of confocal laser scanning microscopy (CLSM) in examining a wood-coating interface was evaluated using a clear coating system. A comparison of the images of the wood-clear coating interface obtained using CLSM and light microscopy (LM) showed a marked superiority of CLSM in revealing the details of the physical nature of the interaction between the clear coating and the wood cell walls in the surface layer. The most distinct advantage of CLSM was in its ability to clearly resolve penetration of the coating into very fine cracks in cell walls, details not obtainable with LM. The information presented here demonstrates that CLSM has the potential to greatly enhance our understanding of the physical aspects of an interaction between the wood and coating at the interface.     

不同结构充油溶聚丁苯橡胶/炭黑/白炭黑复合材料的结构与性能

研究了炭黑/白炭黑填充的苯乙烯/乙烯基含量不同的充油溶聚丁苯橡胶(HPR 757 D和Buna VSL 5025-2 HM)的物理机械性能及动态力学性能,观察了填料在硫化胶中的微观分布情况。结果表明,炭黑与白炭黑相互镶嵌地分布在橡胶基质中,形成交织的填料网络。高苯乙烯基含量的HPR 757 D的拉伸强度、撕裂强度及耐磨性能优异,滚动阻力较小,填料与橡胶间的结合力强,填料的分散性较好。用白炭黑等量取代炭黑可以提高胶料的拉伸强度,降低其动态压缩温升。但炭黑/白炭黑的最佳配比与橡胶基质的分子结构有关,主链双键含量越高,白炭黑的用量也随之增多。