SiC—AlN—Y2O3复相陶瓷的制备与性能

通过热压烧结技术，ＳｉＣ、ＡｌＮ和Ｙ２Ｏ３粉末混合体在１９２０￣２０５０℃、Ａｒ气氛下形成了致密的复相陶瓷。在室温下ＳｉＣ－ＡｌＮ－Ｙ２Ｏ３复相材料的抗弯强度和断裂韧性分别达到６００ＭＰａ和７ＭＰａ·ｍ＾１／２以上。运用ＸＲＤ、ＳＥＭ和ＴＥＭ分析致密样品的断裂裂纹、形貌和组成。ＳｉＣ－ＡｌＮ－Ｙ２Ｏ３复相陶瓷在１３７０℃氧化试验３０ｈ，其氧化产物为莫来石。     

SiC－AlN－Y_2O_3复相陶瓷的氧化行为

经研究致密的ＳｉＣ－ＡｌＮ－Ｙ２Ｏ３复相陶瓷的氧化行为后发现，陶瓷材料的表面在空气中氧化的反应物随着温度的高低而变化．８００℃、２０ｈ氧化试验后，试样表面无任何变化，１１００℃氧化．２０ｈ，表面形成了极少量的ＳｉＯ２，但两者均无增重．１２５０℃与１３２０℃氧化３０ｈ后，试样的重量和表面发生较明显的变化，形成了ＳｉＯ２与α－Ａｌ２Ｏ３，１３７０℃氧化试验３０ｈ后，陶瓷表面的氧化产物ＳｉＯ２与α－Ａｌ２Ｏ３转化成莫来石（３Ａｌ２Ｏ３·２ＳｉＯ２）结构．试样表面的氧化层均匀而且致密．     

碳化硅和氧化铝陶瓷的热等静压氮化

通过对无压烧结、热压烧结和热等静压烧结ＳＩＣ陶瓷以及热压烧结的ＳｉＣ粒子补强Ａｌ２Ｏ３基复相陶瓷（ＳｉＣｐ－Ａｌ２Ｏ３）和ＳｉＣ粒子与ＳｉＣ晶须共同增强的Ａｌ２Ｏ３基复合材料（ＳｉＣｐ－ＳｉＣｗ－Ａｌ２Ｏ３）在氮气氛中进行高温氮化处理，成功地实现了这些材料的开口气孔表面裂纹的愈合。研究表明：热等静压氯化工艺可以显著提高ＳｉＣ和Ａｌ２Ｏ３陶瓷的抗弯强度，对断裂韧性也有较大的改善作用。对于热等静压烧结ＳｉＣ陶瓷，在１８５０℃和２００ＭＰａ氮气压力下氯化处理１小时后，其抗弯强度和断裂韧性分别由５８２ＭＰａ和５．７ＭＰａ·ｍ１／２提高到９０７ＭＰａ和８．４ＭＰａ·ｍ１／２；对于热压烧结的ＳｉＣｐ－Ａｌ２Ｏ３复相陶瓷和ＳｉＣｐ－ＳｉＣｗ－Ａｌ２Ｏ３复合材料，在１７００℃和１５０ＭＰａ氮气压力下氮化处理１小时后，其室温抗弯强度分别由４６０和７０５ＭＰａ提高到８９５和１０３３ＭＰａ。     

无压烧结SiC－AlN复相陶瓷的显微结构

对于ＳｉＣ与ＡｌＮ在１８００℃以上可以发生反应形成固溶体的研究结果有益于碳化硅陶瓷的烧结．在２１００℃Ａｒ气氛的条件下，通过ＸＲＤ、ＳＥＭ和ＴＥＭ等分析手段测试样品的颗粒界面、断裂面和组成后发现，烧结过程中ＡｌＮ扩散并均匀地分市在整个坯体之中，ＳｉＣ颗粒在原位长大成无序排列的长５～８μｍ、宽为１μｍ的棒状晶体结构．ＳｉＣ－ＡｌＮ复相材料的断裂面呈现出拨出与撕裂二种效果，其抗弯强度和断裂韧性分别可达到４２０ＭＰａ和４．８３ＭＰａ．ｍ１／２     

TiC／（Al_2O_3／Y－TZP）复相陶瓷的制备与性能

本文采用热压工艺制备ＴｉＣ和Ａｌ_２Ｏ_３共同补强Ｙ－ＴＺＰ基复相陶瓷，研究了复相陶瓷的相组成、力学性能及显微结构．发现复相陶瓷的高温强度得到显著提高，１０００℃时，组成为３０ｖｏｌ％ＴｉＣ－（２５ｖｏｌ％Ａｌ２Ｏ３／１．８Ｙ－ＴＺＰ）复相陶瓷抗弯强度高达６１４ＭＰａ．ＴｉＣ颗粒补强机制在高温下发挥了重要作用．     

LCMAS微晶玻璃／Y－TZP复相材料

本工作对ＬＣＭＡＳ微晶玻璃／Ｙ－ＴＺＰ复相材料在不同的烧结温度下所出现的晶相进行了研究，发现材料在烧结温度下，Ｙ－ＴＺＰ中的ＺｒＯ２与微晶玻璃中的ＳｉＯ２发生化学反应生成锆英石（ＺｒＯ２·ＳｉＯ２），少量Ｙ－ＴＺＰ的加入起不到相变增初作用．由于Ｙ－ＴＺＰ起到微晶玻璃晶核剂的作用，仍能使材料的抗折强度和断裂韧性得到大幅度的提高．当Ｙ－ＴＺＰ含量为９５ｗｔ％时，复相材料的抗折强度和断裂韧性分别为６３１ＭＰａ和８．４ＭＰａ．ｍ１／２．     

晶内型Al2O3—SiC纳米复合陶瓷的制备

研究了沉淀法制备Ａｌ２Ｏ３－ＳｉＣ纳米复合陶瓷的工艺过程，利用Ａｌ２Ｏ３从γ相到α相的蠕虫状生长过程，使大部分纳米ＳｉＣ颗粒位于Ａｌ２Ｏ３晶粒内，用沉淀法制得的、含有５ｖｏｌ％ＳｉＣ的Ａｌ２Ｏ３－ＳｉＣ纳米复合陶瓷，其强度为４６７ＭＰａ，韧性为４．７ＭＰａ．ｍ＾１／２，与一般的Ａｌ２Ｏ３陶瓷相比有较大的提高，显示了沉淀法制备Ａｌ２Ｏ３－ＳｉＣ纳米复合陶瓷的优点。     

助烧剂对热压Si3N4基陶瓷组织结构的影响

用ＸＲＤ，ＳＥＭ，ＴＥＭ分析了用Ｙ２Ｏ３＋Ａｌ２Ｏ３及Ｙ２Ｏ３＋ＡｌＮ做助烧剂的两种热压Ｓｉ３Ｎ４基陶瓷的组织结构，用ＥＤＸＡ分析了Ｓｉ，Ａｌ，Ｙ等元素的含量。结果表明，两种Ｓｉ３Ｎ４都是由长柱状β相组成；     

TiC／（Al2O3／Y—TZP）复相陶瓷的制备与性能

本文采用热压工艺制备ＴｉＣ和Ａｌ２Ｏ３共同补强Ｙ－ＴＺＰ基复相陶瓷，研究了复相陶瓷的相组成。力学性能及显微结构，发现复相陶瓷的高温强度得到显著提高，１０００℃时，组成为３０ｖｏｌ％ＴｉＣ－（２５ｖｏｌ％，Ａｌ２Ｏ３／１．８Ｙ－ＴＺＰ）复相陶冷饮 抗弯强度高达６１４ＭＰａ，ＴｉＣ颗粒补强机制在高温下发挥了重要作用。     

Sic—AIN—Y2O3复相陶瓷的氧化行为

经研究致密的Ｓｉｃ－ＡＩＮ－Ｙ２Ｏ３复相陶瓷的氧化行为后发现，陶瓷材料的表面在空气中氧化的反应物随着温度的高低而变化。８００℃、２０ｈ氧化试验后，试样表面无任何变化；１１００℃氧化２０ｈ，表面形成了极少量的ＳｉＯ２，但两者均无增重，１２５０℃和１３２０℃氧化３０ｈ后，试样的重量和表面发生较明显的变化，形成了ＳｉＯ２与ａ－Ａｌ２Ｏ３；１３７０℃氧化试验３０ｈ后，陶瓷表面的氧化产物ＳＩＯ２与ａ－Ａｌ２     

The Research of Anti-Wear Properties of Organomolybdenum Compounds in the Engine Oils

A four-ball tester was used to evaluate the anti-wear performance of three kinds of organomolybdemun compounds in the engine oils, i. e., molybdenum dialkyldithiophosphate (MoDDP), molybdenum dialkyldithiocarbamate ( MoDTC), and sulphur and phosphorus freeorganomolybdeum (Molybdate). The results indicate that a low concentration of MoDDP doesn' t improve the anti-wear properties of the commercial engine oils, but a high concentration of MoDDP can obviously improve the anti-wear properties and the load-carrying capacity of the engine oils. MoDTC doesn' t improve the antiwear properties of the engine oils, but worsens the anti-wear properties of the oils. Signifi can timprove ment of frictional and wear characteristics is obtained with Molybdate added in the commercial engine oils and the formulated oils.     

Effect of Permeable Crystalline Material on Steel Reinforcement Corrosion of Concrete

Permeable crystalline materialcan permeate into pores and cracks of concrete and catalyze the reaction between Ca(OH) 2and unhydrated cement to generate a great quantity needle non-soluble crystals, which can stop up the pores and cracks of concrete, and increase the impermeability of concrete. This paper reported the results of a study conducted to evaluate steel reinforcement corrosion of concrete specimens uncoated and coated with permeable crystalline material as well as mixed with the permeable crystalline material. The properties evaluated for corrosion test were water impermeability, water absorption, compressive strength and potential. The results of water impermeability, water absorption, compressive strength clearly showed that the permeable crystalline material could prohibit water, any soluble salts and moisture from penetrating the concrete to cause corrosion, leaking, and other problems, and it did increase the compressive strength, which was favorable for protection of corrosion of reinforcing steel. Moreover, it was concluded from the potential-time curve that the steel reinforcement of uncoated specimen was in the state of activation whereas that of other specimens coated and mixed with the permeable crystalline material was in the state of inactivation. Above all, it was indicated that the permeable crystalline materialis very effective to protect the steel reinforcement of concrete from corrosion.     

The Research and Application About "Dry Peeling Off" Technology for Airplane Surface Paint Layer

In this paper, the principle of spurting take off lacquer were introduced; and with orthogonal method the unsaturate polyester was prepared ;it was easy to peel airplane paint layer off with this material and equipment.     

Quality Study of Honeycomb Core Shaping Without Wax Stabilization

Sandwich panels utilizing honeycomb cores result in lightweight, high-strength units that are very rigid. Indeed, they give honeycomb panels the best strength-to-weight ratio of any construction type available. Conventionally, the wax is poured into the cell of the core to strengthen the structure and prevent the core from being crushed during milling. Much time and labor is required to wax, mill, and clean the cores. In this study, the process of pouring wax into the core was skipped. In other words, the cutter directly milled the core. Experiments showed that the compressive strength of the core produced without wax stabilization was only 3% lower than that of cores produced using the traditional method. In addition, the drum peel strengths of cores produced without wax stabilization were 38.4% higher than cores produced using the traditional method, in which residual wax seriously polluted the adhesive. It was also found that eliminating the wax process can reduce costs.     

Certification Becomes Important for the I Quality; and Safety Supervision of the Chinese Liquor Sector

The end of 2007, over 200 unit products of more than 80 Chinese firms have passed the quality grade certification for liquor products. These products involve distilled spirits, beer, wine, yellow wine, fruit syrup wine and others, and cover over 80% of the national top-branded liquor products.……     

Deposition and Coating Properties on CVD Tungsten

Surface characterization and microstructure studies are performed on chemical vapor deposited (CVD) tungsten coating. There is about 2 μm thickness diffusion layer of tungsten in the molybdenum substrate. The thermal shock test shows tungsten coating has good adhesion with molybdenum substrate, but the elements of oxygen and carbon in the tungsten coating have the bad affection to the adhesion. The result of high-temperature diffusion experiment is the diffusion rate from molybdenum substrate to tungsten coating is faster.     

Analysis of marine hydrobiont lipid extracts as possible cryoprotective agents

We studied a combined effect of the cryoprotectants both of lipid and carbohydrate origin at the presence of DMSO or without it on cell viability and the RNA synthesis in the embryonic mollusc and echinoderm cell cultures obtained at different developmental stages. Cryoprotective properties of exogenous lipids correlated with their thermotropic behavior. Lipid extracts from marine hydrobiontes, which thermal transitions are characterized by relatively small part of calorimetric thermogram area lying at temperatures above 0 °C (6–18%), were found to possess a considerable cryoprotective activity. The results are discussed in relation to the prediction of the cryoprotective activity of lipid extracts for marine animal cells. In addition, it was found that marine invertebrate cells can be cryopreserved without DMSO at the presence of trehalose and lipid extracts of some marine hydrobiontes.     

In-process thermal treatment of polylactic acid in fused deposition modelling

Polylactic acid (PLA) is one of the most widely used open source fused filament fabrication materials due to its ease of extrusion, biodegradability, and mechanical strength. The mechanical strength of PLA largely depends on the proper growth of its semi-crystalline structure, which can be severely impaired by a low rate of crystallization, particularly in open source printers. This can be further aggravated by the non-uniform thermal distribution of heat that causes improper curing among the extruded beads of the printing material. As a result, PLA printed on open source printers does not achieve the best mechanical properties. This research, for the first time, proposes an additive-free solution implemented through a detailed set of experimentation to improve the curing rate through in-process temperature variations to cure the joints among the beads. Scanning electron microscopy (SEM), differential scanning calorimetry (DSC) and Fourier transform infrared (FTIR) spectroscopy is used to confirm the improvements in the bead joints. This work is conducted in two phases of experiments. In the first phase, a full factorial ANOVA is used to investigate various process parameters and the important variables are used in the second phase to print test specimens in four different sets.     

Low-Temperature Properties of Silver

Pure silver is used extensively in the preparation of high-temperature superconductor wires, tapes, films, and other configurations in which the silver not only shields the superconducting material from the surrounding materials, but also provides a degree of flexibility and strain relief, as well as stabilization and low-resistance electrical contact. Silver is relatively expensive, but at this stage of superconductor development, its unique combination of properties seems to offer the only reasonable means of achieving usable lengths of conductor. In this role, the low-temperature physical (electrical, thermal, magnetic, optical) and mechanical properties of the silver all become important. Here we present a collection of properties data extracted from the cryogenic literature and, to the extent possible, selected for reliability.     

Early ironwork in Biscay: Survey,excavation, experimentation and materials characterization. An integral study of the mountainside ironworks (ferrerías de monte or “haizeolak”)

ABSTRACT

The production of iron in Biscay (Basque Country, Spain) has been a hallmark of this territory of the North of the Iberian Peninsula throughout its history. The Archaeology team of the Basque Country Mining Museum has spent 13 years, so far, studying the origins of this activity through the evidences left at the old pre-hydraulic iron production workshops known as mountainside ironworks (ferrerías de monte) or haizeolak. It has catalogued 170 archaeometallurgical sites of this type in Biscay, and the archeological excavation of some of them has led to the knowledge of the different stages of the production process that took place in these workshops. The team has also experimentally reproduced the work carried out in a mountainside ironworks from the High Middle Ages, and it has currently started the characterization process of this type of activity through the study of the collected materials.