MAGNETIC PROPERTIES OF Nd_2(Fe_(1-x)M_x)_(14)B(M=C,Si)ALLOYS

The magnetic properties of Nd_2(Fe_(1-x)M_x)_(14)B(M=C and Si) compounds have been investi-gated.Substituting Fe by small amount of metalloid C and Si atoms,the compounds are intetragonal structure and have uniaxial anisotropy.The substitution of C for part of Fe de-creases the Curie temperature of the compounds and the intrinsic coercivity of bond samples atlow temperature.The replacement of Fe by Si makes the Curie temperature increase with amaximum at the vicinity of x=0.15.When the range of the content of Si is 0≤x≤0.10,thecoercivity distinctly increases at room temperature.from 62.7 kA/m at x=0 to138.7kA/m at x=0.06,where the residual magnetization has a maximum:in the mean timethe saturation magnetization decreases only by a small amount.     

磁控溅射制备BiFeO_3/Sr_(1-x)La_xFe_(12-x)Co_xO_(19)复合薄膜及其磁性能研究

室温下采用射频磁控溅射法,在P型100Si基衬底上分别制备了BiFeO_3(BFO)和Sr_(1-x)La_xFe_(12-x)Co_xO_(19)(x=0~0.3)的单层及2-2型BiFeO_3/Sr_(1-x)La_xFe_(12-x)Co_xO_(19)叠层式复合结构薄膜。采用X射线衍射(XRD)、扫描电子显微镜(SEM)和材料综合物性测试系统(PPMS)对薄膜样品的微观结构、表面形貌以及磁学性能进行了测试分析。结果表明,随着x的增加,Sr_(1-x)La_xFe_(12-x)Co_xO_(19)单层膜的矫顽力先少量减小后增加,剩磁比起初不变然后递增,而剩余磁化强度一直减小。当x=0.3时,其矫顽力和剩磁比均达到最大值,分别为491 kA/m和0.69,而剩余磁化强度达到最小值为50(A·m~2)/kg;复合薄膜的矫顽力及剩磁比先增加后减小,剩余磁化强度一直减小,在x=0.2矫顽力和剩磁比均达到最大值,分别为425 kA/m和0.73,当x=0.3时矫顽力和剩磁比明显减弱,分别为171 kA/m和0.4,此时剩余磁化强度为最小值19(A·m~2)/kg。     

Fe含量对高温稀土永磁Sm(CobalFexCu0.1Zr0.03)7.5 (x=0.09～0.21)磁性能的影响

采用粉末冶金工艺制备了高温稀土永磁Sm(CobalFexCu0.1Zr0.03)7.5 (x=0.09～0.21),研究了Fe含量对磁体磁性能的影响.结果表明:随着Fe含量的增加,剩磁Br和最大磁能积(BH)max逐渐增加,在x=0.21时获得最大值,分别为0.96 T和176.7 kJ/m3;内禀矫顽力Hci先增加后降低,在x=0.15时获得峰值2276.6 kA/m.最佳工艺制备(x=0.15)的磁体温度稳定性良好,B-H退磁曲线在温度为500 ℃时保持为直线;内禀矫顽力温度系数β为-0.16%/℃,最高使用温度(OT)max达到533 ℃.     

球磨制备的La(Fe1-xCox)11.2Si1.8化合物的相形成和磁热效应

将LaSi母合金和元素粉末混合,利用球磨工艺制备了La(Fe1-xCox)11.2Si1.8 (x = 0, 0.02, 0.04, 0.06)样品。在1423K的温度下烧结30分钟,然后放入水中快速冷却,就可以获得几乎为NaZn13型结构的单相化合物。磁性质的研究表明,样品的居里温度随着Co含量从x=0到x=0.06而提高,但是磁熵变减小。在0-1.5T的外加磁场下,LaFe11.2Si1.8合金在其居里温度附近的最大磁熵变达到的6.5 J/kg,而x=0.06的样品的最大磁熵变约为2.1 J/kg K。另外,球磨制备的样品还呈现了二级磁相变的特点,这对于磁热效应的应用非常有意义。     

Mn_(1.35)Fe_(0.65)P_(0.45)Si_(0.55)B_x合金的磁热效应

对Mn1.35Fe0.65P0.45Si0.55Bx(x=0,0.01,0.02,0.03,0.04)合金的结构和磁热效应(MCE)进行了研究。XRD分析结果表明:Mn1.35Fe0.65P0.45Si0.55Bx(x=0,0.01,0.02,0.03,0.04)的合金均为Fe2P型六角结构,空间群为P6-2 m,并随着B元素(原子分数)的增加,晶格常数a增大,c/a减小,晶胞体积V略有减小。磁性测量表明:随着B元素(原子分数)的增加,Curie温度(Tc)从228K升高到315K,热滞(ΔThys)变化不大。0~1.5T外磁场下最大磁熵变(-ΔSmax M)下降,分别为3.6,2.5,2.0,1.7,1.9J/(kg·K)。     

关键工艺参量对Sm(Co_(0.715)Fe_(0.20)Cu_(0.06)Zr_(0.025))_z磁体磁性能的影响

采用真空感应熔炼获得了名义成分为Sm(Co0.715Fe0.20Cu0.06Zr0.025)7和Sm(Co0.715Fe0.20Cu0.06Zr0.025)9.5两种铸锭,经过破碎球磨后以不同的比例混粉制备不同z值的样品。然后使用不同的烧结温度、固溶温度以及时效工艺,对z值分别为7.86、7.63和7.41的三种成分的磁体进行了处理。结果表明,z值为7.86的磁体在室温时拥有最佳磁性能,剩磁、矫顽力和磁能积分别达到1.13T、2 387.32kA/m和226.40kJ/m3。在300℃时其剩磁为1.013T,矫顽力为831.59kA/m,最大磁能积为164.17kJ/m3,磁体综合磁性能良好。     

Sm(CobalFexCu0.088Zr0.025)7.5(x=0-0.30)烧结永磁体的磁性及其高温特性

用粉末冶金艺术制备了Sm(CobalFexCu0.088Zr0.25)7.5(x=0-0.30)烧结磁体，对Fe含量x对磁体的磁性及其高温特性的影响进行了系统研究，随Fe含量的增加，最大磁取积（BH）max和剩磁Br逐渐增加，分别在 x为0．21和0．27时达到了最大值205kJ/m^3和1.055T,然后迅速下降，当x≥0.24时，磁体中开始有FeCo软磁性相析出，破坏了磁体的永磁特性。Fe含量对磁体高温稳定性有巨大的影响，在Fe含量x=0.21时，磁体内禀矫顽力温度系数β为－0.235K,当x=0.07时，β降至－0.14%K(293-723K),制备出有很好的高温稳定性的永磁材料Sm(CbalFe0.07Cu0.088Zr0.025)7.5,在723K时其磁性能力：Br=0.725T,bHc=517kA/m,Hc=764kA/m,(BH)max=95kJ/m^3,B-H退磁曲线保持为直线。     

Pt缓冲层厚度对FePt薄膜合金相转变和磁性能的影响

利用磁控溅射法制备了具有Pt缓冲层的[FePt]50多层膜.通过x射线衍射(XRD)分析和磁性测量研究了不同缓冲层厚度对样品微结构演变和磁性能的影响.结果表明,随着Pt缓冲层厚度(t≤8.6 nm)的增加,薄膜合金的有序化温度明显降低,晶粒尺寸逐渐减小FePt薄膜样品点阵常数c/a的比值逐渐减小,有序度参数S逐渐增大;同时样品的矫顽力也随着缓冲层厚度的增加而增大,在425℃退火的样品,其矫顽力由缓冲层厚度t=0时的398 kA/m增加到t=8.6nm时的523 kA/m(接近无缓冲层样品在500℃退火的值),平均变化率为14.53 kA·m-1/nm,有效地降低了样品的退火温度;与此同时,剩磁比逐渐减小,从0.68减少到0.56.     

Nd含量对纳米晶Nd_xFe_(94-x)B_6合金磁性能的影响

用X射线衍射(XRD)、差示扫描量热分析(DSC)、高分辨扫描电镜(HRSEM)和振动样品磁强计(VSM)等研究了Nd含量对快淬纳米晶NdxFe94-xB6(x=11.0-16.8)合金的组织结构、磁性能、交换耦合作用和矫顽力的影响.结果表明,22 m/s(甩带速度)快淬带在最佳退火条件下,合金带的内禀矫顽力Hci由x=11.0的601.. kA/m单调升高到x=16.8的1277.3 kA/m;相反,剩余磁极化强度Jr由x=11.0的1.047 T单调下降到x=16.8的0.721 T,最大磁能积(BH)max随Nd含量增加先升高后下降Nd11.8Fe82.2B6金带的综合性能最好:Jr=0.992 T,Hci=727.9 kA/m,(BH)max=137.2 kJ/m3.Nd2Fe14B晶粒之间的交换耦合作用随Nd含量增加而降低,但x=16.8的合金带仍具有较强的交换耦合作用.矫顽力主要由钉扎场决定.最佳退火后,合金薄带的晶粒尺寸随Nd含量增加无明显变化.针对不同Nd含量的合金,建立了一个组织模型,利用该模型很好地解释了Nd含量对磁性能及交换耦合作用的影响机制.     

Sm(Co_(bal)Fe_xCu_(0.088)Zr_(0.025))_(7.5)(x=0-0.30)烧结永磁体的磁性及其高温特性

用粉末冶金工艺制备了Sm（CobalFexCu0.88Zr0.025）7.5（x=0-0.30）烧结磁体,对Fe含量x对磁体的磁性及其高温特性的影响进行了系统研究.随Fe含量的增加,最大磁能积（BH）max和剩磁Br逐渐增加,分别在x为0.21和0.27时达到了最大值205kJ/m3和1.055T,然后迅速下降.当x≥0.24时,磁体中开始有FeCo软磁性相析出,破坏了磁体的永磁特性.Fe含量对磁体高温稳定性有巨大的影响,在Fe含量x=0.21时,磁体内禀矫顽力温度系数β为-0.23％/K;当x=0.07时,β降至-0.14％/K（293-723K）.制备出有很好的高温稳定性的永磁材料Sm（CobalFe0.07Cu0.088Zr0.025)7.5,在723K时其磁性能为:Br=0.725T,bHc=517kA/m,iHc=764kA/m,（BH）max=95 kJ/m3,B-H退磁曲线保持为直线.     

Crystallization Behavior of Metallic GlassCo_（65．1）Fe_（4．7）Ni_（4．6）Si_（10．2）B_（15．4）

ＣｒｙｓｔａｌｌｉｚａｔｉｏｎＢｅｈａｖｉｏｒｏｆＭｅｔａｌｌｉｃＧｌａｓｓＣｏ＿（６５．１）Ｆｅ＿（４．７）Ｎｉ＿（４．６）Ｓｉ＿（１０．２）Ｂ＿（１５．４）ＬｉＺｏｎｇｑｕａｎ；ＱｉｎＹｏｎｇａｎｄＨｅＹｉｚｈｅｎ（李宗全），（秦勇）（何怡贞）（...     

机械合金化法制备的Mn15Bi34Te51和La15Bi34Te51热电材料

用机械合金化法制备了Mn15Bi34Te51和La15Bi34Te51合金，XRD分析表明Mn15Bi34Te51和La15Bi34Te51分别在真空球磨150h和100h后实现合金化，La15Bi34Te51在真空球磨150h后形成了纳米结构的合金，镧原子的加入有助于Bi2Te3基合金的晶粒细化及非晶化。对La15Bi34Te51合金的XRD结构分析表明镧原子有可能进入了Bi2Te3层状结构的Te-Te原子层间。La15Bi34Te51合金Seebeck系数的测量表明当晶粒尺寸减小到纳米尺寸时，载流子散射机制有可能发生改变，导致了Seebeck系数的大幅上升。     

Fe_(4.5)Co_(67.5)Nb_(0.5)Mn_(0.5)Si_(12)B_(15)丝材中的巨磁阻抗效应

报道了淬火态Fe45Co675Nb05Mn05Si12B15丝中GMI效应,发现淬火态非晶丝GMI(Z)=|(Z(65Oe)-Z(0))/Z(0)|可高达73%。我们也对简单退火下对Fe45Co675Nb05Mn05Si12B15钴基材料中GMI效应的影响也进行了深入细致的研究,发现GMI峰值随退火温度从300℃增加到450℃而先上升,达到一个最大值,然后下降。350℃退火的效果较佳。同时发现低于1MHz时,淬火态对应的GMI效应优于退火态的值,而高于1MHz时,350℃退火材料的GMI(Z)值相应的要高。     

Mg61Cu28Gd11和(Mg0.61Cu0.28Gd0.11)99.5Sb0.5非晶合金的晶化动力学和腐蚀行为（英文）

研究0.5%(摩尔分数)Sb的引入对Mg61Cu28Gd11块体非晶合金性能的影响。利用差热扫描量热仪测试样品的晶化动力学。结果表明:在等时加热的过程中,非晶合金的玻璃转变温度、起始晶化和峰值晶化温度都表现出对加热速率强的依赖性。基于Oawza方法可以确定非晶合金的起始晶化和峰值晶化激活能。Vogel-Fulcher-Tamman公式分析表明:含Sb元素的非晶合金具有更高的强度系数和更长的延迟时间。采用电化学极化和失重测试方法研究2种玻璃合金的腐蚀行为。与基体非晶合金相比,添加微量Sb降低了非晶合金的在含Cl-的碱性溶液中的钝化电流密度和腐蚀速率,表现出相比基体合金更为优越的耐蚀性。最后基于"点缺陷模型"进一步分析微量Sb元素对基体合金耐蚀性能的影响机理。     

Formation and Structural Evolution of Fe_(72.5)B_(15.6)Si_(7.8)Nb_(1.7)Zr_(1.7)Cu_(0.7) Nanocrystalline Alloy

A 2.5-mm Fe_(72.5)B_(15.6)Si_(7.8)Nb_(1.7)Zr_(1.7)Cu_(0.7) glassy rod was successfully fabricated using copper mold casting.The introduction of Cu resulted in the formation of large quantities of a-Fe nanoparticles embedded in the glassy matrix after isothermal annealing.The Fe_(72.5)B_(15.6)Si_(7.8)Nb_(1.7)Zr_(1.7)Cu_(0.7) nanocrystalline alloy exhibited high saturation magnetization(～1.26 T) and a low coercive force(～0.8 A/m) after annealing at 833 K for 15 min due to the precipitation of ～15-nm-sized a-Fe nanoparticles in the glassy matrix.The structural evolution of the FeBSiNbZrCu amorphous alloy during the annealing process was discussed using a dual-cluster model.     

STRUCTURAL RELAXATION OF AMORPHOUS ALLOYS Fe_(77.8)Si_(7.5)B_(14.7) AND Fe_(78.5)Si_(8.9)B_(12.6)

<正> 本文用Mossbauer技术结合DTA和电阻分析,对两种非晶态合金(Ⅰ)Fe_(77.8)Si_(7.5)B_(14.7)和(Ⅱ)Fe_(78.5)Si_(8.9)B_(12.6)的结构弛豫进行了研究。 Ⅰ和Ⅱ两种非晶态合金的DTA曲线如图1,晶化开始温度分别为530和500℃,晶化前均出现较长的放热峰,预示其结构弛豫过程中可能发生某种结构变化。     

RESISTIVITY ANOMALY IN METALLIC GLASSES(Fe_(1-x)Co_x)_(78)Si_(9.5)B_(12.5)

用四端引线法测量了4.2K到室温的非晶态(Fe_(1-x)Co_x)_(18)Si_(9.5)B_(12.5)(x=0—1.0)合金的电阻率。结果表明,x=0—1.0的所有样品都出现了电阻率与温度关系的极小值。电阻率极小值温度T_(min)随Co含量x的增加而增加,在x=0.9时出现极大值。在T_(min)温度以下,电阻率与温度关系符合-lnT规律。x=0.5—1.0的样品,电阻率与-lnT关系出现两个斜率。在T_(min)温度以上,约100K以下电阻率符合T~2规律,在约100K以上电阻率则按T~(3/2)规律变化。实验结果表明,约在9.5K和100K温区,电阻率与温度关系可近似表达为:ρ/ρ_(min)=ρ_0+AlnT+BT~2。显现类Kondo型电阻极小。电阻率的T~2关系来源于电子-声子散射。     

退火方式对La_(0.75)Mg_(0.25)Ni_(3.44)Co_(0.2)Al_(0.03)Ti_(0.03)合金的电化学性能影响

为了研究不同退火方式对La0.75Mg0.25Ni3.44Co0.2Al0.03Ti0.03铸态合金的电化学性能影响,设计最终退火温度为1223K,并采用不同保温程序对合金进行退火处理。X射线衍射(XRD)与扫描电镜(SEM)分析一段、两段保温法退火后合金的结构与性能结果表明,铸态及退火后合金由LaNi5,(La,Mg)2(Ni,Co,Al)7相以及少量LaNi2、TiNi3相组成,且退火后合金中(La,Mg)(Ni,Co,Al)3相出现。前者微观组织较后者均匀,并且前者的放电容量、放电效率好于后者。一段保温法更有利于改善合金的循环稳定性。     

非晶合金Fe_(80-x)Cu_xSi_5B_(15)和(Fe_(1-y)Co_y)_(82)Cu_(0.4)Si_(4.4)B_(13.2)的晶化行为

用X射线衍射、吸收和内转换电子发射Mossbauer谱技术,研究了Fe_(80-x)Cu_xSi_5B_(15)和(Fe_(1-y)Co_y)_(82)Cu_(0.4)Si_(4.4)B_(13.2)两系列非晶合金的晶化行为.单辊急冷法制备的非晶带,晶化首先从贴辊面开始,晶化产物为α-Fe相.在Fe_(80)Si_5B_(15)非晶合金中以少量Cu替代Fe可以提高晶化温度.我们的结果表明,过渡金属的含量超过80at.-%,如增加到82at.-%,晶化温度就明显降低.所研究两系列含Si的铁基非晶合金在400—450℃范围内退火2h,都出现α-Fe,Fe_3B和Fe_2B三种晶态相共存状态.退火温度再升高,亚稳相Fe_3B逐渐转变为Fe_2B和α-Fe.     

MAGNETIC PERMEABILITY RELAXATIONS IN AMORPHOUS ALLOYS(Fe_(0.1)Ni_(0.55)Co_(0.55))_(78)Si_8B_(14) AND Fe_(40)Ni_(38)Mo_4B_(18)

在0—300℃间研究非晶(Fe_(0.1)Ni_(0.35)Co_(0.55))_(78)si_(?)B_(14)和Fe_(40)Ni_(38)Mo_4B_(18)合金的可逆磁导率等温弛豫行为.给出等时弛豫谱,观察到三个弛豫峰.计算弛豫时间的分布和最可几激活能.初步考查Curie温度以上的退火和较慢冷却对弛豫动力学的影响.对这两种成分截然不同的合金观察到十分相似的动力学行为,表明磁寻率弛豫主要是由基本结构缺陷的局域运动引起的,成分的影响则十分次要.