pH 值和表面活性剂对硅溶胶 CMP 抛光液的影响

目的研究pH值以及表面活性剂种类对CMP抛光液稳定性及抛光性能的影响。方法向硅溶胶中加入酸性或碱性pH值调节剂,配制不同pH值的CMP抛光液;通过添加不同类型的表面活性剂,研究表面活性剂对抛光液的稳定机理。结果硅溶胶CMP抛光液pH值为9.5时,加入非离子表面活性剂,抛光90 min后,铝合金表面粗糙度降低了55.4%,光亮度增加了131%,抛光质量较好。结论弱碱环境下,抛光液的稳定性和抛光性能优良,非离子表面活性剂有利于CMP抛光液的稳定性。     

蓝宝石衬底CMP中氧化硅磨粒粒度分布对抛光液体系性能影响研究

目的 化学机械抛光(CMP)包含化学腐蚀和机械磨削两方面,抛光液pH、磨粒粒径和浓度等因素均会不同程度地影响其化学腐蚀和机械磨削能力,从而影响抛光效果。方法 采用30~150 nm连续粒径磨粒抛光液、120 nm均一粒径磨粒抛光液、50 nm和120 nm配制而成的混合粒径磨粒抛光液,分别对蓝宝石衬底晶圆进行循环CMP实验,研究CMP过程中抛光液体系的变化。结果 连续粒径磨粒抛光液中磨粒大规模团聚,满足高材料去除率的抛光时间仅有4 h,抛光后的晶圆表面粗糙度为0.665 nm;均一粒径磨粒抛光液中磨粒稳定,无团聚现象,抛光9 h内材料去除率较连续粒径磨粒抛光液高94.7%,能至少维持高材料去除率18 h,抛光后的晶圆表面粗糙度为0.204 nm;混合粒径磨粒抛光液初始状态下磨粒稳定性较高,抛光9 h内材料去除率较连续粒径磨粒抛光液高114.8%,之后磨粒出现小规模团聚现象,后9 h材料去除率仅为均一粒径磨粒抛光液的59.6%,18 h内材料去除率仅为均一粒径磨粒抛光液的87.7%,但抛光后的晶圆表面粗糙度为0.151 nm。结论 一定时间内追求较高的材料去除率和较好的晶圆表面粗糙度选用混合粒径磨粒抛光液,但需要长时间CMP使用均一粒径磨粒抛光液更适合,因此,在工业生产中需要根据生产要求配合使用混合粒径磨粒抛光液和均一粒径磨粒抛光液。     

硒化锌晶体精细雾化抛光液及去除机理研究

目的配制适合硒化锌雾化施液化学机械抛光的最优抛光液。方法选取氧化铝磨粒、pH调节剂四甲基氢氧化铵、氧化剂过氧化氢、表面活性剂聚乙烯吡咯烷酮为主要活性成分,以材料去除速率和表面粗糙度为评价指标,通过正交试验对硒化锌晶体进行精细雾化抛光,分析材料去除机理,并与传统抛光对比。结果氧化铝质量分数为9%、pH值为11、过氧化氢含量为3.5%、聚乙烯吡咯烷酮含量为0.75%时,材料去除率较高,为923.67 nm/min,同时表面粗糙度较小,为2.13 nm。在相同工况条件下,传统抛光材料的去除率和表面粗糙度分别为965.53 nm/min和2.27 nm。结论抛光液各组分对试验结果影响最大的为氧化铝磨粒,然后依次为氧化剂、pH值、表面活性剂。精细雾化抛光效果与传统抛光相近,但抛光液用量仅为后者的1/8。     

用碱性抛光液化学机械抛光304不锈钢片研究

为提高化学机械抛光的加工效果,我们研究了pH值、氧化剂种类和氧化剂含量对材料去除率和表面粗糙度的影响。结果表明:不同氧化剂的抛光液在各自的最佳pH值时达到最大的材料去除率,分别为181 nm/min（H₂O₂抛光液,pH=9）,177 nm/min（Cr₂O₃抛光液,pH=11）,172 nm/min（Na₂Cr₂O₇抛光液,pH=11）和147 nm/min（NaClO抛光液,pH=13）;抛光液中氧化剂含量、pH值对抛光后不锈钢的表面粗糙度影响较小。其中,材料去除率较高的H₂O₂和Cr₂O₃可作为304不锈钢化学机械抛光碱性抛光液的氧化剂。      

抛光液pH值、温度和浓度对蓝宝石抛光效率的影响

目的研究抛光液pH值、温度和浓度对化学机械抛光蓝宝石去除率的影响,以提高抛光效率。方法采用CP4单面抛光试验机对直径为50.8 mm C向蓝宝石晶元进行化学机械抛光,通过电子分析天平对蓝宝石抛光过程中的材料去除率进行了分析,采用原子力显微镜(AFM)对蓝宝石晶元抛光前后的表面形貌和粗糙度(Ra)进行了评价。结果蓝宝石在化学机械抛光过程中的材料去除率均随抛光液pH值和温度的升高呈先增大后减小趋势。当抛光原液与去离子水按1:1的体积比混合配制抛光液,KOH调节pH值为12.2,水浴加热抛光液35℃时,蓝宝石抛光的材料去除率(MRR)达到1.119μm/h,Ra为0.101 nm。结论随着pH的增大,化学作用逐渐增强,而机械作用逐渐减弱,在pH为12.2的时候能达到平衡点,此时的MRR最佳;随着温度的升高,化学作用逐渐增强,而机械作用保持不变,抛光液温度为35~40℃时,化学作用与机械作用达到平衡,MRR最佳,当温度高于40℃后,抛光液浓度明显增大,而过高的浓度会导致MRR的减小。抛光液的相关性能优化后,化学机械抛光蓝宝石的MRR较优化前提高了71.4%。     

新型高硬度硅溶胶的制备及其在化学机械抛光中的应用

目的 制造新型高硬度硅溶胶,满足硅晶圆化学机械抛光(CMP)既要高抛光速率,又要高抛光质量的要求.方法 利用恒液面聚合生长法制备硅溶胶的工艺特点,通过在合成过程中加入pH值稳定剂异丙醇胺,提升硅溶胶的硬度和稳定性.采用透射扫描电子显微镜、红外光谱等对硅溶胶的成分、形貌等胶体的性质进行表征和分析.结果 通过设计对比实验,发现新型高硬度硅溶胶抛光时的pH值稳定性较普通市售硅溶胶有很大提升,3组新型高硬度硅溶胶平均抛光速率分别为1.580、1.544、1.582μm/min,较普通市售硅溶胶分别提升了17.41％、17.91％、18.25％.新型高硬度硅溶胶抛光后,硅晶圆的平均表面粗糙度只有0.157 nm,最低达到了0.132 nm,而市售普通硅溶胶抛光后的硅晶圆平均表面粗糙度为0.216 nm.同时,通过检测抛光前后硅溶胶粒径和形貌的变化,发现新型高硬度硅溶胶均优于普通市售硅溶胶.结论 新型高硬度硅溶胶作为抛光的研磨料在去除速率、表面粗糙度等方面都有一定的优势,验证了新型高硬度硅溶胶作为抛光研磨料的实用价值.     

A向蓝宝石化学机械抛光研究

以纳米氧化铝为磨料对A向蓝宝石进行化学机械抛光,实验中考察了磨料浓度、磨料粒径、抛光时间、抛光压力以及NH₄F浓度等因素对A向蓝宝石的材料去除速率和表面粗糙度的影响。利用原子力显微镜（AFM）检测抛光后A向蓝宝石的表面粗糙度,系统分析抛光过程中各影响因素,优化实验条件,结果表明:当抛光液中磨料质量分数为1%、磨料粒度尺寸为50nm、抛光时间为40 min、抛光压力为16.39 kPa、NH₄F质量分数为0.6%、pH=4.0时,抛光后材料去除速率（MRR）为18.2 nm/min,表面粗糙度值R_a 22.3 nm,抛光效果最好。      

二氧化铈抛光液化学机械抛光微晶玻璃的机理及优化

以纳米CeO₂为磨料自制抛光液,研究磨料质量分数、pH值、抛光液流量、抛光盘转速、表面活性剂种类和氟化铵质量分数等因素对微晶玻璃化学机械抛光的影响,分析总结CeO₂在微晶玻璃化学机械抛光中的作用机理,利用原子力显微镜（AFM）检测微晶玻璃抛光后的表面粗糙度。结果表明:当CeO₂质量分数为3%、抛光液流量为25mL/min、抛光盘转速为100r/min、pH=8.0、十二烷基硫酸钠质量分数为0.01%,氟化铵质量分数为0.7%时,抛光后微晶玻璃表面粗糙度（R_a）最低为0.72nm,材料去除速率达到180.91nm/min。      

GaN晶片芬顿反应化学机械抛光液组分优化

针对芬顿反应CMP抛光GaN晶片的抛光液,开展以表面质量为评价指标的参数优化试验,找出抛光液组分的最优配比。结果表明:当H₂O₂质量分数为7.5%时,GaN晶片加工表面效果最优,表面粗糙度达到3.2 nm;催化剂能有效调节芬顿反应的速率,对比液体催化剂FeSO₄溶液和固体催化剂Fe₃O₄粉末,固体催化剂Fe₃O₄粉末能在溶液中持续电离Fe2+,使芬顿反应能在整个加工过程中持续作用。当Fe₃O₄粉末粒径为20 nm时,抛光效果最佳,表面粗糙度达到3.0 nm;对比氧化铝、氧化铈、硅溶胶磨料,硅溶胶磨料抛光的表面效果最佳,晶片表面粗糙度达到3.3 nm;当硅溶胶磨料质量分数为20.0%,磨料粒径为60 nm时,抛光后晶片表面粗糙度达到1.5 nm。抛光液组分优化后,采用最优的抛光液组分参数抛光GaN晶片,其能获得表面粗糙度为0.9 nm的光滑表面。      

CMP抛光半导体晶片中抛光液的研究

本文分析了化学机械抛光(CMP)半导体晶片过程中抛光液的重要作用,总结了抛光液的组成及其化学性能(氧化剂、磨料及pH值等)和物理性能(流速、粘性及温度)对抛光效果的影响规律,研究发现:酸性抛光液常用于抛光金属材料,pH最优值为4,碱性抛光液常用于抛光非金属材料,pH最优值为10～11.5;氧化剂能有效提高金属材料的抛光效率和表面平整度;磨料的种类、浓度及尺寸会影响抛光效果;分散剂有助于保持抛光液的稳定性;抛光初始阶段宜采用较低流速,然后逐渐提高;抛光液的粘性会影响晶片与抛光垫之间的接触模式、抛光液的均布、流动及加工表面的化学反应;抛光液温度的升高有助于提高抛光效率.最后本文指出了抛光液循环使用的重要意义及常用方法.     

Electrochemical behavior and polishing properties of silicon wafer in alkaline slurry with abrasive CeO2

The electrochemical behavior of silicon wafer in alkaline slurry with nano-sized CeO2 abrasive was investigated. The variations of corrosion potential （φcorr） and corrosion current density （Jcorr） of the P-type （100） silicon wafer with the slurry pH value and the concentration of abrasive CeO2 were studied by polarization curve technologies. The dependence of the polishing rate on the pH and the concentration of CeO2 in slurries during chemical mechanical polishing（CMP） were also studied. It is discovered that there is a large change of φcorr and Jcorr when slurry pH is altered and the Jcorr reaches the maximum （1.306 μA/cm^2） at pH 10.5 when the material removal rate（MRR） comes to the fastest value. The Jcorr increases gradually from 0.994 μA/cm^2 with 1% CeO2 to 1.304 μA/cm^2 with 3% CeO2 and reaches a plateau with the further increase of CeO2 concentration. There is a considerable MRR in the slurry with 3% CeO/at pH 10.5. The coherence between Jcorr and MRR elucidates that the research on the electrochemical behavior of silicon wafers in the alkaline slurry could offer theoretic guidance on silicon polishing rate and ensure to adjust optimal components of slurry.     

Mechano-chemical polishing of silicon wafers

Rapid progress in recent IC fabrication industry has increased the demand of tight specification of non-uniformity (NU) and surface polishing in silicon wafer planarization. Chemical–mechanical polishing (CMP) is currently the most popular method for IC wafer planarization. However, the sub-surface damage problem caused by hard abrasives and chemical waste problem of CMP have decreased the throughput and increased the cost of IC fabrication. This study is to investigate the mechano-chemical polishing (MCP) of silicon wafers by slurry of soft abrasives, BaCO₃ and through experiments to verify that the solid phase chemical reaction (SPCR) is the main reaction process involved in MCP. A planarization mechanism with compliance has been designed and tested through MCP experiments. Experimental results of MCP of silicon wafers have achieved the average of surface roughness improvement ratio (SRIR) to 99% and the surface roughness R_a=0.633 nm measured by atomic force microscope (AFM). The material removal rate (MRR) has been calculated and the significant influence of slurry weight percent and polishing pressure have been found. The NU has also been estimated for evaluation of MCP parameters. The sub-surface damage of silicon wafer has not yet been found in experimental results and hence the MCP process of silicon wafers has been verified to become a green or environment-friendly technology of silicon wafer planarization.     

α-Al2O3纳米粒子抛光浆料稳定性及其对蓝宝石抛光性能的影响

目的制备分散稳定性良好的α-Al2O3纳米粒子抛光浆料,提高对蓝宝石的化学机械抛光性能。方法将α-Al2O3分散在硅溶胶、氧化铈溶胶、水等不同分散介质中,于不同pH值、不同硅溶胶浓度及硅溶胶粒径等条件下制备出α-Al2O3纳米粒子的抛光浆料,考察抛光浆料的稳定性及抛光浆料对蓝宝石化学机械抛光性能的影响。采用Zeta电位仪测量抛光浆料中α-Al2O3的电势,进而对其分散稳定性进行分析。采用原子力显微镜(AFM)和分析天平分别对蓝宝石表面粗糙度(Ra)和材料去除速率(MRR)进行评价。结果分散介质为硅溶胶时,抛光浆料的稳定性及对蓝宝石的抛光性能较好。当抛光浆料pH值为10时,其分散稳定性较好,且化学腐蚀与机械研磨达到动态平衡,抛光浆料对蓝宝石的抛光性能较好。随着α-Al2O3浓度的增大,浆料的抛光性能呈现先增加后降低的趋势,当α-Al2O3的质量分数为10.0%时,抛光浆料对蓝宝石的抛光性能较好。当硅溶胶的质量分数为0.02%时,抛光浆料的分散稳定性及对蓝宝石的抛光性能较好。随着硅溶胶粒径的增加,抛光浆料的稳定性及对蓝宝石的抛光性能逐渐变差,所以选择最小粒径5 nm的硅溶胶作分散介质。即在10.0%的α-Al2O3、0.02%粒径为5 nm的硅溶胶、pH值为10等条件下的抛光浆料稳定性较好,该浆料对蓝宝石抛光的材料去除速率为15.16 nm/min,抛光后的表面粗糙度为0.272 nm,满足蓝宝石后续外延工艺要求。结论适宜浓度的硅溶胶能明显改善α-Al2O3抛光浆料的分散稳定性,分散效果明显优于水或氧化铈溶胶作分散介质,且对蓝宝石的抛光性能得到显著提高。     

分散剂对超细CeO2抛光液稳定性的影响

通过对超细CeO2抛光液中Zeta电位及黏度的测定,研究了溶液pH值、分散剂以及分散剂用量等因素对超细CeO2抛光液分散稳定性的影响.结果表明,固相质量分数8％的CeO2抛光液,pH值为4～5,选用非离子表面活性剂异丙醇胺作为分散稳定剂,加入质量分数为0.3％ ～0.4％时,抛光液Zeta电位较高,溶液黏度较低,抛光液...     

紫外光催化辅助SiC抛光过程中化学反应速率的影响

目的为了探究紫外光催化辅助抛光过程中,化学反应速率对SiC化学机械抛光的影响规律。方法通过无光照、光照抛光盘和光照抛光液3种光照方式,研究紫外光催化辅助作用对单晶SiC抛光过程中材料去除率的影响。测量不同条件下光催化反应过程中的氧化还原电位(ORP)值,来表征光催化反应速率,并进行了单晶SiC的紫外光催化辅助抛光实验,考察光催化反应速率对抛光效果的影响规律。结果实验表明,引入紫外光催化辅助作用后,材料去除率提高14%～20%,随着材料去除率的增加,光催化辅助作用对材料去除率的影响程度变小。光照射抛光液方式的材料去除率明显高于光照射抛光盘。不同条件下的抛光结果显示,化学反应速率越快,溶液的ORP值越高,材料去除率越大,表面粗糙度越低。在光照抛光液、H_2O_2体积分数4.5%、TiO_2质量浓度4 g/L、光照强度1500 mW/cm~2、pH=11的条件下,用W0.2的金刚石磨料对SiC抛光120 min后,能够获得表面粗糙度Ra=0.269 nm的光滑表面。结论在单晶SiC的紫外光催化辅助抛光过程中,光催化反应速率越快,溶液ORP值越高,抛光效率越高,表面质量越好。在H_2O_2浓度、TiO_2浓度、光照强度、pH等4个因素中,对抛光效果影响最大的是H_2O_2浓度,光照强度主要影响光催化反应达到稳定的时间。     

紫外光催化辅助Ga面GaN化学机械抛光试验研究

目的 探究在紫外光催化辅助抛光过程中,相关因素对氮化镓晶片Ga面去除率(MRR)及表面粗糙度(Ra)的影响规律,提高单晶氮化镓高效率低损伤的超光滑表面质量。方法 通过结合紫外光与化学机械进行抛光,采用单因素试验方案,对GaN晶片的Ga面进行紫外光催化辅助化学机械抛光试验,比较在无光照、光照抛光盘、光照抛光液3种抛光方式和不同TiO₂浓度、pH值、H₂O₂含量、抛光压力、抛光盘转速和抛光液流条件下的抛光效果。最后通过正交试验进行抛光工艺参数优化,通过测量不同条件下紫外光催化辅助化学机械抛光过程中的MRR值和Ra值,探究GaN晶片Ga面抛光效果。结果在紫外光催化辅助抛光条件下,通过对单因素试验和正交试验的抛光参数进行分析和优化,GaN晶片材料去除率可以达到698.864nm/h,通过白光干涉仪观测可以获得表面粗糙度Ra值为0.430nm的亚纳米级超光滑GaN晶体表面。结论 基于紫外光催化辅助GaN晶片Ga面化学机械抛光试验,紫外光辅助化学机械的复合抛光方式能够促进GaN表面生成物Ga₂O₃